Synthetically quantitative evaluation function of characteristic parameters on CO_2 arc welding process

The statistical probability and their variation regularity of the measurable characteristic parameters in the CO 2 arc welding droplet short circuiting transfer process have been studied. The statistical analysis shows that the sensitivity of each characteristic parameter with regard to the variation of the short circuiting transfer process is different. The sensitivity of 4 kinds among these characteristic parameters is more intense than that of the short circuiting transfer frequency. In order to take account of the synthetic influence of these characteristic parameters, by means of the characteristic parameters synthetic value, a quantitative evaluation function is built up to describe and evaluate the short circuiting transfer process of CO 2 arc welding in real time. The testing shows that the evaluation function can give a suitable synthetic valuation for the short circuiting transfer process with a variety of welding variables.

Keyhole Double-Sided Arc Welding Process

In the proposed method, the current/arc is guided through the keyhole so that the energy of the plasma jet is compensated while it is consumed in heating the workpiece along the keyhole. As a result, deep narrow penetration has been achieved on 12.7 mm (1/2') thick stainless steel plates using 70 A welding current.

Approximate entropy——a new statistic to quantify arc and welding process stability in short-circuiting gas metal arc welding

Based on the phase state reconstruction of welding current in short-circuiting gas metal arc welding using carbon dioxide as shielding gas, the approximate entropy of welding current as well as its standard deviation has been calculated and analysed to investigate their relation with the stability of electric arc and welding process. The extensive experimental and calculated results show that the approximate entropy of welding current is significantly and positively correlated with arc and welding process stability, whereas its standard deviation is correlated with them negatively. A larger approximate entropy and a smaller standard deviation imply a more stable arc and welding process, and vice versa. As a result, the approximate entropy of welding current promises well in assessing and quantifying the stability of electric arc and welding process in short-circuiting gas metal arc welding.

Experimental Investigation on the Performance of Armour Grade Q&T Steel Joints Fabricated by Flux Cored Arc Welding with Low Hydrogen Ferritic Consumables

Quenched and Tempered （Q＆T） steels are widely used in the construction of military vehicles due to its high strength to weight ratio and high hardness. These steels are prone to hydrogen induced cracking （HIC） and softening in the heat affected zone （HAZ） after welding. The use of austenitic stainless steel （ASS） consumables to weld the above steel was the only available remedy to avoid HIC because of higher solubility for hydrogen in austenitic phase. Recent studies revealed that low hydrogen ferritic （LHF） steel consumables can also be used to weld Q＆T steels, which can give very low hydrogen levels in the weld deposits and required resistance against cold cracking. Hence, in this investigation an attempt has been made to study the performance of armour grade Q＆T steel joints fabricated by flux cored arc welding with LHF steel consumables. Two different consumables namely （i） austenitic stainless steel and （ii） low hydrogen ferritic steel have been used to fabricate the joints by flux cored arc welding （FCAW） process. The joints fabricated by LHF consumable exhibited superior transverse tensile properties due to the presence of ferrite microstructure in weld metal. The joints fabricated by ASS consumable showed higher impact toughness due to the presence of austenitic phase in weld metal microstructure. The HAZ softening in coarse grain heat affected zone （CGHAZ） is less in the joints fabricated using LHF consumable due to the lower heat input involved during fabrication compared to the joints fabricated using ASS consumables.

Cold Cracking of Flux Cored Arc Welded Armour Grade High Strength Steel Weldments

In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc welding （FCAW） process were used making welds using austenitic stainless steel （ASS） and low hydrogen ferritic steel （LHF） consumables. The diffusible hydrogen levels in the weld metal of the ASS and LHF consumables were determined by mercury method. Residual stresses were evaluated using X-ray stress analyzer and implant test was carried out to study the cold cracking of the welds. Results indicate that ASS welds offer a greater resistance to cold cracking of armour grade Q＆T steel welds.

Effect of Welding Processes and Consumables on Tensile and Impact Properties of High Strength Quenched and Tempered Steel Joints

Quenched and tempered steels are prone to hydrogen induced cracking in the heat affected zone after welding. The use of austenitic stainless steel consumables to weld the above steel was the only available remedy because of higher solubility for hydrogen in austenitic phase. In this investigation, an attempt was made to determine a suitable consumable to replace expensive austenitic consumables. Two different consumables, namely, austenitie stain less steel and low hydrogen ferritic steel, were used to fabricate the joints by shielded metal are welding （SMAW） and flux cored arc welding （FCAW） processes. The joints fabricated by using low hydrogen ferritic steel consumables showed superior transverse tensile properties, whereas joints fabricated by using austenitic stainless steel consumables exhibited better impact toughness, irrespective of the welding process used. The SMAW joints exhibited superior mechanical and impact properties, irrespective of the consumables used, than their FCAW counterparts.

Comparative Study on Processing Property Between CWW CO_2 Gas Shielded Welding and SAW

Cable welding wire（CWW）CO2gas shielded welding is an innovative process arc welding with high efficiency,high quality and low consumption,in which cable wire is used as consumable electrode.CWW CO2gas shielded welding and submerged arc welding（SAW）are used for contrast studies on processing property of high strength steel A36used in ship structure.The results show that the shapes of weld seam,using CWW CO2gas shielded welding and SAW,are good and no weld defect such as air hole,flaw,slag inclusion,incomplete fusion,lack of penetration and so on are found in the weld seam.Because the rotating of arc during CWW CO2gas shielded welding process has a strong stirring effect on molten pool,the grain in the heat affected zone（HAZ）of the joints,using CWW CO2 gas shielded welding,is small.Tensile failure positions of joints by CWW CO2gas shielded welding and SAW are all in the base metal,but tensile strength of CWW CO2gas shielded welding joint is higher than that of SAW joint by an average of 2.3%.The average impact energy of HAZ,using CWW CO2gas shielded welding and SAW,is almost equal,but the average impact energy of the weld seam using CWW CO2gas shielded welding is increased by 6%,and the average impact energy of the fusion line is increased by 7%.The 180°bending tests for the joints of CWW CO2 gas shielded welding and SAW are all qualified,and the joints hardness is all less than HV 355,but hardness of CWW CO2gas shielded welding wire welding joint near the fusion line is obviously lower.It can be concluded that the properties of CWW CO2gas shielded welding are better than those of the SAW joint,and CWW CO2gas shielded welding is suitable for welding high strength steel A36used in ship structure.