Water-based processed and alkoxide-based processed indium oxide thin-film transistors at different annealing temperatures

In this study,indium oxide（In2O3） thin-film transistors（TFTs） are fabricated by two kinds of low temperature solution-processed technologies（Ta ≤ 300℃）,i.e.,water-based（DIW-based） process and alkoxide-based（2-ME-based）process.The thickness values,crystallization properties,chemical structures,surface roughness values,and optical properties of In2O3 thin-films and the electrical characteristics of In2O3 TFTs are studied at different annealing temperatures.Thermal annealing at higher temperature leads to an increase in the saturation mobility（μsat） and a negative shift in the threshold voltage（VTH）.The DIW-based processed In2O3-TFT annealed at 300℃ exhibits excellent device performance,and one annealed at 200℃ exhibits an acceptable μsat of 0.86 cm^2/V·s comparable to that of a-Si：H TFTs,whereas the 2-ME-based TFT annealed at 300℃ exhibits an abundant μsat of 1.65 cm^2/Vs and one annealed at 200℃ is inactive.The results are attributed to the fact that the DIW-based process induces a higher degree of oxidation and less defect states than the 2-ME-based process at the same temperature.The DIW-based process for fabricating the In2O3 TFT opens the way for the development of nontoxic,low-cost,and low-temperature oxide electronics.

Effect of annealing temperature on microstructure and mechanical properties of Mg-Zn-Zr-Nd alloy with large final rolling deformation

In this study,the Mg-3Zn-0.5Zr-χNd(χ=0,0.6)alloys were subjected to final rolling treatment with large deformation of 50%.The impact of annealing temperatures on the microstructure and mechanical properties was investigated.The rolled Mg-3Zn-0.5Zr-0.6Nd alloy exhibited an ultimate tensile strength of 386 MPa,a yield strength of 361 MPa,and an elongation of 7.1%.Annealing at different temperatures resulted in reduced strength and obviously increased elongation for both alloys.Optimal mechanical properties for the Mg-3Zn-0.5Zr-0.6Nd alloy were achieved after annealing at 200℃,with an ultimate tensile strength of 287 MPa,a yield strength of 235 MPa,and an elongation of 26.1%.The numerous deformed microstructures,twins,and precipitated phases in the rolled alloy could impede the deformation at room temperature and increase the work hardening rate.After annealing,a decrease in the work hardening effect and an increase in the dynamic recovery effect were obtained due to the formation of fine equiaxed grains,and the increased volume fraction of precipitated phases,which significantly improved the elongation of the alloy.Additionally,the addition of Nd element could enhance the annealing recrystallization rate,reduce the Schmid factor difference between basal and prismatic slip systems,facilitate multi-system slip initiation and improve the alloy plasticity.

Surface plasmon resonance and electrical properties of RF: magnetron sputtered carbon–nickel composite films at different annealing temperatures

In this work, the optical absorption spectra of carbon-nickel films annealed at different temperatures（300-1000 ℃） with a special emphasis on the surface plasmon resonance（SPR） were investigated. The films were grown on quartz substrates by radio-frequency（RF）magnetron co-sputtering at room temperature with a deposition time of 600 s. The optical absorption peaks due to the SPR of Ni particle are observed in the wavelength range of 300-330 nm. With annealing temperature increasing up to 500 ℃ due to the increase in Ni particle size, the intensity of the SPR peaks increases, but weakens with annealing temperature increasing over 500 ℃. The Ni nanoparticle size, the dielectric function of carbon matrix（ε_m） and the plasma frequency of the free electrons（ω_p） at500 ℃have the maximum values of 21.63 nm, 0.471 and5.26 9 10^（15）s^（-1）, respectively. The absorption peak shows a redshift trend up to 500 ℃and then turn to blueshift with annealing temperature increasing over 500 ℃ These observations are in a good agreement with the electrical measurements in temperature range of 15-520 K and the Maxwell-Garnett（M-G） effective medium theory（EMT）.

Impact of annealing temperature on the ferroelectric properties of W/Hf_(0.5)Zr_(0.5)O_(2)/W capacitor

Crystallization annealing is a crucial process for the formation of the ferroelectric phase in HfO_(2)-based ferroelectric thin films.Here,we systematically investigate the impact of the annealing process,with temperature varied from 350℃to 550℃,on the electricity,ferroelectricity and reliability of a Hf_(0.5)Zr_(0.5)O_(2)(HZO;7.5 nm)film capacitor.It was found that HZO film annealed at a low temperature of 400℃can effectively suppress the formation of the monoclinic phase and reduce the leakage current.HZO film annealed at 400℃also exhibits better ferroelectric properties than those annealed at 350℃and 550℃.Specifically,the 400℃-annealed HZO film shows an outstanding 2Pr value of 54.6μC·cm^(-2)at±3.0 MV·cm^(-1),which is relatively high compared with previously reported values for HZO film under the same electric field and annealing temperature.When the applied electric field increases to±5.0 MV·cm^(-1),the 2Pr value can reach a maximum of 69.6μC·cm^(-2).In addition,the HZO films annealed at 400℃and 550℃can endure up to bout 2.3×10^(8)cycles under a cycling field of 2.0 MV·cm^(-1)before the occurrence of breakdown.In the 400℃-annealed HZO film,72.1%of the initial polarization is maintained while only 44.9%is maintained in the 550℃-annealed HZO film.Our work demonstrates that HZO film with a low crystallization temperature(400℃)has quite a high ferroelectric polarization,which is of significant importance in applications in ferroelectric memory and negative capacitance transistors.

Effects of annealing temperature on the microstructure and properties of the 25Mn-3Si-3Al TWIP steel

Microstructures and mechanical properties of the 25Mn twinning induced plasticity （TWIP） steel at different annealing temperatures were investigated. The results indicated that when the annealing temperature was 1000℃, the 25Mn steel showed excellent comprehensive mechanical properties, the tensile strength was about 640 MPa, the yield strength was higher than 255 MPa, and the elongation was above 82%. The microstructure was analyzed by optical microscopy （OM）, X-ray diffraction （XRD）, and transmission electron microscopy （TEM）. Before deformation the microstructure was composed of austenitic matrix and annealing twins at room temperature; at the same time, a significant amount of annealing twins and stacking faults were observed by TEM. Mechanical twins played a dominant role in deformation and as a result the mechanical properties were found to be excellent.

Effect of annealing temperature on microstructure and electrochemical performance of La_(0.75)Mg_(0.25)Ni_(3.5)Co_(0.2) hydrogen storage electrode alloy

To improve the cyclic stability of La-Mg-Ni system alloy, as-cast La0.75Mg0.25Ni3.5Co0.2 alloy was annealed at 1123, 1223, and 1323 K for 10 h in 0.3 MPa argon. The microstructure and electrochemical performance of different annealed alloys were investigated systematically by X-Ray Diffraction （XRD）, Scanning Electron Microscopy （SEM）, X-Ray Photoelectron Spectroscopy （XPS）, and electrochemical experiments. The results obtained by XRD and SEM showed that the as-cast and annealed （1123 K） alloys had multiphase structure containing LaNis, （La, Mg）2（Ni, Co）7 and few LaNi2 phases. When annealing temperatures approached 1223 and 1323 K, LaNi2 phase disappeared. The annealed alloys at 1223 and 1323 K were composed of LaNi5, （La, Mg）2（Ni, Co）7 and （La, Mg）（Ni, Co）3 phases. With increasing annealing temperature, the maximum discharge capacity of the alloy decreased monotonously, but the cyclic stability was improved owing to structure homogeneity and grain growth after annealing, as well as the enhancement of anti-oxidation/corrosion ability and the suppression of pulverization during cycling in KOH electrolyte.

Effects of substrate temperature and annealing treatment on the microstructure and magnetic characteristics of TbDyFe films

A series of TbDyFe films were prepared by DC magnetron sputtering. The effects of substrate temperature and annealing temperature on the phase structure and the magnetic properties of the sample films were investigated. The an-nealing treatment has a significant influence on the microstructure and the magnetic properties of the sample. The results obtained by XRD indicate that the films deposited at a temperature lower than 525℃ are amorphous and have an easy magnetization direction perpendicular to the film plane. An RFe2 phase is formed in the sample annealed at 550℃ and the residual phases observed are Fe and rare earth oxide. The magnetic properties Hc and Mr/Ms of the film annealed at 550℃ obtain the maximum values,for which the formation of the RFe2 phase is mainly responsible. An annealing treatment leads to a rotation of the sample’s easy axis from being parallel to the film surface to becoming vertical.

Preparation and Luminescence Properties of Y_2O_3:Eu^(3+) Nanorods via Post Annealing Process

Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrotherma] reaction route using PEG-6000 as template from the starting Y(NO3)3 and KOH reactant system, was used to prepare Y2O3:Eu3 + nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3: Eu3 + product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3: Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that. grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 ~ 60 nm and length of about 500 ~ 700 nm, the nanorod structure and morphology of obtained Y2O3: Eu + product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3 + phase was formed and the size was the smallest at annealing treatment of 500℃. Under the annealing temperature below 500℃its diameter increased with increasing annealing temperature , and remained in a stable size when the annealing temperature was above 500℃. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3 + ions transition from 5D0 to 7F2. Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000℃.

Annealing Temperature Effects of TiO2 Nanofiber Anodes for the Rechargeable Lithium Ion Batteries

TiO2 nanofibers（TiO2/NFs） have been synthesized through an electrospinning method and annealed at 400, 500 and 600 ℃ to optimize their systems. The effects of annealing temperature on the electrochemical properties for lithium ion batteries（LIBs） are assessed. The obtained LIB properties for TiO2 nanofiber anodes annealed at 400 ℃（denoted as TiO2/NFs-400） are much better than those of TiO2/NFs-500 and TiO2/NFs-600. The TiO2/NFs-400 anodes show good LIB performance with capacities of 180 and 150 m Ah/g tested at 200 and 600 m A/g after 100 cycles with almost no capacity loss and superb rate performance. The XRD results show that the pure anatase phase TiO2 can form at 400 ℃ for TiO2/NFs-400, while mixed phases of anatase and rutile are emerged at TiO2/NFs-500 and TiO2/NFs-600. Furthermore, the TiO2 nanoparticles are combined in nanofibers, and their corresponding crystal particle size for TiO2/NFs-400 was smaller than that of the other two samples. It is concluded that the superior electrochemical performance of the TiO2/NFs-400 anodes could be due to their pure crystal of anatase, small nanoparticles and non-ideal crystal lattices.

Effect of Annealing Temperature on the Formation of Silicides and the Surface Morphologies of PtSi Films

The effect of annealing temperature on the formation of the PtSi phase. distribution of silicides and the surface morphologies of silicides films is investigated by XPS. AFM. It is shown that the phase sequences of the films change from Pt-Pt2Si-PtSi-Si to Pt+Pt2Si+PtSi-PtSi-Si or Pt+Pt2Si+PtSi-PtSi-st with an increase of annealing temperature and the reason for the formation of mixed layers is discussed.

Annealing Temperature dependence of Photoluminescence from Silicon-rich silica Films

The silicon-rich silica films were prepared by a dual-ion-beam co-sputtering method from a composite Target in an argon atmosphere. The structure of the films studied by the aid of TEM and XRD is amorphous. The photoluminescence (PL) spectra were found to have a 4- luminescent band peak at 320 nm, 410 nm, 560 nm, and 630 nm, respectively, at room temperature. The intensity and the wavelength position of PL are dependent on annealing temperature (Ta), and the luminescent mechanism is analyzed.

Effect of the annealing temperature on the long-term thermal stability of Pt/Si/Ta/Ti/4H–SiC contacts

The Pt/Si/Ta/Ti multilayer metal contacts on 4H-Si C are annealed in Ar atmosphere at 600°C-1100°C by a rapid thermal processor（RTP）. The long-term thermal stability is evaluated by aging the annealed contact at 600°C in air. The contact＇s properties are determined by current-voltage measurement, and the specific contact resistance is calculated based on the transmission line model（TLM）. Transmission electron microscope（TEM） and energy-dispersive x-ray spectrometry（EDX） are used to characterize the interface morphology, thickness, and composition. The results reveal that a higher annealing temperature is favorable for the formation of an Ohmic contact with a lower specific contact resistance, and causes the rapid degradation of the Ohmic contact in the aging process.

Effect of annealing temperature on structure and electrochemical properties of LiCoO_2 cathode thin films

LiCoO2 thin films, which can be used as a cathode material in microbatteries, were deposited using radio frequency (r.f.) magnetron sputtering system from a LiCoO2 target and in an O2+Ar atmosphere. The films were characterized by various methods such as XRD, SEM and AFM. The LiCoO2 films were annealed in air at 300, 500, 700 and 800 ℃ respectively. The effect of the annealing temperature on the structure, the surface morphology and the electrochemical properties of the films were investigated. The LiCoO2 thin film deposited at room temperature is amorphous and has smaller grain size. With increasing of annealing temperature, the crystallinity of the films is promoted. When the annealing temperature increases to 700 ℃, the films have a perfect crystalline LiCoO2 phase. The LiCoO2 thin film without annealing has no discharge plateau and small discharge capacity (about 27 μAh·cm-2μm). The discharge capacity increases with the increasing of annealing temperature and reaches 47 μAh·cm-2μm for the film annealed with 700 ℃, which also shows the typical discharge plateau of 3.9 V. The cycle performance of LiCoO2 thin films of as grown and annealed at different temperatures were studied. In the case of the film without thermal treatment, the capacity fading is much faster than that of the film annealed at different temperature, showing about 40% capacity loss only after 25 cycles. However, in the case of the film annealed at 700 ℃, the capacity reaches to steady state gradually and maintained constantly with cycling. After 25 times cycling, the discharge capacity of the film annealed at 700 ℃ decreases to about 36.9 μAh·cm-2·μm, only 0.8% capacity loss per cycle.

Effects of Annealing Temperature on Microstructure and Sensing Properties to Alcohol for Nano-La_(0.68)Pb_(0.32)FeO_3

La_(0.68)Pb_(0.32)FeO_3 samples annealed at different temperature were prepared using citrate sol-gel method. With increasing of annealing temperature from 200 to 1000 ℃, the samples crystallize to have single-phase perovskite structure. However, the sensitivity increases at first due to the improvement of crystallization of the perovskite phase, and finally drops attributed to the larger grain size. The optimal sensitivities for La_(0.68)Pb_(0.32)FeO_3 samples annealed at 400, 600, 800, and 1000 ℃ are 12.14, 14.77, 51.07, and 34.55, respectively.

Effect of annealing temperature on interfacial and electrical performance of Au-Pt-Ti/HfAlO/InAlAs metal-oxide-semiconductor capacitor

HfAlO/InAlAs metal-oxide-semiconductor capacitor (MOS capacitor) is considered as the most popular candidate of the isolated gate of InAs/AlSb high electron mobility transistor (HEMT). In order to improve the performance of the HfAlO/InAlAs MOS-capacitor, samples are annealed at different temperatures for investigating the HfAlO/InAlAs interfacial characyeristics and the device's electrical characteristics. We find that as annealing temperature increases from 280 ℃ to 480 ℃, the surface roughness on the oxide layer is improved. A maximum equivalent dielectric constant of 8.47, a minimum equivalent oxide thickness of 5.53 nm, and a small threshold voltage of -1.05 V are detected when being annealed at 380 ℃;furthermore, a low interfacial state density is yielded at 380 ℃, and this can effectively reduce the device leakage current density to a significantly low value of 1×10-7 A/cm2 at 3-V bias voltage. Therefore, we hold that 380 ℃ is the best compromised annealing temperature to ensure that the device performance is improved effectively. This study provides a reliable conceptual basis for preparing and applying HfAlO/InAlAs MOS-capacitor as the isolated gate on InAs/AlSb HEMT devices.

The influence of annealing temperature on the morphology of graphene islands

We report on temperature-programmed growth of graphene islands on Ru （0001） at annealing temperatures of 700 ℃, 800 ℃, and 900 ℃. The sizes of the islands each show a nonlinear increase with the annealing temperature. In 700 ℃ and 800 ℃annealings, the islands have nearly the same sizes and their ascending edges are embedded in the upper steps of the ruthenium substrate, which is in accordance with the etching growth mode. In 900 ℃ annealing, the islands are much larger and of lower quality, which represents the early stage of Smoluchowski ripening. A longer time annealing at 900 ℃ brings the islands to final equilibrium with an ordered moire pattern. Our work provides new details about graphene early growth stages that could facilitate the better control of such a growth to obtain graphene with ideal size and high quality.

Effects of Annealing Temperature on the Electrical Conductivity and Mechanical Property of Cu-Te Alloys

The effects of annealing temperatre on the electrical conducitivity and mechanical property of Cu-Te alloys were studied via an AG-10TA electronic universal machine, an SB2230 digital electric bridge, SEM, EDS and XPS. The results show the electrical conductivity increases while the tensile strength fluctuates when the annealing temperature becomes higher because the recrystallization occurs during the annealing process, leading to the density of dislocation decreasing, grain size growing up, but the second phase precipitating sufficiently and simultaneously.

Porosity Evaluation and the Power Spectral Densities Analyses of Carbon-Nickel Composite Films Annealed at Different Temperatures

The densification and the fractal dimensions of carbon-nickel films annealed at different temperatures 300, 500, 800, and 1000℃ with emphasis on porosity evaluation are investigated. For this purpose, the refractive index of films is determined from transmittance spectra. Three different regimes are identified, T 〈 500℃, 500℃ 〈 T 〈 800℃ and T 〉 800℃. The Rutherford baekscattering spectra show that with increasing the annealing temperature, the concentration of nickel atoms into films decreases. It is shown that the effect of annealing temperatures for increasing films densification at T 〈 500℃ and T 〉 800℃ is greater than the effect of nickel concentrations. It is observed that the effect of decreasing nickel atoms into films at 500℃ 〈 T 〈 800℃ strongly causes improving porosity and decreasing densification. The fractal dimensions of carbon-nickel films annealed from 300 to 500℃ are increased, while from 500 to 1000℃ these characteristics are decreased. It can be seen that at 800℃, films have maximum values of porosity and roughness.

Effect of Annealing Temperature on Magnetic Aftereffect and Positron Lifetime in Fe_(73.5)Cu_1Nb_3Si_(13.5)B_9 Alloy

The magnetic aftereffect (MAE) and the positron lifetime were measured at room temperature on the Fe_73.5Cu_1 Nb_3Si_13.5 B_9 alloy in as-cast and after annealing at temperature T_a in the range from 450 to 750℃ It was found that both the MAE and the positron lifetime decrease with increasing T_a when T_≤600℃. While Ta≥650℃, MAE is essentially suppressed, and two positron lifetimes appear.

Effect of continuous annealing temperature on the microstructure and mechanical property of an aluminum killed steel

The continuous annealing process of a typical aluminum killed steel was investigated. A cold rolled sheet was annealed continuously at holding temperature ranging from 580 to 760 ℃. The microstructures were analyzed in detail based on contiuous cooling transformation（ CCT） curves that were simulated with JM artP ro softw are. The results show ed that recrystallization and perlitic transformations caused a diversity of microstructures and mechanical properties. In comparison with annealed steel that was produced from insufficient recrystallization,annealed steel produced from sufficient recrystallization had more isometric grains and exhibited low er strength and higher ductility. Higher annealing temperatures than A_1 provided steel with lamellar pearlite zones,large ferrite grains,low strength,and high ductility. The results are attributed to the property optimization of the steel.