The precipitation behaviors of an A1-Cu-Li-Mn-Zr alloy at different ageing temperatures （120, 160 and 200 ~C） were investigated using Vickers hardness measurements and transmission electron microscopy （TEM） charac...The precipitation behaviors of an A1-Cu-Li-Mn-Zr alloy at different ageing temperatures （120, 160 and 200 ~C） were investigated using Vickers hardness measurements and transmission electron microscopy （TEM） characterization. Age hardening curves show an increase in precipitation kinetics with increasing ageing temperature. The results of TEM show that for the samples peak aged at 120 ~C, the amount of g＇ （A13Li）, GP zones/0＇ （A12Cu） and Z （A15Cu6Li2） phases is obviously higher than that of T1 （A12CuLi） precipitates; while the samples peak aged at 160 and 200 ~C are usually dominated by T1 phase with a minor fraction of GP zones/0＇ and g＇, and the Z phase almost does not form. In addition, quantitative analysis on the T1 platelets demonstrates that the samples peak aged at 200 ~C have larger plate diameter and smaller area fraction of T1, as compared to the samples peak aged at 160 ~C. Correspondingly, the possible reasons for such phenomena are discussed.展开更多
The effect of the quenching rate after solution treatment on the residual stress and precipitation behavior of a high strength Mg-5 Zn-3.5 Sn-1 Mn-0.5 Ca-0.5 Cu plate is studied.The simulation results show decreasing ...The effect of the quenching rate after solution treatment on the residual stress and precipitation behavior of a high strength Mg-5 Zn-3.5 Sn-1 Mn-0.5 Ca-0.5 Cu plate is studied.The simulation results show decreasing temperature gradient in the plate with decreasing quenching rate,which leads to weakened inhomogeneous plastic deformation and decreased residual stress.No dynamic precipitation on the grain boundary happens after either cold water cooling or air cooling,however,air cooling leads to dynamic precipitation of Mg-Zn phase on Mn particles around which a low-density precipitate zone develops after aging treatment.Moreover,the fine and densely distributed Mg-Zn precipitates observed after aging treatment of the cold water cooled alloy are replaced by coarse precipitates with low density for the air cooled alloy.Both the low-density precipitate zone near Mn particles and the coarsening of precipitates are the source of the decrease in hardness and tensile properties of the air cooled alloy.The residual stress drops faster than the hardness with decreasing quenching rate,which makes it possible to lower the residual stress without sacrificing too much age-hardening ability of the alloy.展开更多
Effects of Mg content on the microstructure and mechanical properties of low Zn-containing Al−xMg−3Zn−1Cu cast alloys(x=3−5,wt.%)were investigated.As Mg content increased in the as-cast alloys,the grains were refined ...Effects of Mg content on the microstructure and mechanical properties of low Zn-containing Al−xMg−3Zn−1Cu cast alloys(x=3−5,wt.%)were investigated.As Mg content increased in the as-cast alloys,the grains were refined due to enhanced growth restriction,and the formation ofη-Mg(AlZnCu)_(2) and S-Al_(2)CuMg phases was inhibited while the formation of T-Mg_(32)(AlZnCu)_(49 )phase was promoted when Mg content exceeded 4 wt.%.The increase of Mg content encumbered the solution kinetics by increasing the size of eutectic phase but accelerated and enhanced the age-hardening through expediting precipitation kinetics and elevating the number density of the precipitates.As Mg content increased,the yield strength and tensile strength of the as-cast,solution-treated and peak-aged alloys were severally improved,while the elongation of the alloys decreased.The tensile strength and elongation of the peak-aged Al−5Mg−3Zn−1Cu alloy exceed 500 MPa and 5%,respectively.Precipitation strengthening implemented by T′precipitates is the predominant strengthening mechanism in the peak-aged alloys and is enhanced by increasing Mg content.展开更多
The ordering of the α-Fe(Si) crystallization phase in annealed Fe73.5Cu1Mo3Si13.5B9 alloy has been studied using XRD method. The α-Fe(Si) phase in Fe73.5Cu1Mo3Si13.5B9 alloy annealed at 460℃ for 1 h consists of th...The ordering of the α-Fe(Si) crystallization phase in annealed Fe73.5Cu1Mo3Si13.5B9 alloy has been studied using XRD method. The α-Fe(Si) phase in Fe73.5Cu1Mo3Si13.5B9 alloy annealed at 460℃ for 1 h consists of the DO3-type ordered region with spherical shape and disordered region. The size of DO3 ordered region increases with the annealing temperature. When the annealing temperature is 560℃, the size of the ordered region in the α-Fe(Si) grain is 14.0nm,which is nearly as large as that of the α-Fe(Si) grain (14.2 nm) and the degree of order of the α-Fe(Si) phase is about 0.78. When Fe73.5Cu1 Mo3Si13.5B9 amorphous alloy is annealed at 520℃， with the increment of the annealing time, the shape of the DO3 ordered region in the α-Fe(Si) phase is spheroidal at the beginning of the annealing and becomes spherical and has asize of 12.8 nm when the annealing time is 60 min. In addition, the DO3 superlattice lines of the α-Fe(Si) phase will vanish if Fe73.5Cu1Mo3Si13.5 B9 amorphous alloy is annealed for 1 h at 750℃.展开更多
The synthetical soft magnetic properties including d.c. and a.c. magnetic properties and pulse magnetic property are reported for a newly-developed nanocrystalline Fe73.5Cu1 Nb1.5V1.5Si13.5B9 alloy The new alloy posse...The synthetical soft magnetic properties including d.c. and a.c. magnetic properties and pulse magnetic property are reported for a newly-developed nanocrystalline Fe73.5Cu1 Nb1.5V1.5Si13.5B9 alloy The new alloy possesses high d.c. relative initial permeability of 12.5×104 and low coerciv ity of 0.54 A/m. Under the conditions of Bm=0.3 T, f=100 kHz and Bm=0.2 T, f=200 kHz the core losses of the new alloy are 543 kW·m-3 and 834 kW.m-3, respectively which can be compa rable with those of nanocrystalline Fe73.5Cu1Nb3Si13.5B9 alloy. The analyses of core losses have been carried out in the wider range of f=20～104 kHz and Bm=0.0025～0.8 T and the approxi mate expression P(kW·m-3)=1.803 B:f1.77 has been obtained. The analyses of core losses in the range of f=20～104 kHz and Bmf=(10～40)×103(T.Hz) have shown that the core loss and the corresponding amplitude permeability roughly vary as P = 2.347×10-6(Bmf)1.97f-0.2231 and μa = 9.56× 105f-0.7464, respectively for the given product B.f. Some practical applica tions have also been mentioned.展开更多
Under different magnetic field intensities, the dependence of the permeability μ on temperature T(μ-T curve) for the Fe7.3Cu1Nb3Si13.5B9 alloy annealed at 350-620℃ was investigated. The results showed that the magn...Under different magnetic field intensities, the dependence of the permeability μ on temperature T(μ-T curve) for the Fe7.3Cu1Nb3Si13.5B9 alloy annealed at 350-620℃ was investigated. The results showed that the magnetic field intensity had a remarkable influence on the shape of μ-T curves. For amorphous alloy, the sharp Hopkinson peak of μ-T curve disappeared gradually with the increase of magnetic field intensity.展开更多
The results of thermomagnetic (TM) and calorimetric (DSC) measurements have been compared in order to clarify some details of the mechanism of nanophase-formation from Finemet-type precursors with different Nb content...The results of thermomagnetic (TM) and calorimetric (DSC) measurements have been compared in order to clarify some details of the mechanism of nanophase-formation from Finemet-type precursors with different Nb contents. It was found that the main features of the DSC thermograms (shape, relative separation and amplitude of the exothermic peaks characteristic for the precipitation of the Fe-(Si) solid solution and the transition metal borides) depend mainly on the composition of the precursor glass, and are only slightly affected by the heating rate between 20 and 80 K/min. The amplitude of the uprise of the magnetization in the TM curves (attributed to the precipitation of bcc-Fe(Si) and borides) decreases with increasing Nb-content. The Curietemperature of the precursor glasses. Tc(am1), the remainder amorphous phases, Tc(am2) and the bcc nanophase, Tc(n-Fe) are determined from the thermomagnetic curves. The shape of the TM curves is interpreted on the basis of the reactions describing the crystalIization of the hypo-eutectic Fe-B glasses.展开更多
High-frequency magnetic properties, such as core loss, coercivity and amplitude permeabilityof a newly-developed nanocrystalline Fe72.5Cu1Nb2V2Si13.5B9 alloy in the wide ranges of f =20-103 kHz, Bm = 0.01~0.6 T and Bm...High-frequency magnetic properties, such as core loss, coercivity and amplitude permeabilityof a newly-developed nanocrystalline Fe72.5Cu1Nb2V2Si13.5B9 alloy in the wide ranges of f =20-103 kHz, Bm = 0.01~0.6 T and Bmf = 10~40 (T.kHz) have been measured. A largeamount of experimental data have been fitted by a computer, thus obtaining several expressionsrepresenting the influence of frequency on high-frequency magnetic properties, that are useful inpractical applications.展开更多
The isothermal compression tests were carried out in the Thermecmastor-Z thermo-simulator at temperatures of 800, 850, 900, 950, 1000 and 1050 ℃ and the strain rates of 0.01, 0.1, 1 and 10 s-1. The influence of defor...The isothermal compression tests were carried out in the Thermecmastor-Z thermo-simulator at temperatures of 800, 850, 900, 950, 1000 and 1050 ℃ and the strain rates of 0.01, 0.1, 1 and 10 s-1. The influence of deformation temperature and strain rate on the flow stress of Ti-6Al-2Zr-IMo-IV alloy was studied. Based on the experimental data sets, the high temperature deformation behavior of Ti-6A1-2Zr-IMo-IV alloy was presented using the intelligent method of artificial neural network （ANN）. The results indicate that the predicted flow stress values by ANN model is quite consistent with the experimental results, which implies that the artificial neural network is an effective tool for studying the hot deformation behavior of the present alloy. In addition, the development of graphical user interface is implemented using Visual Basic programming language.展开更多
A novel Cu (Ⅱ) complex of 1-phenyl-3-methyl-4-acyl-5-pyrazolone was synthesized and crystallogra- phically characterized. The single-crystal structure of the complex reveals that the crystal belongs triclinic, space ...A novel Cu (Ⅱ) complex of 1-phenyl-3-methyl-4-acyl-5-pyrazolone was synthesized and crystallogra- phically characterized. The single-crystal structure of the complex reveals that the crystal belongs triclinic, space group P1 with cell parameters a=0.938 7(4) nm, b=1.124 4(5) nm, c=1.222 3(5) nm, α=99.538(7)°, β=104.049(8)°, γ=113.806(6)°, and Z=2, V=1.093 3(8) nm3. Cu(Ⅱ) ion is coordinated by two 1-phenyl-3-methyl-4-acyl-5-pyrazolone ligands, and one methanol molecule giving a coordination number of five, the coordination polyhedron around Cu(Ⅱ) ion can be described as a square pyramid. Two complex units link to each other through the hydrogen-bonding interactions to form a dimer. Meanwhile, a staircase-like layer structure was built up by offset face-to-face π…π stacking interactions and weak interactions between the dimers.展开更多
基金Project（2016YFB0300901） supported by the National Key R＆D Program of China Project（51421001） supported by the National Natural Science Foundation of China Project（2018CDJDCL0019） supported by the Fundamental Research Funds for the Central Universities, China
文摘The precipitation behaviors of an A1-Cu-Li-Mn-Zr alloy at different ageing temperatures （120, 160 and 200 ~C） were investigated using Vickers hardness measurements and transmission electron microscopy （TEM） characterization. Age hardening curves show an increase in precipitation kinetics with increasing ageing temperature. The results of TEM show that for the samples peak aged at 120 ~C, the amount of g＇ （A13Li）, GP zones/0＇ （A12Cu） and Z （A15Cu6Li2） phases is obviously higher than that of T1 （A12CuLi） precipitates; while the samples peak aged at 160 and 200 ~C are usually dominated by T1 phase with a minor fraction of GP zones/0＇ and g＇, and the Z phase almost does not form. In addition, quantitative analysis on the T1 platelets demonstrates that the samples peak aged at 200 ~C have larger plate diameter and smaller area fraction of T1, as compared to the samples peak aged at 160 ~C. Correspondingly, the possible reasons for such phenomena are discussed.
基金supported by the National Key Research and Development Program of China[2016YFB0301105]the National Key Research and Development Plan[2017YFB0103904]
文摘The effect of the quenching rate after solution treatment on the residual stress and precipitation behavior of a high strength Mg-5 Zn-3.5 Sn-1 Mn-0.5 Ca-0.5 Cu plate is studied.The simulation results show decreasing temperature gradient in the plate with decreasing quenching rate,which leads to weakened inhomogeneous plastic deformation and decreased residual stress.No dynamic precipitation on the grain boundary happens after either cold water cooling or air cooling,however,air cooling leads to dynamic precipitation of Mg-Zn phase on Mn particles around which a low-density precipitate zone develops after aging treatment.Moreover,the fine and densely distributed Mg-Zn precipitates observed after aging treatment of the cold water cooled alloy are replaced by coarse precipitates with low density for the air cooled alloy.Both the low-density precipitate zone near Mn particles and the coarsening of precipitates are the source of the decrease in hardness and tensile properties of the air cooled alloy.The residual stress drops faster than the hardness with decreasing quenching rate,which makes it possible to lower the residual stress without sacrificing too much age-hardening ability of the alloy.
基金supported by the National Natural Science Foundation of China (Nos. 51674166, U1902220)the National Key R&D Program of China (No. 2021YFB3701303)。
文摘Effects of Mg content on the microstructure and mechanical properties of low Zn-containing Al−xMg−3Zn−1Cu cast alloys(x=3−5,wt.%)were investigated.As Mg content increased in the as-cast alloys,the grains were refined due to enhanced growth restriction,and the formation ofη-Mg(AlZnCu)_(2) and S-Al_(2)CuMg phases was inhibited while the formation of T-Mg_(32)(AlZnCu)_(49 )phase was promoted when Mg content exceeded 4 wt.%.The increase of Mg content encumbered the solution kinetics by increasing the size of eutectic phase but accelerated and enhanced the age-hardening through expediting precipitation kinetics and elevating the number density of the precipitates.As Mg content increased,the yield strength and tensile strength of the as-cast,solution-treated and peak-aged alloys were severally improved,while the elongation of the alloys decreased.The tensile strength and elongation of the peak-aged Al−5Mg−3Zn−1Cu alloy exceed 500 MPa and 5%,respectively.Precipitation strengthening implemented by T′precipitates is the predominant strengthening mechanism in the peak-aged alloys and is enhanced by increasing Mg content.
文摘The ordering of the α-Fe(Si) crystallization phase in annealed Fe73.5Cu1Mo3Si13.5B9 alloy has been studied using XRD method. The α-Fe(Si) phase in Fe73.5Cu1Mo3Si13.5B9 alloy annealed at 460℃ for 1 h consists of the DO3-type ordered region with spherical shape and disordered region. The size of DO3 ordered region increases with the annealing temperature. When the annealing temperature is 560℃, the size of the ordered region in the α-Fe(Si) grain is 14.0nm,which is nearly as large as that of the α-Fe(Si) grain (14.2 nm) and the degree of order of the α-Fe(Si) phase is about 0.78. When Fe73.5Cu1 Mo3Si13.5B9 amorphous alloy is annealed at 520℃， with the increment of the annealing time, the shape of the DO3 ordered region in the α-Fe(Si) phase is spheroidal at the beginning of the annealing and becomes spherical and has asize of 12.8 nm when the annealing time is 60 min. In addition, the DO3 superlattice lines of the α-Fe(Si) phase will vanish if Fe73.5Cu1Mo3Si13.5 B9 amorphous alloy is annealed for 1 h at 750℃.
文摘The synthetical soft magnetic properties including d.c. and a.c. magnetic properties and pulse magnetic property are reported for a newly-developed nanocrystalline Fe73.5Cu1 Nb1.5V1.5Si13.5B9 alloy The new alloy possesses high d.c. relative initial permeability of 12.5×104 and low coerciv ity of 0.54 A/m. Under the conditions of Bm=0.3 T, f=100 kHz and Bm=0.2 T, f=200 kHz the core losses of the new alloy are 543 kW·m-3 and 834 kW.m-3, respectively which can be compa rable with those of nanocrystalline Fe73.5Cu1Nb3Si13.5B9 alloy. The analyses of core losses have been carried out in the wider range of f=20～104 kHz and Bm=0.0025～0.8 T and the approxi mate expression P(kW·m-3)=1.803 B:f1.77 has been obtained. The analyses of core losses in the range of f=20～104 kHz and Bmf=(10～40)×103(T.Hz) have shown that the core loss and the corresponding amplitude permeability roughly vary as P = 2.347×10-6(Bmf)1.97f-0.2231 and μa = 9.56× 105f-0.7464, respectively for the given product B.f. Some practical applica tions have also been mentioned.
基金This work was supported by the National Natural Science Foundation of China(No.59871013).
文摘Under different magnetic field intensities, the dependence of the permeability μ on temperature T(μ-T curve) for the Fe7.3Cu1Nb3Si13.5B9 alloy annealed at 350-620℃ was investigated. The results showed that the magnetic field intensity had a remarkable influence on the shape of μ-T curves. For amorphous alloy, the sharp Hopkinson peak of μ-T curve disappeared gradually with the increase of magnetic field intensity.
文摘The results of thermomagnetic (TM) and calorimetric (DSC) measurements have been compared in order to clarify some details of the mechanism of nanophase-formation from Finemet-type precursors with different Nb contents. It was found that the main features of the DSC thermograms (shape, relative separation and amplitude of the exothermic peaks characteristic for the precipitation of the Fe-(Si) solid solution and the transition metal borides) depend mainly on the composition of the precursor glass, and are only slightly affected by the heating rate between 20 and 80 K/min. The amplitude of the uprise of the magnetization in the TM curves (attributed to the precipitation of bcc-Fe(Si) and borides) decreases with increasing Nb-content. The Curietemperature of the precursor glasses. Tc(am1), the remainder amorphous phases, Tc(am2) and the bcc nanophase, Tc(n-Fe) are determined from the thermomagnetic curves. The shape of the TM curves is interpreted on the basis of the reactions describing the crystalIization of the hypo-eutectic Fe-B glasses.
文摘High-frequency magnetic properties, such as core loss, coercivity and amplitude permeabilityof a newly-developed nanocrystalline Fe72.5Cu1Nb2V2Si13.5B9 alloy in the wide ranges of f =20-103 kHz, Bm = 0.01~0.6 T and Bmf = 10~40 (T.kHz) have been measured. A largeamount of experimental data have been fitted by a computer, thus obtaining several expressionsrepresenting the influence of frequency on high-frequency magnetic properties, that are useful inpractical applications.
基金Project (2007CB613807) supported by the National Basic Research Program of ChinaProject (35-TP-2009) supported by the Fund of the State Key Laboratory of Solidification Processing in NWPU,ChinaProject (51075333) supported by the National Natural Science Foundation of China
文摘The isothermal compression tests were carried out in the Thermecmastor-Z thermo-simulator at temperatures of 800, 850, 900, 950, 1000 and 1050 ℃ and the strain rates of 0.01, 0.1, 1 and 10 s-1. The influence of deformation temperature and strain rate on the flow stress of Ti-6Al-2Zr-IMo-IV alloy was studied. Based on the experimental data sets, the high temperature deformation behavior of Ti-6A1-2Zr-IMo-IV alloy was presented using the intelligent method of artificial neural network （ANN）. The results indicate that the predicted flow stress values by ANN model is quite consistent with the experimental results, which implies that the artificial neural network is an effective tool for studying the hot deformation behavior of the present alloy. In addition, the development of graphical user interface is implemented using Visual Basic programming language.
文摘A novel Cu (Ⅱ) complex of 1-phenyl-3-methyl-4-acyl-5-pyrazolone was synthesized and crystallogra- phically characterized. The single-crystal structure of the complex reveals that the crystal belongs triclinic, space group P1 with cell parameters a=0.938 7(4) nm, b=1.124 4(5) nm, c=1.222 3(5) nm, α=99.538(7)°, β=104.049(8)°, γ=113.806(6)°, and Z=2, V=1.093 3(8) nm3. Cu(Ⅱ) ion is coordinated by two 1-phenyl-3-methyl-4-acyl-5-pyrazolone ligands, and one methanol molecule giving a coordination number of five, the coordination polyhedron around Cu(Ⅱ) ion can be described as a square pyramid. Two complex units link to each other through the hydrogen-bonding interactions to form a dimer. Meanwhile, a staircase-like layer structure was built up by offset face-to-face π…π stacking interactions and weak interactions between the dimers.