Cr1-xAlxN coatings have been deposited on a Ti3Al based alloy by reactive sputtering method. The results of the isothermal oxidation test at 800-900℃ showed that Cr1-xAlxN coatings could remarkably reduce the oxidati...Cr1-xAlxN coatings have been deposited on a Ti3Al based alloy by reactive sputtering method. The results of the isothermal oxidation test at 800-900℃ showed that Cr1-xAlxN coatings could remarkably reduce the oxidation rate of the alloy owing to the formation of Al2O3＋Cr2O3 mixture oxide scale on the surface of the coatings. No spallation of the coatings or oxide scales took place during the cyclic oxidation at 800℃. Ti was observed to diffuse into the coatings, the diffusion distance of which was very short, and the diffusion ability of it was proportional to the AI content in the coatings. Compared to Ti, Nb can diffuse much more easily through the whole coatings and oxide scales.展开更多
The Sr/F co-doped CaP(Sr/F-CaP)coatings were prepared by micro-arc oxidation(MAO)under different voltages to modify the microstructure and corrosion behavior of Mg-4Zn-1Mn alloy.The surface and interface characteristi...The Sr/F co-doped CaP(Sr/F-CaP)coatings were prepared by micro-arc oxidation(MAO)under different voltages to modify the microstructure and corrosion behavior of Mg-4Zn-1Mn alloy.The surface and interface characteristics investigated using scanning electron microscopy(SEM)and energy dispersive X-ray spectrometer(EDS)showed that the MAO coatings displayed uneven crater-like holes and tiny cracks under lower voltage,while they exhibited relatively homogeneous crater-like holes without cracks under higher voltage.The thickness of MAO coatings increased with increasing voltage.The corrosion behavior of Mg-4Zn-1Mn alloy was improved by the MAO coatings.The MAO coatings prepared under 450 V and 500 V voltages possessed the best corrosion resistance with regard to the electrochemical corrosion tests and immersion corrosion tests,respectively.The MAO coatings fabricated under 450-500 V could provide a better corrosion protection effect for the substrate.展开更多
The development of methods to produce nanoparticles with unique properties via the aerosol route is progressing rapidly. Typical characterization techniques extract particles from the synthesis process for subsequent ...The development of methods to produce nanoparticles with unique properties via the aerosol route is progressing rapidly. Typical characterization techniques extract particles from the synthesis process for subsequent offiine analysis, which may alter the particle characteristics. In this work, we use laser-vaporization aerosol mass spectrometry （LV-AMS） with 70-eV electron ionization for real-time, in-situ nanoparticle characterization. The particle characteristics are examined for various aerosol synthesis methods, degrees of sintering, and for controlled condensation of organic material to simulate surface coating/functionalization. The LV-AMS is used to characterize several types of metal nanoparticles （Ag, Au, Pd, PdAg, Fe, Ni, and Cu）. The degree of oxidation of the Fe and Ni nanoparticles is found to increase with increased sintering temperature, while the surface organic-impurity content of the metal particles decreases with increased sintering temperature. For aggregate metal particles, the organic-impurity content is found to be similar to that of a monolayer. By comparing different equivalent-diameter measurements, we demonstrate that the LV-AMS can be used in tandem with a differential mobility analyzer to determine the compactness of synthesized metal particles, both during sintering and during material addition for surface functionalization. Further, materials supplied to the particle production line downstream of the particle generators are found to reach the generators as contaminants. The capacity for such in-situ observations is important, as it facilitates rapid response to undesired behavior within the particle production process. This study demonstrates the utility of real-time, in-situ aerosol mass spectrometric measurements to characterize metal nanoparticles obtained directly from the synthesis process line, including their chemical composition, shape, and contamination, providing the potential for effective optimization of process operating parameters.展开更多
基金the National Natural Science Foundation of China under grant Nos. 50371095 , 50571106.
文摘Cr1-xAlxN coatings have been deposited on a Ti3Al based alloy by reactive sputtering method. The results of the isothermal oxidation test at 800-900℃ showed that Cr1-xAlxN coatings could remarkably reduce the oxidation rate of the alloy owing to the formation of Al2O3＋Cr2O3 mixture oxide scale on the surface of the coatings. No spallation of the coatings or oxide scales took place during the cyclic oxidation at 800℃. Ti was observed to diffuse into the coatings, the diffusion distance of which was very short, and the diffusion ability of it was proportional to the AI content in the coatings. Compared to Ti, Nb can diffuse much more easily through the whole coatings and oxide scales.
文摘The Sr/F co-doped CaP(Sr/F-CaP)coatings were prepared by micro-arc oxidation(MAO)under different voltages to modify the microstructure and corrosion behavior of Mg-4Zn-1Mn alloy.The surface and interface characteristics investigated using scanning electron microscopy(SEM)and energy dispersive X-ray spectrometer(EDS)showed that the MAO coatings displayed uneven crater-like holes and tiny cracks under lower voltage,while they exhibited relatively homogeneous crater-like holes without cracks under higher voltage.The thickness of MAO coatings increased with increasing voltage.The corrosion behavior of Mg-4Zn-1Mn alloy was improved by the MAO coatings.The MAO coatings prepared under 450 V and 500 V voltages possessed the best corrosion resistance with regard to the electrochemical corrosion tests and immersion corrosion tests,respectively.The MAO coatings fabricated under 450-500 V could provide a better corrosion protection effect for the substrate.
文摘The development of methods to produce nanoparticles with unique properties via the aerosol route is progressing rapidly. Typical characterization techniques extract particles from the synthesis process for subsequent offiine analysis, which may alter the particle characteristics. In this work, we use laser-vaporization aerosol mass spectrometry （LV-AMS） with 70-eV electron ionization for real-time, in-situ nanoparticle characterization. The particle characteristics are examined for various aerosol synthesis methods, degrees of sintering, and for controlled condensation of organic material to simulate surface coating/functionalization. The LV-AMS is used to characterize several types of metal nanoparticles （Ag, Au, Pd, PdAg, Fe, Ni, and Cu）. The degree of oxidation of the Fe and Ni nanoparticles is found to increase with increased sintering temperature, while the surface organic-impurity content of the metal particles decreases with increased sintering temperature. For aggregate metal particles, the organic-impurity content is found to be similar to that of a monolayer. By comparing different equivalent-diameter measurements, we demonstrate that the LV-AMS can be used in tandem with a differential mobility analyzer to determine the compactness of synthesized metal particles, both during sintering and during material addition for surface functionalization. Further, materials supplied to the particle production line downstream of the particle generators are found to reach the generators as contaminants. The capacity for such in-situ observations is important, as it facilitates rapid response to undesired behavior within the particle production process. This study demonstrates the utility of real-time, in-situ aerosol mass spectrometric measurements to characterize metal nanoparticles obtained directly from the synthesis process line, including their chemical composition, shape, and contamination, providing the potential for effective optimization of process operating parameters.