The aggregating properties of Cz-C-n (n = 3, 6, 10) have been investigated by means of fluorescence method in DMSO-H2O binary solvent. The measured CAC and C F values indicate that the aggregating tendency of the amp...The aggregating properties of Cz-C-n (n = 3, 6, 10) have been investigated by means of fluorescence method in DMSO-H2O binary solvent. The measured CAC and C F values indicate that the aggregating tendency of the amphiphilic compounds Cz-C-n containing crown ether increases with the length of alkyl chains, similar to that of carbazole compounds with long alkyl chains.展开更多
Barium metaborate (BaB 2O 4) exists in two forms the high temperature for m α phase and the low temperature form β phase,with the phase transition poi nt at around 925℃.The low temperature phase (β BBO) is an exce...Barium metaborate (BaB 2O 4) exists in two forms the high temperature for m α phase and the low temperature form β phase,with the phase transition poi nt at around 925℃.The low temperature phase (β BBO) is an excellent NLO cryst al for UV region,while the high temperature one (α BBO) is known as a good bir efringent material.α BBO crystal possesses better transparency in the ultravio let region compared with commonly used YVO 4 and CaCO 3 crystals.However,due t o phase transition problem,it is difficult to grow single α BBO crystals by D CZ method,which restricts its wider application.α BBO crystal usually cracks upon cooling resulted from phase transition to β phase.Therefore,it is difficult to grow β BBO single crystals directly from pure BaB 2O 4 mel t;however,to grow single crystals of α BBO is not easy,either. Our recent experiments showed that one could avoid cracking of α BBO cryst als by Sr 2+ doping.This minute amount of Sr 2+ plays the role of structure stabilizer,which inhibits structural reconstruction. In this way,Sr 2+ d op ed BBO single crystals do not subject to phase transition from 925℃ down to roo m temperature. We have mow successfully grown out α BBO single crystals 30mm in diameter by D CZ method from Sr x Ba 1- x BO 4 melt with Sr concentration 0.3 0 .5%.The ratation rate is 10 15r/min,pulling speed is 1 2mm/h.Preliminary tests revealed that its structure and physic chemical properties were almost identic al to those grown from pure melts.These Sr 2+ doped α BBO crystals are no w being widely used in optical isolators.展开更多
Red,blue and green visible lasers are more attractive with the development of the science and technology.Self frequency doubling is an important approach to realize visible lasers.For self frequency doubling,the basic...Red,blue and green visible lasers are more attractive with the development of the science and technology.Self frequency doubling is an important approach to realize visible lasers.For self frequency doubling,the basic requests are high figure of merit(FOM),high damage threshold,good chemical stability and mechanical properties.Perfection and growth characters are also important for a practical SFD crystal. In recent years,the discovery of rare earth calcium oxyborates has resulted in the renewal in the field of SFD crystal.ReCaO(BO 3) 3(ReCOB)is a new type of novel nonlinear optical crystals which is nearly congruently melt and can be grown with Czochralski method.ReCOB crystals possess high nonlinear coefficients and damage thresholds.They are non hydroscopic and easy cutting and polishing.They belong to monoclinic with point group m and space group cm.The strong anisotropy originated from the low symmetry makes the measurement and application of the crystal more complicated.More than half of naturally existed crystals belongs to low symmetry,consequently,the research on the nonlinear and anisotropic laser optical properties are not only important for ReCOB crystal,but also useful for the applications of other low symmetry crystals.展开更多
Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re...Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re∶GdYCOB single crystals growth were synthesized by multistage solid phase reaction method.Re∶GdYCOB single crystals were grown by Czochralski technique.The pulling rates are 0.5-2mm/h and the rotation rates are 10-30r/min.Usually 65-75% polycrystalline materials can be transformed into good quality single crystals under our growth conditions. The structures of some as grown Re∶GdYCOB single crystals were measured by using a four circle diffractometer.The results measured show that the space group of the crystals is C 3 s Cm.The determined lattice constants of 8 at% Nd doped Ca 4YO(BO 3) 3 single crystal are a =0.8076nm, b =1.6020nm, c =0.3527nm , β =101.23°.展开更多
基金We thank the National Natural Science Foundation of China. The foundation of the Ministry of Science and Technology of China (grant No. G2000078104 and No. G2000077502) for financial supports.
文摘The aggregating properties of Cz-C-n (n = 3, 6, 10) have been investigated by means of fluorescence method in DMSO-H2O binary solvent. The measured CAC and C F values indicate that the aggregating tendency of the amphiphilic compounds Cz-C-n containing crown ether increases with the length of alkyl chains, similar to that of carbazole compounds with long alkyl chains.
基金National Natural Science Foundation of China(51832007,52220105010)Natural Science Foundation of Shandong Province(ZR2020ZD35)Qilu Young Scholars Program of Shandong University。
文摘Barium metaborate (BaB 2O 4) exists in two forms the high temperature for m α phase and the low temperature form β phase,with the phase transition poi nt at around 925℃.The low temperature phase (β BBO) is an excellent NLO cryst al for UV region,while the high temperature one (α BBO) is known as a good bir efringent material.α BBO crystal possesses better transparency in the ultravio let region compared with commonly used YVO 4 and CaCO 3 crystals.However,due t o phase transition problem,it is difficult to grow single α BBO crystals by D CZ method,which restricts its wider application.α BBO crystal usually cracks upon cooling resulted from phase transition to β phase.Therefore,it is difficult to grow β BBO single crystals directly from pure BaB 2O 4 mel t;however,to grow single crystals of α BBO is not easy,either. Our recent experiments showed that one could avoid cracking of α BBO cryst als by Sr 2+ doping.This minute amount of Sr 2+ plays the role of structure stabilizer,which inhibits structural reconstruction. In this way,Sr 2+ d op ed BBO single crystals do not subject to phase transition from 925℃ down to roo m temperature. We have mow successfully grown out α BBO single crystals 30mm in diameter by D CZ method from Sr x Ba 1- x BO 4 melt with Sr concentration 0.3 0 .5%.The ratation rate is 10 15r/min,pulling speed is 1 2mm/h.Preliminary tests revealed that its structure and physic chemical properties were almost identic al to those grown from pure melts.These Sr 2+ doped α BBO crystals are no w being widely used in optical isolators.
文摘Red,blue and green visible lasers are more attractive with the development of the science and technology.Self frequency doubling is an important approach to realize visible lasers.For self frequency doubling,the basic requests are high figure of merit(FOM),high damage threshold,good chemical stability and mechanical properties.Perfection and growth characters are also important for a practical SFD crystal. In recent years,the discovery of rare earth calcium oxyborates has resulted in the renewal in the field of SFD crystal.ReCaO(BO 3) 3(ReCOB)is a new type of novel nonlinear optical crystals which is nearly congruently melt and can be grown with Czochralski method.ReCOB crystals possess high nonlinear coefficients and damage thresholds.They are non hydroscopic and easy cutting and polishing.They belong to monoclinic with point group m and space group cm.The strong anisotropy originated from the low symmetry makes the measurement and application of the crystal more complicated.More than half of naturally existed crystals belongs to low symmetry,consequently,the research on the nonlinear and anisotropic laser optical properties are not only important for ReCOB crystal,but also useful for the applications of other low symmetry crystals.
文摘Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re∶GdYCOB single crystals growth were synthesized by multistage solid phase reaction method.Re∶GdYCOB single crystals were grown by Czochralski technique.The pulling rates are 0.5-2mm/h and the rotation rates are 10-30r/min.Usually 65-75% polycrystalline materials can be transformed into good quality single crystals under our growth conditions. The structures of some as grown Re∶GdYCOB single crystals were measured by using a four circle diffractometer.The results measured show that the space group of the crystals is C 3 s Cm.The determined lattice constants of 8 at% Nd doped Ca 4YO(BO 3) 3 single crystal are a =0.8076nm, b =1.6020nm, c =0.3527nm , β =101.23°.