The durability of the cement was mainly studied. Under 1.0 MPa of hydraulic pressure for 8 hours, water could penetrate completely through the sample made by portland cement, but could not penetrate through that by al...The durability of the cement was mainly studied. Under 1.0 MPa of hydraulic pressure for 8 hours, water could penetrate completely through the sample made by portland cement, but could not penetrate through that by alite-barium sulphoaluminate cement. Under the condition of freezing and thawing cycle, the loss ratio of compressive strength of the cement was only about 17.3% at curing 28 d ages, but the loss of portland cement was as high as 29.5%. Alite-calcium barium sulphoaluminate cement also has an excellent resistance to sulfate attack. The coefficients of resistance to sulfate attack of the cement exceeded 1.0. Meanwhile, the composition and microstructure of the hardened paste of alite-calcium barium sulphoaluminate cement were analyzed by XRD and SEM.展开更多
A new type of high water content material which is made up of two pastes is prepared, one is refute from lime and gypsum, and another is based on Ba-bearing sulphoaluminate cement. It has excellent properties such as ...A new type of high water content material which is made up of two pastes is prepared, one is refute from lime and gypsum, and another is based on Ba-bearing sulphoaluminate cement. It has excellent properties such as slow single paste solidifing ,fust double pustes solidifing ,fast coagulating and hardening, high early strength, good suspeasion property at high W/C ratio and low cost. Meanwhile, the properties and hydration mechanism of the material were analyzed by using XRD, DTA- TG and SEM. The hydrated products of new type of high water content material are Ba-bearing ettringite, BaSO4 , aluminum gel and C-S-H gel.展开更多
基金Funded by the National Natural Science Foundation of China (No.50672033)the "973"National Key Fundamental Research Plan ofChina (No.2009CB623101-1)
文摘The durability of the cement was mainly studied. Under 1.0 MPa of hydraulic pressure for 8 hours, water could penetrate completely through the sample made by portland cement, but could not penetrate through that by alite-barium sulphoaluminate cement. Under the condition of freezing and thawing cycle, the loss ratio of compressive strength of the cement was only about 17.3% at curing 28 d ages, but the loss of portland cement was as high as 29.5%. Alite-calcium barium sulphoaluminate cement also has an excellent resistance to sulfate attack. The coefficients of resistance to sulfate attack of the cement exceeded 1.0. Meanwhile, the composition and microstructure of the hardened paste of alite-calcium barium sulphoaluminate cement were analyzed by XRD and SEM.
文摘A new type of high water content material which is made up of two pastes is prepared, one is refute from lime and gypsum, and another is based on Ba-bearing sulphoaluminate cement. It has excellent properties such as slow single paste solidifing ,fust double pustes solidifing ,fast coagulating and hardening, high early strength, good suspeasion property at high W/C ratio and low cost. Meanwhile, the properties and hydration mechanism of the material were analyzed by using XRD, DTA- TG and SEM. The hydrated products of new type of high water content material are Ba-bearing ettringite, BaSO4 , aluminum gel and C-S-H gel.