High purity Y_2O_3 nano-powders was synthesized directly from solution ofindustrial YCl_3 by method of oxalate precipitation through super-micro-reactors made by complexnon-ionic surfactant. The purity and diameter of...High purity Y_2O_3 nano-powders was synthesized directly from solution ofindustrial YCl_3 by method of oxalate precipitation through super-micro-reactors made by complexnon-ionic surfactant. The purity and diameter of Y_2O_3 particles were controlled by such processingparameters as concentration of YCl_3 and oxalic acid and complex non-ionic surfactant etc. TEMphotomicrographs show that Y_2O_3 particles are spherical in shape, with an average diameter of lessthan 30 nm. Test results certify that the purity and particle diameter as well as the dispersion ofY_2O_3 nano-powder depend on the concentrations of YCl_3, oxalic acid and complex non-ionicsurfactant. The optimum ranges of the concentrations for YCl_3 and complex non-ionic surfactant whenthe diameter of Y_2O_3 particles is smaller than 100 nm are 0.43 ～1.4 mol ? L^(-1) and0.031～0.112 mol·L^(-1) respectively, while the mass fraction range of oxalic acid is 10% ～18% .The purity of Y_2O_3 nano-powder tested by ICP-AES analysis is 99.99% .展开更多
Traditional wastewater mostly contains pharmaceutical ingredients. Therefore, the wastewater must be completely free from antibiotics before its release into the environment. In the present study, photocatalytic degra...Traditional wastewater mostly contains pharmaceutical ingredients. Therefore, the wastewater must be completely free from antibiotics before its release into the environment. In the present study, photocatalytic degradation was done to investigate the removal efficiency of Oxytetracycline Dihydrate (OTC) using ZnO, ZnO/3%BaTiO<sub>3</sub> (3 BZ), ZnO/18%BaTiO<sub>3</sub> (18 BZ), ZnO/ 33%BaTiO3 (33 BZ) and ZnO/48%BaTiO<sub>3</sub> (48 BZ) under UV light. After the exposure time of 420 min, about 99.57% and 97.87% of OTC was degraded using ZnO and 3 BZ respectively. Further, increasing the amount of BaTiO<sub>3</sub> in ZnO prolongs the degradation time. Therefore, faster efficiency was found using ZnO nanoparticles. The observed reaction rate constant using ZnO was 0.00933 min<sup>-1</sup> which decreased to 0.00532 min<sup>-1</sup> using 48 BZ, indicating the decrease of reaction rate for increasing the amount of BaTiO<sub>3</sub>. Hence, the use of ZnO photocatalyst is anticipated to be a promising technique for the photocatalytic degradation of contaminated wastewater with oxytetracycline antibiotics using UV light.展开更多
Yb 3+-doped TiO_2 composite nano-particles were prepared by the acid-catalyzed sol-gel method using Ti(OC_4H_9)_4 and Yb(NO_3)_3 as precursors. The effects of the amount of Yb 3+ doping and calcination temperature on ...Yb 3+-doped TiO_2 composite nano-particles were prepared by the acid-catalyzed sol-gel method using Ti(OC_4H_9)_4 and Yb(NO_3)_3 as precursors. The effects of the amount of Yb 3+ doping and calcination temperature on the phase transformation, crystallite size, surface texture of the nanopowders were investigated by XRD and BET specific surface area. Their photocatalytic activities were evaluated using the photocatalytic degradation of methylene blue in aqueous solution as a probe reaction. At the interface, titanium ions substitute for ytterbium ions in the lattice of Yb_2O_3 to form Ti-O-Yb bonds, which cause distortion and inhibit the anatase to rutile phase transformation in TiO_2. The results indicate that Yb 3+-doping can enhance the photocatalytic activity of TiO_2 nano-powders as compared with pure TiO_2. 0.125%(mass fraction) Yb 3+ doped TiO_2 nano-powders calcined at 600 ℃ for 2 h show the highest photocatalytic activity. The increase in photoactivity is due to the effects of the factors such as crystal phase, crystallite size, surface chemical property, surface density of OH groups, and surface texture properties of the TiO_2 nano-powders.展开更多
用硅烷和钛酸酯偶联剂对 Ba Ti O3粉进行了表面处理 ,使用溶剂法制备了 PVDF/Ba Ti O3复合薄膜。通过疏水亲油实验定性地分析了硅烷和钛酸酯偶联剂对 Ba Ti O3粉的偶联作用可以改善 PVDF/Ba-Ti O3的界面结合 ,通过测定 PVDF/Ba Ti O3的...用硅烷和钛酸酯偶联剂对 Ba Ti O3粉进行了表面处理 ,使用溶剂法制备了 PVDF/Ba Ti O3复合薄膜。通过疏水亲油实验定性地分析了硅烷和钛酸酯偶联剂对 Ba Ti O3粉的偶联作用可以改善 PVDF/Ba-Ti O3的界面结合 ,通过测定 PVDF/Ba Ti O3的介电常数和介电损耗角正切值表征了复合材料的介电性能 ,PVDF/Ba Ti O3扫描电子显微镜 (SEM)的微观形态分析发现 ,经过偶联剂表面处理 ,Ba Ti O3粉在PVDF中的分散情况改善 。展开更多
研究了在 Ba Ti O3水浆料中通过加入丙烯酰胺有机单体原位聚合形成聚丙烯酰胺的过程制备厚膜。生坯的柔韧性通过加入丙三醇作为增塑剂加以改善。实验结果表明 ,由于所制备浆料的均匀性好 ,这种由原位聚合形成的厚膜显微结构均匀 ,电性...研究了在 Ba Ti O3水浆料中通过加入丙烯酰胺有机单体原位聚合形成聚丙烯酰胺的过程制备厚膜。生坯的柔韧性通过加入丙三醇作为增塑剂加以改善。实验结果表明 ,由于所制备浆料的均匀性好 ,这种由原位聚合形成的厚膜显微结构均匀 ,电性能优良。展开更多
BaTiO 3 ceramics doped with Nd 2 O 3 (the additive content was respectively 0.001,0.002,0.003,0.005,0.01,0.03mol)were prepared by Sol-Gel method.Effects of Nd 2 O 3 contents on the dielectric constant (ε),the dielect...BaTiO 3 ceramics doped with Nd 2 O 3 (the additive content was respectively 0.001,0.002,0.003,0.005,0.01,0.03mol)were prepared by Sol-Gel method.Effects of Nd 2 O 3 contents on the dielectric constant (ε),the dielectric loss(tanδ),the Curie-temperature(T C )and the resistivity(ρ)of BaTiO 3 ceramic were studied.When Nd 2 O 3 content was 0.001mol and 0.002mol,t he dielectric constant was increase d obviously,but the dielectric loss was also increased.When Nd 2 O 3 content was 0.003mol,the dielectric constant was increased,and the die lectric loss was decreased,which was suitable fo r application in condenser.The resistivity was decreased obviously with the increasing of Nd 2 O 3 contents,the resistivity was the sm allest when Nd 2 O 3 content was 0.001mol.The Curie-temperature was also decreased with the increasing of Nd 2 O 3 contents.展开更多
文摘High purity Y_2O_3 nano-powders was synthesized directly from solution ofindustrial YCl_3 by method of oxalate precipitation through super-micro-reactors made by complexnon-ionic surfactant. The purity and diameter of Y_2O_3 particles were controlled by such processingparameters as concentration of YCl_3 and oxalic acid and complex non-ionic surfactant etc. TEMphotomicrographs show that Y_2O_3 particles are spherical in shape, with an average diameter of lessthan 30 nm. Test results certify that the purity and particle diameter as well as the dispersion ofY_2O_3 nano-powder depend on the concentrations of YCl_3, oxalic acid and complex non-ionicsurfactant. The optimum ranges of the concentrations for YCl_3 and complex non-ionic surfactant whenthe diameter of Y_2O_3 particles is smaller than 100 nm are 0.43 ～1.4 mol ? L^(-1) and0.031～0.112 mol·L^(-1) respectively, while the mass fraction range of oxalic acid is 10% ～18% .The purity of Y_2O_3 nano-powder tested by ICP-AES analysis is 99.99% .
文摘Traditional wastewater mostly contains pharmaceutical ingredients. Therefore, the wastewater must be completely free from antibiotics before its release into the environment. In the present study, photocatalytic degradation was done to investigate the removal efficiency of Oxytetracycline Dihydrate (OTC) using ZnO, ZnO/3%BaTiO<sub>3</sub> (3 BZ), ZnO/18%BaTiO<sub>3</sub> (18 BZ), ZnO/ 33%BaTiO3 (33 BZ) and ZnO/48%BaTiO<sub>3</sub> (48 BZ) under UV light. After the exposure time of 420 min, about 99.57% and 97.87% of OTC was degraded using ZnO and 3 BZ respectively. Further, increasing the amount of BaTiO<sub>3</sub> in ZnO prolongs the degradation time. Therefore, faster efficiency was found using ZnO nanoparticles. The observed reaction rate constant using ZnO was 0.00933 min<sup>-1</sup> which decreased to 0.00532 min<sup>-1</sup> using 48 BZ, indicating the decrease of reaction rate for increasing the amount of BaTiO<sub>3</sub>. Hence, the use of ZnO photocatalyst is anticipated to be a promising technique for the photocatalytic degradation of contaminated wastewater with oxytetracycline antibiotics using UV light.
文摘Yb 3+-doped TiO_2 composite nano-particles were prepared by the acid-catalyzed sol-gel method using Ti(OC_4H_9)_4 and Yb(NO_3)_3 as precursors. The effects of the amount of Yb 3+ doping and calcination temperature on the phase transformation, crystallite size, surface texture of the nanopowders were investigated by XRD and BET specific surface area. Their photocatalytic activities were evaluated using the photocatalytic degradation of methylene blue in aqueous solution as a probe reaction. At the interface, titanium ions substitute for ytterbium ions in the lattice of Yb_2O_3 to form Ti-O-Yb bonds, which cause distortion and inhibit the anatase to rutile phase transformation in TiO_2. The results indicate that Yb 3+-doping can enhance the photocatalytic activity of TiO_2 nano-powders as compared with pure TiO_2. 0.125%(mass fraction) Yb 3+ doped TiO_2 nano-powders calcined at 600 ℃ for 2 h show the highest photocatalytic activity. The increase in photoactivity is due to the effects of the factors such as crystal phase, crystallite size, surface chemical property, surface density of OH groups, and surface texture properties of the TiO_2 nano-powders.
文摘用硅烷和钛酸酯偶联剂对 Ba Ti O3粉进行了表面处理 ,使用溶剂法制备了 PVDF/Ba Ti O3复合薄膜。通过疏水亲油实验定性地分析了硅烷和钛酸酯偶联剂对 Ba Ti O3粉的偶联作用可以改善 PVDF/Ba-Ti O3的界面结合 ,通过测定 PVDF/Ba Ti O3的介电常数和介电损耗角正切值表征了复合材料的介电性能 ,PVDF/Ba Ti O3扫描电子显微镜 (SEM)的微观形态分析发现 ,经过偶联剂表面处理 ,Ba Ti O3粉在PVDF中的分散情况改善 。
文摘BaTiO 3 ceramics doped with Nd 2 O 3 (the additive content was respectively 0.001,0.002,0.003,0.005,0.01,0.03mol)were prepared by Sol-Gel method.Effects of Nd 2 O 3 contents on the dielectric constant (ε),the dielectric loss(tanδ),the Curie-temperature(T C )and the resistivity(ρ)of BaTiO 3 ceramic were studied.When Nd 2 O 3 content was 0.001mol and 0.002mol,t he dielectric constant was increase d obviously,but the dielectric loss was also increased.When Nd 2 O 3 content was 0.003mol,the dielectric constant was increased,and the die lectric loss was decreased,which was suitable fo r application in condenser.The resistivity was decreased obviously with the increasing of Nd 2 O 3 contents,the resistivity was the sm allest when Nd 2 O 3 content was 0.001mol.The Curie-temperature was also decreased with the increasing of Nd 2 O 3 contents.