The chrome pollution from cement industry was introduced briefly,the research on chrome free basic refractories for cement kilns was reviewed,the production technologies of magnesia calcia,magnesium aluminate spinel,m...The chrome pollution from cement industry was introduced briefly,the research on chrome free basic refractories for cement kilns was reviewed,the production technologies of magnesia calcia,magnesium aluminate spinel,magnesia hercynite refractories,etc. were specified,the principles to improve thermal shock resistance and coating adhesiveness of refractories were analyzed,the measures to extend service life by improving production equipment and service conditions of refractories were put forward,the future of chrome free refractories was expected and some developing suggestions were given.展开更多
The importance of basic refractories during the development of steel,non-ferrous and cement industries was introduced.The process of magnesia-chrome bricks was expounded.The development history of basic refractories o...The importance of basic refractories during the development of steel,non-ferrous and cement industries was introduced.The process of magnesia-chrome bricks was expounded.The development history of basic refractories of Sinosteel Luonai as well as the research and application of magnesia-chrome bricks and chrome free bricks for RH vacuum refining furnaces,heavy non-ferrous smelting furnaces,and cement kilns was emphasized.展开更多
The low cost and high efficient clean steels metallur- gy has been focused much attention in China. Among the factors affecting the cleanliness and consequent quali- ty of steel products, refractories are one of the k...The low cost and high efficient clean steels metallur- gy has been focused much attention in China. Among the factors affecting the cleanliness and consequent quali- ty of steel products, refractories are one of the key fac- tors. Meanwhile the restriction of resource, energy and environment is getting stronger, thus the improvement of refractories becontes much more important. In this paper, refractories selection principle Jbr clean steel production according to their thermodynamic features was ex- plained; refractories for tundLsh and flow control in con- tinuous casting, which play important roles in prohibi- ring secondary contamination of molten steel, were intro- duced. Moreover, new development of low-carbon and carbon-free refractory materials was also described.展开更多
In order to develop new basic light-weight refractory raw materials,natural forsterite(<0.045 mm)and magnesite(<0.045 mm)were batched according to the chemical composition of forsterite(2MgO·SiO_(2)),wet mi...In order to develop new basic light-weight refractory raw materials,natural forsterite(<0.045 mm)and magnesite(<0.045 mm)were batched according to the chemical composition of forsterite(2MgO·SiO_(2)),wet milled,semi-dry molded and calcined at different temperatures.Then cylinder samples with diameter of 36 mm were prepared.The effects of the wet milling jar rotation speed,the calcination temperature and the anthracite addition on the properties of the samples were researched.The results show that:when the calcination temperature exceeds 1300℃,all the mineral phases have converted to the desired phases;with the increase of the rotation speed and the calcination temperature,the bulk density of the samples increases,the apparent porosity decreases and the compressive strength improves.By comprehensive consideration,400 r·min^(-1) and 1450℃ are taken as the optimal scheme.High addition of anthracite makes the samples light,so series of light-weight raw materials with uniformly distributed micro-pores can be gained.The light-weight raw materials achieved were used for insulation refractory castables,obtaining good application.展开更多
基金funded by National 973 High Tech Project"Lowpower Preparation and High Efficient Applications of Cement " ( 2009CB623100 )the National 12th Five Years Scientific and Technological Projects "High Resistance to Corrosion Cast Aluminum Series Refractories Research" ( 2013BAE03B01 - 01B )
文摘The chrome pollution from cement industry was introduced briefly,the research on chrome free basic refractories for cement kilns was reviewed,the production technologies of magnesia calcia,magnesium aluminate spinel,magnesia hercynite refractories,etc. were specified,the principles to improve thermal shock resistance and coating adhesiveness of refractories were analyzed,the measures to extend service life by improving production equipment and service conditions of refractories were put forward,the future of chrome free refractories was expected and some developing suggestions were given.
文摘The importance of basic refractories during the development of steel,non-ferrous and cement industries was introduced.The process of magnesia-chrome bricks was expounded.The development history of basic refractories of Sinosteel Luonai as well as the research and application of magnesia-chrome bricks and chrome free bricks for RH vacuum refining furnaces,heavy non-ferrous smelting furnaces,and cement kilns was emphasized.
文摘The low cost and high efficient clean steels metallur- gy has been focused much attention in China. Among the factors affecting the cleanliness and consequent quali- ty of steel products, refractories are one of the key fac- tors. Meanwhile the restriction of resource, energy and environment is getting stronger, thus the improvement of refractories becontes much more important. In this paper, refractories selection principle Jbr clean steel production according to their thermodynamic features was ex- plained; refractories for tundLsh and flow control in con- tinuous casting, which play important roles in prohibi- ring secondary contamination of molten steel, were intro- duced. Moreover, new development of low-carbon and carbon-free refractory materials was also described.
基金The work was supported by Student Research Training Program of Henan University of Science and Technology in 2020(No.2020029).
文摘In order to develop new basic light-weight refractory raw materials,natural forsterite(<0.045 mm)and magnesite(<0.045 mm)were batched according to the chemical composition of forsterite(2MgO·SiO_(2)),wet milled,semi-dry molded and calcined at different temperatures.Then cylinder samples with diameter of 36 mm were prepared.The effects of the wet milling jar rotation speed,the calcination temperature and the anthracite addition on the properties of the samples were researched.The results show that:when the calcination temperature exceeds 1300℃,all the mineral phases have converted to the desired phases;with the increase of the rotation speed and the calcination temperature,the bulk density of the samples increases,the apparent porosity decreases and the compressive strength improves.By comprehensive consideration,400 r·min^(-1) and 1450℃ are taken as the optimal scheme.High addition of anthracite makes the samples light,so series of light-weight raw materials with uniformly distributed micro-pores can be gained.The light-weight raw materials achieved were used for insulation refractory castables,obtaining good application.