In this paper, Fe30Pt70/Fe3O4 core/shell nanoparticles were synthesized by chemical routine and the layered polyethylenimine （PEI）-Fe30Pt70/Fe3O4 structure was constructed by molecule-mediated self-assembly techniqu...In this paper, Fe30Pt70/Fe3O4 core/shell nanoparticles were synthesized by chemical routine and the layered polyethylenimine （PEI）-Fe30Pt70/Fe3O4 structure was constructed by molecule-mediated self-assembly technique. The dimension of core/shell structured nanoparticles was that of 4nm core and 2 nm shell. After annealing under a flow of forming gas （50%Ar2＋30%H2） for 1 h at or above 400℃, the iron oxide shell was reduced to Fe and diffused to Pt-rieh core, which leaded to the formation of L1. phase FePt at low temperature. The x-ray diffraction results and magnetic properties measurement showed that the chemical ordering temperature of Fe30Pt70/Fe3O4 core/shell nanoparticles assembly can be reduced to as low as 400℃. The sample annealed at 400℃ showed the eoereivity of 4KOe with the applied field of 1.5T. The core/shell structure was suggested to be an effective way to reduce the ordering temperature obviously.展开更多
Monodisperse microspheres （mean diameter 200-300 nm） with polystyrene cores and poly（acrylamide-co-butyl methacrylate） shells were prepared by using a free radical polymerization method. Moreover, the effect of mi...Monodisperse microspheres （mean diameter 200-300 nm） with polystyrene cores and poly（acrylamide-co-butyl methacrylate） shells were prepared by using a free radical polymerization method. Moreover, the effect of mixed solvent on the preparation, morphology and monodispersity was investigated. The experimental results showed that solubility parameter of butyl methacrylate and solvent affected mainly the molding of monodisperse core-shell microspheres. When the microspheres were fabricated in a sequential synthesis process, addition of hydrophilic and organic solvent including butyl methacrylate led to spherical degree of the particles becoming worse, and the mean diameter of the microspheres decreased and the monodispersity became better with increasing the crosslinker methylenebisacrylamide dosage.展开更多
Core-shell structured polyacrylic（named CSSP） impact modifiers consisting of a rubbery poly（n-butyl acrylate） core and a rigid poly（methyl methacrylate） shell with a size of about 353 nm were prepared by seed em...Core-shell structured polyacrylic（named CSSP） impact modifiers consisting of a rubbery poly（n-butyl acrylate） core and a rigid poly（methyl methacrylate） shell with a size of about 353 nm were prepared by seed emulsion polymerization. The CSSP modifiers with different core-shell weight ratios（90/10, 85/15, 80/20, 75/25, 70/30, 65/35 and 60/40） were used to modify the toughness of poly（butylene terephthalate）（PBT） by melt blending. It was found that the polymerization had a very high instantaneous conversion（ 95.7%） and overall conversion（99.7%）. The morphology of the core-shell structure was confirmed by means of transmission electron microscopy. Scanning electron microscopy was used to observe the morphology of the fractured surfaces. Differential scanning calorimeter was used to study the crystallization behaviors of PBT/CSSP blends. The dynamic mechanical analyses of PBT/CSSP blends showed two merged transition peaks of PBT matrix, with the presence of CSSP core-shell structured modifier, that were responsible for the improvement of PBT toughness. The results indicated that the notch impact strength of PBT/CSSP blends with a core-shell weight ratio of 75/25 was almost 8.64 times greater than that of pure PBT, and the mechanical properties agreed well with the SEM observation.展开更多
基金Project supported by the National Natural Science Foundation of China （Grant No 50641006） and the Science Foundation of Education Commission of Beijing, China.
文摘In this paper, Fe30Pt70/Fe3O4 core/shell nanoparticles were synthesized by chemical routine and the layered polyethylenimine （PEI）-Fe30Pt70/Fe3O4 structure was constructed by molecule-mediated self-assembly technique. The dimension of core/shell structured nanoparticles was that of 4nm core and 2 nm shell. After annealing under a flow of forming gas （50%Ar2＋30%H2） for 1 h at or above 400℃, the iron oxide shell was reduced to Fe and diffused to Pt-rieh core, which leaded to the formation of L1. phase FePt at low temperature. The x-ray diffraction results and magnetic properties measurement showed that the chemical ordering temperature of Fe30Pt70/Fe3O4 core/shell nanoparticles assembly can be reduced to as low as 400℃. The sample annealed at 400℃ showed the eoereivity of 4KOe with the applied field of 1.5T. The core/shell structure was suggested to be an effective way to reduce the ordering temperature obviously.
基金Funded by the National Natural Science Foundation of China (No. 20976202)
文摘Monodisperse microspheres （mean diameter 200-300 nm） with polystyrene cores and poly（acrylamide-co-butyl methacrylate） shells were prepared by using a free radical polymerization method. Moreover, the effect of mixed solvent on the preparation, morphology and monodispersity was investigated. The experimental results showed that solubility parameter of butyl methacrylate and solvent affected mainly the molding of monodisperse core-shell microspheres. When the microspheres were fabricated in a sequential synthesis process, addition of hydrophilic and organic solvent including butyl methacrylate led to spherical degree of the particles becoming worse, and the mean diameter of the microspheres decreased and the monodispersity became better with increasing the crosslinker methylenebisacrylamide dosage.
基金financially supported by Program for Changjiang Scholars and Innovative Research Team in University-IRT13060Key Lab for Micro-and Nano-Scale Boron Nitride Materials in Hebei Province
文摘Core-shell structured polyacrylic（named CSSP） impact modifiers consisting of a rubbery poly（n-butyl acrylate） core and a rigid poly（methyl methacrylate） shell with a size of about 353 nm were prepared by seed emulsion polymerization. The CSSP modifiers with different core-shell weight ratios（90/10, 85/15, 80/20, 75/25, 70/30, 65/35 and 60/40） were used to modify the toughness of poly（butylene terephthalate）（PBT） by melt blending. It was found that the polymerization had a very high instantaneous conversion（ 95.7%） and overall conversion（99.7%）. The morphology of the core-shell structure was confirmed by means of transmission electron microscopy. Scanning electron microscopy was used to observe the morphology of the fractured surfaces. Differential scanning calorimeter was used to study the crystallization behaviors of PBT/CSSP blends. The dynamic mechanical analyses of PBT/CSSP blends showed two merged transition peaks of PBT matrix, with the presence of CSSP core-shell structured modifier, that were responsible for the improvement of PBT toughness. The results indicated that the notch impact strength of PBT/CSSP blends with a core-shell weight ratio of 75/25 was almost 8.64 times greater than that of pure PBT, and the mechanical properties agreed well with the SEM observation.