Allyl terminated polyether was used to improve the hydrophilicity of addition-cured room temperature vulcanization silicone rubber. With the increasing of the polyether, both the hydrophilicity and water absorbed of t...Allyl terminated polyether was used to improve the hydrophilicity of addition-cured room temperature vulcanization silicone rubber. With the increasing of the polyether, both the hydrophilicity and water absorbed of the vulcanizates were increased. The mechanical properties were also improved by adding the polyether. The result showed that 1.5wt% of the polyether provided the silicone rubber with proper hydrophilicity.展开更多
A new kind of modified thermoset resins were synthesized by phase-transfer Williamson reaction from novolac resin and mixtures of allyl- and propargyl-chlorides. The compositions of the resins were defined by 1H NMR ...A new kind of modified thermoset resins were synthesized by phase-transfer Williamson reaction from novolac resin and mixtures of allyl- and propargyl-chlorides. The compositions of the resins were defined by 1H NMR （nuclear magnetic resonanse） spectroscopy and the dependence of the cured materials properties on the composition was established. Increase of a propargyl content resulted in char yield raise and the maximum value had been found for propargylated resin--58%. DSC （differential scanning calorimetry）-analysis of the resins has demonstrated that exothermic enthalpy of the curing process could be adjusted by varying the content of propargyl and allyl groups in the resin.展开更多
Non-isothermal kinetic simulation analysis was carried for CFRP （carbon fiber reinforced plastic） based on PN （propargylated novolac） resins with various curing enthalpy. The simulation study was performed for CFR...Non-isothermal kinetic simulation analysis was carried for CFRP （carbon fiber reinforced plastic） based on PN （propargylated novolac） resins with various curing enthalpy. The simulation study was performed for CFRP with 40% mass resin content. It was shown that, curing enthalpy of PN resin must be less than 600 J/g to avoid uncontrolled heat emission causing destruction of composite sample.展开更多
文摘Allyl terminated polyether was used to improve the hydrophilicity of addition-cured room temperature vulcanization silicone rubber. With the increasing of the polyether, both the hydrophilicity and water absorbed of the vulcanizates were increased. The mechanical properties were also improved by adding the polyether. The result showed that 1.5wt% of the polyether provided the silicone rubber with proper hydrophilicity.
文摘A new kind of modified thermoset resins were synthesized by phase-transfer Williamson reaction from novolac resin and mixtures of allyl- and propargyl-chlorides. The compositions of the resins were defined by 1H NMR （nuclear magnetic resonanse） spectroscopy and the dependence of the cured materials properties on the composition was established. Increase of a propargyl content resulted in char yield raise and the maximum value had been found for propargylated resin--58%. DSC （differential scanning calorimetry）-analysis of the resins has demonstrated that exothermic enthalpy of the curing process could be adjusted by varying the content of propargyl and allyl groups in the resin.
文摘Non-isothermal kinetic simulation analysis was carried for CFRP （carbon fiber reinforced plastic） based on PN （propargylated novolac） resins with various curing enthalpy. The simulation study was performed for CFRP with 40% mass resin content. It was shown that, curing enthalpy of PN resin must be less than 600 J/g to avoid uncontrolled heat emission causing destruction of composite sample.