Co30Cr8W1.6C3Ni1.4Si coatings were fabricated on Ti6Al4V alloy using a laser thermal spraying(LTS).The surface and cross-section morphologies,phases and bonding strength of obtained coatings were investigated using sc...Co30Cr8W1.6C3Ni1.4Si coatings were fabricated on Ti6Al4V alloy using a laser thermal spraying(LTS).The surface and cross-section morphologies,phases and bonding strength of obtained coatings were investigated using scanning electronic microscopy(SEM),X-ray diffraction(XRD),and scratch test,respectively.The effects of laser power on the coefficients of friction(COFs)and corrosive-wear behaviors of Co30Cr8W1.6C3Ni1.4Si coatings were investigated using a wear tester in 3.5%NaCl solution,and the electrochemical corrosion performance was analyzed using an electrochemical workstation.The experimental results show that the Co30Cr8W1.6C3Ni1.4Si coating is bonded with the substrate in the metallurgical form,and the bonding strengths of Co30Cr8W1.6C3Ni1.4Si coatings fabricated at the laser power of 1000,1200,and 1400 W are 76.5,56.5,and 55.6 N,respectively.The average COFs of Co30Cr8W1.6C3Ni1.4Si coatings fabricated at the laser power of 1000,1200,and 1400 W are 0.769,0.893,and 0.941,respectively;and the corresponding wear rates are 0.267×105,0.3178×105,and 0.325×105μm3/Nm,respectively,which increases with the increase of laser power,the wear mechanism is primarily abrasive wear.The corrosion potential of Co30Cr8W1.6C3Ni1.4Si coatings fabricated at the laser power of 1000,1200,and 1400 W is-0.05,-0.25,and-0.31 V,respectively,higher than-0.45 V of substrate which enhances the electrochemical corrosion resistance of substrate.展开更多
对生产的96 t 30Cr1Mo1V高中压转子进行超声检测时,发现水口端缺陷。对该缺陷部位解剖后,采用扫描电镜能谱分析手段,确定了该缺陷主要是由钙铝酸盐类夹杂(以Al2O3为主)造成。对夹杂物的来源进行分析,确定了钢水不纯净的主要原因,为后续...对生产的96 t 30Cr1Mo1V高中压转子进行超声检测时,发现水口端缺陷。对该缺陷部位解剖后,采用扫描电镜能谱分析手段,确定了该缺陷主要是由钙铝酸盐类夹杂(以Al2O3为主)造成。对夹杂物的来源进行分析,确定了钢水不纯净的主要原因,为后续同类型钢锭的冶炼工艺改进及过程质量控制提供依据。展开更多
基金Funded by the Key Research and Development Project of Jiangsu Province(BE2016052)。
文摘Co30Cr8W1.6C3Ni1.4Si coatings were fabricated on Ti6Al4V alloy using a laser thermal spraying(LTS).The surface and cross-section morphologies,phases and bonding strength of obtained coatings were investigated using scanning electronic microscopy(SEM),X-ray diffraction(XRD),and scratch test,respectively.The effects of laser power on the coefficients of friction(COFs)and corrosive-wear behaviors of Co30Cr8W1.6C3Ni1.4Si coatings were investigated using a wear tester in 3.5%NaCl solution,and the electrochemical corrosion performance was analyzed using an electrochemical workstation.The experimental results show that the Co30Cr8W1.6C3Ni1.4Si coating is bonded with the substrate in the metallurgical form,and the bonding strengths of Co30Cr8W1.6C3Ni1.4Si coatings fabricated at the laser power of 1000,1200,and 1400 W are 76.5,56.5,and 55.6 N,respectively.The average COFs of Co30Cr8W1.6C3Ni1.4Si coatings fabricated at the laser power of 1000,1200,and 1400 W are 0.769,0.893,and 0.941,respectively;and the corresponding wear rates are 0.267×105,0.3178×105,and 0.325×105μm3/Nm,respectively,which increases with the increase of laser power,the wear mechanism is primarily abrasive wear.The corrosion potential of Co30Cr8W1.6C3Ni1.4Si coatings fabricated at the laser power of 1000,1200,and 1400 W is-0.05,-0.25,and-0.31 V,respectively,higher than-0.45 V of substrate which enhances the electrochemical corrosion resistance of substrate.
