Anode oxidation of HCHO in THPED-containing electroless copper plating solution

The electrochemical mechanism of anode oxidation of HCHO in electroless copper plating solution with N, N, N′, N′-tetrakis(2-hydroxypropyl)ethylenediamine (THPED) was investigated by measuring cyclic voltammetry curves and anodic polarization curves. Three different oxidation peaks occur at the potentials of -0.62 V (Peak 1), -0.40 V (Peak 2) and -0.17 V (Peak 3) in the anode oxidation process of THPED-containing solution. The reaction at Peak 1, a main oxidation reaction, is the irreversible reaction of adsorbed HCHO with hydrogen evolution. The reaction at Peak 2, a secondary oxidation reaction, is the quasi-reversible reaction of adsorbed HCHO without hydrogen evolution. The reaction at Peak 3 is the irreversible oxidation of anode copper. The current density of Peak 1 increases gradually, that of Peak 2 remains constant and that of Peak 3 decreases with the increase of HCHO concentration. The current density of Peak 3 increases with the increase of THPED concentration and the complexation of THPED promotes the dissolution of anode copper.

Enhancing capacitive deionization performance and cyclic stability of nitrogen-doped activated carbon by the electro-oxidation of anode materials

Electrode materials with high desalination capacity and long-term cyclic stability are the focus of capacitive deionization(CDI) community. Understanding the causes of performance decay in traditional carbons is crucial to design a high-performance material. Based on this, here, nitrogen-doped activated carbon(NAC) was prepared by pyrolyzing the blend of activated carbon powder(ACP) and melamine for the positive electrode of asymmetric CDI. By comparing the indicators changes such as conductivity, salt adsorption capacity, pH, and charge efficiency of the symmetrical ACP-ACP device to the asymmetric ACP-NAC device under different CDI cycles, as well as the changes of the electrochemical properties of anode and cathode materials after long-term operation, the reasons for the decline of the stability of the CDI performance were revealed. It was found that the carboxyl functional groups generated by the electro-oxidation of anode carbon materials make the anode zero-charge potential(E_(pzc)) shift positively,which results in the uneven distribution of potential windows of CDI units and affects the adsorption capacity. Furthermore, by understanding the electron density on C atoms surrounding the N atoms, we attribute the increased cyclic stability to the enhanced negativity of the charge of carbon atoms adjacent to quaternary-N and pyridinic-oxide-N.

Electrochemical anodic oxidation assisted fabrication of memristors

Owing to the advantages of simple structure,low power consumption and high-density integration,memristors or memristive devices are attracting increasing attention in the fields such as next generation non-volatile memories,neuromorphic computation and data encryption.However,the deposition of memristive films often requires expensive equipment,strict vacuum conditions,high energy consumption,and extended processing times.In contrast,electrochemical anodizing can produce metal oxide films quickly(e.g.10 s) under ambient conditions.By means of the anodizing technique,oxide films,oxide nanotubes,nanowires and nanodots can be fabricated to prepare memristors.Oxide film thickness,nanostructures,defect concentrations,etc,can be varied to regulate device performances by adjusting oxidation parameters such as voltage,current and time.Thus memristors fabricated by the anodic oxidation technique can achieve high device consistency,low variation,and ultrahigh yield rate.This article provides a comprehensive review of the research progress in the field of anodic oxidation assisted fabrication of memristors.Firstly,the principle of anodic oxidation is introduced;then,different types of memristors produced by anodic oxidation and their applications are presented;finally,features and challenges of anodic oxidation for memristor production are elaborated.

Influence of oxidation heat on hard anodic film of aluminum alloy

The special experimental device and sulfuric acid electrolyte were adopted to study the influence of anodic oxidation heat on hard anodic film for 2024 aluminum alloy. Compared with the oxidation heat transferred to the electrolyte through anodic film, the heat transferred to the coolant through aluminum substrate is more beneficial to the growth of anodic film. The film forming speed, film thickness, density and hardness are significantly increased as the degree of undercooling of the coolant increases. The degree of undercooling of the coolant, which is necessary for the growth of anodic film, is related to the degree of undercooling of the electrolyte, thickness of aluminum substrate, thickness of anodic film, natural parameters of bubble covering and current density. The microstructure and performance of the oxidation film could be controlled by the temperature of the coolant.

Electroless Deposition of Nickel Nanowire and Nanotube Arrays as Supports for Pt-Pd Catalyst for Ethanol Electrooxidation

Nickel nanowire and nanotube arrays as supports for Pt-Pd catalyst were prepared by elec- troless deposition with anodic aluminum oxide template. Pt-Pd composite catalyst was de- posited on the arrays by displacement reaction. SEM images show that the nickel nanowires have an average diameter of I00 nm and the nickel nanotubes have an average inner diameter of 200 nm. EDS scanning reveals that elemental Pt and Pd disperse uniformly on the arrays. Cyclic voltammetry study indicates that the nickel nanotube array loaded with Pt-Pd pos- sesses a higher electrochemical activity for ethanol oxidation than the nickel nanowire array with Pt-Pd.

Electrochemical behavior of mesh and plate oxide coated anodes during zinc electrowinning

The catalytic performance of two oxides coated anodes （OCSs） meshes and one OCA plate was investigated in a zinc electrowinning electrolyte at 38 ℃. Their electrochemical behaviors were compared with that of a conventional Pb-0.7%Ag alloy anode. Electrochemical measurements such as cyclic voltammetric, galvanostatic, potentiodynamic, open-circuit potential （OCP） and in situ electrochemical noise measurements were considered. After 2 h of OCP test, the linear polarization shows that the corrosion current density of the Ti/（IrO2-Ta2O5） mesh electrode is the lowest （3.37μA/cm^2） among the three OCAs and shows excellent performance. Additionally, after 24 h of galvanostatic polarization at 50 mA/cm^2and 38 ℃, the Ti/MnO2mesh anode has the highest potential （1.799 V）, followed by the Ti/（IrO2-Ta2O5） plate （1.775 V） and Ti/（IrO2-Ta2O5） mesh （1.705 V） anodes. After 24 h of galvanostatic polarization followed by 16 h of decay, the linear polarization method confirms the sequence obtained after 2 h of OCP test, and the Ti/（IrO2-Ta2O5） mesh attains the lowest corrosion current density. The Ti/（IrO2-Ta2O5） mesh anode also shows better performance after 24 h of galvanostatic polarization with the overpotential lower than that of the conventional Pb-Ag anode by about 245 mV.

Phenol degradation by anodic oxidation on boron-doped diamond electrode combining TiO_2 Photocatalysis

Boron-doped diamond （BDD） electrocatalysis is combined with photocatalysis using titanium dioxide （TiO2） as a catalyst to improve pollutant-oxidation efficiency. Phenol solution is chosen as model wastewater. Different methods involving BDD and/or TiO2 during the degradation processes are compared. Parameters such as the currency density and initial concentration are varied in order to determine their effects on the oxidation process. Moreover, the degradation kinetics of phenol is experimentally studied. The results reveal the superiority of series combination of BDD and TiO2, especially the treatment process of electrocatalysis and succedent photocatalysis, and the optimum working currency density for electrocatalysis is 25.48 mA/cm2. The removal rate decreases with the increase in the initial phenol concentration and the degradation reaction follows quasi-first-order kinetics equation.

Effect of Deposition Temperature on Optical Properties of Porous Amorphous SiC Film

To study the effect of different deposition temperatures on the optical properties of porous SiC films,single crystal Si was used as the substrate,a layer of anodic aluminum oxide(AAO)film was transferred on the Si substrate by chemical method,and then a layer of SiC was deposited on anodic aluminum oxide(AAO)template to prepare porous fluorescent SiC film by magnetron sputtering.The deposition temperature was ranged from 373 to 873 K.The thickness of the porous SiC film coated on the AAO surface was around 283 nm.It is found that the porous SiC with the deposition temperature of 873 K has the strongest photoluminescence(PL)intensity excited by 375 nm laser.The time-resolved PL spectra prove that the PL is mainly from intrinsic light emitting of SiC.With the optimized process,porous amorphous SiC film may have potential applications in the field of warm white LEDs.

Efficient concentration of trace analyte with ordered hotspot construction for a robust and sensitive SERS platform

Surface-enhanced Raman scattering(SERS)platform,which enables trace analyte detection,has important application prospects.By structuring/modifying the surface of the SERSsubstrate,analyte in highly diluted solutions can be concentrated into localized active areas for highly sensitive detection.However,subject to the difficulty of the fabrication process,itremains challenging to balance hot-spot construction and the concentration capacity of analyte simultaneously.Therefore,preparing SERS substrates with densely ordered hot spots andefficient concentration capacity is of great significance for highly sensitive detection.Herein,we propose an Ag and fluoroalkyl-modified hierarchical armour substrate(Ag/F-HA),which has a double-layer stacking design to combine analyte concentration with hotspot construction.The microarmour structure is fabricated by femtosecond-laser processing to serve as asuperhydrophobic and low-adhesive surface to concentrate analyte,while the anodic aluminium oxide(AAO)template creates a nanopillar array serving as dense and ordered hot spots.Under the synergistic action of hot spots and analyte concentration,Ag/F-HA achieves a detectionlimit down to 10^(-7)M doxorubicin(DOX)molecules with a RSD of 7.69%.Additionally,Ag/F-HA exhibits excellent robustness to resist external disturbances such as liquid splash or abrasion.Based on our strategy,SERS substrates with directional analyte concentrations are further explored by patterning microcone arrays with defects.This work opens a way to the realistic implementation of SERS in diverse scenarios.

Effect of intermetallic phases on the anodic oxidation and corrosion of 5A06 aluminum alloy

Intermetallic phases were found to influence the anodic oxidation and corrosion behavior of 5A06 aluminum alloy. Scattered in- termetallic particles were examined by scanning electron microscopy （SEM） and energy dispersive spectroscopy （EDS） after pretreatment. The anodic film was investigated by transmission electron microscopy （TEM）, and its corrosion resistance was analyzed by electrochemical impedance spectroscopy （EIS） and Tafel polarization in NaC1 solution. The results show that the size of A1-Fe-Mg-Mn particles gradually decreases with the iron content. During anodizing, these intermetallic particles are gradually dissolved, leading to the complex porosity in the anodic film beneath the particles. After anodizing, the residual particles are mainly silicon-containing phases, which are embedded in the an- odic film. Electrochemical measurements indicate that the porous anodic film layer is easily penetrated, and the barrier plays a dominant role in the overall protection. Meanwhile, self-healing behavior is observed during the long immersion time.

Photocatalytic activity of porous TiO_2 films prepared by anodic oxidation

Anatase titanium dioxide is an active photocatalyst, however, it is difficult to be immobilized on the substrate. The crystalline TiO2 porous film was prepared directly on the surface of pure titanium by anodic oxidation. The film was then used for photocatalysis via the methyl orange degradation method. The effects of anodization voltage, pH value, TiO2 film area and degradation time on the photocatalyst were investigated respectively by UV-visible spectrum. It was indicated that the TiO2 film prepared by anodic oxidation at 140 V had the best photocatalysis capability and the degradation of methyl orange was accelerated with acid addition.

Application of advanced oxidation processes for removing salicylic acid from synthetic wastewaters

In this study,advanced oxidation processes(AOPs) such as anodic oxidation(AO),UV/H_2O_2 and Fenton processes(FP) were investigated for the degradation of salicylic acid(SA) in lab-scale experiments.Boron-doped diamond(BDD) film electrodes using Ta as substrates were employed for AO of SA.In the case of FP and UV/H_2O_2,most favorable experimental conditions were determined for each process and these were used for comparing with AO process.The study showed that the FP was the most effective process under aci...

Electrochemical incineration of dimethyl phthalate by anodic oxidation with boron-doped diamond electrode

The anodic oxidation of aqueous solutions containing dimethyl phthalate （DMP） up to 125 mg/L with sodium sulfate （Na2SO4） as supporting electrolyte within the pH range 2.0-10.0 was studied using a one-compartment batch reactor employing a boron-doped diamond （BDD） as anode. Electrolyses were carded out at constant current density （1.5-4.5 mA/cm^2）. Complete mineralization was always achieved owing to the great concentration of hydroxyl radical （-OH） generated at the BDD surface. The effects of pH, apparent current density and initial DMP concentration on the degradation rate of DMP, the specific charge required for its total mineralization and mineralization current efficiency were investigated systematically. The mineralization rate of DMP was found to be pH-independent and to increase with increasing applied current density. Results indicated that this electrochemical process was subjected, at least partially, to the mass transfer of organics onto the BDD surface. Kinetic analysis of the temporal change of DMP concentration during electrolysis determined by High Performance Liquid Chromatography （HPLC） revealed that DMP decay under all tested conditions followed a pseudo first-order reaction. Aromatic intermediates and generated carboxylic acids were identified by Gas Chromatography- Mass Spectrometry （GC-MS） and a general pathway for the electrochemical incineration of DMP on BDD was proposed.

Preparation and crystalline phase of a TiO_2 porous film by anodic oxidation

Anatase titanium dioxide is an active photocatalyst, but it is difficult to immobilize on the substrate. A crystalline TiO2 porous film was prepared directly on the surface of pure titanium by anodic oxidation in this work. Constant voltage and constant current anodic oxidation were adopted with sulphuric acid used as the electrolyte, pure titanium as the anode and copper as the cathode. The morphology and structure of the porous film on the substrate were analyzed with the aid of Field Emission Scanning Electron Microscopy （FESEM） and X-ray Diffraction （XRD）. The effects of the parameters of anodic oxidation （such as voltage, the concentration of sulphuric acid, anodization time and current density） on the aperture and the crystalline phase of the TiO2 porous film were systematically investigated. The results indicate that the increase of current density facilitates the augment of the aperture and the generation of anatase and mille. In addition, the forming mechanism of anatase and mille TiO2 porous films was discussed.

Optimizing the nickel boride layer thickness in a spectroelectrochemical ATR-FTIR thin-film flow cell applied in glycerol oxidation

The influence of the drop-casted nickel boride catalyst loading on glassy carbon electrodes was investigated in a spectroelectrochemical ATR-FTIR thin-film flow cell applied in alkaline glycerol electrooxidation.The continuously operated radial flow cell consisted of a borehole electrode positioned 50μm above an internal reflection element enabling operando FTIR spectroscopy.It is identified as a suitable tool for facile and reproducible screening of electrocatalysts under well-defined conditions,additionally providing access to the selectivities in complex reaction networks such as glycerol oxidation.The fast product identification by ATR-IR spectroscopy was validated by the more time-consuming quantitative HPLC analysis of the pumped electrolyte.High degrees of glycerol conversion were achieved under the applied laminar flow conditions using 0.1 M glycerol and 1 M KOH in water and a flow rate of 5μL min^(–1).Conversion and selectivity were found to depend on the catalyst loading,which determined the catalyst layer thickness and roughness.The highest loading of 210μg cm^(–2)resulted in 73%conversion and a higher formate selectivity of almost 80%,which is ascribed to longer residence times in rougher films favoring readsorption and C–C bond scission.The lowest loading of 13μg cm^(–2)was sufficient to reach 63%conversion,a lower formate selectivity of 60%,and,correspondingly,higher selectivities of C_(2)species such as glycolate amounting to 8%.Thus,only low catalyst loadings resulting in very thin films in the fewμm thickness range are suitable for reliable catalyst screening.

EFFECT OF SnO_2 ADDITION ON THE SERVICE LIFE AND ELECTROCHEMICAL PROPERTIES OF Ti/IrO_2,+Ta_2O_5 ANODES IN PHENOLSULFONIC ACID SOLUTION

Service life of two different oxide anodes in phenolsulfonic acid (PSA) solution was investigated by accelerated electrolysis. The durability of Ti/IrO_2+Ta_2 O_5 anode increased by the addition of SnO_2 in the mixed oxides. The degradation mechanisms of Ti/IrO_2+ Ta_2 O_5 and Ti/IrO_2 +Ta_2 O_5 +SnO+2 anodes were different. It was shown from the observation of scanning electron microscopy (SEM) and the electrochcmical measurement that, the deactivation of Ti/IrO_2 + Ta_2 O_5 anode was due to the build-up of an organic film on surface. The growth of the covered film on surface was restricted by addition of SnO_2, which resulted in increasing of the service life of anodes. The over-potential for oxygen evolution on Ti/IrO_2 +Ta_2 O_5 electrode increased after doping SnO_2, and the intermediate products of PSA building-up on the surface was much more rapidly oxidized. Meanwhile, a certain part of the surface oxide deposit entered into the solution leading to loss of oxides, which resulted in degradation of Ti/IroO_2 + Ta_2 O_5 anode containing SnO_2 component.

Improvement of stability of trivalent chromium electroplating of Ti based IrO_2+Ta_2O_5 coating anodes

The preparation process and properties of the thermally prepared Ti anodes coated with IrO2+Ta2O5 was studied. The structure and morphologies of the IrO2+Ta2O5 coatings were determined by XRD and SEM. Their electrochemical properties were studied by polarization curve and cyclic voltammetry. Trivalent chromium electroplating using Ti/IrO2+Ta2O5 anodes is carried out and the results were analyzed. Results show that this anode exhibits excellent electrochemical activity and stability in sulfate electrolysis. The electrocatalytic activity is determined not only by the content of IrO2 but also the structure and morphology of the anode coatings. The electroplating results indicats that Ti/IrO2+Ta2O5 anodes have excellent capabilities and merits in improving the stability of trivalent chromium electroplating in sulfate system.

A Study on the Relationship between Anodic Oxidation and the Thermal Load on the Aluminum Alloy Piston of a Gasoline Engine

In order to analyze the influence of the anodizing process on the thermal load of an aluminum alloy piston,dedicated temperature tests have been carried out using the Hardness Plug method and the results for the anodized piston have been compared with those obtained separately for an original aluminum piston.In addition,numerical simulations have been conducted to analyze the temperature field and thermal stress distribution.Simulations and experiments show that the maximum temperature of the anodized piston is 16.36%and 5.4%smaller than that of the original piston under the condition of maximum torque and maximum power,respectively.The thermal stress of the temperature field of both pistons is within 50 Mpa,which meets the strength requirements of the material at high temperature.However,the area with significant thermal stress of the anodized piston is significantly smaller than that of the original piston.Combined with the fatigue analysis data,it can be seen that the safety factor of the anodized piston greater than 1.8 is 99.13%.Therefore,adopting the anodizing process not only reduces the piston thermal load,but also helps to extend its life and improve its reliability.

Improvement on electrochemical performances of nanoporous titania as anode of lithium-ion batteries through annealing of pure titanium foils

The effect of annealing of Ti foils before anodization on the morphology and electrochemical performance of resultant nanoporous anatase TiO2 （np-TiO2） as anode in rechargeable lithium-ion batteries （LIBs） was investigated. The np-TiO2 anode fabricated from annealed Ti foils exhibited higher specific surface area and reduced pore diameter compared to np-TiO2 electrode fabricated from as-received Ti foils. The highly porous np-TiO2 anode fabricated from annealed Ti foils exhibited 1st discharge capacity of 453.25 mAh/g and reduced to 172.70 mAh/g at 1 C current rate after 300 cycles; whilst the np-TiO2 electrode fabricated from the as-received Ti foils exhibited 1st discharge capacity of 213.30 mAh/g and reduced to 160.0 mAh/g at 1 C current rate after 300cycles. Even after 400cycles, such np-TiO2 electrode exhibited a reversible capacity of 125.0 mAh/g at 2.5 C current rate. Compared to the untreated Ti foils, the enhanced electro- chemical performance of np-TiO2 anode fabricated from annealed Ti foils was ascribed to the annealing- induced removal of residual stress among the Ti atoms. The benefit of annealing process can reduce pore size of as-fabricated np-TiO2.

Evolution of insoluble eutectic Si particles in anodic oxidation films during adipic–sulfuric acid anodizing processes of ZL114A aluminum alloys

The effects of insoluble eutectic Si particles on the growth of anodic oxide films on ZL114A aluminum alloy substrates were in- vestigated by optical microscopy （OM） and scanning electron microscopy （SEM）. The anodic oxidation was performed at 25℃ and a con- stant voltage of 15 V in a solution containing 50 g/L sulfuric acid and 10 g/L adipic acid. The thickness of the formed anodic oxidation film was approximately 7.13 μm. The interpore distance and the diameters of the major pores in the porous layer of the film were within the ap- proximate ranges of 10~20 nm and 5-10 nm, respectively. Insoluble eutectic Si particles strongly influenced the morphology of the anodic oxidation films. The anodic oxidation films exhibited minimal defects and a uniform thickness on the ZL114A substrates; in contrast, when the front of the oxide oxidation films encountered eutectic Si particles, defects such as pits and non-uniform thickness were observed, and pits were observed in the films.