Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO...Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO 2(a natase), Al 2SiO 5, and ZrO 2 in these membranes. Changing the molar ratio of Al∶Si∶Ti∶Zr,the kinds and content of crystal phases of composite membranes could be different, which may lead to a variety of microstructure of membranes. The surface nanoscale topography and microstructure of membranes were investiga ted by XRD,SEM,AFM,EPMA. The effects of additives and heat treatments on the sur face nanoscale topography and microstructure of composite ceramic membranes were also analyzed.展开更多
MoS2/γ－Al2O3 ceramic composite membrane is successfully synthesized by the sol-gel method based on the inorganic salt route. The aluminum hydrate sol derived from the inorganic salt Al(NO3)3, whose transparence and ...MoS2/γ－Al2O3 ceramic composite membrane is successfully synthesized by the sol-gel method based on the inorganic salt route. The aluminum hydrate sol derived from the inorganic salt Al(NO3)3, whose transparence and viscosity are 97% and 1.2 × 10-3 Pa. s, respectively, can be formed through adjusting the ratio of the peptizing agent H+ to Al3+ to 0.3. The aluminum hydrate gel at 110℃ is amorphous in structure and is heat-treated in air at 800℃ to form γ－Al2O3. The precursor derived from the mixture solution of ammonium molybdate, thioacetamide and a reducing agent, can be transformed into crystal MoS2 under reducing condition at 800℃. MoS2/γ－Al2O3 composite membrane is an organic whole and bps no gradation from MoS2 layer to γ－Al2O3 Iayer. The separation factor a H2/H2S through the MoS2/γ－Al2O3 composite membrane increase with rising temperature and a H2/H2S at 600℃ is 4.45 higher than the theoretical separation factor produced by the ideal Knudsen diffusion.展开更多
The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was disc...The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was discussed. Indentation-quench test was conducted to evaluate the effect of thermal fatigue temperature difference （ΔT） and number of thermal cycles （Ⅳ） on fatigue crack growth （Δa）. The mechanical properties and thermal fatigue resistance of TiC/Al203 composites are remarkably improved by the addition of TiC. The thermal shock fatigue of monolithic alumina and TiC/Al2O3 composites is due to a ＂true＂ cycling effect （thermal fatigue）. Crack deflection and bridging are the predominant reasons for the improvement of thermal shock fatigue resistance of the composites.展开更多
In situ Al2O3 whiskers reinforced Ti-Al intermetallic composites were fabricated at ~1200℃ by reaction sintering of cold-consolidated fillets consisting mainly of Ti, Al, and different additives. The phases and micro...In situ Al2O3 whiskers reinforced Ti-Al intermetallic composites were fabricated at ~1200℃ by reaction sintering of cold-consolidated fillets consisting mainly of Ti, Al, and different additives. The phases and microstructures of the sintered composites were characterized using X-ray diffraction (XRD) and scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS). The process of synthesis was investigated using differential thermal analysis (DTA). The effects of processing parameters and additives on the microstructures of the composites and the development of whisker were examined. It is found that the morphology of the whisker is strongly influenced by the additives, the exothermal reaction process, and the processing parameters.展开更多
Non-isothermal kinetic research has been carried out on oxidation behavior of β-Sialon in diphaseβ-Sialon/Al_2O_3 composite at high temperatures. A kinetic formula is established for non-isothermal oxidation process...Non-isothermal kinetic research has been carried out on oxidation behavior of β-Sialon in diphaseβ-Sialon/Al_2O_3 composite at high temperatures. A kinetic formula is established for non-isothermal oxidation process of β-Sialon. The rate of oxidation process is controlled by chemicalreaction at the initial stage and then by diffusion. The apparent activation energies and appar-ent rate constants at different temperatures are determined by treating TG data of the overallprocess.展开更多
The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics...The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics analyses show that the chemical reactions are 3Cu 2O+2Al=6Cu+Al 2O 3 or 3CuO+2Al=3Cu+Al 2O 3. A related equilibrium diagram was drawn. The experiments and investigation show that the formation rate of Al 2O 3 was controlled by the diffusion of oxygen in matrix.展开更多
To improve the mechanical properties of alumina particulates reinforced steel matrix composite, Ti powder was added into the alumina preform, a 5140 steel matrix composite was fabricated by squeeze casting, and the in...To improve the mechanical properties of alumina particulates reinforced steel matrix composite, Ti powder was added into the alumina preform, a 5140 steel matrix composite was fabricated by squeeze casting, and the influences of Ti powder on the microstructure, hardness and bending strength of the composite were investigated, compared with the composite without adding Ti powder. Applied Ti powder and alumina particulates were 10-25 μm and 100-180 μm in size, respectively. Both composites were successfully fabricated, however Ti powder addition increased the infiltration thickness of the composite. In the Ti contained composite, a TiC film in micron scale is formed on the surface of alumina particles, many TiC aggregates are dispersed in the steel matrix without obvious remaining Ti powder. The hardness and the three-point bending strength of the composite reach 49.5 HRC and 1 018 MPa, respectively, which are 17.9% and 52.4% higher than those of the composite in the absence of Ti addition. Fracture morphology shows that the debonding of alumina particulates is eliminated for the composite in the presence of Ti addition. Sessile drop test shows the average wetting angle between 5140 steel and that of Ti coated Al2O3 is about 82.15°, much lower than the wetting angle 150° between steel and pure Al2O3. Therefore, the increase in the mechanical properties of the composite is attributed to the improvement of Al2O3 p/steel interface wetting and bonding by adding Ti powder in the preform.展开更多
Alumina-(0-20 vol. pct) iron composites were fabricated by hot-pressing of well-mixed alumina and iron powders at 1400℃ and 30 MPa for 30 mm. Hot-pressed bodies with nearly theoretical density were obtained for addit...Alumina-(0-20 vol. pct) iron composites were fabricated by hot-pressing of well-mixed alumina and iron powders at 1400℃ and 30 MPa for 30 mm. Hot-pressed bodies with nearly theoretical density were obtained for addition up to 10 vol. pct Fe, but relative density decreased gradually with further increase in Fe addition. The materials exhibit a homogeneous dispersion of Fe. Fracture strength of the composites exhibits a maximum value of 604 MPa at 15 vol. pct Fe, which is 1.5 times that of alumina alone. Fracture toughness increases with the increase in Fe content, reaching 7.5 MPa.m1/2 at 20 vol. pct Fe. The theoretical values of fracture toughness was calculated and compared with the experimental one. Toughening mechanisms of the composites are also discussed.展开更多
In-situ Al2O3/TiAl composites were fabricated by pressure-assisted exothermic dispersion （PAXD） method from elemental powder mixtures of Ti, Al, TiO2, and Nb2O5. The microstructures and mechanical properties of the ...In-situ Al2O3/TiAl composites were fabricated by pressure-assisted exothermic dispersion （PAXD） method from elemental powder mixtures of Ti, Al, TiO2, and Nb2O5. The microstructures and mechanical properties of the as-sintered composites are investigated. The results show that the as-sintered products consist of γ-TiAl, α2-Ti3Al, Al2O3, and NbAl3 phases. Microstructure analysis indicates that Al2O3 particles tend to disperse on the grain boundaries. Application of a moderate pressure of 35 MPa at 1200℃ yields Al2O3/TiAl composites with fine Al2O3 reinforcement and a discontinuous network linking by Al2O3 particles. The aluminide component has a fine submicron γ ＋α2 lamellar microstructure. With increasing Nb2O5 content, Al2O3 particles are dispersed uniformly in the matrix. The hardness of the composites increases gradually, and the bending strength and fracture toughness of the composites reach to the maximum value, respectively.展开更多
Thermal shock resistance of Al2O3-TiCN(30%)-Y2O3(0.2%) composite was studied by hot pressing(HP) method at different temperatures. The study shows that thermal shock resistance of the material is determined by its mic...Thermal shock resistance of Al2O3-TiCN(30%)-Y2O3(0.2%) composite was studied by hot pressing(HP) method at different temperatures. The study shows that thermal shock resistance of the material is determined by its microstructure and reinforced mechanism. According to SEM and calculation of thermal shock, the fractured surface of Al2O3-30%TiCN-0.2%Y2O3 composite is undulate. The residual strength of Al2O3-30%TiCN-0.2%Y2O3 is higher than Al2O3-30%TiCN at 200～800 ℃ after thermal shock. Cracks initiation resistance (R′)and cracks propagation resistance (R″″)of Al2O3-30%TiCN-0.2%Y2O3 composite increases 12% and 5% respectively compared with that of Al2O3-30%TiCN. It matches with experimental results. The addition of Y2O3 forms YAG that inhibits crystal growth, and increases fracture stress, fracture toughness, cracks initiation resistance and cracks propagation resistance. Therefore, thermal shock resistance increases. The fracture work of Al2O3-30%TiCN and Al2O3-30%TiCN-0.2%Y2O3 composites are 132 and 148 J·m-2 respectively.展开更多
Aluminum-matrix boron carbide (B4Cp/Al) is a kind of neutron absorbing material widely used in nuclear spent fuel storage. In order to improve the tensile property of B4Cp/Al composites, a new type of nano-Al2O3 parti...Aluminum-matrix boron carbide (B4Cp/Al) is a kind of neutron absorbing material widely used in nuclear spent fuel storage. In order to improve the tensile property of B4Cp/Al composites, a new type of nano-Al2O3 particle (Al2O3np) reinforced B4Cp/Al + Al2O3np composites were prepared by powder metallurgy method. The Monte Carlo particle transport program (MCNP) was used to determine the influence of Al2O3np on the thermal neutron absorptivity of composites. The universal material testing machine and scanning electron microscope (SEM) were used to study the mechanical properties, microstructure and fracture morphology of B4Cp/Al composites. The results indicated that the neutron absorption properties of B4Cp/Al composites were not affected by the addition of nano-Al2O3 particles in the range of 1 wt%-15 wt%. The addition of Al2O3np can obviously reduce the grain size of B4Cp/Al matrix metals thus improve the tensile strength of the composites. The addition threshold of Al2O3np is about 2.5 wt%. Both B4Cp and Al2O3np change the fracture characteristics of the composites from toughness to brittleness, and the latter is more important.展开更多
ZA22/Al2O3 composites were prepared by means of squeeze casting process. The effects of Ce on the ultimate tensile strength (UTS), impact toughness, and hardness of the composites were studied. The results show that b...ZA22/Al2O3 composites were prepared by means of squeeze casting process. The effects of Ce on the ultimate tensile strength (UTS), impact toughness, and hardness of the composites were studied. The results show that both the UTS and the hardness are improved and the impact toughness is decreased with the increase of the volume fraction of fibers (Vf). After Ce is added ,UTS (Vf>15%) and the hardness are improved at room temperature because of the modification of Ce, but the impact toughness and UTS at elevated temperature are lowered.The filtered action of the fiber preform results in that the influence of the amount of Ce added from 0. 1 wt% to 0. 5 wt% on the mechanical properties of the composites can be ignored.展开更多
Nanoparticles and microparticles reinforced Al matrix composites were fabricated by spark plasma sintering, and the microstructure and tribological properties were investigated systemically. The nano-Al2O3 particle an...Nanoparticles and microparticles reinforced Al matrix composites were fabricated by spark plasma sintering, and the microstructure and tribological properties were investigated systemically. The nano-Al2O3 particle and micro-Al2O3 particle uniformly dispersed in Al matrix composites. The introduction of nanoparticles is beneficial to the decrease of friction coefficient and wear rate, while microparticles are responsible to the high friction coefficient, resulting in the abrasive wear. With the introduction of both nanoparticles and microparticles, their synergic effect will lead to the variation of tribological behavior.展开更多
文摘Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO 2(a natase), Al 2SiO 5, and ZrO 2 in these membranes. Changing the molar ratio of Al∶Si∶Ti∶Zr,the kinds and content of crystal phases of composite membranes could be different, which may lead to a variety of microstructure of membranes. The surface nanoscale topography and microstructure of membranes were investiga ted by XRD,SEM,AFM,EPMA. The effects of additives and heat treatments on the sur face nanoscale topography and microstructure of composite ceramic membranes were also analyzed.
文摘MoS2/γ－Al2O3 ceramic composite membrane is successfully synthesized by the sol-gel method based on the inorganic salt route. The aluminum hydrate sol derived from the inorganic salt Al(NO3)3, whose transparence and viscosity are 97% and 1.2 × 10-3 Pa. s, respectively, can be formed through adjusting the ratio of the peptizing agent H+ to Al3+ to 0.3. The aluminum hydrate gel at 110℃ is amorphous in structure and is heat-treated in air at 800℃ to form γ－Al2O3. The precursor derived from the mixture solution of ammonium molybdate, thioacetamide and a reducing agent, can be transformed into crystal MoS2 under reducing condition at 800℃. MoS2/γ－Al2O3 composite membrane is an organic whole and bps no gradation from MoS2 layer to γ－Al2O3 Iayer. The separation factor a H2/H2S through the MoS2/γ－Al2O3 composite membrane increase with rising temperature and a H2/H2S at 600℃ is 4.45 higher than the theoretical separation factor produced by the ideal Knudsen diffusion.
文摘The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was discussed. Indentation-quench test was conducted to evaluate the effect of thermal fatigue temperature difference （ΔT） and number of thermal cycles （Ⅳ） on fatigue crack growth （Δa）. The mechanical properties and thermal fatigue resistance of TiC/Al203 composites are remarkably improved by the addition of TiC. The thermal shock fatigue of monolithic alumina and TiC/Al2O3 composites is due to a ＂true＂ cycling effect （thermal fatigue）. Crack deflection and bridging are the predominant reasons for the improvement of thermal shock fatigue resistance of the composites.
基金This work was supported by the National Natural Science Foundation of China (No. 50432010, 50372037).
文摘In situ Al2O3 whiskers reinforced Ti-Al intermetallic composites were fabricated at ~1200℃ by reaction sintering of cold-consolidated fillets consisting mainly of Ti, Al, and different additives. The phases and microstructures of the sintered composites were characterized using X-ray diffraction (XRD) and scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS). The process of synthesis was investigated using differential thermal analysis (DTA). The effects of processing parameters and additives on the microstructures of the composites and the development of whisker were examined. It is found that the morphology of the whisker is strongly influenced by the additives, the exothermal reaction process, and the processing parameters.
文摘Non-isothermal kinetic research has been carried out on oxidation behavior of β-Sialon in diphaseβ-Sialon/Al_2O_3 composite at high temperatures. A kinetic formula is established for non-isothermal oxidation process of β-Sialon. The rate of oxidation process is controlled by chemicalreaction at the initial stage and then by diffusion. The apparent activation energies and appar-ent rate constants at different temperatures are determined by treating TG data of the overallprocess.
文摘The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics analyses show that the chemical reactions are 3Cu 2O+2Al=6Cu+Al 2O 3 or 3CuO+2Al=3Cu+Al 2O 3. A related equilibrium diagram was drawn. The experiments and investigation show that the formation rate of Al 2O 3 was controlled by the diffusion of oxygen in matrix.
基金Funded by National Natural Science Foundation of China(No.51265019)
文摘To improve the mechanical properties of alumina particulates reinforced steel matrix composite, Ti powder was added into the alumina preform, a 5140 steel matrix composite was fabricated by squeeze casting, and the influences of Ti powder on the microstructure, hardness and bending strength of the composite were investigated, compared with the composite without adding Ti powder. Applied Ti powder and alumina particulates were 10-25 μm and 100-180 μm in size, respectively. Both composites were successfully fabricated, however Ti powder addition increased the infiltration thickness of the composite. In the Ti contained composite, a TiC film in micron scale is formed on the surface of alumina particles, many TiC aggregates are dispersed in the steel matrix without obvious remaining Ti powder. The hardness and the three-point bending strength of the composite reach 49.5 HRC and 1 018 MPa, respectively, which are 17.9% and 52.4% higher than those of the composite in the absence of Ti addition. Fracture morphology shows that the debonding of alumina particulates is eliminated for the composite in the presence of Ti addition. Sessile drop test shows the average wetting angle between 5140 steel and that of Ti coated Al2O3 is about 82.15°, much lower than the wetting angle 150° between steel and pure Al2O3. Therefore, the increase in the mechanical properties of the composite is attributed to the improvement of Al2O3 p/steel interface wetting and bonding by adding Ti powder in the preform.
文摘Alumina-(0-20 vol. pct) iron composites were fabricated by hot-pressing of well-mixed alumina and iron powders at 1400℃ and 30 MPa for 30 mm. Hot-pressed bodies with nearly theoretical density were obtained for addition up to 10 vol. pct Fe, but relative density decreased gradually with further increase in Fe addition. The materials exhibit a homogeneous dispersion of Fe. Fracture strength of the composites exhibits a maximum value of 604 MPa at 15 vol. pct Fe, which is 1.5 times that of alumina alone. Fracture toughness increases with the increase in Fe content, reaching 7.5 MPa.m1/2 at 20 vol. pct Fe. The theoretical values of fracture toughness was calculated and compared with the experimental one. Toughening mechanisms of the composites are also discussed.
基金supported by the Special Program for Education Bureau of Shaanxi Province, China(Grant No.08JK240)the Breeding Program for Provincial Level Key Research Base of Shaanxi University of Technology, China (Grant No.SLGJD0806)Scientific Research Start up Program for Introduced Talents of Shaanxi University of Technology, China (Grant No.SLGQD0751).
文摘In-situ Al2O3/TiAl composites were fabricated by pressure-assisted exothermic dispersion （PAXD） method from elemental powder mixtures of Ti, Al, TiO2, and Nb2O5. The microstructures and mechanical properties of the as-sintered composites are investigated. The results show that the as-sintered products consist of γ-TiAl, α2-Ti3Al, Al2O3, and NbAl3 phases. Microstructure analysis indicates that Al2O3 particles tend to disperse on the grain boundaries. Application of a moderate pressure of 35 MPa at 1200℃ yields Al2O3/TiAl composites with fine Al2O3 reinforcement and a discontinuous network linking by Al2O3 particles. The aluminide component has a fine submicron γ ＋α2 lamellar microstructure. With increasing Nb2O5 content, Al2O3 particles are dispersed uniformly in the matrix. The hardness of the composites increases gradually, and the bending strength and fracture toughness of the composites reach to the maximum value, respectively.
文摘Thermal shock resistance of Al2O3-TiCN(30%)-Y2O3(0.2%) composite was studied by hot pressing(HP) method at different temperatures. The study shows that thermal shock resistance of the material is determined by its microstructure and reinforced mechanism. According to SEM and calculation of thermal shock, the fractured surface of Al2O3-30%TiCN-0.2%Y2O3 composite is undulate. The residual strength of Al2O3-30%TiCN-0.2%Y2O3 is higher than Al2O3-30%TiCN at 200～800 ℃ after thermal shock. Cracks initiation resistance (R′)and cracks propagation resistance (R″″)of Al2O3-30%TiCN-0.2%Y2O3 composite increases 12% and 5% respectively compared with that of Al2O3-30%TiCN. It matches with experimental results. The addition of Y2O3 forms YAG that inhibits crystal growth, and increases fracture stress, fracture toughness, cracks initiation resistance and cracks propagation resistance. Therefore, thermal shock resistance increases. The fracture work of Al2O3-30%TiCN and Al2O3-30%TiCN-0.2%Y2O3 composites are 132 and 148 J·m-2 respectively.
基金Funded by Natural National Science Foundation of China(NSFC)(No.11305149)National High-Tech R&D Program(863 Program)(No.2013AA030704)。
文摘Aluminum-matrix boron carbide (B4Cp/Al) is a kind of neutron absorbing material widely used in nuclear spent fuel storage. In order to improve the tensile property of B4Cp/Al composites, a new type of nano-Al2O3 particle (Al2O3np) reinforced B4Cp/Al + Al2O3np composites were prepared by powder metallurgy method. The Monte Carlo particle transport program (MCNP) was used to determine the influence of Al2O3np on the thermal neutron absorptivity of composites. The universal material testing machine and scanning electron microscope (SEM) were used to study the mechanical properties, microstructure and fracture morphology of B4Cp/Al composites. The results indicated that the neutron absorption properties of B4Cp/Al composites were not affected by the addition of nano-Al2O3 particles in the range of 1 wt%-15 wt%. The addition of Al2O3np can obviously reduce the grain size of B4Cp/Al matrix metals thus improve the tensile strength of the composites. The addition threshold of Al2O3np is about 2.5 wt%. Both B4Cp and Al2O3np change the fracture characteristics of the composites from toughness to brittleness, and the latter is more important.
文摘ZA22/Al2O3 composites were prepared by means of squeeze casting process. The effects of Ce on the ultimate tensile strength (UTS), impact toughness, and hardness of the composites were studied. The results show that both the UTS and the hardness are improved and the impact toughness is decreased with the increase of the volume fraction of fibers (Vf). After Ce is added ,UTS (Vf>15%) and the hardness are improved at room temperature because of the modification of Ce, but the impact toughness and UTS at elevated temperature are lowered.The filtered action of the fiber preform results in that the influence of the amount of Ce added from 0. 1 wt% to 0. 5 wt% on the mechanical properties of the composites can be ignored.
基金Funded by the National Key R&D Program of China(No.2017YFB1103500)National Science and Technology Major Project(No.2017-VI-0007-0077)the National Natural Science Foundation of China(Nos.51632007,51672218)
文摘Nanoparticles and microparticles reinforced Al matrix composites were fabricated by spark plasma sintering, and the microstructure and tribological properties were investigated systemically. The nano-Al2O3 particle and micro-Al2O3 particle uniformly dispersed in Al matrix composites. The introduction of nanoparticles is beneficial to the decrease of friction coefficient and wear rate, while microparticles are responsible to the high friction coefficient, resulting in the abrasive wear. With the introduction of both nanoparticles and microparticles, their synergic effect will lead to the variation of tribological behavior.