Carbon Fiber Breakage Mechanism in Aluminum(Al)/Carbon Fibers(CFs) Composite Sheet during Accumulative Roll Bonding(ARB) Process

We put forward a method of fabricating Aluminum(Al)/carbon fibers(CFs) composite sheets by the accumulative roll bonding(ARB) method. The finished Al/CFs composite sheet has CFs and pure Al sheets as sandwich and surface layers. After cross-section observation of the Al/CFs composite sheet, we found that the CFs discretely distributed within the sandwich layer. Besides, the tensile test showed that the contribution of the sandwich CFs layer to tensile strength was less than 11% compared with annealed pure Al sheet. With ex-situ observation of the CFs breakage evolution with-16%,-32%, and-45% rolling reduction during the ARB process, the plastic instability of the Al layer was found to bring shear damages to the CFs. At last, the bridging strengthening mechanism introduced by CFs was sacrificed. We provide new insight into and instruction on Al/CFs composite sheet preparation method and processing parameters.

Evaluation of Tribological Performance of PTFE Composite Filled with Rare Earths Treated Carbon Fibers under Water-Lubricated Condition

Carbon fibers （CFs） were surface treated with air-oxidation, rare earths （RE） after air-oxidation, and rare earths, respectively. Erichsen test was conducted to study the interfacial adhesion of PTFE composites filled with carbon fibers treated with different treatment methods. Tribological properties of the PTFE composites, sliding against GCr15 steel under water-lubricated condition, were investigated on a reciprocating ball-on-disk UMT-2MT tribometer. The worn surfaces of the composites were examined using scanning electron microscopy. Experimental results reveal that RE treatment is superior to air oxidation in promoting tribological properties of CF reinforced PTFE （CF/PTFE） composite. The friction and wear properties of PTFE composite filled with RE treated CF are the best of the PTFE composites. RE treatment is more effective than air oxidation to improve the tribological properties of CF/PTFE composite owing to the effective improvement of interfacial adhesion between carbon fibers and PTFE matrix.

Improved wettability and mechanical properties of metal coated carbon fiber-reinforced aluminum matrix composites by squeeze melt infiltration technique

In order to improve the wettability and bonding performance of the interface between carbon fiber and aluminum matrix,nickel-and copper-coated carbon fiber-reinforced aluminum matrix composites were fabricated by the squeeze melt infiltration technique.The interface wettability,microstructure and mechanical properties of the composites were compared and investigated.Compared with the uncoated fiber-reinforced aluminum matrix composite,the microstructure analysis indicated that the coatings significantly improved the wettability and effectively inhibited the interface reaction between carbon fiber and aluminum matrix during the process.Under the same processing condition,aluminum melt was easy to infiltrate into the copper-coated fiber bundles.Furthermore,the inhibited interface reaction was more conducive to maintain the original strength of fiber and improve the fiber−matrix interface bonding performance.The mechanical properties were evaluated by uniaxial tensile test.The yield strength,ultimate tensile strength and elastic modulus of the copper-coated carbon fiber-reinforced aluminum matrix composite were about 124 MPa,140 MPa and 82 GPa,respectively.In the case of nickel-coated carbon fiber-reinforced aluminum matrix composite,the yield strength,ultimate tensile strength and elastic modulus were about 60 MPa,70 MPa and 79 GPa,respectively.The excellent mechanical properties for copper-coated fiber-reinforced composites are attributed to better compactness of the matrix and better fiber−matrix interface bonding,which favor the load transfer ability from aluminam matrix to carbon fiber under the loading state,giving full play to the bearing role of carbon fiber.

Effect of rare earths surface treatment on tribological properties of carbon fibers reinforced PTFE composite under oil-lubricated condition

The effect of rare earths （RE） surface treatment of carbon fibers （CF） on tribological properties of CF reinforced polytetrafluoroethylene （PTFE） composites under oil-lubricated condition was investigated. Experimental results revealed that RE treated CF reinforced PTFE （CF/PTFE） composite had the lowest friction coefficient and wear under various applied loads and sliding speeds compared with untreated and air-oxidated composites. X-ray photoelectron spectroscopy （XPS） study of carbon fiber surface showed that, after RE treatment, oxygen concentration increased obviously, and the amount of oxygen-containing groups on CF surfaces were largely increased. The increase in the amount of oxygen-containing groups enhanced interfacial adhesion between CF and PTFE matrix. With strong interfacial adhesion of the composite, stress could be effectively transmitted to carbon fibers; carbon fibers were strongly bonded with VITE matrix, and large scale rubbing-off of PTFE be prevented, therefore, tribological properties of the composite was improved.

Preparation and Arc Erosion Resistance of C_f/Cu Composite by Vacuum Melting Infiltration

Cf/Cu composite was prepared by vacuum melting infiltration. Ti and Cr were doped to the Cu alloy to improve the wettability between Cu and carbon. The microstrueture was investigated by XRD, SEM and EDS. The arc erosion rate of Cf/Cu composite was investigated in vacuum. The results showed that the Ti and Cr could improve the wettability between Cu and C/C preform and the infiltration ability of Cu into C/ C preform greatly. A TiC interface formed between the fibers and matrix. The good bonding between the fiber and matrix guaranteed that part of the Cu matrix can still be bonded on the fibers even when the material was exposed to the plasma. Consequently, the carbon fibers were protected from the erosion. In comparison, Cu was completely consumed by the arc erosion. Hence, the graphite was eroded and presented a cauliflower-like morphology. Therefore, the prepared C/Cu bad better ability to resist the arc erosion, compared with common Cu-C material.

Feasibility Study on Cryogenic Milling of Carbon Fiber Reinforced Silicon Carbide Composites

Carbon fiber reinforced silicon carbide matrix(Cf/SiC)composites have the most potential application for high-temperature components of aerospace high-end equipment.However,high cutting temperature,rapid tool wear and severe surface damages are the main problems in dry cutting Cf/SiC composites process.The feasibility study on cryogenic milling of Cf/SiC composites using liquid nitrogen as coolant is investigated.Influences of milling parameters and coolant on temperature,cutting force,surface quality and tool wear are investigated,which is compared with dry cutting.Experimental results reveal that the cutting temperature in cryogenic milling of Cf/SiC composites is reduced by about 40%—60%compared with dry cutting.The milling force increases gradually with the increase of spindle speed,feed rate,depth and width of milling in cryogenic milling process.In addition,the machined surface quality in cryogenic milling is superior to that in dry cutting process.Fiber fracture,matrix damage and fiber matrix debonding are main material removal mechanisms.Flank face wear is the main wear form of the polycrystalline diamond(PCD)end mills.The tool life is prolonged in the cryogenic milling process because the reduced temperature inhibits the softening of Co binder and phase transition of diamond in the PCD end mills.

Study on Anticorrosive Cerium Conversion Coating of C_f/6061A1 Composite Surface

The optimum chemical passivation process of the rare earth metal (REM) conversion coating on the Cf/6061Al composite surface was introduced in this paper and its polarization curves properties were investigated. Ridge-like coatings were found by scanning electro microscope (SEM) observations, and the Al matrix and carbon fibre reinforcement were both coated with Ce conversion coatings, with some minor cracks. The energy dispersive spectroscopy (EDS) plane scan analysis indicates that the major elements in the coating are Ce, O, Si, Al and the Ce content reaches 47.48% (mass fraction). The Ce conversion coatings increase the corrosion resisting properties of Cf/6061A1 composite, with a higher free corrosion potential (Ecorr) and a lower free corrosion current density (icorr) for the coated composite than those of the bare composite. And the Boehmite-treatment would enhance the corrosion resistance of the REM conversion coating. The ca-thodic polarization and anodic polarization were retarded by REM conversion coating, resulting in an improved corrosion resistance.

Study on vacuum brazing of C_f/C composites

Vacuum brazing experiments of Cf/C composites were carried out using pure Al and Al-5 Ti-B as brazing fillers , and shearing strength of the joints was measured. The microstructures of the brazed joints were studied by means of scanning electron microscopy （SEM） and energy dispersive X-ray spectrometer. The results indicate that the brazing temperature is the important processing parameter affecting the quality of the brazed joints. Vacuum brazing of Cf/C composites can be achieved employing the pure Al and AI-S Ti-B brazing fillers at a brazing temperature of 730 ℃ or 750 ℃ , respectively. Moreover, the joints have excellent microstructures with shear strength reaching the level of practical applications.

Improving Corrosion Resistance of C_f/Mg Composites using Rare Earth Conversion Coatings

The surface of carbon fiber reinforced Mg matrix (Cf/Mg) composites was modified by treatment of rare earth conversion coating, and nontoxic, non-pollution Ce conversion coatings were prepared. The effect of the coatings on corrosion behaviors of composites was investigated by electrochemical polarization technology and electrochemical impedance spectroscopy (EIS) in 3.5% NaCl solution. The higher Ecorr and lower icorr were obtained by Ce conversion coatings. EIS results showed that the higher values of R2 were obtained by treatment containing CeCl3, the high corrosion resistance occured in treatment containing CeCl3, the low corrosion resistance in uncoating sample, the coating of treatment containing Ce(NO3)3 was medium. The microstructure of Ce conversion coatings was observed by scanning electron microscopy (SEM), and the elements of corresponding for coatings was characterized by energy dispersive spectrometer (EDS). The micro-cracks and Ce-riched spherical particles were characteristics of these coatings.

Processing and characterization of C_f/SiC composites

Carbon fiber-reinforced SiC composites were prepared by precursor pyrolysis-hot pressing （PP-HP） and precursor impregnation-pyrolysis （PIP）, respectively. The effect of fabrication methods on the microstructure and mechanical properties of the composites was investigated. It was found that the composite prepared by PP-HP exhibits a brittle fracture behavior, which is mainly ascribed to a strongly bonded fiber/matrix interface and the degradation of the fibers caused by a higher processing temperature. On the contrary, the composite prepared by PIP shows a tough fracture behavior, which could be rationalized on the basis of a weakly bonded fiber/matrix interface as well as a higher strength retention of the fibers. As a result, in comparison with the composite prepared by PP-HP, the composite prepared by PIP achieves better mechanical properties with a flexural strength of 573.4 MPa and a fracture toughness of 17.2 MPa.m^1/2.

Effect of Ti-Al content on microstructure and mechanical properties of C_f/Al and TiAl joint by laser ignited self-propagating high-temperature synthesis

Cf/Al composites and TiAl alloys were joined by laser ignited self-propagating high-temperature synthesis（SHS） with Ni-Al-Ti interlayer. The effect of Ti-Al content on interfacial microstructure and mechanical properties of the joints was investigated. Localized melt of the substrates occurred in the joints. γ-Ni0.35Al0.30Ti0.35, NiA l3 and Ni2Al3 reaction layers formed adjacent to the substrates. Joint flaws, such as pores and cracks, made the joint density decrease and worked as the fracture source, which led to the sharp decline of joint strength. Additive Ti-Al increased joint density and strengthened the interlayer adhesion to Cf/Al. The joint flaws could be controlled by changing the Ti-Al content. When the Ti-Al content was 0.1, the joint was free of cracks with high density and reached the maximum shear strength of 24.12 MPa.

Simultaneously improving the EMI shielding performances and mechanical properties of CF/PEKK composites via MXene interfacial modification

In this study, two-dimensional MXene (Ti3 C2 Tx ) was employed to modify the interface of carbon fiber-reinforced polyetherketoneketone (CF/PEKK) composites, in order to simultaneously improve the electromagnetic interference (EMI) shielding performances and mechanical properties. The obtained CF/PEKK composites possessed outstanding EMI and mechanical performances, as anticipated. Specifically, the CF/PEKK composites modified with MXene at 1 mg mL–1 exhibited an excellent EMI shielding effectiveness of 65.2 dB in the X-band, a 103.1% enhancement compared with the unmodified CF/PEKK composites. The attractive EMI shielding performances of CF/PEKK composites originated from enhanced ohmic losses and multiple reflections of electromagnetic waves with the help of the MXene and CF layers. In addition, CF/PEKK composites achieved the best mechanical properties by optimizing the dispersion concentration of MXene to 0.1 mg mL–1 . The flexural strength, flexural modulus, and interlaminar shear strength of CF/PEKK composites reached 1127 MPa, 81 GPa, and 89 MPa, which were 28.5%, 9.5%, and 29.7% higher than that of the unmodified CF/PEKK composites, respectively. Such improvement in mechanical properties could be ascribed to the comprehensive effect of mechanical interlocking, hydrogen bonds, and Van der Waals forces between the introduced MXene and CF, PEKK, respectively.

Joining of C_f/SiBCN composite with CuPd-V filler alloy

Two compositions of CuPd-V system filler alloy were designed for joining the Cf/SiBCN composite. Their dynamic wettability on the Cf/SiBCN composite was studied with the sessile drop method. The CuPd-8 V alloy exhibited a contact angle of 57° after holding at 1170℃ for 30 min, whereas for CuPd-13 V alloy,a lower contact angle of 28°can be achieved after heating at 1200 ℃ for 20 min. Sound Cf/SiBCN joints were successfully produced using the latter filler alloy under the brazing condition of（1170-1230）℃for 10 min. The results showed that the active element V strongly diffused to the surface of Cf/SiBCN composite, with the formation of V2 C/VN reaction layer. The microstructure in the central part of the joint brazed at 1200 ℃ was characterized by the V2 C/VN particles distributing scatteringly in CuPd matrix. The corresponding joints showed the maximum three-point bend strength of 82.4 MPa at room temperature.When the testing temperature was increased to 600 0 C, the joint strength was even elevated to 108.8 MPa.Furthermore, the joints exhibited the strength of 92.4 MPa and 39.8 MPa at 800 ℃ and 900 ℃, respectively.

Microstructural regulation,oxidation resistance,and mechanical properties of C_(f)/SiC/SiHfBOC composites prepared by chemical vapor infiltration with precursor infiltration pyrolysis

To further improve the oxidation resistance of polymer derived ceramic(PDC)composites in harsh environments,Cf/SiC/SiHfBOC composites were prepared by chemical vapor infiltration(CVI)and precursor impregnation pyrolysis(PIP)methods.The weight retention change,mechanical properties,and microstructure of C/SiC/SiHfBOC before and after oxidation in air were studied in details.Microscopic analyses showed that only the interface between the ceramics and fibers was oxidized to some extent,and hafnium had been enriched on the composite surface after oxidizing at different temperature.The main oxidation products of Cf/SiC/SiHfBOC composites were Hf0_(2)and HfSi04 after oxidation at 1500℃for 60 min.Moreover,the weight retention ratio and compressive strength of the Cf/SiC/SiHfBOC composites are 83.97%and 23.88±3.11 MPa,respectively.It indicates that the Cf/SiC/SiHfBOC composites should be promising to be used for a short time in the oxidation environment at 1500℃.

Joining of C_f/SiBCN composite with two Ni-based brazing fillers and interfacial reactions

G/SiBCN ceramic composite was joined using Ni-19Cr-10Si （BNi5） and Ni-33Cr-24Pd-3.5Si-0.5B filler alloys at 1170 ℃ for 10 min. Two kinds of Ni-based filler alloys exhibited good wettability on the CdSiBCN com- posite, with a contact angle of 13° and 4°, respectively, The microstructures of the brazed joints were investigated by electron-probe microanalysis （EPMA）, and three-point bend test was conducted for the joints at room temperature. When being brazed with BNi5 filler alloy, no evident reaction layer was ob- served at the surface of the joined composite, and the joint microstructure was characterized by Ni2Si matrix with scatteringly distributing mixture compounds of Cr23C6, Ni2Si and CrB. While Ni-Cr-Pd（Si,B） brazing alloy was used, a Cr23C6 reaction layer with a thickness of 11 μm was formed at the surface of the base composite. In the central part of the brazed joint, the phases were composed of Ni（Cr, Si） solid solution and complex compounds including Pd2Si, （Ni,Pd）2Si and Ni-B. The strength of Cf/SiBCN joint brazed with BNi5 filler alloy was 62.9 MPa at room temperature, whereas that with Ni-Cr-Pd（Si,B） filler alloy was at the same level.

Self-propagating synthesis joining of C_(f)/Al composites and TC4 alloy using AgCu filler with Ni-Al-Zr interlayer

The successful joining of carbon fiber-reinforced aluminum matrix(C_(f)/Al)composites and TC4 alloy can produce composite structure and meet the demands of lightweight in aerospace field.Up to now,few experimental researches have been reported on the joining of C_(f)/Al composites and TC4 alloy.In this study,the AgCu foils and Ni-Al-Zr compact were designed for the self-propagating high-temperature synthesis joining of these two materials.C_(f)/Al composites were joined with a reactive Ti plated on its joining surface.The typical microstructure of TC4/(AgCu/Ni-Al-Zr/AgCu)/Ti/C_(f)/Al joint was analyzed,and the effects of joining condition on microstructural evolution of the SHS joint were investigated.A thin reaction layer of Ni-Al-Ti intermetallic compounds was formed adjacent to the TC4 alloy.As a result,AgCu foils could reduce the effect of reaction heat on the substrates and improve the joint shear strength.When the thickness of AgCu foils reaches 150 lm,the Ni-Al-Zr interlayer mainly acts as auxiliary heat source.High joining pressure caused the active elements to diffuse into C_(f)/Al composites and weakened the shear strength of the joint.Finally,the joint shear strength could reach 36.4 MPa when the AgCu foils were 50 lm and the joining pressure was 2 MPa.

An eco-friendly and highly sensitive loofah@CF/CNT 3D piezoresistive sensor for human activity monitoring and mechanical cotrol

Three-dimensional(3D)porous piezoresistive sensors are widely used because of their simple fabrication and convenient signal acquisition.However,because of the dependence on organic skeleton materials and the complexity of conductive coating preparation,the electrical and mechanical properties of 3D wearable piezoresistive sensors have gradually failed to accommodate many emerging fields.Here,a new flexible 3D piezoresistive sensor(NF3PS)with high sensitivity and a wide measurement range is proposed,which comprises a natural porous loofah as a flexible framework and carbon fiber/carbon nanotube(CF/CNT)multiscale composite as a conductive coating.Composed of cellulose and lignin,the irregular,porous loofah has excellent mechanical strength,elasticity,and toughness,ensuring a repeated compression/recovery behavior of the NF3PS.In addition,compared with the single-size carbon coating,the coupling of multiscale CF/CNT composite coating improves sensitivities over a range of pressures.The NF3PS demonstrates a sensitivity of 6.94 kPa^(-1) with good linearity in the pressure range of 0–11.2 kPa and maintains a sensitivity of 0.28 kPa^(-1) in an ultrawide measurement range of 11.2–84.6 kPa.Considering flexibility,robustness,and wide-ranging linear resistance variation,the feasibility of the NF3PS in human activity monitoring,mechanical control,and smart homes is verified.This work provides a novel strategy for a new generation of 3D flexible pressure sensors for improving sensitivity and measurement range and demonstrates attractive applications in wearable sensors.