Application of amphoteric polymers in the process of leather post-tanning

With the characteristics of controllable charge and environmental friendliness,amphoteric polymers can be used in post-tanning process to solve the problems that arise during leather making and are caused by the low absorption rate of single-charge chemicals,incompatibility with new tanning methods,and complex operation process.In this review,the structure,performance,and preparation of amphoteric polymers are reported.Then,the charge change of collagen during different tanning and pH treatments is introduced.Finally,the application and development of amphoteric polymers during the post-tanning process of leather making are discussed.This review has certain guiding significance to the preparation and application of amphoteric polymers for tanning system.

STUDY ON SYNTHESIS OF AMPHOTERIC POLYACRYLAMIDE IN INVERSE EMULSION

Amphoteric polyacrylamide was prepared first by the copolymerization of acrylamide with sodium acrylate and then through Mannich reaction.The copolymerization was carried out with a redox initiation system using the method of inverse emulsion polymerization.In this paper the reaction conditions and factors that affect emulsion stability were studied.Experiments show that a stable latex can be obtained under the following conditions:anionic degree is five percent,the ratio among acrylamide,formaldehyde and dimethylamine is 1∶1∶1.2,reaction temperature is 45 ℃,reaction time lasts four hours,and pH equals 5.0.The amphoteric copolymer has a higher molecular weight and cationic degree,so it is an ideal filler retention and drainage aid in paper making.

Effect of cationic monomer structure on the aggregation behavior of amphoteric acrylic polymer around isoelectric point

Amphoteric polymer can be used as retanning agent in leather manufacture.It is particularly useful in chrome-free tanning systems since it can regulate the charge properties of chrome-free leather and enhance the fixation of anionic post-tanning chemicals in leather.However,the aggregation and precipitation of amphoteric polymer retanning agents around the isoelectric point(pl)hinder their wide application.Herein,we synthesized five amphoteric acrylic polymers(AAPs)by free radical copolymerization with acrylic acid and five different cationic acrylic monomers.The effect of cationic monomer structure on the aggregation behavior of AAPs was investigated.The aggregation of AAPs in aqueous solution showed pH and concentration dependence.Light scattering analysis showed that Poly(AAA-co-MAPTAC)and Poly(AA-co-DMAPMA)were in the shape of coiled linear flexible chains with small particle size(R_(g)7.6 nm and 14.8 nm,respectively)near the pl.However,Poly(AA-co-DAC),Poly(AA-co-DMC)and Poly(AA-co-DMAEMA)were in the shape of hollow spheres and exhibited serious aggregation.Quantum chemical calculations suggested that the amide groups in the cationic monomers MAPTAC and DMAPMA enhanced the nucleophilicity of AAPs.Thus the corresponding AAPs could carry a large number of cationic charges to slow their aggregation when the pH just climbed over the pl.The results are expected to provide theoretical reference for the synthesis and wide-spread application of AAPs.

Effect of cationic monomer structure on the aggregation behavior of amphoteric acrylic polymer around isoelectric point

Amphoteric polymer can be used as retanning agent in leather manufacture. It is particularly useful in chrome-free tanning systems since it can regulate the charge properties of chrome-free leather and enhance the fixation of anionic post-tanning chemicals in leather. However, the aggregation and precipitation of amphoteric polymer retanning agents around the isoelectric point (pI) hinder their wide application. Herein, we synthesized five amphoteric acrylic polymers (AAPs) by free radical copolymerization with acrylic acid and five different cationic acrylic monomers. The effect of cationic monomer structure on the aggregation behavior of AAPs was investigated. The aggregation of AAPs in aqueous solution showed pH and concentration dependence. Light scattering analysis showed that Poly (AA-co-MAPTAC) and Poly (AA-co-DMAPMA) were in the shape of coiled linear flexible chains with small particle size (Rg 7.6 nm and 14.8 nm, respectively) near the pI. However, Poly (AA-co-DAC), Poly (AA-co-DMC) and Poly (AA-co- DMAEMA) were in the shape of hollow spheres and exhibited serious aggregation. Quantum chemical calculations suggested that the amide groups in the cationic monomers MAPTAC and DMAPMA enhanced the nucleophilicity of AAPs. Thus the corresponding AAPs could carry a large number of cationic charges to slow their aggregation when the pH just climbed over the pI. The results are expected to provide theoretical reference for the synthesis and widespread application of AAPs.