Oxidation of As（Ⅲ） by three types of manganese oxides and the effects ofpH, ion strength and tartaric acid on the oxidation were investigated by means of chemical analysis, equilibrium redox, X-ray diffraction （XR...Oxidation of As（Ⅲ） by three types of manganese oxides and the effects ofpH, ion strength and tartaric acid on the oxidation were investigated by means of chemical analysis, equilibrium redox, X-ray diffraction （XRD） and transmission electron microscopy （TEM）. Three synthesized Mn oxide minerals, bimessite, cryptomelane, and hausmannite, which widely occur in soil and sediments, could actively oxidize As（Ⅲ） to As（Ⅴ）. However, their ability in As（Ⅲ）-oxidation varied greatly depending on their structure, composition and surface properties. Tunnel structured cryptomelane exhibited the highest ability of As （Ⅲ） oxidation, followed by the layer structured birnessite and the lower oxide hausmannite. The maximum amount of As （Ⅴ） produced by the oxidation was in the order （mmol/kg） of cryptomelane （824.2） 〉 bimessite （480.4） 〉 hausmannite （117.9）, As pH increased from the very low value（pH 2.5）, the amount of As（Ⅲ） oxidized by the tested Mn oxides was firstly decreased, then negatively peaked in pH 3.0 6.5, and eventually increased remarkably. Oxidation of As（Ⅲ） by the Mn oxides had a buffering effects on the pH variation in the solution. It is proposed that the oxidative reaction processes between As （Ⅲ） and biruessite（or cryptomelane） are as follows： （1） at lower pH condition： （MnO2）x＋ H3AsO3 ＋ 0.5H^＋=0.5H2AsO4^- ＋ 0.5HAsO4^2- ＋Mn〉^2＋ （MnO2）x-1 ＋ H2O; （2） at higher pH condition： （MnO2）x ＋ H3AsO3 = 0.5H2AsO4^- ＋ 0.5HAsO4^2- ＋ 1.5H^＋ ＋ （MnO2）x-1. MnO. With increase of ion strength, the As（Ⅲ） oxidized by bimessite and cryptomelane decreased and was negatively correlated with ion strength. However, ion strength had little influence on As （Ⅲ） oxidation by the hausmarmite. The presence of tartaric acid promoted oxidation of As（Ⅲ） by birnessite. As for cryptomelane and hansmannite, the same effect was observed when the concentration of tartaric acid was below 4 mmol/L, otherwise the oxidized As（Ⅲ） decreased. These findings are of great significance in improving our understanding of As geochemical cycling and controlling As contamination.展开更多
The present work deals with the As（Ⅴ） removal from an aqueous medium by calcined refractory grade bauxite （CRB） as a function of solution pH, time, As（Ⅴ） concentration and temperature. The residual As（Ⅴ） wa...The present work deals with the As（Ⅴ） removal from an aqueous medium by calcined refractory grade bauxite （CRB） as a function of solution pH, time, As（Ⅴ） concentration and temperature. The residual As（Ⅴ） was lowered from 2 mg/L to below 0.01 mg/L in the optimum pH range 4.0-7.0 using a 5 g/L CRB within 3 h contact time. The adsorption data fits well with Langmuir isotherm and yielded Langmuir monolayer capacity of 1.78 mg As（Ⅴ）/g of CRB at pH 7.0. Presence of anions such as silicate and phosphate decreased As（Ⅴ） adsorption efficiency. An increase temperature resulted a decrease in the amount of As（Ⅴ） adsorbed by 6%. The continuous fixed bed column study showed that at the adsorbent bed depth of 30 cm and residence time of 168 min, the CRB was capable of treating 340 bed volumes of As（V） spiked water （C0 = 2 mg/L） before breakthrough （Ce = 0.01 mg/L）. This solid adsorbent, although not reusable, can be considered for design of adsorption columns as an efficiency arsenic adsorption media.展开更多
文摘Oxidation of As（Ⅲ） by three types of manganese oxides and the effects ofpH, ion strength and tartaric acid on the oxidation were investigated by means of chemical analysis, equilibrium redox, X-ray diffraction （XRD） and transmission electron microscopy （TEM）. Three synthesized Mn oxide minerals, bimessite, cryptomelane, and hausmannite, which widely occur in soil and sediments, could actively oxidize As（Ⅲ） to As（Ⅴ）. However, their ability in As（Ⅲ）-oxidation varied greatly depending on their structure, composition and surface properties. Tunnel structured cryptomelane exhibited the highest ability of As （Ⅲ） oxidation, followed by the layer structured birnessite and the lower oxide hausmannite. The maximum amount of As （Ⅴ） produced by the oxidation was in the order （mmol/kg） of cryptomelane （824.2） 〉 bimessite （480.4） 〉 hausmannite （117.9）, As pH increased from the very low value（pH 2.5）, the amount of As（Ⅲ） oxidized by the tested Mn oxides was firstly decreased, then negatively peaked in pH 3.0 6.5, and eventually increased remarkably. Oxidation of As（Ⅲ） by the Mn oxides had a buffering effects on the pH variation in the solution. It is proposed that the oxidative reaction processes between As （Ⅲ） and biruessite（or cryptomelane） are as follows： （1） at lower pH condition： （MnO2）x＋ H3AsO3 ＋ 0.5H^＋=0.5H2AsO4^- ＋ 0.5HAsO4^2- ＋Mn〉^2＋ （MnO2）x-1 ＋ H2O; （2） at higher pH condition： （MnO2）x ＋ H3AsO3 = 0.5H2AsO4^- ＋ 0.5HAsO4^2- ＋ 1.5H^＋ ＋ （MnO2）x-1. MnO. With increase of ion strength, the As（Ⅲ） oxidized by bimessite and cryptomelane decreased and was negatively correlated with ion strength. However, ion strength had little influence on As （Ⅲ） oxidation by the hausmarmite. The presence of tartaric acid promoted oxidation of As（Ⅲ） by birnessite. As for cryptomelane and hansmannite, the same effect was observed when the concentration of tartaric acid was below 4 mmol/L, otherwise the oxidized As（Ⅲ） decreased. These findings are of great significance in improving our understanding of As geochemical cycling and controlling As contamination.
文摘The present work deals with the As（Ⅴ） removal from an aqueous medium by calcined refractory grade bauxite （CRB） as a function of solution pH, time, As（Ⅴ） concentration and temperature. The residual As（Ⅴ） was lowered from 2 mg/L to below 0.01 mg/L in the optimum pH range 4.0-7.0 using a 5 g/L CRB within 3 h contact time. The adsorption data fits well with Langmuir isotherm and yielded Langmuir monolayer capacity of 1.78 mg As（Ⅴ）/g of CRB at pH 7.0. Presence of anions such as silicate and phosphate decreased As（Ⅴ） adsorption efficiency. An increase temperature resulted a decrease in the amount of As（Ⅴ） adsorbed by 6%. The continuous fixed bed column study showed that at the adsorbent bed depth of 30 cm and residence time of 168 min, the CRB was capable of treating 340 bed volumes of As（V） spiked water （C0 = 2 mg/L） before breakthrough （Ce = 0.01 mg/L）. This solid adsorbent, although not reusable, can be considered for design of adsorption columns as an efficiency arsenic adsorption media.