Influence of Heat Treatment on Microstructure and Mechanical Properties of Plasma Sprayed FeCrMoCBY Amorphous Coatings

The changes of the microstructure and the mechanical properties of FeCrMoCBY amorphous coatings prepared by plasma spraying after heat treatment were investigated.300,400,500 and 600℃were selected as the heat treatment temperature,and the crystallization phenomenon occurred after the heat treatment at 600℃.The crystallization products of the coating heat-treated at 600℃were a-Fe and Fe23(C,B)6.Heat treatment was beneficial to the microhardness and the bonding strength of the coatings.The microhardness of the coating heat-treated at 600℃increased obviously,and the strongest bonding strength occurred in the coating heat-treated at 500℃.The improvement of the wear resistance of the coatings could attribute to heat treatment as well,and the wear resistance of the coating heat-treated at 600℃was the optimum,compared with the coating heat-treated at 500℃.

Fe-based amorphous coating prepared using high-velocity oxygen fuel and its corrosion behavior in static lead-bismuth eutectic alloy

The Fe_(949.7)Cr_(18)Mn_(1.9)Mo_(7.4)W_(1.6)B_(15.2)C_(3.8)Si_(2) amorphous coating was deposited on T91 steel substrate by using the high-velocity oxygen fuel(HVOF)spray technique to enhance the corrosion resistance of T91 stainless steel in liquid lead-bismuth eutectic(LBE).The corrosion behavior of the T91 steel and coating exposed to oxygen-saturated LBE at 400℃ for 500 h was investigated.Results showed that the T91 substrate was severely corroded and covered by a homogeneously distributed dual-layer oxide on the interface contacted to LBE,consisting of an outer magnetite layer and an inner Fe-Cr spinel layer.Meanwhile,the amorphous coating with a high glass transition temperature(Tg=550℃)and crystallization temperature(T_(x)=600℃)exhibited dramatically enhanced thermal stability and corrosion resistance.No visible LBE penetration was observed,although small amounts of Fe_(3)O_(4),Cr_(2)O_(3),and PbO were found on the coating surface.In addition,the amorphicity and interface bonding of the coating layer remained unchanged after the LBE corrosion.The Fe-based amorphous coating can act as a stable barrier layer in liquid LBE and have great application potential for long-term service in LBE-cooled fast reactors.

Effect of Kerosene Flowing Rate on Microstructure and Wearing Properties for Fe-based Amorphous Coatings

The effects of kerosene flow rate on the microstructure and wearing properties were investigated for Fe-based amorphous coatings sprayed by High Velocity Oxygen Fuel (HVOF).The microstructures and wearing properties of the Fe-based amorphous coatings were analyzed with scanning electron microscope (SEM),X-ray diffraction analyzer (XRD),and ball-on-disc tribometer (CFT-1),respectively.The experimental results show that the well interfacial bonding can be observed between the amorphous coating layer and the substrate,and the porosity in amorphous coating layer is less to 1%.Only some crystalline a-Fe and FeO phases can be detected by XRD in the amorphous coatings,while the amorphous content is up to 99.4%.The wearing coefficient is near to 0.15,which is superior to SUS316 of 0.28.As the increasing of wearing loads,the failure mode is changed from oxidation wear to the composite of oxidation and abrasive wear.

Formation and properties of a Zr-based amorphous coating by laser cladding

(Zr_(0.53)Al_(0.1)Ni_(0.05)Cu_(0.3)Ti_(0.02))_(99)Y_1(at%)coating with amorphous layer of about 180μm thick was prepared on a steel substrate by using laser cladding method.The coating is compact and shows good metallurgical bonding with substrate.The microstructure,microhardness and corrosion behavior along the depth from the coating surface to the substrate were investigated.It is found that a gradient structure consisted of amorphous surface layer,amorphous-crystalline transitional layer and substrate is formed after the laser cladding.The microhardness and corrosion behavior exhibit variation with the microstructural evolution at different depths from the coating surface.The microhardness and corrosion resistance in 3.5 wt%NaCl solution of the amorphous surface layer are comparable to those of the as-cast Zr-based BMG with the same composition,and higher than those of the steel substrate.

Superhydrophobic Fe-based amorphous coating fabricated by detonation spraying with excellent anti-corrosion and self-cleaning properties

Amorphous alloys without crystalline defects(dislocation,crystal boundary)are ideal hydrophobic coating materials due to their low surface energy.This work used a synergistic method of detonation spraying and surface modification to obtain the superhydrophobic Febased amorphous coatings with high hardness and dense structure on the Q 235 substrate.The results showed that the water contact angles(WCA)of the superhydrophobic coating was 160°±3.6°,and water droplets could bounce off the superhydrophobic coating surface,illustrating the excellent self-cleaning performance of coating.Notably,the corrosion current density(i_(corr))of the superhydrophobic coating further decreased by 2 orders of magnitude down to8.008×10^(-8)A·cm^(-2)compared to the as-deposited coating with 5.473×10^(-6)A·cm^(-2);the corrosion potential(E_(corr))of the superhydrophobic coating shifted by 34 mV to the positive side compared with that of the as-deposited coating(-310 mV).Likewise,the impedance modulus|Z|values of the superhydrophobic coating increased by nearly2 orders of magnitude up to 1×10^(5.6)compared to the asdeposited coating with 1×10^(3.8).Even through lasting immersion in NaCl for 10 days,|Z|values of the superhydrophobic coating were still much higher than those of the as-deposited coating.The superhydrophobic Fe-based amorphous coatings could respond to their applications under extreme conditions due to their excellent hydrophobicity and self-cleaning properties,illustrating their promising future in aerospace,automotive,and machinery industries.

Hot corrosion behaviors of 921A alloy and HVAF-sprayed Fe-based amorphous coating covered with KCl-ZnCl_(2) salts

Hot corrosion behaviors of the 921A alloy and Fe-based amorphous coating induced by KCl-10% ZnCl_(2) and KCl-55% ZnCl_(2) salts at 450℃ in air for 40 h were investigated.Results show that the 921A alloy suffers more serious corrosion damage than the coating and KCl-55% ZnCl_(2) salts are more corrosive than KCl-10% ZnCl_(2) salts.In the two salts,an Fe_(2)O_(3) layer is formed on the 921A alloy surface,while an outer Fe-rich oxide layer and an inner Cr-rich oxide layer are formed on the surface of the coating.Moreover,a certain amount of metal chloride can be found at the oxide/alloy(coating)interface,which can be explained by "active oxidation".However,the corrosion resistance of the Fe-based amorphous coating did not achieve the desired results,probably because the intersplats in the coating serve as corrosion diffusing channels,which facilitate the corrosion damage rate.Nevertheless,the coating is still in amorphous state after hot corrosion exposure.

Effects of Annealing Below Glass Transition Temperature on the Wettability and Corrosion Performance of Fe-based Amorphous Coatings

This study investigated the effect of annealing below glass transition temperature(T_(g))on the microstructural characteristics,mechanical property,wettability,and electrochemical performance of activated combustion-high velocity air fuel(AC-HVAF)-sprayed Fe-Cr-Mo-W-C-B-Y amorphous coatings(ACs).Results showed that Fe-based ACs with a thickness of~300μm exhibited a fully amorphous structure with low oxidization.Originating from the reduced free volume,sub-T_(g) annealing increased the thermal stability,hardness,and surface hydrophobicity of Fe-based ACs.The enhanced corrosion resistance of sub-T_(g) annealed ACs in 3.5 wt%NaCl solution was attributed to the increased surface hydrophobicity and passivation capability.This finding elucidates the correlation between sub-T_(g) annealing and the properties of Fe-based ACs,which promotes ameliorating ACs with superior performance.

Corrosion and irradiation behavior of Fe-based amorphous coating in lead-bismuth eutectic liquids

Lead-bismuth eutectics (LBE) have considerable potential as a candidate material for accelerator-driven sub-critical systems(ADS).However,LBE corrosion and irradiation damage are two urgent challenges remaining to be solved for impellers of primary pumps.In this study,we have explored the possibility of using Fe-based amorphous coatings to overcome LBE corrosion and concurrently to sustain irradiation damage.Specifically,the Fe_(54)Cr_(18)Mo_(2)Zr_(8)B_(18)amorphous coating was prepared by high-velocity oxygen-fuel (HVOF) spraying on 316L steel and exposed to saturated oxygen static LBE for 500 h at 400℃.The coating with high thermal stability (T_(g)=615℃ and T_(x)=660℃) effectively prevented the substrate steel from being corroded by LBE owing to its unique long-range disordered atomic packing.The coating also exhibited strong irradiation resistance when being subjected to 45 dpa (displacement per atom) Au ion irradiation at room temperature,with no sign of crystallization even at the maximum implantation depth of 300 nm.Consequently,the hardness of the coatings before and after irradiation increased slightly.The current findings shed new insights into understanding corrosion mechanism and irradiation behavior of amorphous solids in LBE and expand the application range of amorphous materials.

Microstructure and Wear Properties of Fe-based Amorphous Coatings Deposited by High-velocity Oxygen Fuel Spraying

Fe-based powder with a composition of Fe_（42.87）Cr_（15.98）Mo_（16.33）C_（15.94）B_（8.88）（at.%）was used to fabricate coatings by high-velocity oxygen fuel spraying.The effects of the spraying parameters on the microstructure and the wear properties of the Fe-based alloy coatings were systematically studied.The results showed that the obtained Fe-based coatings with a thickness of about 400μm consisted of a large-volume amorphous phase and some nanocrystals.With increasing the fuel and oxygen flow rates,the porosity of the obtained coatings decreased.The coating deposited under optimized parameters exhibited the lowest porosity of 2.8%.The excellent wear resistance of this coating was attributed to the properties of the amorphous matrix and the presence of nanocrystals homogeneously distributed within the matrix.The wear mechanism of the coatings was discussed on the basis of observations of the worn surfaces.

Microstructure of Cu-based Amorphous Composite Coatings on AZ91D Magnesium Alloy by Laser Cladding

To improve the sliding wear resistance of AZ91D magnesium alloy, Cu-based amorphous composite coatings made of CuaTTi34Zr11Nis and Cu47Ti34Zr11Ni8＋20 wt pct SiC powders were fabricated on AZ91D magnesium alloy by laser cladding, respectively. SEM （scanning electron microscopy）, EDS （energy dispersive X-ray spectroscopy）, XRD （X-ray diffraction） and TEM （transmission electron microscopy） techniques were employed to study the phases of the coatings. The results show that the coatings mainly consist of amorphous phase and different intermetallic compounds. The reason of formation of amorphous phase and the function of SiC particles were explained in details.

Friction and Wear Properties of Amorphous Carbon Nitride Coatings in Water Lubrication

The friction and wear properties of amorphous carbon nitride(a-CN x)coatings in water lubrication were reviewed.The influences of mating materials and tribological variables such as normal load(W)and sliding speed(V)on the friction and wear properties of the a-CN x coatings were analyzed.It was indicated that the specific wear rate of the a-CN x coatings was related to the hydration reaction of mating materials with water.If the mating materials were easily hydrated,the specific wear rate of a-CN x coatings was low.The water-lubricated properties of the a-CN x coatings were better in comparison to the a-C coatings.The a-CN x/Si-based non-oxide ceramics tribo-pairs exhibited the lowest friction coefficient and wear rate.To describe their friction and wear properties at the normal loads of 3—15Nand the sliding speeds of 0.05—0.5m/s,the wear-mechanism maps for the a-CN x/SiC(Si3N4)tribo-pairs in water were developed.

Fabrication of Ni34.1Fe27.9B18Si18Nb2 amorphous matrix coating on mild steel by laser processing

Ni34.1 Fe27.9B18 Si18 Nb2 coating was deposited on mild steel substrate using high power laser cladding followed by laser remelting process. The laser processing was conducted by the powder feeding method using low purity materials without shielding box. To learn the surface amorphous matrix coating forming mechanism, the coating without remelting process was also studied. The phases and microstructures were analyzed by X-ray diffraction （XRD）, scanning- and transmission-electron microscopy（ SEM, TEM）. The microhardness and corrosion resistance property of the coating were also measured. The results of SEM, XRD and TEM analysis show that the remelted coating has an amorphous matrix layer embedded with some crystals due to high cooling rate during remelting process. The crystals phases are identified as Fe2 B phase, γ （Fe, Ni ） phase and α- Fe phase. No oxidation phases are found in the coating surface. Hardness profiles reveal microhardness more than 1 100 HVo.5 over the full depth of the amorphous matrix layer, while the unremtled coating and the substrate show relatively lower hardness than the remelted layer. Corrosion resistance tests exhibit that the remelted coating is nobler than the unremelted coating and the substrate material.

Microstructure characteristics of coating with amorphous phases prepared from Fe-based alloy powders by plasma spray

In this paper, alloy powders mixed with a molar ratio of Fe ： P ： C of 80 ： 13 ： 7 were sprayed on Q235 steel by plasma spray method to prepare coating with amorphous phases. The phase composition of the mixed alloy powders and prepared coating were characterized by X-ray diffraction （ XRD ）. The morphology and the composition cf the coating were analyzed by scanning eleetron microscopy （SEM） nnd energy dispersive apectroscopy （ EDS ）. In addition, the thermal stability ef the coating with amorphous phases was characterized by differential thermal analyzer （ DTA ）. Tile results showed that, usirtg mixed alloy powders with a molar ratio of Fe： P： C of 80：13：7, the coating containing certain amount of amorphous alloys was suceessathlly prepared through atmospheric plasma spray technique. In the coating, the main phases were determined to be Fe, FeP aad Fe2P. The crystallization of the coating started from about 461°. Tile coating was mechanically adhered to the substrate.

Microstructures and properties of Fe-Co-B-Si-Nb coating prepared by laser cladding and remelting

High power laser cladding of [ （ Fe0. 5 Co0. 5 ） 0. 75 B0. 2 Si0.05 ] 95. 7 Nb4. 3 powder mixture afier-remelting was performed to fabricate Fe-based metallic glass coating on the surface of steel of China Classification Society： Grade B （CCS-B）. Scanning electron microscopy （SEM）, X-ray diffraction （XRD）, transmission electron microscopy （TEM） with energy dispersive spectrometer （EDS）, Vickers hardness tester and corrosion resistance tester were employed to characterize microstructures and evaluate properties of this coating. According to the results of SEM, XRD and TEM, the cladding coating consisted of nanocrystalline embedded in amorphous phase. EDS data indicated that Nb segregated in the amorphous matrix. The results of hardness test revealed that the hardness of the top layer was higher than that of the inner layer of the coating. The coating exhibited excellent corrosion resistance in a 3.5% NaCl solution.

Microstructure and Internal Friction Behavior of Laser 3D Printed Fe-Based Amorphous Composites

Laser 3D printing,also known as laser additive manufacturing(LAM),is favored for its ability to form bulk metallic glass(BMG)and its composite materials(BMGcs)with freeform geometries.In this work,two different kinds of Fe_(41)Co_(7)Cr_(15)Mo_(14)C_(15)B_(6)Y_(2)amorphous coatings(A and B)were prepared by using LAM technology under air-and water-cooled conditions,respectively;meanwhile,to reduce the cracks generated due to the residual thermal stresses,coating C obtained by air-sweep annealing of B with a low energy-density laser.The morphology and amorphous content and microstructure of the coatings were investigated,the results show many cracks in coating B deposited under water-cooled conditions,and its microstructure shows an amorphous-crystal-nanocrystalline mixed structure.Cracking was suppressed in coating C,obtained by air-sweep annealing based on coating B,but the amorphous content was reduced from 32.6 to 13.4%.And the hardness and corrosion resistance of the coating will increase with the increase in the amorphous content.Finally,the internal friction behavior of a BMGcs was prepared on the basis of the process of sample C is compared with that of as-cast amorphous alloys.The results show that the low temperature internal friction behavior of BMGcs is affected by the defects produced during printing,and the high temperature internal friction behavior is affected by the precipitated hard phase.

Microstructure and Mechanical Properties of Fe-based Amorphous Composite Coatings Reinforced by Stainless Steel Powders

In this study,a few Fe-based amorphous matrix composite coatings reinforced with various portions(4,8 and16 vol.%) of 31 6L stainless steel powders have been successfully produced through high velocity oxy-fuel(HVOF) spraying.The microstructure of the composite coatings was systematically characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM) and transmission electron microscopy(TEM).The main structure of composite coatings remained amorphous while 31 6L stainless steel splats were distributed homogeneously in the amorphous matrix and well connected with surrounding amorphous phase.Bonding strength of coatings to the substrate was determined by 'pull-off' tensile tests.The results revealed that the31 6L stainless steel phase effectively improved the bonding strength of amorphous coatings,which is mainly contributed by the strong metallurgical bonding between stainless steel and amorphous splats.The addition of31 6L stainless steel also enhanced the ductility and fracture resistance of the coatings due to the ductile stainless steel phases,which can arrest crack propagation and increase energy dissipation.

High-temperature friction behavior of amorphous carbon coating in glass molding process

In the glass molding process,the sticking reaction and fatigue wear between the glass and mold hinder the service life and functional application of the mold at the elevated temperature.To improve the chemical inertness and anti-friction properties of the mold,an amorphous carbon coating was synthesized on the tungsten carbide-cobalt(WC–8Co)substrate by magnetron sputtering.The friction behavior between the glass and carbon coating has a significant influence on the functional protection and service life of the mold.Therefore,the glass ring compression tests were conducted to measure the friction coefficient and friction force of the contact interface between the glass and amorphous carbon coating at the high temperature.Meanwhile,the detailed characterization of the amorphous carbon coating was performed to study the microstructure evolution and surface topography of the amorphous carbon coating during glass molding process by scanning electron microscopy(SEM),X-ray photoelectron spectroscopy(XPS),Ramon spectroscopy,and atomic force microscope(AFM).The results showed that the amorphous carbon coating exhibited excellent thermal stability,but weak shear friction strength.The friction coefficient between the glass and coating depended on the temperature.Besides,the service life of the coating was governed by the friction force of the contact interface,processing conditions,and composition diffusion.This work provides a better understanding of the application of carbon coatings in the glass molding.

Co-based Amorphous/Nanocrystalline Composite Coatings Deposited by Arc Ion Plating

Cobalt-based amorphous/nanocrystalline composite coatings have been grown by arc ion plating together with a specimen cooling system. With decreasing substrate temperature, the coatings undergo significant structure evolution. The degree of crystallization first decreases and subsequently increases as confirmed by X-ray diffraction. The cluster size first decreases and then remains constant as confirmed by transmission electron microscopy. The effect of substrate temperature on the evolution of the structure has been studied as a result of a competition between nucleation thermodynamics and kinetics of crystalline growth. With decreasing the substrate temperature, the microhardness and the critical load of the composite coatings firstly increased, and then remained almost constant. And the saturation magnetization revealed the opposite trend over the same range. The essence of these phenomena was ascribed to the microstructural variations caused by the decrease of the substrate temperature.

Control of epitaxial growth at a-Si:H/c-Si heterointerface by the working pressure in PECVD

The epitaxial-Si（epi-Si） growth on the crystalline Si（c-Si） wafer could be tailored by the working pressure in plasmaenhanced chemical vapor deposition（PECVD）.It has been systematically confirmed that the epitaxial growth at the hydrogenated amorphous silicon（a-Si：H）/c-Si interface is suppressed at high pressure（hp） and occurs at low pressure（1p）.The hp a-Si：H,as a purely amorphous layer,is incorporated in the 1p-epi-Si/c-Si interface.We find that：（i） the epitaxial growth can also occur at a-Si：H coated c-Si wafer as long as this amorphous layer is thin enough;（ii） with the increase of the inserted hp layer thickness,lp epi-Si at the interface is suppressed,and the fraction of a-Si：H in the thin films increases and that of c-Si decreases,corresponding to the increasing minority carrier lifetime of the sample.Not only the epitaxial results,but also the quality of the thin films at hp also surpasses that at lp,leading to the longer minority carrier lifetime of the hp sample than the lp one although they have the same amorphous phase.

Magnetic-electric composite coating with oriented segregated structure for enhanced electromagnetic shielding

Manipulation of the internal architecture is essential for electromagnetic interference(EMI)shielding performance of metal-based coatings,which can address the electromagnetic pollution in large-size,complex geometries,and harsh environments.In this work,oriented segregated structure with conductive networks embedded in magnetic matrix was achieved in Fe-based amorphous coatings via Ni-Cu-P functionalization of(Fe_(0.76)Si_(0.09)B_(0.1)P_(0.05))_(99)Nb_(1)amorphous powder precursors and then thermal spraying them onto aluminum(Al)substrate.Benefiting from the unique magnetic-electric structure,the coating@Al composite delivered prominent EMI shielding performance.The EMI shielding effectiveness(SE)of modified coating@Al composite is~41 dB at 8-12 GHz,doubling the value of Al substrate and is 15 dB greater than that of Ni-Cu-P-free coating@Al composite.Microstructure analysis showed that the introduced Ni−Cu−P insertions forcefully suppress the serious oxidation of the magnetic precursors during thermal spraying and form a dense conductive network in the magnetic matrix.Electron holography observation and electromagnetism simulation clarified that the modified coating can effectively trap and attenuate the incident radiations because of the electric loss from Ni−Cu−P conductive network,magnetic loss from Fe-based amorphous coating,and the electromagnetic interactions in the oriented segregated architectures.Moreover,the optimized thermal isolation and mechanical properties brought by structural improvement enable the coating to shield complex parts in thermal shock and mechanical loading environments.Our work gives an insight on the design strategies for metal-based EMI shielding materials and enriches the fundamental understanding of EMI shielding mechanisms.