Commercial cathode material （LiCoO2） was modified by coating with a thin layer of SrO/Li2O/La2O3/Ta2O5/TiO2 for improving its performance in lithium ion battery. The morphology and structure of the modified cathode ...Commercial cathode material （LiCoO2） was modified by coating with a thin layer of SrO/Li2O/La2O3/Ta2O5/TiO2 for improving its performance in lithium ion battery. The morphology and structure of the modified cathode material were characterized by scanning electron microscopy （SEM） and X-ray diffraction （XRD）. The performance including cycling stability, diffusion coefficient under different voltage, C-rate discharge of the batteries with this modified cathode material was examined. The results showed that the battery with the coated cathode material could discharge at a large current density, and it possessed a stable cycle performance in the range from 3.0 V to 4.2 V. It was explained that the rate of Li ion diffusion increased in the batteries using SrO/Li2O/La2O3/Ta2O5/TiO2-coated LiCoO2 as the cathode and the coated layer could act as a fast ion conductor （SrO/Li2O/La2O3/Ta2O5/TiO2） and as a protecting shell to prevent LiCoO2particles from being attacked by the acidic electrolyte.展开更多
Alumina membranes without pinholes and cracks were prepared by the sol-gel process using anunordum aluminium sulphate as the starting material. The effects of different preparing conditions on morphology characteristi...Alumina membranes without pinholes and cracks were prepared by the sol-gel process using anunordum aluminium sulphate as the starting material. The effects of different preparing conditions on morphology characteristics of the membrane were investigated by scanning electron microscopy and 3D rotational microscopy. The preparing conditions include the amounts of drying control chemical additives （DCCA）, sintering procedure and sol-gel concentration. The results showed that PVA is a good crack-preventing reagent and the morphology of supported membranes was affected by ninny factors, including Al2O3 concentration, PVA/Al2O3 ratio, heating rate, membrane thickness and intrinsic defects of the substrate surface.展开更多
Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub&...Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.展开更多
Several lithium-ion batteries of 18650-type were assembled with pristine or Al2O3-coated LiNi0.4Co0.2Mn0.4O2（NCM） as cathode material and mesocarbon microbeads（MCMB） as anode material.The cycling performance of th...Several lithium-ion batteries of 18650-type were assembled with pristine or Al2O3-coated LiNi0.4Co0.2Mn0.4O2（NCM） as cathode material and mesocarbon microbeads（MCMB） as anode material.The cycling performance of the batteries was examined under 25 °C at a 2C rate within a potential range of 2.75―4.20 V.The changes of the crystal structure,the lattice parameter,the mean crystallite size,and the mean micro-strain of pristine NCM and Al2O3-coated NCM during the charge-discharge cycling were determined by X-ray diffraction（XRD）.The results indicate that the bulk structure of Al2O3-coated NCM is more stable than that of pristine NCM,which leads to the better cycling performance of Al2O3-coated NCM compared to that of pristine NCM.展开更多
以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO ...以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。展开更多
基金supported by the Natural Science Foundation of Guangdong Province,China (06105562)the Foundation of Manyang Bureau of Sci-ence and Technology,China (07Y003-1)
文摘Commercial cathode material （LiCoO2） was modified by coating with a thin layer of SrO/Li2O/La2O3/Ta2O5/TiO2 for improving its performance in lithium ion battery. The morphology and structure of the modified cathode material were characterized by scanning electron microscopy （SEM） and X-ray diffraction （XRD）. The performance including cycling stability, diffusion coefficient under different voltage, C-rate discharge of the batteries with this modified cathode material was examined. The results showed that the battery with the coated cathode material could discharge at a large current density, and it possessed a stable cycle performance in the range from 3.0 V to 4.2 V. It was explained that the rate of Li ion diffusion increased in the batteries using SrO/Li2O/La2O3/Ta2O5/TiO2-coated LiCoO2 as the cathode and the coated layer could act as a fast ion conductor （SrO/Li2O/La2O3/Ta2O5/TiO2） and as a protecting shell to prevent LiCoO2particles from being attacked by the acidic electrolyte.
基金Project supported by National Natural Science Foundation ofChina (Grant No .20373040) Science Foundation of Science andTechnology Commission of Zhejiang Province ( Grant No .0252nm101) Science Foundation of Shanghai MunicipalCommission of Science and Technology (Grant No .0452nm019)
文摘Alumina membranes without pinholes and cracks were prepared by the sol-gel process using anunordum aluminium sulphate as the starting material. The effects of different preparing conditions on morphology characteristics of the membrane were investigated by scanning electron microscopy and 3D rotational microscopy. The preparing conditions include the amounts of drying control chemical additives （DCCA）, sintering procedure and sol-gel concentration. The results showed that PVA is a good crack-preventing reagent and the morphology of supported membranes was affected by ninny factors, including Al2O3 concentration, PVA/Al2O3 ratio, heating rate, membrane thickness and intrinsic defects of the substrate surface.
文摘Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.
基金Supported by the Project of Shanghai Committee of Science and Technology,China(Nos.1052nm00100,09ZR1437600)
文摘Several lithium-ion batteries of 18650-type were assembled with pristine or Al2O3-coated LiNi0.4Co0.2Mn0.4O2（NCM） as cathode material and mesocarbon microbeads（MCMB） as anode material.The cycling performance of the batteries was examined under 25 °C at a 2C rate within a potential range of 2.75―4.20 V.The changes of the crystal structure,the lattice parameter,the mean crystallite size,and the mean micro-strain of pristine NCM and Al2O3-coated NCM during the charge-discharge cycling were determined by X-ray diffraction（XRD）.The results indicate that the bulk structure of Al2O3-coated NCM is more stable than that of pristine NCM,which leads to the better cycling performance of Al2O3-coated NCM compared to that of pristine NCM.
文摘以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。