Niobium oxide nanowire-deposited carbon fiber（CF） samples were prepared using a hydrothermal method with amorphous Nb2O5·nH2O as precursor. The physical properties of the samples were characterized by means of ...Niobium oxide nanowire-deposited carbon fiber（CF） samples were prepared using a hydrothermal method with amorphous Nb2O5·nH2O as precursor. The physical properties of the samples were characterized by means of numerous techniques, including X-ray diffraction（XRD）, energy-dispersive spectroscopy（EDS）, scanning electron microscopy（SEM）, transmission electron microscopy（TEM）, selected-area electron diffraction（SAED）, UV–visible spectroscopy（UV–vis）, N2 adsorption–desorption, Fourier transform infrared spectroscopy（FT-IR）, and X-ray photoelectron spectroscopy. The efficiency for the removal of Cr（VI） was determined.Parameters such as pH value and initial Cr（VI） concentration could influence the Cr（VI） removal efficiency or adsorption capacity of the Nb2O5/carbon fiber sample obtained after hydrothermal treatment at 160°C for 14 hr. The maximal Cr（VI） adsorption capacity of the Nb2O5 nanowire/CF sample was 115 mg/g. This Nb2O5/CF sample also showed excellent photocatalytic activity and stability for the reduction of Cr（Ⅵ） under UV-light irradiation： the Cr（VI） removal efficiency reached 99.9% after UV-light irradiation for 1 hr and there was no significant decrease in photocatalytic performance after the use of the sample for 10 repeated cycles. Such excellent Cr（VI） adsorption capacity and photocatalytic performance was related to its high surface area,abundant surface hydroxyl groups, and good UV-light absorption ability.展开更多
基金financially supported by the major Project of the national science and technology of China (No. SQ2017YFGX010248)the Beijing Natural Science Foundation (No. 2172011)
文摘Niobium oxide nanowire-deposited carbon fiber（CF） samples were prepared using a hydrothermal method with amorphous Nb2O5·nH2O as precursor. The physical properties of the samples were characterized by means of numerous techniques, including X-ray diffraction（XRD）, energy-dispersive spectroscopy（EDS）, scanning electron microscopy（SEM）, transmission electron microscopy（TEM）, selected-area electron diffraction（SAED）, UV–visible spectroscopy（UV–vis）, N2 adsorption–desorption, Fourier transform infrared spectroscopy（FT-IR）, and X-ray photoelectron spectroscopy. The efficiency for the removal of Cr（VI） was determined.Parameters such as pH value and initial Cr（VI） concentration could influence the Cr（VI） removal efficiency or adsorption capacity of the Nb2O5/carbon fiber sample obtained after hydrothermal treatment at 160°C for 14 hr. The maximal Cr（VI） adsorption capacity of the Nb2O5 nanowire/CF sample was 115 mg/g. This Nb2O5/CF sample also showed excellent photocatalytic activity and stability for the reduction of Cr（Ⅵ） under UV-light irradiation： the Cr（VI） removal efficiency reached 99.9% after UV-light irradiation for 1 hr and there was no significant decrease in photocatalytic performance after the use of the sample for 10 repeated cycles. Such excellent Cr（VI） adsorption capacity and photocatalytic performance was related to its high surface area,abundant surface hydroxyl groups, and good UV-light absorption ability.