The rheological behavior of partially solidified Al-10% Cu alloy is in-vestigated.It is found that the slurry presents the character of a psoudoplastie fluid inisothermally holding and the apparent viscosity increases...The rheological behavior of partially solidified Al-10% Cu alloy is in-vestigated.It is found that the slurry presents the character of a psoudoplastie fluid inisothermally holding and the apparent viscosity increases with increasing cooling ratein continuously cooling.The effect of cooling rate on the apparent viscosity decreasesin high stirring rate range.The measured value of apparent viscosity is influenced bythe diameter of the screw propeller.展开更多
The structure change of α2/γ interface in a Ti-45Al-10Nb alloy induced by hot deformation was investigated by conventional and high-resolution transmission eIectron microscopy. Two types of hot deformation induced s...The structure change of α2/γ interface in a Ti-45Al-10Nb alloy induced by hot deformation was investigated by conventional and high-resolution transmission eIectron microscopy. Two types of hot deformation induced special α2/γ intedeces, coherent intedeces with high density of ledges and semi-coherent α2/γ intedeces were found to be due to the absorption of mobile dislocations into the α2/γ inteface. For the misoriented semi-coherent α2/γ interfaces, the densities of dislocation ledges increase with the misoriented angle between (111)γ and (0001)α2 planes, and 1/3[111] Frank partial dislocations were involved in the dislocation ledges. Formation mechanism of these deformation-induced α2/γ interfaces was discussed to be related to the role of α2/γ interface5 adjusting the deformation as a dislocation sink absorbing the slipping dislocations in the γ phase展开更多
The texture evaluation of α2 phase in Ti-25Al-10Nb-3V-1Mo sheet during rolling and annealing has been investigated by means of microstructure observation and ODF analysis. From the weak initial {1010} (1210) and {000...The texture evaluation of α2 phase in Ti-25Al-10Nb-3V-1Mo sheet during rolling and annealing has been investigated by means of microstructure observation and ODF analysis. From the weak initial {1010} (1210) and {0001}(1210) textures a {1210}(1010) texture and a {0001}(uvtw)fibre texture are formed after cold rolling. The {0001} (1210) texture is also strengthened simultaneously. The activation process of slip systems is discussed concerning formation of the rolling texture. Because of the disappearance of {0001} (nvtw) fibre texture the primary recrystallization process should occur and the {1210}(1010) texture forms during annealing展开更多
High-resolution transmission electron microscope (HRTEM) was employed to investigate the deformation-induced α2→γ phase transformation phenomenon in a hot deformed Ti-45Al-10Nb alloy. Such a tronsformation can be n...High-resolution transmission electron microscope (HRTEM) was employed to investigate the deformation-induced α2→γ phase transformation phenomenon in a hot deformed Ti-45Al-10Nb alloy. Such a tronsformation can be nucleated either at α2/γ interfaces or at stacking faults on the basal planes of the α2 phase. The growth of deformation-induced γplate is accomplished by the motion of α/6<100> Shockley partials on alternate basal planes (0001)α2, and the α/6<100> Shockley partials move in coordination rather than sweep on (0001)α2 plane one by one. It appears that no atom transportation is involved in this stress-induced α2→γ transfromation.展开更多
Effects of natural aging and test temperature on the tensile behaviors have been studied for a highperformance cast aluminum alloy Al–10Si–1.2Cu–0.7Mn. Based on self-strengthening mechanism and spheroidization micr...Effects of natural aging and test temperature on the tensile behaviors have been studied for a highperformance cast aluminum alloy Al–10Si–1.2Cu–0.7Mn. Based on self-strengthening mechanism and spheroidization microstructures, the alloy tested at room temperature（RT） exhibits higher 0.2% proof stress（YS） of 206 MPa, ultimate tensile strength（UTS） of 331 MPa and elongation of 10%. Increasing aging time improves the YS and UTS and reduces the ductility of the alloy. Further increasing aging time beyond72 h does not signi？cantly increase the tensile strengths. Increasing test temperature significantly decreases the tensile strengths and increases the ductility of the alloy. The UTS of the alloy can be estimated by using the hardness. The Portevin–Le Chatelier effect occurs at RT due to the interactions between solid solution atoms and dislocations. Similar behaviors occurring at 250℃ are attributed to dynamic strain aging mechanism. Increasing aging time leads to decrease in the strain-hardening exponent（n） value and increase in the strain-hardening coeficient（k） value. Increasing test temperature apparently decreases the n and k values. Eutectic phase particles cracking and debonding determine the fracture mechanism of the alloy. Final failure of the alloy mainly depends on the global instability（high temperature, necking） and local instability（RT, shearing）. Different tensile behaviors of the alloy are mainly attributed to different matrix strengths, phase particle strengths and damage rate.展开更多
文摘The rheological behavior of partially solidified Al-10% Cu alloy is in-vestigated.It is found that the slurry presents the character of a psoudoplastie fluid inisothermally holding and the apparent viscosity increases with increasing cooling ratein continuously cooling.The effect of cooling rate on the apparent viscosity decreasesin high stirring rate range.The measured value of apparent viscosity is influenced bythe diameter of the screw propeller.
文摘The structure change of α2/γ interface in a Ti-45Al-10Nb alloy induced by hot deformation was investigated by conventional and high-resolution transmission eIectron microscopy. Two types of hot deformation induced special α2/γ intedeces, coherent intedeces with high density of ledges and semi-coherent α2/γ intedeces were found to be due to the absorption of mobile dislocations into the α2/γ inteface. For the misoriented semi-coherent α2/γ interfaces, the densities of dislocation ledges increase with the misoriented angle between (111)γ and (0001)α2 planes, and 1/3[111] Frank partial dislocations were involved in the dislocation ledges. Formation mechanism of these deformation-induced α2/γ interfaces was discussed to be related to the role of α2/γ interface5 adjusting the deformation as a dislocation sink absorbing the slipping dislocations in the γ phase
文摘The texture evaluation of α2 phase in Ti-25Al-10Nb-3V-1Mo sheet during rolling and annealing has been investigated by means of microstructure observation and ODF analysis. From the weak initial {1010} (1210) and {0001}(1210) textures a {1210}(1010) texture and a {0001}(uvtw)fibre texture are formed after cold rolling. The {0001} (1210) texture is also strengthened simultaneously. The activation process of slip systems is discussed concerning formation of the rolling texture. Because of the disappearance of {0001} (nvtw) fibre texture the primary recrystallization process should occur and the {1210}(1010) texture forms during annealing
文摘High-resolution transmission electron microscope (HRTEM) was employed to investigate the deformation-induced α2→γ phase transformation phenomenon in a hot deformed Ti-45Al-10Nb alloy. Such a tronsformation can be nucleated either at α2/γ interfaces or at stacking faults on the basal planes of the α2 phase. The growth of deformation-induced γplate is accomplished by the motion of α/6<100> Shockley partials on alternate basal planes (0001)α2, and the α/6<100> Shockley partials move in coordination rather than sweep on (0001)α2 plane one by one. It appears that no atom transportation is involved in this stress-induced α2→γ transfromation.
基金supported by the Project Funded by China Postdoctoral Science Foundation(No.2015M571562)
文摘Effects of natural aging and test temperature on the tensile behaviors have been studied for a highperformance cast aluminum alloy Al–10Si–1.2Cu–0.7Mn. Based on self-strengthening mechanism and spheroidization microstructures, the alloy tested at room temperature（RT） exhibits higher 0.2% proof stress（YS） of 206 MPa, ultimate tensile strength（UTS） of 331 MPa and elongation of 10%. Increasing aging time improves the YS and UTS and reduces the ductility of the alloy. Further increasing aging time beyond72 h does not signi？cantly increase the tensile strengths. Increasing test temperature significantly decreases the tensile strengths and increases the ductility of the alloy. The UTS of the alloy can be estimated by using the hardness. The Portevin–Le Chatelier effect occurs at RT due to the interactions between solid solution atoms and dislocations. Similar behaviors occurring at 250℃ are attributed to dynamic strain aging mechanism. Increasing aging time leads to decrease in the strain-hardening exponent（n） value and increase in the strain-hardening coeficient（k） value. Increasing test temperature apparently decreases the n and k values. Eutectic phase particles cracking and debonding determine the fracture mechanism of the alloy. Final failure of the alloy mainly depends on the global instability（high temperature, necking） and local instability（RT, shearing）. Different tensile behaviors of the alloy are mainly attributed to different matrix strengths, phase particle strengths and damage rate.