In the present paper, three dimensional analyses of some general constraint parameters and fracture parameters near the crack tip of Mode I CT specimens in two different thicknesses are carried out by employing ADINA ...In the present paper, three dimensional analyses of some general constraint parameters and fracture parameters near the crack tip of Mode I CT specimens in two different thicknesses are carried out by employing ADINA program. The results reveal that the constraints along the thickness direction are obviously separated into two parts: the keeping similar high constraint field (Z1) and rapid reducing constraints one(Z2). The two fields are experimentally confiremed to correspond to the smooth region and the shear lip on the fracture face respectively. So the three dimensional stress structure of Mode I specimens can be derived through discussing the two fields respectively. The distribution of the Crack Tip Opening Displacement (CTOD) along the thickness direction and the three dimensional distribution of the void growth ratio (Vg) near the crack tip are also obtained. The two fracture parameters are in similar trends along the thickness direction, and both of them can reflect the effect of thickness and that of the loading level to a certain degree.展开更多
文摘In the present paper, three dimensional analyses of some general constraint parameters and fracture parameters near the crack tip of Mode I CT specimens in two different thicknesses are carried out by employing ADINA program. The results reveal that the constraints along the thickness direction are obviously separated into two parts: the keeping similar high constraint field (Z1) and rapid reducing constraints one(Z2). The two fields are experimentally confiremed to correspond to the smooth region and the shear lip on the fracture face respectively. So the three dimensional stress structure of Mode I specimens can be derived through discussing the two fields respectively. The distribution of the Crack Tip Opening Displacement (CTOD) along the thickness direction and the three dimensional distribution of the void growth ratio (Vg) near the crack tip are also obtained. The two fracture parameters are in similar trends along the thickness direction, and both of them can reflect the effect of thickness and that of the loading level to a certain degree.