Superfine cerium-zinc oxides Ce1-xZnxO2-x with x = 0, 0.1, 0.3, 0.5, and 1.0 were obtained by grinding Ce（SO4）2·4H2O, ZnSO4·7H2O and NH4HCO3 under the condition of surfactant PEG-400 being present at room ...Superfine cerium-zinc oxides Ce1-xZnxO2-x with x = 0, 0.1, 0.3, 0.5, and 1.0 were obtained by grinding Ce（SO4）2·4H2O, ZnSO4·7H2O and NH4HCO3 under the condition of surfactant PEG-400 being present at room temperature, washing the mixture with water to remove soluble inorganic salts, drying at 80°C, and calcining.The precursor and its calcined samples were characterized using thermogravimetry and differential thermal analyses（TG/DTA）, UV-vis absorption spectroscopy, X-ray powder diffraction（XRD）, and scanning electron microscopy（SEM）.The results showed that superfine Ce1-xZnxO2-x behaved as an excellent UV-shielding material.The ZnO-doped CeO2 can facilitate the formation of crystalline state CeO2.The catalytic ability of products used in air oxidation of castor oil was investigated.The results showed that the catalytic abilities of products decreased with increasing zinc amount.展开更多
Nano-sized cerium-titanium pyrophosphates Ce1-xTixP2O7 （with x = 0, 0.2, 0.5, 0.7, 0.9, and 1.0） were obtained by grinding a mixture of Ce（SO4）2·4H2O, Ti（SO4）2, and Na4P2O7·10H2O in the presence of sur...Nano-sized cerium-titanium pyrophosphates Ce1-xTixP2O7 （with x = 0, 0.2, 0.5, 0.7, 0.9, and 1.0） were obtained by grinding a mixture of Ce（SO4）2·4H2O, Ti（SO4）2, and Na4P2O7·10H2O in the presence of surfactant PEG-400 at room temperature, washing the mixture with water to remove soluble inorganic salts, and drying at 100℃. The products and their calcined samples were characterized using ultraviolet-visible spectroscopy （UV-vis）, thermogravimetry and differential thermal analyses （TG/DTA）, X-ray powder diffraction （XRD）, and transmission electron microscopy （TEM）. The results show that nano-sized Ce1-xTixP2O7 behave as an excellent UV-shielding material. Thereinto, the CeP2O7 has the most excellent UV-shielding effect, and the amorphous state of Ce0.8Ti0.2P2O7 can keep at a higher temperature than CeP2O7. Therefore, the stabilization of the amorphous state of the cerium pyrophosphates was carded out by doping titanium. This stabilization is a significant improvement, which enables to apply these amorphous pyrophosphates not only to cosmetics and paints, but also plastics and films.展开更多
基金supported by the Natural Scientific Foundation of Guangxi Province (No. 0832111)the Large Apparatus Cooperation Community Net Foundation of Guangxi Province, China (No. 695-2008-108)the Undergraduate Innovation Foundation of School of Chemistry and Chemical Engineering of Guangxi University
文摘Superfine cerium-zinc oxides Ce1-xZnxO2-x with x = 0, 0.1, 0.3, 0.5, and 1.0 were obtained by grinding Ce（SO4）2·4H2O, ZnSO4·7H2O and NH4HCO3 under the condition of surfactant PEG-400 being present at room temperature, washing the mixture with water to remove soluble inorganic salts, drying at 80°C, and calcining.The precursor and its calcined samples were characterized using thermogravimetry and differential thermal analyses（TG/DTA）, UV-vis absorption spectroscopy, X-ray powder diffraction（XRD）, and scanning electron microscopy（SEM）.The results showed that superfine Ce1-xZnxO2-x behaved as an excellent UV-shielding material.The ZnO-doped CeO2 can facilitate the formation of crystalline state CeO2.The catalytic ability of products used in air oxidation of castor oil was investigated.The results showed that the catalytic abilities of products decreased with increasing zinc amount.
基金supported by the Natural Sci-ence Foundation of Guangxi Province, China (No. 0640009)
文摘Nano-sized cerium-titanium pyrophosphates Ce1-xTixP2O7 （with x = 0, 0.2, 0.5, 0.7, 0.9, and 1.0） were obtained by grinding a mixture of Ce（SO4）2·4H2O, Ti（SO4）2, and Na4P2O7·10H2O in the presence of surfactant PEG-400 at room temperature, washing the mixture with water to remove soluble inorganic salts, and drying at 100℃. The products and their calcined samples were characterized using ultraviolet-visible spectroscopy （UV-vis）, thermogravimetry and differential thermal analyses （TG/DTA）, X-ray powder diffraction （XRD）, and transmission electron microscopy （TEM）. The results show that nano-sized Ce1-xTixP2O7 behave as an excellent UV-shielding material. Thereinto, the CeP2O7 has the most excellent UV-shielding effect, and the amorphous state of Ce0.8Ti0.2P2O7 can keep at a higher temperature than CeP2O7. Therefore, the stabilization of the amorphous state of the cerium pyrophosphates was carded out by doping titanium. This stabilization is a significant improvement, which enables to apply these amorphous pyrophosphates not only to cosmetics and paints, but also plastics and films.