A ceramic layer was prepared on the surface of Al2O3f/ZL109 composites by means of micro-arc oxidation （MAO） technique. The surface morphology and phase constituent of the ceramic layer were analyzed using scanning ...A ceramic layer was prepared on the surface of Al2O3f/ZL109 composites by means of micro-arc oxidation （MAO） technique. The surface morphology and phase constituent of the ceramic layer were analyzed using scanning electron microscope and X-ray diffraction. The polarization curves of the composites before and after MAO treatment were measured and analyzed. The results showed that after Al2O3f/ZL109 composites were treated using MAO technique in silicate solution, the ceramic layer formed, and it was composed of Al, Si, and mullite phase. Al and Si came from Al alloy matrix of the composites, and the mullite phase formed in process of MAO. Al2O3 fiber in the composites affects the electric conductivity of the composites, the MAO reaction is promoted, and the cera- mic layer forming on the composite material side is slightly thicker than that on the Al alloy side. After Al2O3f/ZL109 composites were treated using MAO technique, the corro- sion resistance of the composites is significantly improved.展开更多
The superplasticity of an Al203p/6061Al composite, fabricated by powder metallurgy techniques, has been investigated. Instead of any special thermomechanical processing or hot rolling, simple ...The superplasticity of an Al203p/6061Al composite, fabricated by powder metallurgy techniques, has been investigated. Instead of any special thermomechanical processing or hot rolling, simple hot extrusion has been employed to obtain a fine grained structure before superplastic testing. Superplastic tensile tests were performed at strain rates ranging from 10-2 to 10-4 s-1 and at temperatures from 833 to 893 K. A maximum elongation of 200% was achieved at a temperature of 853 K and an initial strain rate of 1.67×103 s-1. The highest value obtained for the strain rate sensitivity index (in) was 0.32. Differential scanning calorimeter was used to ascertain the possibility of any partial melting in the vicinity of optimum superplastic temperature. These results suggested that no liquid phase existed where maximum elongation was achieved and deformation took place entirely in the solid state.展开更多
Al/Mg alloy multilayered composites were produced successfully at the lower temperature（280 C） by accumulative roll bonding（ARB） processing technique.The microstructures of Al and Mg alloy layers were characterize...Al/Mg alloy multilayered composites were produced successfully at the lower temperature（280 C） by accumulative roll bonding（ARB） processing technique.The microstructures of Al and Mg alloy layers were characterized by scanning electron microscopy and transmission electron microscopy.Vickers hardness and three-point bending tests were conducted to investigate mechanical properties of the composites.It is found that Vickers hardness,bending strength and stiffness modulus of the Al/Mg alloy multilayered composite increase with increasing the ARB pass.Delamination and crack propagation along the interface are the two main failure modes of the multilayered composite subjected to bending load.Strengthening and fracture mechanisms of the composite are analyzed.展开更多
Al alloy matrix composites reinforced with copper-coated graphite particle have been prepared by melt stirring process in this work.The effect of the addition of Mg on distribution of the graphite particles has been i...Al alloy matrix composites reinforced with copper-coated graphite particle have been prepared by melt stirring process in this work.The effect of the addition of Mg on distribution of the graphite particles has been investigated.Scanning electron microscopy （SEM） was used to observe the micro-morphology of Al alloy matrix composites reinforced with graphite particles.Meanwhile,the content of graphite was analyzed in the different position of casting by dissolution method and the mechanical properties of the composites were detected.The results show that the content of graphite increase with increasing Mg content;the graphite particles distribute uniformly in the particle reinforced metal matrix composites （PMMC） with 0.6 wt pct Mg;however,the agglomeration of the graphite particles is observed obviously in the matrix when Mg content is more than 1.0 wt pct.In addition,the proper Mg addition amount is beneficial to enhance the mechanical properties of the graphite particles reinforced Al alloy matrix composites and the abrasion resistance of the materials due to a reduce friction coefficient.展开更多
基金financially supported by the National University Student Innovation Program (No. 101011202)
文摘A ceramic layer was prepared on the surface of Al2O3f/ZL109 composites by means of micro-arc oxidation （MAO） technique. The surface morphology and phase constituent of the ceramic layer were analyzed using scanning electron microscope and X-ray diffraction. The polarization curves of the composites before and after MAO treatment were measured and analyzed. The results showed that after Al2O3f/ZL109 composites were treated using MAO technique in silicate solution, the ceramic layer formed, and it was composed of Al, Si, and mullite phase. Al and Si came from Al alloy matrix of the composites, and the mullite phase formed in process of MAO. Al2O3 fiber in the composites affects the electric conductivity of the composites, the MAO reaction is promoted, and the cera- mic layer forming on the composite material side is slightly thicker than that on the Al alloy side. After Al2O3f/ZL109 composites were treated using MAO technique, the corro- sion resistance of the composites is significantly improved.
基金This work was supported by the National Natural Science Foundation of China,under grant No.59781004.
文摘The superplasticity of an Al203p/6061Al composite, fabricated by powder metallurgy techniques, has been investigated. Instead of any special thermomechanical processing or hot rolling, simple hot extrusion has been employed to obtain a fine grained structure before superplastic testing. Superplastic tensile tests were performed at strain rates ranging from 10-2 to 10-4 s-1 and at temperatures from 833 to 893 K. A maximum elongation of 200% was achieved at a temperature of 853 K and an initial strain rate of 1.67×103 s-1. The highest value obtained for the strain rate sensitivity index (in) was 0.32. Differential scanning calorimeter was used to ascertain the possibility of any partial melting in the vicinity of optimum superplastic temperature. These results suggested that no liquid phase existed where maximum elongation was achieved and deformation took place entirely in the solid state.
基金supported by the National Natural Science Foundation of China (Grant No. 50890173)
文摘Al/Mg alloy multilayered composites were produced successfully at the lower temperature（280 C） by accumulative roll bonding（ARB） processing technique.The microstructures of Al and Mg alloy layers were characterized by scanning electron microscopy and transmission electron microscopy.Vickers hardness and three-point bending tests were conducted to investigate mechanical properties of the composites.It is found that Vickers hardness,bending strength and stiffness modulus of the Al/Mg alloy multilayered composite increase with increasing the ARB pass.Delamination and crack propagation along the interface are the two main failure modes of the multilayered composite subjected to bending load.Strengthening and fracture mechanisms of the composite are analyzed.
基金supported financially by the National Natural Science Foundation of China (No. 50774021)the Ministry of Science and Technology of China (No.2008AA03Z512)
文摘Al alloy matrix composites reinforced with copper-coated graphite particle have been prepared by melt stirring process in this work.The effect of the addition of Mg on distribution of the graphite particles has been investigated.Scanning electron microscopy （SEM） was used to observe the micro-morphology of Al alloy matrix composites reinforced with graphite particles.Meanwhile,the content of graphite was analyzed in the different position of casting by dissolution method and the mechanical properties of the composites were detected.The results show that the content of graphite increase with increasing Mg content;the graphite particles distribute uniformly in the particle reinforced metal matrix composites （PMMC） with 0.6 wt pct Mg;however,the agglomeration of the graphite particles is observed obviously in the matrix when Mg content is more than 1.0 wt pct.In addition,the proper Mg addition amount is beneficial to enhance the mechanical properties of the graphite particles reinforced Al alloy matrix composites and the abrasion resistance of the materials due to a reduce friction coefficient.