Al-8%Si铝硅亚共晶合金电磁离心铸造凝固组织研究

采用电磁离心铸造的方法制备Al-8%Si的铝硅亚共晶合金空心管坯,研究了电磁场(electromagnetic field,EMF)对合金凝固宏观及微观组织的影响。结果表明,与传统离心铸造的铝硅亚共晶合金微观组织相比,施加电磁场后凝固组织中α-Al相得到细化,柱状晶随磁场强度增加逐渐成为等轴晶;共晶硅相尺寸在减小,片层间距增加,在硅片层间发现了断裂的共晶硅颗粒。

Structural evolution of spray-formed Al-70wt.%Si alloys during iso-thermal holding in the semi-solid state

The grain growth behavior of spray-formed Al-70wt.%Si alloys was studied in the semi-solid state. The specimens were isothermally heat-treated at various temperatures between the solidus and liquidus of Al-Si alloys and then quenched in water. The microstructure of reheated specimens was characterized using optical and scanning electron microscopies. The isothermal holding experiment was carried out to investigate grain growth behavior as a function of holding time and temperature in the semi-solid state. The coarsening mechanism and the effect of porosity on microstructure were also studied.

Microstructure of Mg-8Zn-4Al-1Ca aged alloy

The microstructure of Mg-8Zn-4Al-1Ca aged alloy was investigated by TEM and HRTEM. The results show that the hardening produced in the Mg-8Zn-4Al-1Ca alloy is considerably higher than that in the Mg-8Zn-4A1 alloy. A dense dispersion of disc-like Ca2Mg6Zn3 precipitates are formed in Mg-8Zn-4Al-1Ca alloy aged at 160 ℃ for 16 h. In addition, the lattice distortions, honeycomb-looking Moir＆#233; fringes, edge dislocations and dislocation loop also exist in the microstructure. The precipitates of alloy aged at 160 ℃ for 48 h are coarse disc-like and fine dispersed grainy. When the alloy is subjected to aging at 160 ℃ for 227 h, the microstructure consists of numerous MgZn2 precipitates and Ca2Mg6Zn3 precipitates. All the analyses show that Ca is a particularly effective trace addition in improving the age-hardening and postponing the formation of MgZn2 precipitates in Mg-8Zn-4Al alloy aged at 160 ℃.

Effects of ZrO_2 Nanoparticles on the Microstructure and Thermal-protective Properties of PEO Coating on Al-12.5%Si Alloy

PEO ceramic coatings including ZrO_2-Al_2O_3-SiO_2 in three phases were prepared on an Al-12.5%Si alloy in electrolyte solutions containing ZrO_2 nanoparticles. The microstructures and phases of the coatings were analyzed by SEM and XRD, and the heat insulation performance and the thermal shock resistance of the coatings were investigated. The compactness of the coating increased significantly and the hindrance of the Si element on plasma electrolytic oxidation process was effectively weakened. The growth rate of the coating was improved substantially with the addition of ZrO_2 nanoparticles. The PEO ceramic coatings are primarily composed of SiO_2 and high temperature steady phases such as a-Al_2O_3 and c-ZrO_2. Both the content of c-ZrO_2 and the heat-insulating property of the coating increased significantly. The ceramic coatings with special microstructure and composition formed in the solutions containing ZrO_2 nanoparticles possess excellent heat insulation performance and thermal shock resistance.

MICROSTRUCTURE AND MACROSEGREGATION OF Al-7%Si ALLOY SOLIDIFIED UNDER COMPLEX EFFECTS OF ELECTROMAGNETIC AND CENTRIFUGAL FORCES

Macrosegregations and microstructures of Al-7%Si alloy solidified under complex of fects of magnetic field and centrifugal forces are studied by means of a set of selfdesigned electromagnetic centrifugal casting (EMCC) device. It is shown that electromagnetic field (EMF) has an important effect on the macrosegregation of centrifugal casting specimen of Al-7%Si alloy in two respects: one is that there exists always a kind of convection in the liquid in front of the S/L interface caused by effect ofthe electromagnetic force; the other is that different atomic clusters of solidparticles with different physical characteristics are subjected to quite different electromagnetic (Lorentz) force. Therefore, their movements get changed. In addition, the formation process of a complex band structure consisting of primary α-Al dendrites and (α-Al+β-Si) eutectics in hypoeutectic Al-Si alloys during EMCC and the effect of EMF are discussed.

Effect of non-isothermal retrogression and re-ageing on through-thickness homogeneity of microstructure and properties of Al-8Zn-2Mg-2Cu alloy thick plate

In order to improve the through-thickness homogeneity and properties of aviation aluminum alloy thick plate.The effect of heating-cooling retrogression and re-ageing on the performance of Al-8Zn-2Mg-2Cu alloy thick plate was investigated by hardness tests, electrical conductivity tests and transmission electron microscopy(TEM) observation.Results revealed that, during retrogression heating, the fine pre-precipitates in surface layer dissolve more and the undissolved η′ or η phases are more coarsened than that of center layer. During slow cooling after retrogression,precipitates continue coarsening but with a lower rate and the secondary precipitation occurs in both layers. Finer precipitates resulting from the secondary precipitation are more in surface. However, the coarsening and secondary precipitation behaviors are restrained in both layers under quick cooling condition. The electrical conductivity and through-thickness homogeneity of precipitates increases while the hardness decreases with cooling rate decreasing. After the optimized non-isothermal retrogression and re-ageing(NRRA) including air-cooling retrogression, the throughthickness homogeneity which is evaluated by integrated retrogression effects has been improved to 94%. The tensile strength, fracture toughness and exfoliation corrosion grade of Al-8Zn-2Mg-2Cu alloy plate is 619 MPa, 24.7 MPa·m^(1/2)and EB, respectively, which indicates that the non-isothermal retrogression and re-aging(NRRA) could improve the mechanical properties and corrosion resistance with higher through-thickness homogeneity.

STRUCTURAL TRANSFORMATION AND ITS REVERSIBILITY IN LIQUID Al-13%Si ALLOY AT HIGH TEMPERATURES

ＳＴＲＵＣＴＵＲＡＬＴＲＡＮＳＦＯＲＭＡＴＩＯＮＡＮＤＩＴＳＲＥＶＥＲＳＩＢＩＬＩＴＹＩＮＬＩＱＵＩＤＡｌ１３％ＳｉＡＬＬＯＹＡＴＨＩＧＨＴＥＭＰＥＲＡＴＵＲＥＳ①ＷａｎｇＷｅｉｍｉｎ，ＢｉａｎＸｉｕｆａｎｇ，ＱｉｎＪｉｎｇｙｕａｎｄＹｅＹｉｆｕＣ...

Influence of surface finish and annealing treatment on oxidation behavior of Ti-48Al-8Cr-2Ag alloy

The effect of surface finish and annealing treatment on the oxidation behavior of Ti-48Al-8Cr-2Ag (molar fraction, %) alloy was investigated at 900 and 1 000 ℃, respectively in air. Thermal gravimetric analysis (TGA) was conducted for the characterization of oxidation kinetics. The microstructures of oxide scales were studied by scanning electron microscopy (SEM) and transmission election microscopy (TEM) techniques. Unfavorable effect of the annealing treatment on the oxidation behavior of the coating was also investigated. The results indicate that the oxidation behavior of the alloy is influenced by surface finish and annealing treatment. The oxidation rate of ground sample is lower than that of the polished alloy at 1 000 ℃ in air. The former forms a scale of merely Al2O3, and the latter forms a scale of the mixture of Al2O3 and TiO2. Annealing can improve the formation of TiO2.

Modification and aging precipitation behavior of hypereutectic AI-21wt.%Si alloy treated by P+Ce combination

In the present study, the tested hypereutectic Al-21wt.%Si alloys were prepared by modifying the melt using different proportions of P and Ce, and then applying T6 heat treatment. The modification effects and mechanism of P＋Ce complex modifier on the Si phase of hypereutectic Al-21wt.%Si alloy were studied, and the aging precipitation behavior after modification was characterized by means of tensile strength measurement, OM, SEM and TEM analysis. The results show that the massive primary silicon phase particles are significantly refined after modification, while the needle-like eutectic silicon crystals become fibrous and short. It was found that the mechanism of phosphorus modification on the primary silicon can be attributed to heterogeneous nucleation of AlP, while the modification mechanism of Ce can be explained by adsorbing-twinning theory. In the aged microstructure of the modified hypereutectic Al-21wt.%Si alloy, there existed some strengthening phases such as AI4Cu9, Al2Cu, AlCu3, and Al57Mn12. The P＋Ce complex modifier not only affected the size of primary silicon and eutectic silicon, but also the aging behavior of alloys under the heat treatment process. When Al-21wt.%Si alloy was modified using 0.08%wt.P ＋ 0.6wt.% Ce, the aging precipitates were dispersed uniformly in the alloy, and its mechanical properties at room and elevated temperatures are optimized （Rm = 287.6 MPa at RT, Rm = 210 MPa at 300 ℃）.

母合金成分和混合温度对受控扩散凝固组织的影响

采用强制对流混合方式的受控扩散凝固技术制备了亚共晶Al-8%Si合金,研究了不同的母合金成分和混合温度对亚共晶Al-8%Si合金组织中初生α-Al相的形貌和尺寸的影响。结果表明,在纯Al与Al-12%Si合金混合后制备的Al-8%Si合金中初生α-Al相为细小圆整的球状晶,而且在纯Al的混合温度为665℃时,初生α-Al相的细化效果最好,晶粒尺寸可以达到43μm。随着母合金中Si含量的增加与纯Al混合温度的升高,初生α-Al相的细化效果变差。