Semi-quantitative electron probe microanalysis （EPMA） mapping, scanning electron microscopy （SEM） and transmission electron microscopy （TEM） were employed to study the effect of one-step and two-step treatments ...Semi-quantitative electron probe microanalysis （EPMA） mapping, scanning electron microscopy （SEM） and transmission electron microscopy （TEM） were employed to study the effect of one-step and two-step treatments on the Zr distribution and Al3Zr dispersoid characteristics in as-cast commercial AA7150 aluminum alloy. It is shown that the Zr concentration in the dendrite centre regions is higher than that near the dendrite edges in the as-cast condition, and that homogenization at 460 °C for 20 h is insufficient to remove these concentration gradients. After homogenizing at 460-480 °C, a high number density of larger dispersoids can be observed in dendrite centre regions but not near dendrite edges. Furthermore, the dispersoid size increases with increasing the temperature during both one-step and two-step homogenization treatments.展开更多
The dynamic recrystallization behavior of 7085 aluminum alloy during hot compression at various temperatures （573？723 K） and strain rates （0.01-10 s^-1） was studied by electron back scattered diffraction （EBSD...The dynamic recrystallization behavior of 7085 aluminum alloy during hot compression at various temperatures （573？723 K） and strain rates （0.01-10 s^-1） was studied by electron back scattered diffraction （EBSD）, electro-probe microanalyzer （EPMA） and transmission electron microscopy （TEM）. It is shown that dynamic recovery is the dominant softening mechanism at high Zener？Hollomon （Z） values, and dynamic recrystallization tends to appear at low Z values. Hot compression with ln Z=24.01 （723 K, 0.01 s？1） gives rise to the highest fraction of recrystallization of 10.2%. EBSD results show that the recrystallized grains are present near the original grain boundaries and exhibit similar orientation to the deformed grain. Strain-induced boundary migration is likely the mechanism for dynamic recrystallization. The low density of Al3Zr dispersoids near grain boundaries can make contribution to strain-induced boundary migration.展开更多
The effect of homogenization time on quench sensitivity of a cast 7085 aluminum alloy was investigated by means of end-quenching test, optical microscope （OM）, scanning electron microscope （SEM） and transmission e...The effect of homogenization time on quench sensitivity of a cast 7085 aluminum alloy was investigated by means of end-quenching test, optical microscope （OM）, scanning electron microscope （SEM） and transmission electron microscope （TEM）. The results show that with the increase of homogenization time from 48 h to 384 h, quench sensitivity increased slightly as the largest difference in the hardness was increased from 5.2% to 6.9% in the end-quenched and aged specimens. Prolonging homogenization had little effect on the grain structure, but improved the dissolution of soluble T phase and resulted in larger Al3Zr dispersoids with a low number density. Some small quench-induced η phase particles on Al3Zr dispersoids were observed inside grains during slow quenching, which decreased hardness after subsequent aging. The change in the character of Al3Zr dispersoids exerted slight influence on quench sensitivity.展开更多
文摘Semi-quantitative electron probe microanalysis （EPMA） mapping, scanning electron microscopy （SEM） and transmission electron microscopy （TEM） were employed to study the effect of one-step and two-step treatments on the Zr distribution and Al3Zr dispersoid characteristics in as-cast commercial AA7150 aluminum alloy. It is shown that the Zr concentration in the dendrite centre regions is higher than that near the dendrite edges in the as-cast condition, and that homogenization at 460 °C for 20 h is insufficient to remove these concentration gradients. After homogenizing at 460-480 °C, a high number density of larger dispersoids can be observed in dendrite centre regions but not near dendrite edges. Furthermore, the dispersoid size increases with increasing the temperature during both one-step and two-step homogenization treatments.
基金Project(2012CB619500)supported by the National Basic Research Program of China
文摘The dynamic recrystallization behavior of 7085 aluminum alloy during hot compression at various temperatures （573？723 K） and strain rates （0.01-10 s^-1） was studied by electron back scattered diffraction （EBSD）, electro-probe microanalyzer （EPMA） and transmission electron microscopy （TEM）. It is shown that dynamic recovery is the dominant softening mechanism at high Zener？Hollomon （Z） values, and dynamic recrystallization tends to appear at low Z values. Hot compression with ln Z=24.01 （723 K, 0.01 s？1） gives rise to the highest fraction of recrystallization of 10.2%. EBSD results show that the recrystallized grains are present near the original grain boundaries and exhibit similar orientation to the deformed grain. Strain-induced boundary migration is likely the mechanism for dynamic recrystallization. The low density of Al3Zr dispersoids near grain boundaries can make contribution to strain-induced boundary migration.
基金Project(2012CB619500)supported by the National Basic Research Program of ChinaProject supported by Yuying Project of Central South University
文摘The effect of homogenization time on quench sensitivity of a cast 7085 aluminum alloy was investigated by means of end-quenching test, optical microscope （OM）, scanning electron microscope （SEM） and transmission electron microscope （TEM）. The results show that with the increase of homogenization time from 48 h to 384 h, quench sensitivity increased slightly as the largest difference in the hardness was increased from 5.2% to 6.9% in the end-quenched and aged specimens. Prolonging homogenization had little effect on the grain structure, but improved the dissolution of soluble T phase and resulted in larger Al3Zr dispersoids with a low number density. Some small quench-induced η phase particles on Al3Zr dispersoids were observed inside grains during slow quenching, which decreased hardness after subsequent aging. The change in the character of Al3Zr dispersoids exerted slight influence on quench sensitivity.