Among the numerous transition metal catalysts,manganese-based compounds are considered as promising peroxymonosulfate(PMS)catalysts due to their low cost and environmental friendliness,such as cryptomelane manganese o...Among the numerous transition metal catalysts,manganese-based compounds are considered as promising peroxymonosulfate(PMS)catalysts due to their low cost and environmental friendliness,such as cryptomelane manganese oxide(K_(2-x)Mn_(8)O_(16):abbreviation KMnO).However,the limited catalytic performance of KMnO limits its practical application.In this work,iron-doped KMnO(Fe-KMnO)was prepared by one-step hydrothermal method to optimize its catalytic performance.Compared with KMnO/PMS system,Fe-KMnO/PMS system possessed more excellent removal efficiency of tetracycline(TC).Meanwhile,the Fe-KMnO/PMS system also exhibited good practical application potential and excellent stability.The mechanism of Fe-KMnO activation of PMS was further analyzed in detail.It was found that Fe participated in the redox of high-valent Mn,which promoted the activation of PMS.Moreover,The Fe site as an adsorption site enhanced the TC enrichment ability of the catalyst,reducing the mass transfer resistance and further enhancing the TC removal ability of Fe-KMnO/PMS system.This work not only provides an excellent PMS catalyst,but also offers new insights into the mechanism of PMS activation by bimetallic manganese-based catalysts.展开更多
The oxide ZrW_2O_8 displays unusual property of isotropic negative thermalexpansion in a large wide temperature range, which makes it have a number of important potentialapplications. The cubic Zr_(1-x)Hf_xW_2O_8 (x v...The oxide ZrW_2O_8 displays unusual property of isotropic negative thermalexpansion in a large wide temperature range, which makes it have a number of important potentialapplications. The cubic Zr_(1-x)Hf_xW_2O_8 (x velence 0,0.3, 0.5, 0.7, and 1.0) were synthesized bystandard solid state reaction technique. The high and low temperature X-ray diffraction analysisindicate that the substitution of the Hf^(4+) for Zr^(4+) only leads to reducing the latticeconstants, and the changes of negative thermal expansion coefficients are not obvious. The linearexpansion coefficients of Zr_(1-x)Hf_xW_2O_8 (x velence 0,0.3, 0.5, 0.7, and 1.0) are about -6 X 10^(-6) K^(-1) in the temperature range of 298 to 973 K, while that of Zr_(0.5)Hf_(0.5)W_2O_8 is -9.6X 10^(-6) K_(-1) from 83 to 298 K. The phase transition temperatures from alpha-ZrW_2O_8 tobeta-ZrW_2O_8 structure were also determined by X-ray diffraction method. Thermogravimetric analysis(TGA) exhibits that Zr_(1-x)Hf_xW_2O_8 is not hygroscopic in air.展开更多
The effects of different x values on the dielectric properties in the Ba6-3xSm8+2xTi18O54 microwave dielectric ceramics(0.3≤x≤0.7) were studied. The results showed that the major crystal phase was BaSm2Ti4O12 and th...The effects of different x values on the dielectric properties in the Ba6-3xSm8+2xTi18O54 microwave dielectric ceramics(0.3≤x≤0.7) were studied. The results showed that the major crystal phase was BaSm2Ti4O12 and the sintering temperature of the ceramics was 1340 ℃ when the x value was 0.67. The dielectric properties were better: εr≈79, tanδ≈1×10-4(1 MHz); εr≈80, Q·f=9230 GHz(3.97 GHz), τf=-17 ppm·℃-1.展开更多
In an effort to improve the performance of superconductors in the field and high temperatures it is important to study the superconducting mechanism. For this reason, the cation substitution can be conducted. One of t...In an effort to improve the performance of superconductors in the field and high temperatures it is important to study the superconducting mechanism. For this reason, the cation substitution can be conducted. One of the high Tc superconductors Gd1Ba2Cu3O7−δ phase with Sr substitution has been synthesized, i.e. Gd1(Ba2−xSrx)Cu3O7−δ compound. The sample was synthesized by using a solid-state reaction method with a wet mixing, sintered for 12 hours at temperature 900°C. The synthesis results are characterized by using XRD. The results of Match-3 software analysis showed high (higher 85%) Gd1Ba2Cu3O7−δ phase was formed. The Sr substitution causes changes to the structure, i.e. the lattice parameters a, b and c, where the orthorhombicity tends to decrease with increasing Sr content. Refinement results show that based on the oxygen occupancy, the total oxygen content tends to increase.展开更多
基金supported by the National Natural Science Foundation of China (21806115)Sichuan Science and Technology Program (2020YJ0149)+1 种基金the Power Construction of China (P42819,DJ-ZDXM-2019-42)the Supported by Sichuan Science and Technology Program (2021ZDZX0012)。
文摘Among the numerous transition metal catalysts,manganese-based compounds are considered as promising peroxymonosulfate(PMS)catalysts due to their low cost and environmental friendliness,such as cryptomelane manganese oxide(K_(2-x)Mn_(8)O_(16):abbreviation KMnO).However,the limited catalytic performance of KMnO limits its practical application.In this work,iron-doped KMnO(Fe-KMnO)was prepared by one-step hydrothermal method to optimize its catalytic performance.Compared with KMnO/PMS system,Fe-KMnO/PMS system possessed more excellent removal efficiency of tetracycline(TC).Meanwhile,the Fe-KMnO/PMS system also exhibited good practical application potential and excellent stability.The mechanism of Fe-KMnO activation of PMS was further analyzed in detail.It was found that Fe participated in the redox of high-valent Mn,which promoted the activation of PMS.Moreover,The Fe site as an adsorption site enhanced the TC enrichment ability of the catalyst,reducing the mass transfer resistance and further enhancing the TC removal ability of Fe-KMnO/PMS system.This work not only provides an excellent PMS catalyst,but also offers new insights into the mechanism of PMS activation by bimetallic manganese-based catalysts.
基金This project is financially supported by the National Natural Science Foundation of China (No. 50002001) the Natural Science Foundation of Yunnan Province (No. 2000E0006Q)
文摘The oxide ZrW_2O_8 displays unusual property of isotropic negative thermalexpansion in a large wide temperature range, which makes it have a number of important potentialapplications. The cubic Zr_(1-x)Hf_xW_2O_8 (x velence 0,0.3, 0.5, 0.7, and 1.0) were synthesized bystandard solid state reaction technique. The high and low temperature X-ray diffraction analysisindicate that the substitution of the Hf^(4+) for Zr^(4+) only leads to reducing the latticeconstants, and the changes of negative thermal expansion coefficients are not obvious. The linearexpansion coefficients of Zr_(1-x)Hf_xW_2O_8 (x velence 0,0.3, 0.5, 0.7, and 1.0) are about -6 X 10^(-6) K^(-1) in the temperature range of 298 to 973 K, while that of Zr_(0.5)Hf_(0.5)W_2O_8 is -9.6X 10^(-6) K_(-1) from 83 to 298 K. The phase transition temperatures from alpha-ZrW_2O_8 tobeta-ZrW_2O_8 structure were also determined by X-ray diffraction method. Thermogravimetric analysis(TGA) exhibits that Zr_(1-x)Hf_xW_2O_8 is not hygroscopic in air.
文摘The effects of different x values on the dielectric properties in the Ba6-3xSm8+2xTi18O54 microwave dielectric ceramics(0.3≤x≤0.7) were studied. The results showed that the major crystal phase was BaSm2Ti4O12 and the sintering temperature of the ceramics was 1340 ℃ when the x value was 0.67. The dielectric properties were better: εr≈79, tanδ≈1×10-4(1 MHz); εr≈80, Q·f=9230 GHz(3.97 GHz), τf=-17 ppm·℃-1.
基金This report is part of the fundamental research report with contract No.486 127/UN14.2/PNL.01.03.00/2016.
文摘In an effort to improve the performance of superconductors in the field and high temperatures it is important to study the superconducting mechanism. For this reason, the cation substitution can be conducted. One of the high Tc superconductors Gd1Ba2Cu3O7−δ phase with Sr substitution has been synthesized, i.e. Gd1(Ba2−xSrx)Cu3O7−δ compound. The sample was synthesized by using a solid-state reaction method with a wet mixing, sintered for 12 hours at temperature 900°C. The synthesis results are characterized by using XRD. The results of Match-3 software analysis showed high (higher 85%) Gd1Ba2Cu3O7−δ phase was formed. The Sr substitution causes changes to the structure, i.e. the lattice parameters a, b and c, where the orthorhombicity tends to decrease with increasing Sr content. Refinement results show that based on the oxygen occupancy, the total oxygen content tends to increase.