The mathematical models are developed to evaluate the ultimate tensile strength( UTS) and hardness of CNTs / Al2024 composites fabricated by high-energy ball milling. The effects of the preparation variables which are...The mathematical models are developed to evaluate the ultimate tensile strength( UTS) and hardness of CNTs / Al2024 composites fabricated by high-energy ball milling. The effects of the preparation variables which are milling time,rotational speed,mass fraction of CNTs and ball to powder ratio on UST and hardness of CNTs / Al2024 composites are investigated. Based on the central composite design( CCD),a quadratic model is developed to correlate the fabrication variables to the UST and hardness. From the analysis of variance( ANOVA),the most influential factor on each experimental design response is identified. The optimum conditions for preparing CNTs / Al2024 composites are found as follows: 1. 53 h milling time,900 r / min rotational speed,mass fraction of CNTs 2. 87% and Ball to powder ratio 25 ∶ 1. The predicted maximum UST and hardness are 273.30 MPa and 261.36 HV,respectively. And the experimental values are 283.25 MPa and256.8 HV,respectively. It is indicated that the predicted UST and hardness after process optimization are found to agree satisfactory with the experimental values.展开更多
This study investigated the effects of adding graphene nanoplates(GNPs)and carbon nanotubes(CNTs)into the Al7075 matrix via the stir casting method on the microstructure and mechanical properties of the fabricated com...This study investigated the effects of adding graphene nanoplates(GNPs)and carbon nanotubes(CNTs)into the Al7075 matrix via the stir casting method on the microstructure and mechanical properties of the fabricated composites.By increasing the volume fraction of rein-forcements,the fraction of porosity increased.The X-ray diffraction results showed that the addition of reinforcements into the Al7075 changed the dominant crystal orientation from(002)to(111).Field emission scanning electron microscopy images also showed the distribution of clustered reinforcements in the matrix.Between the two reinforcements,the addition of CNTs generated a lower fraction of porosities.Through the addition of 0.52vol%GNPs into the matrix,the hardness,ultimate tensile strength and uniform elongation increased by 44%,32%,and 180%,respectively.Meanwhile,the presence of 0.71vol%CNTs in the matrix increased the hardness,tensile strength and uniform elongation by 108%,129%,and 260%,respectively.展开更多
Carbon nauotube（ CNT） reinforced aluminum metal matrix composites were welded by electron beam welding and the microstructures of welded joints were investigated. The result showed that the interracial reaction happ...Carbon nauotube（ CNT） reinforced aluminum metal matrix composites were welded by electron beam welding and the microstructures of welded joints were investigated. The result showed that the interracial reaction happened between the CNTs and Al matrix, which resulted in producing brittle Al4 C3 compounds in electron beam welds. The extent of interfacial reaction varies gradually in the depth and width direction. The length of the reactants Al4C3 became short duo to the temperature gradient in the molten pool. The quantity and size of Al4 C3 compounds increased with the increase of beam current and the decrease of welding speed in the middle zone of weld. However, no needle-like phase Al4C3 was observed in HAZ.展开更多
Molybdenum disilicide(MoSi_2) based composites with various contents of carbon nanotubes(CNTs) were fabricated by spark plasma sintering(SPS) in vacuum under a pressure of 25 MPa.The composites obtained under a sinter...Molybdenum disilicide(MoSi_2) based composites with various contents of carbon nanotubes(CNTs) were fabricated by spark plasma sintering(SPS) in vacuum under a pressure of 25 MPa.The composites obtained under a sintering temperature of 1500 °C and time of 10 min exhibited optimum mechanical properties at room temperature in terms of fracture toughness and transverse rupture strength.MoSi_2 based composite with 6.0% CNTs(volume fraction) had the highest fracture toughness,transverse rupture strength and hardness,which were improved by about 25.7%,51.5% and 24.4% respectively,as compared with pure MoSi_2.A Mo_(4.8)Si_3C_(0.6) phase was detected in CNTs/MoSi_2 composites by both X-ray diffraction(XRD) method and microstructure analysis with scanning electron microscopy(SEM).It is believed that the fine grains and well dispersed small Mo_(4.8)Si_3C_(0.6) particles had led to a higher hardness and strength of CNTs/MoSi_2 composites because of their particle pullout,crack deflection and micro-bridging effects.展开更多
Deformation behaviors of CNTs/Al alloy composite fabricated by the method of flake powder metallurgy were investigated by hot compression tests, which were performed in the temperature range of 300?550 °C and str...Deformation behaviors of CNTs/Al alloy composite fabricated by the method of flake powder metallurgy were investigated by hot compression tests, which were performed in the temperature range of 300?550 °C and strain rate range of 0.001? 10 s?1 with Gleeble?3500 thermal simulator system. Processing maps of the CNTs/Al alloy at different strains were calculated to study the optimum processing domain. Microstructures before and after hot compressions were characterized by electron backscattered diffraction (EBSD) method. Stress?strain curves indicate that the flow stress increases with the increase of strain rate and the decrease of temperature. The processing maps of the CNTs/Al alloy at different strains show that the optimum processing domain is 500?550 °C, 10 s?1 for hot working. EBSD analysis demonstrates that fully dynamic recrystallization occurs in the optimum processing domain (high strainrate 10 s?1), whereas the main soften mechanism is dynamic recovery at low strain rate (0.001 s?1).展开更多
Carbon nanotubes （CNTs） reinforced aluminum matrix composites were fabricated by mechanical milling followed by hot extrusion. The commercial Al-2024 alloy with 1% CNTs was milled under various ball milling conditio...Carbon nanotubes （CNTs） reinforced aluminum matrix composites were fabricated by mechanical milling followed by hot extrusion. The commercial Al-2024 alloy with 1% CNTs was milled under various ball milling conditions. Microstructure evolution and mechanical properties of the milled powder and consolidated bulk materials were examined by X-ray diffraction （XRD）, field emission scanning electron microscopy （FESEM） and mechanical test. The effect of CNTs concentration and milling time on the microstructure of the CNTs/Al-2024 composites was studied. Based on the structural observation, the formation behavior of nanostructure in ball milled powder was discussed. The results show that the increment in the milling time and ration speed, for a fixed amount of CNTs, causes a reduction of the particle size of powders resulting from MM. The finest particle size was obtained after 15 h of milling. Moreover, the composite had an increase in tensile strength due to the small amount of CNTs addition.展开更多
基金Sponsored by the Program for Innovative Research Team in University of Yunnan Province and Major Projects of Yunnan Province(Grant No.2014FC001)
文摘The mathematical models are developed to evaluate the ultimate tensile strength( UTS) and hardness of CNTs / Al2024 composites fabricated by high-energy ball milling. The effects of the preparation variables which are milling time,rotational speed,mass fraction of CNTs and ball to powder ratio on UST and hardness of CNTs / Al2024 composites are investigated. Based on the central composite design( CCD),a quadratic model is developed to correlate the fabrication variables to the UST and hardness. From the analysis of variance( ANOVA),the most influential factor on each experimental design response is identified. The optimum conditions for preparing CNTs / Al2024 composites are found as follows: 1. 53 h milling time,900 r / min rotational speed,mass fraction of CNTs 2. 87% and Ball to powder ratio 25 ∶ 1. The predicted maximum UST and hardness are 273.30 MPa and 261.36 HV,respectively. And the experimental values are 283.25 MPa and256.8 HV,respectively. It is indicated that the predicted UST and hardness after process optimization are found to agree satisfactory with the experimental values.
文摘This study investigated the effects of adding graphene nanoplates(GNPs)and carbon nanotubes(CNTs)into the Al7075 matrix via the stir casting method on the microstructure and mechanical properties of the fabricated composites.By increasing the volume fraction of rein-forcements,the fraction of porosity increased.The X-ray diffraction results showed that the addition of reinforcements into the Al7075 changed the dominant crystal orientation from(002)to(111).Field emission scanning electron microscopy images also showed the distribution of clustered reinforcements in the matrix.Between the two reinforcements,the addition of CNTs generated a lower fraction of porosities.Through the addition of 0.52vol%GNPs into the matrix,the hardness,ultimate tensile strength and uniform elongation increased by 44%,32%,and 180%,respectively.Meanwhile,the presence of 0.71vol%CNTs in the matrix increased the hardness,tensile strength and uniform elongation by 108%,129%,and 260%,respectively.
基金supported by the fund of Doctoral Startup Research of Nanchang Hangkong University(EA201203402)Aeronautical Science Foundation(20135456009)+1 种基金National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology(gf201401003)State Key Laboratory of Solidification Processing in NWPU(SKLSP201412)
文摘Carbon nauotube（ CNT） reinforced aluminum metal matrix composites were welded by electron beam welding and the microstructures of welded joints were investigated. The result showed that the interracial reaction happened between the CNTs and Al matrix, which resulted in producing brittle Al4 C3 compounds in electron beam welds. The extent of interfacial reaction varies gradually in the depth and width direction. The length of the reactants Al4C3 became short duo to the temperature gradient in the molten pool. The quantity and size of Al4 C3 compounds increased with the increase of beam current and the decrease of welding speed in the middle zone of weld. However, no needle-like phase Al4C3 was observed in HAZ.
基金Project(51371155)supported by the National Natural Science Foundation of ChinaProject(2014H0046)supported by the Key Science and Technology Project of Fujian Province,China+2 种基金Project(3502Z20143036)supported by the Scientific Research Fund of Xiamen,ChinaProject(JB13149)supported by the Education Department Science and Technology Project of Fujian Province,ChinaProject(2012D131)supported by the Natural Science Foundation Guidance Project of Fujian Province,China
文摘Molybdenum disilicide(MoSi_2) based composites with various contents of carbon nanotubes(CNTs) were fabricated by spark plasma sintering(SPS) in vacuum under a pressure of 25 MPa.The composites obtained under a sintering temperature of 1500 °C and time of 10 min exhibited optimum mechanical properties at room temperature in terms of fracture toughness and transverse rupture strength.MoSi_2 based composite with 6.0% CNTs(volume fraction) had the highest fracture toughness,transverse rupture strength and hardness,which were improved by about 25.7%,51.5% and 24.4% respectively,as compared with pure MoSi_2.A Mo_(4.8)Si_3C_(0.6) phase was detected in CNTs/MoSi_2 composites by both X-ray diffraction(XRD) method and microstructure analysis with scanning electron microscopy(SEM).It is believed that the fine grains and well dispersed small Mo_(4.8)Si_3C_(0.6) particles had led to a higher hardness and strength of CNTs/MoSi_2 composites because of their particle pullout,crack deflection and micro-bridging effects.
基金Project(2012AA030311)supported by the National High-tech Research and Development Program of ChinaProject(51421001)supported by the National Natural Science Foundation of ChinaProject(106112015CDJXY130002)supported by the Fundamental Research Funds for the Central Universities,China
文摘Deformation behaviors of CNTs/Al alloy composite fabricated by the method of flake powder metallurgy were investigated by hot compression tests, which were performed in the temperature range of 300?550 °C and strain rate range of 0.001? 10 s?1 with Gleeble?3500 thermal simulator system. Processing maps of the CNTs/Al alloy at different strains were calculated to study the optimum processing domain. Microstructures before and after hot compressions were characterized by electron backscattered diffraction (EBSD) method. Stress?strain curves indicate that the flow stress increases with the increase of strain rate and the decrease of temperature. The processing maps of the CNTs/Al alloy at different strains show that the optimum processing domain is 500?550 °C, 10 s?1 for hot working. EBSD analysis demonstrates that fully dynamic recrystallization occurs in the optimum processing domain (high strainrate 10 s?1), whereas the main soften mechanism is dynamic recovery at low strain rate (0.001 s?1).
基金Project(2012CB619503)supported by the National Basic Research Program of ChinaProject(2013AA031001)supported by the National High-tech Research and Development Program of ChinaProject(2012DFA50630)supported by the International Science&Technology Cooperation Program of China
文摘Carbon nanotubes （CNTs） reinforced aluminum matrix composites were fabricated by mechanical milling followed by hot extrusion. The commercial Al-2024 alloy with 1% CNTs was milled under various ball milling conditions. Microstructure evolution and mechanical properties of the milled powder and consolidated bulk materials were examined by X-ray diffraction （XRD）, field emission scanning electron microscopy （FESEM） and mechanical test. The effect of CNTs concentration and milling time on the microstructure of the CNTs/Al-2024 composites was studied. Based on the structural observation, the formation behavior of nanostructure in ball milled powder was discussed. The results show that the increment in the milling time and ration speed, for a fixed amount of CNTs, causes a reduction of the particle size of powders resulting from MM. The finest particle size was obtained after 15 h of milling. Moreover, the composite had an increase in tensile strength due to the small amount of CNTs addition.