SrTiO_3 nano-crystal samples with floccule or flake crystal morphology,which were indexed as a perovskite-type crystal structure based on the results of XRD and TEM,were successfully prepared by one-step liquid reacti...SrTiO_3 nano-crystal samples with floccule or flake crystal morphology,which were indexed as a perovskite-type crystal structure based on the results of XRD and TEM,were successfully prepared by one-step liquid reaction method.And the growth mechanism of the SrTiO_3 nano-crystals under the liquid condition with/without adding the surface active agent was investigated.It was found that adding the surface active agent contributes to the processing in which the ions gathering bodies transit to a more stable phase through the chemical reaction and form the flake SrTiO_3 nano-crystals.展开更多
The Er^3＋/yb^3＋ co-doped transparent oxyfluoride glass-ceramics containing CaF2 nano-crystals were successfully prepared. After heat treatments, transmission electron microscopy （TEM） images showed that CaF2 nano-...The Er^3＋/yb^3＋ co-doped transparent oxyfluoride glass-ceramics containing CaF2 nano-crystals were successfully prepared. After heat treatments, transmission electron microscopy （TEM） images showed that CaF2 nano-crystals of 20-30 nm in diameter precipitated uniformly in the glass matrix. luminescence of Er^3＋ at 540 nm and 658 nm was observed in Comparing with the host glass, high efficiency upconversion the glass ceramics under the excitation of 980 nm. Moreover, the size of the precipitated nano-crystals can be controlled by heat-treatment temperature and time. With the increase of the nano-crystal size, the intensity of the red emission increased more rapidly than that of the green emission. The energy transfer process of Er^3＋ and Yb^3＋ was convinced and the possible mechanism of Er^3＋ up-conversion was discussed.展开更多
Traditional wastewater mostly contains pharmaceutical ingredients. Therefore, the wastewater must be completely free from antibiotics before its release into the environment. In the present study, photocatalytic degra...Traditional wastewater mostly contains pharmaceutical ingredients. Therefore, the wastewater must be completely free from antibiotics before its release into the environment. In the present study, photocatalytic degradation was done to investigate the removal efficiency of Oxytetracycline Dihydrate (OTC) using ZnO, ZnO/3%BaTiO<sub>3</sub> (3 BZ), ZnO/18%BaTiO<sub>3</sub> (18 BZ), ZnO/ 33%BaTiO3 (33 BZ) and ZnO/48%BaTiO<sub>3</sub> (48 BZ) under UV light. After the exposure time of 420 min, about 99.57% and 97.87% of OTC was degraded using ZnO and 3 BZ respectively. Further, increasing the amount of BaTiO<sub>3</sub> in ZnO prolongs the degradation time. Therefore, faster efficiency was found using ZnO nanoparticles. The observed reaction rate constant using ZnO was 0.00933 min<sup>-1</sup> which decreased to 0.00532 min<sup>-1</sup> using 48 BZ, indicating the decrease of reaction rate for increasing the amount of BaTiO<sub>3</sub>. Hence, the use of ZnO photocatalyst is anticipated to be a promising technique for the photocatalytic degradation of contaminated wastewater with oxytetracycline antibiotics using UV light.展开更多
用硅烷和钛酸酯偶联剂对 Ba Ti O3粉进行了表面处理 ,使用溶剂法制备了 PVDF/Ba Ti O3复合薄膜。通过疏水亲油实验定性地分析了硅烷和钛酸酯偶联剂对 Ba Ti O3粉的偶联作用可以改善 PVDF/Ba-Ti O3的界面结合 ,通过测定 PVDF/Ba Ti O3的...用硅烷和钛酸酯偶联剂对 Ba Ti O3粉进行了表面处理 ,使用溶剂法制备了 PVDF/Ba Ti O3复合薄膜。通过疏水亲油实验定性地分析了硅烷和钛酸酯偶联剂对 Ba Ti O3粉的偶联作用可以改善 PVDF/Ba-Ti O3的界面结合 ,通过测定 PVDF/Ba Ti O3的介电常数和介电损耗角正切值表征了复合材料的介电性能 ,PVDF/Ba Ti O3扫描电子显微镜 (SEM)的微观形态分析发现 ,经过偶联剂表面处理 ,Ba Ti O3粉在PVDF中的分散情况改善 。展开更多
研究了在 Ba Ti O3水浆料中通过加入丙烯酰胺有机单体原位聚合形成聚丙烯酰胺的过程制备厚膜。生坯的柔韧性通过加入丙三醇作为增塑剂加以改善。实验结果表明 ,由于所制备浆料的均匀性好 ,这种由原位聚合形成的厚膜显微结构均匀 ,电性...研究了在 Ba Ti O3水浆料中通过加入丙烯酰胺有机单体原位聚合形成聚丙烯酰胺的过程制备厚膜。生坯的柔韧性通过加入丙三醇作为增塑剂加以改善。实验结果表明 ,由于所制备浆料的均匀性好 ,这种由原位聚合形成的厚膜显微结构均匀 ,电性能优良。展开更多
BaTiO 3 ceramics doped with Nd 2 O 3 (the additive content was respectively 0.001,0.002,0.003,0.005,0.01,0.03mol)were prepared by Sol-Gel method.Effects of Nd 2 O 3 contents on the dielectric constant (ε),the dielect...BaTiO 3 ceramics doped with Nd 2 O 3 (the additive content was respectively 0.001,0.002,0.003,0.005,0.01,0.03mol)were prepared by Sol-Gel method.Effects of Nd 2 O 3 contents on the dielectric constant (ε),the dielectric loss(tanδ),the Curie-temperature(T C )and the resistivity(ρ)of BaTiO 3 ceramic were studied.When Nd 2 O 3 content was 0.001mol and 0.002mol,t he dielectric constant was increase d obviously,but the dielectric loss was also increased.When Nd 2 O 3 content was 0.003mol,the dielectric constant was increased,and the die lectric loss was decreased,which was suitable fo r application in condenser.The resistivity was decreased obviously with the increasing of Nd 2 O 3 contents,the resistivity was the sm allest when Nd 2 O 3 content was 0.001mol.The Curie-temperature was also decreased with the increasing of Nd 2 O 3 contents.展开更多
文摘SrTiO_3 nano-crystal samples with floccule or flake crystal morphology,which were indexed as a perovskite-type crystal structure based on the results of XRD and TEM,were successfully prepared by one-step liquid reaction method.And the growth mechanism of the SrTiO_3 nano-crystals under the liquid condition with/without adding the surface active agent was investigated.It was found that adding the surface active agent contributes to the processing in which the ions gathering bodies transit to a more stable phase through the chemical reaction and form the flake SrTiO_3 nano-crystals.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.61265004,51272097,and 11204113)the Nature and Science Fund from Yunnan Province Ministry of Education,China(Grant No.2011C13211708)
文摘The Er^3＋/yb^3＋ co-doped transparent oxyfluoride glass-ceramics containing CaF2 nano-crystals were successfully prepared. After heat treatments, transmission electron microscopy （TEM） images showed that CaF2 nano-crystals of 20-30 nm in diameter precipitated uniformly in the glass matrix. luminescence of Er^3＋ at 540 nm and 658 nm was observed in Comparing with the host glass, high efficiency upconversion the glass ceramics under the excitation of 980 nm. Moreover, the size of the precipitated nano-crystals can be controlled by heat-treatment temperature and time. With the increase of the nano-crystal size, the intensity of the red emission increased more rapidly than that of the green emission. The energy transfer process of Er^3＋ and Yb^3＋ was convinced and the possible mechanism of Er^3＋ up-conversion was discussed.
文摘Traditional wastewater mostly contains pharmaceutical ingredients. Therefore, the wastewater must be completely free from antibiotics before its release into the environment. In the present study, photocatalytic degradation was done to investigate the removal efficiency of Oxytetracycline Dihydrate (OTC) using ZnO, ZnO/3%BaTiO<sub>3</sub> (3 BZ), ZnO/18%BaTiO<sub>3</sub> (18 BZ), ZnO/ 33%BaTiO3 (33 BZ) and ZnO/48%BaTiO<sub>3</sub> (48 BZ) under UV light. After the exposure time of 420 min, about 99.57% and 97.87% of OTC was degraded using ZnO and 3 BZ respectively. Further, increasing the amount of BaTiO<sub>3</sub> in ZnO prolongs the degradation time. Therefore, faster efficiency was found using ZnO nanoparticles. The observed reaction rate constant using ZnO was 0.00933 min<sup>-1</sup> which decreased to 0.00532 min<sup>-1</sup> using 48 BZ, indicating the decrease of reaction rate for increasing the amount of BaTiO<sub>3</sub>. Hence, the use of ZnO photocatalyst is anticipated to be a promising technique for the photocatalytic degradation of contaminated wastewater with oxytetracycline antibiotics using UV light.
文摘用硅烷和钛酸酯偶联剂对 Ba Ti O3粉进行了表面处理 ,使用溶剂法制备了 PVDF/Ba Ti O3复合薄膜。通过疏水亲油实验定性地分析了硅烷和钛酸酯偶联剂对 Ba Ti O3粉的偶联作用可以改善 PVDF/Ba-Ti O3的界面结合 ,通过测定 PVDF/Ba Ti O3的介电常数和介电损耗角正切值表征了复合材料的介电性能 ,PVDF/Ba Ti O3扫描电子显微镜 (SEM)的微观形态分析发现 ,经过偶联剂表面处理 ,Ba Ti O3粉在PVDF中的分散情况改善 。
文摘BaTiO 3 ceramics doped with Nd 2 O 3 (the additive content was respectively 0.001,0.002,0.003,0.005,0.01,0.03mol)were prepared by Sol-Gel method.Effects of Nd 2 O 3 contents on the dielectric constant (ε),the dielectric loss(tanδ),the Curie-temperature(T C )and the resistivity(ρ)of BaTiO 3 ceramic were studied.When Nd 2 O 3 content was 0.001mol and 0.002mol,t he dielectric constant was increase d obviously,but the dielectric loss was also increased.When Nd 2 O 3 content was 0.003mol,the dielectric constant was increased,and the die lectric loss was decreased,which was suitable fo r application in condenser.The resistivity was decreased obviously with the increasing of Nd 2 O 3 contents,the resistivity was the sm allest when Nd 2 O 3 content was 0.001mol.The Curie-temperature was also decreased with the increasing of Nd 2 O 3 contents.