Hybrid materials collected from organic and inorganic sources,which are traditionally used as brake lining materials,generally include fly ash,cashew shell powder,phenolic resins,aluminium wool,barites,lime powder,car...Hybrid materials collected from organic and inorganic sources,which are traditionally used as brake lining materials,generally include fly ash,cashew shell powder,phenolic resins,aluminium wool,barites,lime powder,carbon powder and copper powder.The present research focuses on the specific effects produced by fly ash and aims to provide useful indications for the replacement of asbestos due to the health hazards caused by the related fibers.Furthermore,the financial implications related to the use of large-volume use of fly ash,lime stone and cashew shell powder,readily available in most countries in the world,are also discussed.It is shown that many manufacturing and automotive industries,which are currently experiencing difficulties in meeting the increasing demand for brake lining material,may take advantage from the proposed solution.展开更多
Friction-wear properties of the ZrSiO4 reinforced samples were measured and compared with those of plain bronze based ones. For this purpose, density, hardness, friction coefficient wear behaviour of the samples were ...Friction-wear properties of the ZrSiO4 reinforced samples were measured and compared with those of plain bronze based ones. For this purpose, density, hardness, friction coefficient wear behaviour of the samples were tested. Microstructures of samples before and after sintering and worn surfaces were also investigated by scanning electron microscopy （SEM）, and the wear types were determined. The optimum friction-wear behaviour was obtained in the sample compacted at 500 MPa and sintered at 820℃. Density of the final samples decreased with increasing the amount of reinforcing elements （ZrSiO4） before pre-sintering. However after sintering, there is no change in density of the samples including reinforcing elements （ZrSiO4）. With increasing friction surface temperature, a reduction in the friction coefficient of the samples was observed. However, the highest reductions in the friction coefficients were observed in the as-received samples containing 0. 5% reinforced ZrSiO4. The SEM images of the sample indicated that while bronze-based break lining material without ZrSiO4 showed abrasive wear behaviour, increasing the amount of ZrSiO4 resulted a change in abrasive to adhesive wear mechanism. All samples exhibited friction-wear values, which were within the values shown in SAE-J661 standard. With increasing the amount of reinforcing ZrSiO4, wear resistance of the samples was increased. However samples reinforced with 5% and 6% ZrSiO4 showed the best results.展开更多
文摘Hybrid materials collected from organic and inorganic sources,which are traditionally used as brake lining materials,generally include fly ash,cashew shell powder,phenolic resins,aluminium wool,barites,lime powder,carbon powder and copper powder.The present research focuses on the specific effects produced by fly ash and aims to provide useful indications for the replacement of asbestos due to the health hazards caused by the related fibers.Furthermore,the financial implications related to the use of large-volume use of fly ash,lime stone and cashew shell powder,readily available in most countries in the world,are also discussed.It is shown that many manufacturing and automotive industries,which are currently experiencing difficulties in meeting the increasing demand for brake lining material,may take advantage from the proposed solution.
文摘Friction-wear properties of the ZrSiO4 reinforced samples were measured and compared with those of plain bronze based ones. For this purpose, density, hardness, friction coefficient wear behaviour of the samples were tested. Microstructures of samples before and after sintering and worn surfaces were also investigated by scanning electron microscopy （SEM）, and the wear types were determined. The optimum friction-wear behaviour was obtained in the sample compacted at 500 MPa and sintered at 820℃. Density of the final samples decreased with increasing the amount of reinforcing elements （ZrSiO4） before pre-sintering. However after sintering, there is no change in density of the samples including reinforcing elements （ZrSiO4）. With increasing friction surface temperature, a reduction in the friction coefficient of the samples was observed. However, the highest reductions in the friction coefficients were observed in the as-received samples containing 0. 5% reinforced ZrSiO4. The SEM images of the sample indicated that while bronze-based break lining material without ZrSiO4 showed abrasive wear behaviour, increasing the amount of ZrSiO4 resulted a change in abrasive to adhesive wear mechanism. All samples exhibited friction-wear values, which were within the values shown in SAE-J661 standard. With increasing the amount of reinforcing ZrSiO4, wear resistance of the samples was increased. However samples reinforced with 5% and 6% ZrSiO4 showed the best results.
