A new inorganic-organic hybrid framework microporous material Cd 3(BDC) 0.5(BTC) 2·(DMF)(H 2O)·3DMF·H 3O·H 2O, in which two kinds of carboxylate ligands coordinate with cadmium ions synchronously, ...A new inorganic-organic hybrid framework microporous material Cd 3(BDC) 0.5(BTC) 2·(DMF)(H 2O)·3DMF·H 3O·H 2O, in which two kinds of carboxylate ligands coordinate with cadmium ions synchronously, was obtained under a mild synthesis condition. The titled compound is crystallized in a monoclinic system, space group P2(1)/c with a=1.584 7(7) nm, b=1.426 7(6) nm, c=1.936 3(6) nm, β=113.186(7)°, V=4.024 6(3) nm 3, Z=4, D X=1.947 mg/m 3, M r=1 179.92, μ=1.662 mm -1, F(000)=2 344, R=0.074 8, wR=0.215 1. Three cadmium centers link with each other through BDC or BTC ligand to form a 3-D open framework.展开更多
The novel seven coordinate complex [(n Bu)2Sn(C10H8N2O3)(C2H5OH)]2 (C10H8N2O32- is the dinegative ion of 2 oxo propionic acid benzoyl hydrazone) was synthesized by the reaction of (n Bu)2SnO with 2 oxo propionic acid ...The novel seven coordinate complex [(n Bu)2Sn(C10H8N2O3)(C2H5OH)]2 (C10H8N2O32- is the dinegative ion of 2 oxo propionic acid benzoyl hydrazone) was synthesized by the reaction of (n Bu)2SnO with 2 oxo propionic acid benzoyl hydrazone in 1∶ 1 molar ratio in benzene ethanol (V/V, 3/1), and its structure was characterized by X ray single crystal diffraction. The crystal belongs to a tetragonal system with space group I41/a, a=2.4890(2)nm, b=2.4890(2)nm, c=1.5170(3)nm, V=9.398(2)nm3, Z=8, F(000)=3968, Dc=1.366g· cm- 3, and the structure was refined to final R1=0.0530, wR2=0.0971. The structure of the title complex is described as a dimer through weak interactions of Sn… O bonding and hydrogen bond. The tin atoms rendered seven coordination in a distorted pentagonal bipyramid geometry structure, four oxygen atoms [O1, O2, O2# 1 and O4] and one nitrogen atom N2 formed the equatorial plane and C11 Sn1 C15 is the axis. CCDC: 212696.展开更多
A nanosolid heteropoly acid of H 3PW 12 O 40 /SiO 2 was prepared with the sol-gel method and used to catalyze sythesis of methyl 5-amino-1,2,4,-trazolylformate sulfate.The structure of the nanosolid heteropoly acid H ...A nanosolid heteropoly acid of H 3PW 12 O 40 /SiO 2 was prepared with the sol-gel method and used to catalyze sythesis of methyl 5-amino-1,2,4,-trazolylformate sulfate.The structure of the nanosolid heteropoly acid H 3PW 12 O 40 /SiO 2 was characterized by IR,XRD and TEM.The following optimum condition were that the mole ratio of alcohol to carboxylic acid is 27∶1,the temperature is 75℃,the reaction time is 5 hours,and the catalyst is 2 5% of feedstock.Under the optimum conditions,the yield of esters was above 94%.展开更多
采用溶胶-凝胶法制备H3PW6Mo6O40/SiO2催化剂,以苯甲醛,乙酰乙酸乙酯和尿素为原料,无水乙醇为溶剂催化合成4-苯基-6-甲基-5-乙氧羰基-3,4-二氢嘧啶-2(H)-酮,研究结果表明:反应物的摩尔比、反应温度、催化剂用量和反应时间是影响4-苯基-6...采用溶胶-凝胶法制备H3PW6Mo6O40/SiO2催化剂,以苯甲醛,乙酰乙酸乙酯和尿素为原料,无水乙醇为溶剂催化合成4-苯基-6-甲基-5-乙氧羰基-3,4-二氢嘧啶-2(H)-酮,研究结果表明:反应物的摩尔比、反应温度、催化剂用量和反应时间是影响4-苯基-6-甲基-5-乙氧羰基-3,4-二氢嘧啶-2(H)-酮合成收率的重要因素.当n(苯甲醛)∶n(乙酰乙酸乙酯)∶n(尿素)=1.0∶1.2∶1.5,反应温度为90℃,催化剂的用量占反应物料总质量的1.5%,反应时间为75min时,产品收率可达70.3%.通过熔点、IR、1 H NMR和MS对合成目标化合物进行了表征确认.展开更多
文摘A new inorganic-organic hybrid framework microporous material Cd 3(BDC) 0.5(BTC) 2·(DMF)(H 2O)·3DMF·H 3O·H 2O, in which two kinds of carboxylate ligands coordinate with cadmium ions synchronously, was obtained under a mild synthesis condition. The titled compound is crystallized in a monoclinic system, space group P2(1)/c with a=1.584 7(7) nm, b=1.426 7(6) nm, c=1.936 3(6) nm, β=113.186(7)°, V=4.024 6(3) nm 3, Z=4, D X=1.947 mg/m 3, M r=1 179.92, μ=1.662 mm -1, F(000)=2 344, R=0.074 8, wR=0.215 1. Three cadmium centers link with each other through BDC or BTC ligand to form a 3-D open framework.
文摘The novel seven coordinate complex [(n Bu)2Sn(C10H8N2O3)(C2H5OH)]2 (C10H8N2O32- is the dinegative ion of 2 oxo propionic acid benzoyl hydrazone) was synthesized by the reaction of (n Bu)2SnO with 2 oxo propionic acid benzoyl hydrazone in 1∶ 1 molar ratio in benzene ethanol (V/V, 3/1), and its structure was characterized by X ray single crystal diffraction. The crystal belongs to a tetragonal system with space group I41/a, a=2.4890(2)nm, b=2.4890(2)nm, c=1.5170(3)nm, V=9.398(2)nm3, Z=8, F(000)=3968, Dc=1.366g· cm- 3, and the structure was refined to final R1=0.0530, wR2=0.0971. The structure of the title complex is described as a dimer through weak interactions of Sn… O bonding and hydrogen bond. The tin atoms rendered seven coordination in a distorted pentagonal bipyramid geometry structure, four oxygen atoms [O1, O2, O2# 1 and O4] and one nitrogen atom N2 formed the equatorial plane and C11 Sn1 C15 is the axis. CCDC: 212696.
文摘A nanosolid heteropoly acid of H 3PW 12 O 40 /SiO 2 was prepared with the sol-gel method and used to catalyze sythesis of methyl 5-amino-1,2,4,-trazolylformate sulfate.The structure of the nanosolid heteropoly acid H 3PW 12 O 40 /SiO 2 was characterized by IR,XRD and TEM.The following optimum condition were that the mole ratio of alcohol to carboxylic acid is 27∶1,the temperature is 75℃,the reaction time is 5 hours,and the catalyst is 2 5% of feedstock.Under the optimum conditions,the yield of esters was above 94%.
文摘采用溶胶-凝胶法制备H3PW6Mo6O40/SiO2催化剂,以苯甲醛,乙酰乙酸乙酯和尿素为原料,无水乙醇为溶剂催化合成4-苯基-6-甲基-5-乙氧羰基-3,4-二氢嘧啶-2(H)-酮,研究结果表明:反应物的摩尔比、反应温度、催化剂用量和反应时间是影响4-苯基-6-甲基-5-乙氧羰基-3,4-二氢嘧啶-2(H)-酮合成收率的重要因素.当n(苯甲醛)∶n(乙酰乙酸乙酯)∶n(尿素)=1.0∶1.2∶1.5,反应温度为90℃,催化剂的用量占反应物料总质量的1.5%,反应时间为75min时,产品收率可达70.3%.通过熔点、IR、1 H NMR和MS对合成目标化合物进行了表征确认.