Structure and superconducting properties of Ru_(1-x)Mo_(x)(x=0.1-0.9)alloys

We report the detailed crystal structures and physical properties of Ru_(1-x)Mo_(x)alloys in the solid solution range of x=0.1-0.9.Structure characterizations indicate that the crystal structure changes from the hcp-Mg-type,toβ-CrFe-type,and then bcc-W-type.The measurements of physical properties show that the Ru_(1-x)Mo_(x)samples with x≥0.2are superconductors and the superconducting transition temperature T_c as a function of Mo content exhibits a dome-like behavior.

Al-Cr-Fe-Mn-Ni高熵合金中的L2_(1)相的相稳定性及其性能研究

为开发兼具良好强度与塑性的BCC基高熵合金,可引入与基体共格的B2或L2_(1)相。L2_(1)相具有更好的抗蠕变性能,有望在高温环境中得到应用。但是,目前对BCC型高熵合金中L2_(1)相的存在规律、相稳定性及其对合金性能的影响还缺乏深入的研究。为此,本工作研究了电弧熔炼制备的铸态Al_(0.5)Cr_(2.5-x)FeMn_(x)Ni(x=0.5~1.75)、Al_(0.75)Cr_(2.25-y)FeMn_(y)Ni(y=0.25~1.5)、AlCr_(2-z)FeMn_(z)Ni(z=0.5~1.5)高熵合金的相组成,及800℃或1000℃真空退火120 h对合金组织和相组成的影响。研究表明,这些合金中L2_(1)相的成分特征由40%~50%(原子分数)Ni和15%~20%(原子分数)Al、Mn组成。L2_(1)相只存在于Al含量为10%~15%(原子分数)的合金中,且多以BCC+L2_(1)两相共存,获得的组织为编织网状的调幅分解组织。当Al含量达到20%(原子分数)后,合金则由BCC+B2两相构成。L2_(1)相的存在会使BCC型XRD特征峰出现明显的峰分裂。经过800℃或1000℃退火后,合金中L2_(1)相仍能稳定存在,合金显微组织发生粗化并会形成σ或FCC相。铸态合金的硬度随Mn含量的增加而降低,含L2_(1)相的合金的硬度在463HV~558HV范围内。800℃退火会使含5%~15%(原子分数)Mn的合金硬度降低70HV~100HV,但由于硬质σ相的析出,含20%~30%(原子分数)Mn的合金硬度提高200HV以上;1000℃退火后,由于软质FCC相的形成,合金的硬度略有降低,这些结果将为BCC型高熵合金的设计奠定基础。

轧制应变速率对Mg-1%Al合金组织、阻尼和力学性能的影响

在不同应变速率下轧制Mg-1%Al合金板材,研究了轧制应变速率对Mg-1%Al合金显微组织、力学性能和阻尼性能的影响。随着轧制应变速率增加,Mg-1%Al合金的平均晶粒尺寸和再结晶体积分数增加;抗拉强度、屈服强度和织构强度减小;延伸率先升高后降低,在应变速率20 s^(-1)时达到最高,为25.33%。随着应变速率增加,室温阻尼性能增加,应变速率30 s^(-1)下应变振幅0.1%时阻尼值为0.061,是应变速率15 s^(-1)时的1.5倍。应变速率一定时,阻尼性能随着频率增加而降低。

Improved Corrosion Behavior of Biodegradable Mg-4Zn-1Mn Alloy Modified by Sr/F co-doped CaP Micro-arc Oxidation Coatings

The Sr/F co-doped CaP(Sr/F-CaP)coatings were prepared by micro-arc oxidation(MAO)under different voltages to modify the microstructure and corrosion behavior of Mg-4Zn-1Mn alloy.The surface and interface characteristics investigated using scanning electron microscopy(SEM)and energy dispersive X-ray spectrometer(EDS)showed that the MAO coatings displayed uneven crater-like holes and tiny cracks under lower voltage,while they exhibited relatively homogeneous crater-like holes without cracks under higher voltage.The thickness of MAO coatings increased with increasing voltage.The corrosion behavior of Mg-4Zn-1Mn alloy was improved by the MAO coatings.The MAO coatings prepared under 450 V and 500 V voltages possessed the best corrosion resistance with regard to the electrochemical corrosion tests and immersion corrosion tests,respectively.The MAO coatings fabricated under 450-500 V could provide a better corrosion protection effect for the substrate.

高性能聚丁烯-1/聚丙烯釜内合金管材的结构与性能

采用单螺杆管材挤出机,制备了高等规聚丁烯-1(iPB)与聚丁烯-1/聚丙烯合金(PBA)管材,通过差式扫描量热、小角X射线衍射、耐热蠕变、爆破性能、静液压性能与力学性能测试,考察了iPB与PBA管材的结晶性能与力学性能,PBA管材中PB的片晶厚度,熔融温度与结晶温度均得到提升,耐热蠕变性、爆破与静液压性能、力学性能均优于iPB管材,可作为新一代高性能热水管材使用。

Al-Li-Cu-Zr合金中T_1相结构、形核和长大机制研究

T_1(Al_2CuLi)相是Al-Li-Cu-Zr合金中的重要强化相。通过TEM在对T1相结构和形貌分析的基础上,构造了T1相的结构。T1相晶核以ABCBA的堆垛顺序,共由36个原子组成,其晶格常数a=0.495nm,c=0.933nm。与基体的位相关系为:狖0001狚T1∥狖111狚α,<1010>T1∥<110>α。合金中铜原子的偏聚降低了基体的层错能,从而为T1相依赖扩散层错形核提供了有利条件。T1相长大依赖于原子扩散和台阶滑移,是一种长程扩散控制的台阶机制。

Effect of ultrasonic melt treatment on degassing of Mg-6Zn-1Ca alloy

The effect of ultrasonic power and treatment time on degassing of Mg-6Zn-1Ca alloy was studied in this paper. The degassing effect was characterized by measuring densities of ingots. The results show that proper ultrasonic treatment can remove hydrogen from the melt of the Mg-6Zn-1Ca alloy. The ultrasonic degassing effect is closely related to the ultrasonic power density and treatment time. The degassing efficiency increases with an increase in ultrasonic power density when the melt is treated at 690 °C for 120 s, reaching its highest value at 1.2 W·cm-3. When the power density is 1.2 W·cm-3, with an increase in ultrasonic treatment time, the degassing efficiency increases at first, reaches its peak value at 120 s, then decreases as the ultrasonic treatment is further prolonged. In this experiment, the optimum degassing effect with an efficiency of 67.5 % is obtained by ultrasonic treatment with the power density of 1.2 W·cm-3 for 120 s. The maximum density of ingot can be increased from 1.8069 g·cm-3 to 1.8146 g·cm-3(increased by 0.43%).

INFLUENCE OF Al-5Ti-1B MASTER ALLOY ON MICROSTRUCTURE AND DAMPING CAPACITY OF ZA27 ALLOY

１ＩＮＴＲＯＤＵＣＴＩＯＮＴｈｅｄａｍｐｉｎｇｃａｐａｃｉｔｙｏｆａｍａｔｅｒｉａｌｉｓａｍｅａｓｕｒｅｏｆｔｈｅｅｎｅｒｇｙｔｈａｔｉｓｄｉｓｓｉｐａｔｅｄｉｎｔｈｅｍａｔｅｒｉａｌｄｕｒｉｎｇｍｅｃｈａｎｉｃａｌｖｉｂｒａｔｉｏｎｕｎｄｅｒｃｙｃ...

Simulation on function mechanism of T1(Al_2CuLi) precipitate in localized corrosion of Al-Cu-Li alloys

To clarify the corrosion mechanism associated with the precipitate of T1(Al2CuLi)in Al-Li alloys,the simulated bulk precipitate of T1 was fabricated through melting and casting.Its electrochemical behavior and coupling behavior with α(Al)in 3.5% NaCl solution were investigated.Meanwhile,the simulated Al alloy containing T1 particle was prepared and its corrosion morphology was observed.The results show that there exists a dynamic conversion corrosion mechanism associated with the precipitate of T1.At the beginning,the precipitate of T1 is anodic to the alloy base and corrosion occurs on its surface.However,during its corrosion process,its potential moves to a positive direction with immersion time increasing,due to the preferential dissolution of Li and the enrichment of Cu.As a result,the corroded T1 becomes cathodic to the alloy base at a later stage,leading to the anodic dissolution and corrosion of the alloy base at its adjacent periphery.It is suggested that the localized corrosion associated with the precipitate of T1 in Al-Li alloys is caused by the alternate anodic dissolution of the T1 precipitate and the alloy base at its adjacent periphery.

Microstructures and tensile properties of as-cast Mg-5Sn-1Si magnesium alloy modified with trace elements of Y,Bi,Sb and Sr

The microstructures and mechanical properties of as-cast Mg-5 Sn-1 Si magnesium alloy modified with trace elements Y,Bi,Sb and Sr were investigated and compared.Results show that the microstructure of the as-cast Mg-5 Sn-1 Si alloy consists ofα-Mg,Mg_(2) Si,Mg_(2) Sn and Mg_(2)(Si_xSn_(1-x))phases.After adding 0.8 wt.%Y,0.3 wt.%Bi,0.9 wt.%Sb and 0.9 wt.%Sr,respectively into the Mg-5 Sn-1 Si magnesium alloy,Mg_(24)Y_(5),Mg_(3) Bi_(2),Mg_(3) Sb_(2) and Mg_(2) Sr phases are precipitated accordingly.Trace elements can refineα-Mg grain and Chinese scriptshaped Mg_(2) Si phase.Refinement efficiency of different trace elements onα-Mg grain and Mg_(2) Si phase is varied.Sr element has the best refinement effect,followed by Sb and Bi,while Y has the least refinement effect.Mg-5 Sn-1 Si-0.9 Sr alloy has higher tensile properties than the other three modified alloys.The refinement mechanism of Y,Bi and Sr elements on Mg-5 Sn-1 Si magnesium alloy can be explained by the growth restriction factors and the solute undercooling.For Mg-5 Sn-1 Si-0.9 Sb alloy,the heterogeneous nuclei of Mg_(3) Sb_(2) phase is the main reason for the refinement of grains and second phases.

Refining Effect of a New Al3Ti1B1RE Master Alloy on Al Sheets Used for Can Manufacture and Behavior of Rare Earths in Master Alloy

The refining effect of Al3Ti1B1RE master alloy on Al sheets used for pressure can manufacture and the behavior of mixed rare earths in master alloy were investigated with XRD, OM, SEM and EDAX. It is found that the refining effect of the refiner on the material has superiority over foreign or domestic Al5Ti1B refiner, and the refiner still retains its refining ability for 6 h after adding it to molten Al, thus improving the strength and plasticity of the material remarkably. The excellent refining effect and stability of AlTiBRE refiner result from that RE can lower the surface energy of molten Al and improve the wetting characteristics of molten Al on refinement nuclei such as TiAl 3, TiB 2, etc., thus giving full play to the effect of heterogeneous nucleation and impeding the congregating tendency of TiB 2 phase in molten Al. At the same time, RE gathering in front of solid/liquid interface are also easy to cause composition supercooling in molten Al, thus impeding the growth of α Al grains and promoting α Al nucleation on refinement nuclei. In addition, RE also play certain role in purification and grain refinement, or modification, especially their effect of purification can improve the metallurgical quality of AlTiBRE master alloy.

Influence of rare earth elements on corrosion resistance of BFe10-1-1 alloys in flowing marine water

The corrosion behavior of BFe10-1-1 alloy with different rare earth （RE） contents in simulated flowing marine water was investigated by X-ray diffractometer and scanning electron microscope （SEM）. It was demonstrated that the corrosion rate of BFel0-1-1 alloy with the same chemical compositions in faster flow velocity of marine water was higher than that in a lower flow velocity of marine water. Fixing the flow velocity, BFe 10-1-1 alloy had the best flushing corrosion resistance when the RE content was 0.04wt.%. The consequence of such good corrosion resistance was attributed to the formation of compact protective film on alloy surface containing RE phase such as CeNis. The RE-contained film combines with other corrosion products firmly, which was difficult to fall off from the alloy surface in the flowing marine water. Additionally, SEM analysis confirmed that pitting mechanism, which would be transformed to spalling mechanism gradually with further increasing RE content, was the prevalent mechanism when the alloy contained 0.04wt.%RE.

Influence of Al-5Ti-1B master alloy addition on the grain size of AZ91 alloy

The mechanical properties of castings depend on the grain size.There is evidence that titanium and boron(Al-5Ti-1B master alloy)affect the grain size of magnesium alloys.Here,the influence of the addition of 0-1 wt.%of Al-5Ti-1B master alloy on the grain size of AZ91 magnesium alloy was investigated.Melting of the alloy was performed in steel and corundum crucibles.To study the effect of cooling rate on grain size,cylindrical samples were cast in steel and fireclay molds.The Al-5Ti-1B master alloy addition did not change the phase composition of the AZ91 alloy.This study demonstrates that the addition of Al-5Ti-1B did not contribute to the grain refinement of the AZ91 alloy,but rather led to its coarsening for samples cast in both the steel and fireclay molds.Increasing the holding time after the addition of the Al-5Ti-1B master alloy from 15 to 110 minutes also did not lead to significant grain coarsening.The mechanical properties of the AZ91 alloy samples slightly improved after Al-5Ti-1B addition.

Effects of conform continuous extrusion and heat treatment on the microstructure and mechanical properties of Al–13Si–7.5Cu–1Mg alloy

The effects of conform continuous extrusion and subsequent heat treatment on the mechanical and wear-resistance properties of high-alloying Al–13Si–7.5Cu–1Mg alloy were investigated.The microstructures of alloys before and after conform processing and aging were compared by transmission electron microscopy and scanning electron microscopy,respectively.The results reveal that the primary phases were broken and refined by intense shear deformation during conform processing.After the conform-prepared Al–13Si–7.5Cu–1Mg alloy was subjected to solid-solution treatment at 494℃for 1.5 h and aging at 180℃for 4 h,its hardness improved from HBS 115.8 to HBS 152.5 and its ultimate tensile strength increased from 112.6 to 486.8 MPa.Its wear resistance was also enhanced.The factors leading to the enhanced strength,hardness,and wear resistance of the alloy were discussed in detail.

Determination of critical parameters for dynamic recrystallization in Ti-6Al-2Zr-1Mo-1V alloy

The true stress-strain curves of Ti-6Al-2Zr-1Mo-1V alloy were achieved by a series of isothermal compression tests with height reduction of 60% under the deformation temperatures of 1073-1323 K and the strain rates of 0.01-10s 1.The critical conditions for the onset of DRX were attained when the value of d /d,where strain hardening rate d /d,reached the minimum which corresponds to an inflection of θ versus σ curve.Thus,two important potential parameters,critical strain and critical stress,were identified,and expressed as εc/εp=0.37-0.60,σc/σp=0.81-0.91.Furthermore,by the regression analysis for conventional hyperbolic sine equation,the main material parameters such as α,β,n,and DRX activation energy,Q,were calculated.In addition,the evolution of Q with strain rate and temperature was revealed as a 3D response surface.

Effect of Ca addition on grain refinement of Mg–9Li–1Al alloy

The as-cast and as-extruded Mg–9Li–1Al–xCa alloys(x=0,0.2;wt%)were prepared by a simple alloying process followed by hot extrusion with an extrusion ratio of 28.2.The microstructures of the as-cast and as-extruded Mg–9Li–1Al–xCa alloys were observed to investigate the effect of calcium(Ca)element on the Mg–9Li–1Al(LA91)alloy,and the crystallographic calculations between Al_(2)Ca and the matrix(α-Mg andβ-Li phases)were examined on the basis of the edge-to-edge matching model.The experimental results indicate that the addition of 0.2 wt%Ca into LA91 alloy reduce the size of theα-Mg phases in the as-cast alloy and that ofβ-Li phases in the as-extruded alloy due to the Al_(2)Ca particles distributed inside the matrix.Crystallographic calculation results suggested that there is a good crystallographic matching between the matrix and Al_(2)Ca,which confirmed that Al_(2)Ca particles can act as a heterogeneous nucleation site for bothα-Mg andβ-Li phases and were effective grain refiners for LA91 alloy.

Improvement on the Oxidation Resistance of a Ti_3Al Based Alloy by Cr1-xAl_xN (0≤x≤0.47) Coatings

Cr1-xAlxN coatings have been deposited on a Ti3Al based alloy by reactive sputtering method. The results of the isothermal oxidation test at 800-900℃ showed that Cr1-xAlxN coatings could remarkably reduce the oxidation rate of the alloy owing to the formation of Al2O3＋Cr2O3 mixture oxide scale on the surface of the coatings. No spallation of the coatings or oxide scales took place during the cyclic oxidation at 800℃. Ti was observed to diffuse into the coatings, the diffusion distance of which was very short, and the diffusion ability of it was proportional to the AI content in the coatings. Compared to Ti, Nb can diffuse much more easily through the whole coatings and oxide scales.

Effect of Trace Sc and Zr on the Mechanical Properties and Microstructure of A1 Alloy 2618

An experimental 2618(Al-Cu-Mg-Fe-Ni) alloy added with trace Sc and Zr was prepared by ingot metallurgy (IM) method. The aging behavior of the alloy was studied by Vickers hardness measurement at 200℃ and 300℃. and the tensile properties of alloy specimens were measured at 20℃, 200℃, 250℃ and 300℃. The microstructure was observed by using optical microscope, SEM and TEM. It was found that the addition of Sc and Zr to 2618 alloy resulted in a primary Al_3(Sc,Zr) phase which could refine the grain because it acts as nuclei of heterogeneous crystallization in the melt during solidification. The secondary Al_3(Sc,Zr) particles were full coherent with matrix and had obvious precipitation hardening effect. They also made the S' phase precipitate more homogeneous. So the strength of alloy increases at both ambient and elevated temperatures without a decrease of ductility. The ductile fracture of alloy occurs by microvoid nucleation, growth and coalescence, so the microvoid coalescence is the dominant fracture mechanism.

In-situ SEM Observation of Monotonic and Cyclic Deformed Structure in Ti-2A1-2.5Zr Alloy

The SEM observation in situ of monotonic and cyclic deformed structure in Ti-ZA1-2.5Zr alloy was performed. The regularity of slippage, crack nucleation, propagation and the typical dislocation configuration were also investigated. The twin and twist play an important role in maintaining homogeneous deformation in the final plastic deformation stage.

Effect of TiB2 and Al3Ti on the microstructure,mechanical properties and fracture behaviour of near eutectic Al−12.6Si alloy

A near eutectic Al−12.6Si alloy was developed with 0.0wt%,2.0wt%,4.0wt%,and 6.0wt%Al−5Ti−1B master alloy.The micro-structural morphology,hardness,tensile strength,elongation,and fracture behaviour of the alloys were studied.The unmodified Al−12.6Si al-loy has an irregular needle and plate-like eutectic silicon(ESi)and coarse polygonal primary silicon(PSi)particles in the matrix-likeα-Al phase.The P_(Si),E_(Si),andα-Al morphology and volume fraction were changed due to the addition of the Al−5Ti−1B master alloy.The hardness,UTS,and elongation improved due to the microstructural modification.Nano-sized in-situ Al3Ti particles and ex-situ TiB_(2)particles caused the mi-crostructural modification.The fracture images of the developed alloys exhibit a ductile and brittle mode of fracture at the same time.The Al−5Ti−1B modified alloys have a more ductile mode of fracture and more dimples compared to the unmodified alloy.