Y^3＋-doped （Bi 1/2 Na 1/2） TiO 3-CaTiO 3-BaTiO 3 （BNCBT） positive temperature coefficient of resistivity （PTCR） ceramics sintered in air atmosphere were investigated in this study. （Bi 1/2 Na 1/2） TiO 3 （BNT...Y^3＋-doped （Bi 1/2 Na 1/2） TiO 3-CaTiO 3-BaTiO 3 （BNCBT） positive temperature coefficient of resistivity （PTCR） ceramics sintered in air atmosphere were investigated in this study. （Bi 1/2 Na 1/2） TiO 3 （BNT） component can remarkably increase the onset temperature T c of PTCR ceramics with the expense of the resistivity R 25 increase. CaTiO 3 （9–27 mol%） component can decrease the resistivity, and adjust the effects of BNT phase on the T c point. For the sample containing 3 mol% CaTiO 3 , T c raises from 122 ℃ to 153 ℃ when only 0.6 mol% BNT added, while for the ones with higher CaTiO 3 content （9–27 mol%）, T c is only increased by a rate of 8–9℃/1.0 mol% BNT. The effects of BNT and CaTiO 3 components on R25/Rmin （negative temperature coefficient effect） are also discussed.展开更多
In this paper, a detailed study was carried out on the PTFE reinforced with TiO2 and CaTiO3. The filler content of ceramic powder was a fixed value of 61 wt% and the content of CaTiO3 in PTFE matrix varied from 0 wt% ...In this paper, a detailed study was carried out on the PTFE reinforced with TiO2 and CaTiO3. The filler content of ceramic powder was a fixed value of 61 wt% and the content of CaTiO3 in PTFE matrix varied from 0 wt% to 16 wt% with a step size of 4 wt%. The effects of CaTiO3 loading on the density, moisture absorption, thermal expansion, microstructure and microwave dielectric properties were investigated. As CaTiO3 loading content increased from 0 wt% to 16 wt%, the thermal expansion initially displayed a sharp increase, and showed a slight enhancement when the content of CaTiO3 exceeded 12 wt%. The density experienced a continuous decrease with the addition of CaTiO3. The moisture absorption displayed a steady increase with the increasing CaTiO3 loading amount. The changing of dielectric constant (εr) and loss tangent (tanδ) were similar to that of the moisture absorption in a manner. Good dielectric properties with values of εr = 11.60, tanδ = 0.002 were obtained in the PTFE matrix with 16 wt% CaTiO3 and 45 wt% TiO2.展开更多
Pure K2Ti4O9 whiskers were prepared by KDC（Kneading-Drying-Calcination） method with TiO2 and K2CO3 as raw materials. The influences of TiO2/K2CO3 molar ratio（RT/K）, calcination temperature（TC） and cooling proces...Pure K2Ti4O9 whiskers were prepared by KDC（Kneading-Drying-Calcination） method with TiO2 and K2CO3 as raw materials. The influences of TiO2/K2CO3 molar ratio（RT/K）, calcination temperature（TC） and cooling process on phase composition and morphology of the whiskers were investigated by TG-DSC（thermo gravimetric-differential scanning calorimeter）, XRD（X-ray diffraction）, and SEM（scanning electron microscope）. Pure K2Ti4O9 potassium titanate whiskers with large length-diameter ratio（r）（over 250） can be obtained at RT/K = 2.9 and TC = 950 ℃.展开更多
The purpose of this work is to explore the effects of the introduction methods of Ce^4+and Zr^4+on the physicochemical properties,activity,and K tolerance of V2 O5-WO3/TiO2 catalyst for the selective catalytic reducti...The purpose of this work is to explore the effects of the introduction methods of Ce^4+and Zr^4+on the physicochemical properties,activity,and K tolerance of V2 O5-WO3/TiO2 catalyst for the selective catalytic reduction of NOx by NH3.Four different methods,namely pre-impregnation,post-impregnation,coimpregnation,and co-precipitation,were used to synthesize a series of V2 O5-WO3-TiO2-CeO2-ZrO2 catalysts.The catalysts were characterized by XRD,BET,NH3-TPD,XPS,and H2-TPR techniques.Moreover,the activity and anti-K poisoning performance were tested by an NH3-SCR model reaction.The results show that the introduction of Ce^4+and Zr^4+can improve the catalytic performance of V2O5-WO3/TiO2 catalyst,but the impregnation method cannot enhance the anti-K poisoning performance.Ce^4+and Zr^4+introduced by co-precipitation method can effectively improve the tolerance of K,which is mainly due to the incorporation of Ce^4+and Zr^4+into TiO2 lattice to form a uniform TiO2-CeO2-ZrO2 solid solution,resulting in the optimal surface acidity and redox performance,and reducing the decreases caused by Kpoisoning.Furthermore,based on the best introduction method,we further optimized the molar ratio of Ce^4+/Zr^4+,It is found that the catalyst exhibits the best anti-K poisoning performance when the molar ratio of Ce^4+/Zr^4+is 2:1.展开更多
基金Project supported by the SPAT of Shanghai Committee of Chinese People's Political Consultative Conference and Shanghai Education Development Foundation (Grant No.2008012)
文摘Y^3＋-doped （Bi 1/2 Na 1/2） TiO 3-CaTiO 3-BaTiO 3 （BNCBT） positive temperature coefficient of resistivity （PTCR） ceramics sintered in air atmosphere were investigated in this study. （Bi 1/2 Na 1/2） TiO 3 （BNT） component can remarkably increase the onset temperature T c of PTCR ceramics with the expense of the resistivity R 25 increase. CaTiO 3 （9–27 mol%） component can decrease the resistivity, and adjust the effects of BNT phase on the T c point. For the sample containing 3 mol% CaTiO 3 , T c raises from 122 ℃ to 153 ℃ when only 0.6 mol% BNT added, while for the ones with higher CaTiO 3 content （9–27 mol%）, T c is only increased by a rate of 8–9℃/1.0 mol% BNT. The effects of BNT and CaTiO 3 components on R25/Rmin （negative temperature coefficient effect） are also discussed.
文摘In this paper, a detailed study was carried out on the PTFE reinforced with TiO2 and CaTiO3. The filler content of ceramic powder was a fixed value of 61 wt% and the content of CaTiO3 in PTFE matrix varied from 0 wt% to 16 wt% with a step size of 4 wt%. The effects of CaTiO3 loading on the density, moisture absorption, thermal expansion, microstructure and microwave dielectric properties were investigated. As CaTiO3 loading content increased from 0 wt% to 16 wt%, the thermal expansion initially displayed a sharp increase, and showed a slight enhancement when the content of CaTiO3 exceeded 12 wt%. The density experienced a continuous decrease with the addition of CaTiO3. The moisture absorption displayed a steady increase with the increasing CaTiO3 loading amount. The changing of dielectric constant (εr) and loss tangent (tanδ) were similar to that of the moisture absorption in a manner. Good dielectric properties with values of εr = 11.60, tanδ = 0.002 were obtained in the PTFE matrix with 16 wt% CaTiO3 and 45 wt% TiO2.
基金Funded by the Natural Science Foundation Key Project of Hubei Province(No.2011CDA060)
文摘Pure K2Ti4O9 whiskers were prepared by KDC（Kneading-Drying-Calcination） method with TiO2 and K2CO3 as raw materials. The influences of TiO2/K2CO3 molar ratio（RT/K）, calcination temperature（TC） and cooling process on phase composition and morphology of the whiskers were investigated by TG-DSC（thermo gravimetric-differential scanning calorimeter）, XRD（X-ray diffraction）, and SEM（scanning electron microscope）. Pure K2Ti4O9 potassium titanate whiskers with large length-diameter ratio（r）（over 250） can be obtained at RT/K = 2.9 and TC = 950 ℃.
基金Project supported by the National Natural Science Foundation of China(21876168)the Key Projects for Common Key Technology Innovation in Key Industries in Chongqing(cstc2016zdcy-ztzx0020-01)+1 种基金Youth Innovation Promotion Association CAS(2019376)the Graduate Innovation Project of Chongqing Technology and Business University(yjscxx201803-028-22)。
文摘The purpose of this work is to explore the effects of the introduction methods of Ce^4+and Zr^4+on the physicochemical properties,activity,and K tolerance of V2 O5-WO3/TiO2 catalyst for the selective catalytic reduction of NOx by NH3.Four different methods,namely pre-impregnation,post-impregnation,coimpregnation,and co-precipitation,were used to synthesize a series of V2 O5-WO3-TiO2-CeO2-ZrO2 catalysts.The catalysts were characterized by XRD,BET,NH3-TPD,XPS,and H2-TPR techniques.Moreover,the activity and anti-K poisoning performance were tested by an NH3-SCR model reaction.The results show that the introduction of Ce^4+and Zr^4+can improve the catalytic performance of V2O5-WO3/TiO2 catalyst,but the impregnation method cannot enhance the anti-K poisoning performance.Ce^4+and Zr^4+introduced by co-precipitation method can effectively improve the tolerance of K,which is mainly due to the incorporation of Ce^4+and Zr^4+into TiO2 lattice to form a uniform TiO2-CeO2-ZrO2 solid solution,resulting in the optimal surface acidity and redox performance,and reducing the decreases caused by Kpoisoning.Furthermore,based on the best introduction method,we further optimized the molar ratio of Ce^4+/Zr^4+,It is found that the catalyst exhibits the best anti-K poisoning performance when the molar ratio of Ce^4+/Zr^4+is 2:1.