Continuous thermo-mechanical processing (CTMP) of 6201 aluminum alloy was simulated on Gleeble-1500. The deformed specimens were analyzed by the observation of TEM and the measurement of hardness. It was shown that r...Continuous thermo-mechanical processing (CTMP) of 6201 aluminum alloy was simulated on Gleeble-1500. The deformed specimens were analyzed by the observation of TEM and the measurement of hardness. It was shown that rapid solid solution and aging treatment can be effectively combined in one procedure by the strain induced during CTMP. The deformation temperature is ranging from 540* C to 300* C, the hardness increases directly before the 6th pass followed by a slight drop, the amount of precipitates increases with the holding time after deformation. Uniformly distributed and stabilized Mg2Si precipitates, as well as dislocation substructure can be observed on deformed specimens which have been subsequently held at 300℃ for 60 seconds.展开更多
A continuous semisolid extending extrusion （CSEP） method was proposed. Temperature field and metal flow during continuous semisolid extending extrusion process of 6201 alloy tube were studied. During the process, th...A continuous semisolid extending extrusion （CSEP） method was proposed. Temperature field and metal flow during continuous semisolid extending extrusion process of 6201 alloy tube were studied. During the process, the temperature in the roll-shoe cavity decreases gradually, and the isothermal lines of the alloy deviate from the shoe side to the work roll side in the roll–shoe gap. Metal flow velocity decreases gradually from the surface of the work roll to the surface of the shoe. In the extrusion mould, alloy temperature decreases gradually from the entrance to the exit and from the center to the sidewall of the mould. The extending cavity is radially filled with the alloy. The flow lines in the tube corresponding to the centers of the splitflow orifices and the welding gaps are dense, and the corresponding harness values are high; there are 8 transitional bands between them. In order to prepare 6201 alloy tubes with good surface quality, the pouring temperature from 750 ℃ to 780 ℃ was suggested.展开更多
文摘Continuous thermo-mechanical processing (CTMP) of 6201 aluminum alloy was simulated on Gleeble-1500. The deformed specimens were analyzed by the observation of TEM and the measurement of hardness. It was shown that rapid solid solution and aging treatment can be effectively combined in one procedure by the strain induced during CTMP. The deformation temperature is ranging from 540* C to 300* C, the hardness increases directly before the 6th pass followed by a slight drop, the amount of precipitates increases with the holding time after deformation. Uniformly distributed and stabilized Mg2Si precipitates, as well as dislocation substructure can be observed on deformed specimens which have been subsequently held at 300℃ for 60 seconds.
基金Projects (51034002, 50974038) supported by the National Natural Science Foundation of ChinaProject (132002) supported by the Fok Ying Tong Education FoundationProject (2011CB610405) supported by National Basic Research Program of China
文摘A continuous semisolid extending extrusion （CSEP） method was proposed. Temperature field and metal flow during continuous semisolid extending extrusion process of 6201 alloy tube were studied. During the process, the temperature in the roll-shoe cavity decreases gradually, and the isothermal lines of the alloy deviate from the shoe side to the work roll side in the roll–shoe gap. Metal flow velocity decreases gradually from the surface of the work roll to the surface of the shoe. In the extrusion mould, alloy temperature decreases gradually from the entrance to the exit and from the center to the sidewall of the mould. The extending cavity is radially filled with the alloy. The flow lines in the tube corresponding to the centers of the splitflow orifices and the welding gaps are dense, and the corresponding harness values are high; there are 8 transitional bands between them. In order to prepare 6201 alloy tubes with good surface quality, the pouring temperature from 750 ℃ to 780 ℃ was suggested.