Synthesis of Organic-Inorganic Hybrid Aluminum Hypophosphite Microspheres Flame Retardant and Its Flame Retardant Research on Thermoplastic Polyurethane

Aluminum hypophosphite microspheres(AHP) were synthesized by hydrothermal method using NaH2PO2·H2O and AlCl3·6H2O as raw materials, and then the AHP microspheres were polymerized by surface polymerization of micro-nanospheres with cyclic cross-linked poly(cyclotriphosphazene-co-4,4'-sulfonyldiphenol)(PZS). A new organic-inorganic poly(phosphonitrile)-modified aluminum hypophosphite microspheres(PZS-AHP) were synthesized by encapsulation and applied to flame retardant thermoplastic polyurethane(TPU). The microstructure and chemical composition of the PZS-AHP microsphere were characterized by scanning electron microscopy, transmission electron microscopy, Fourier transform infrared spectroscopy and X-ray spectroscopy. The thermal stability of PZS-AHP microsphere was explored with thermogravimetric analysis. Thermogravimetric data indicate that the PZS-AHP microspheres have excellent thermal stability. The thermal and flame-retarding properties of the TPU composites were evaluated by thermogravimetric(TG), limited oxygen index tests(LOI), and cone calorimeter test(CCT). The TPU composite achieved vertical burning(UL-94) V-0 grade and LOI value reached 29.2% when 10 wt% PZS-AHP was incorporated. Compared with those of pure TPU, the peak heat release rate(pHRR) and total heat release(THR) of TPU/10%PZS-AHP decreased by 82.2% and 42.5%, respectively. The results of CCT indicated that PZS-AHP microsphere could improve the flame retardancy of TPU composites.

Synergistic Effects of Aluminum Hypophosphite on Intumescent Flame Retardant Polypropylene System

The effects of aluminum hypophosphite（AHP） as a synergistic agent on the flame retardancy and thermal degradation behavior of intumescent flame retardant polypropylene composites（PP/IFR） containing ammonium polyphosphate（APP） and triazine charring-foaming agent（CFA） were investigated by limiting oxygen index（LOI）, UL-94 measurement, thermogravimetric analysis（TGA）, cone calorimeter test（CONE）, scanning electron microscopy（SEM） and X-ray photoelectron spectroscopy（XPS）. It was found that the combination of IFR with AHP exhibited an evident synergistic effect and enhanced the flame retardant efficiency for PP matrix. The specimens with the thickness of 0.8 mm can pass UL-94 V-0 rating and the LOI value reaches 33.5% based on the total loading of flame retardant of 24 wt%, and the optimum mass fraction of AHP/IFR is 1：6. The TGA data revealed that AHP could change the degradation behavior of IFR and PP/IFR system, enhance the thermal stability of the IFR and PP/IFR systems at high temperatures and promote the char residue formation. The CONE results revealed that IFR/AHP blends can efficiently reduce the combustion parameters of PP, such as heat release rate（HRR）, total heat release（THR）, smoke production rate（SPR） and so on. The morphological structures of char residue demonstrated that AHP is of benefit to the formation of a more compact and homogeneous char layer on the materials surface during burning. The analysis of XPS indicates that AHP may promote the formation of sufficient char on the materials surface and improve the flame retardant properties.

Facile modification of aluminum hypophosphate and its flame retardancy for polystyrene

A phosphorus-containing flame retardant, aluminum hypophosphite(AHPi), has been modified by(3-aminopropyl) triethoxysilane(KH550) to prepare flame-retardant polystyrene(PS). The influence of modified AHPi on the morphology and characterization was investigated, and differences in flame retardant properties of the PS/AHPi and PS/modified AHPi were compared. The PS composite can pass the vertical burning tests(UL-94 standard) with a V-0 rating when the mass content of modified AHPi reaches20%, compared with the mass content of 25% AHPi. The element mapping of the PS composite shows that modified AHPi has better dispersion in PS than AHPi. Thermogravimetric analysis results indicated that adding modified AHPi can advance the initial decomposition temperature of the composite material.With the addition of modified AHPi, the decrease in peak heat release rate(p HRR) is more evident than AHPi, and the char yield of the resultant PS composites gradually increased. With the addition of 25%modified AHPi, the p HRR and total heat release of PS composites decreased by 81.4% and 37.6%. The modification of AHPi promoted its dispersion in the PS matrix and improved the char formation of PS composites. The results of real-time infrared spectrometry of PS composites, Fourier transform infrared spectra and X-ray photoelectron analysis of the char layer indicated that modified AHPi has flame retardancy in condensed and gas phases.