CN x /SiCN composite films were prepared on titanium ( Ti ) alloy substrates by Radio Frequency Plasma Enhanced Chemical Vapor Deposition ( RF\|PECVD ). As a buffer layer, SiCN ensured the adhesion of the CN ...CN x /SiCN composite films were prepared on titanium ( Ti ) alloy substrates by Radio Frequency Plasma Enhanced Chemical Vapor Deposition ( RF\|PECVD ). As a buffer layer, SiCN ensured the adhesion of the CN x thin films on Ti substrates. X\|ray diffraction ( XRD) measurement revealed that the composite films possessed α\|C 3 N 4 structure. The microhardness of the films was 48 to 50 GPa. In order to test the characteristics of wear and corrosion resistances, we prepared Ti alloy samples with and without CN x /SiCN composite films. Also for strengthening the effect of wear and corrosion, the wear tests were carried out under high load (12 MPa) and in 0.9% NaCl solution. Results of the wear tests and the corrosive electrochemical measurements showed that the samples coated with CN x films had excellent characteristics of wear and corrosion resistances compared with Ti alloy substrate samples.展开更多
Cubic C3N4 compound in the C-N thin films on Si and NaCl substrates was prepared by ion beam sputtering of a pure graphite target with discharge gas of pure N2. X-ray photoelectron spectroscopy indicated that nitrogen...Cubic C3N4 compound in the C-N thin films on Si and NaCl substrates was prepared by ion beam sputtering of a pure graphite target with discharge gas of pure N2. X-ray photoelectron spectroscopy indicated that nitrogen atoms combined with sp2- and sp3- coordinated C atoms in the film, respectively. X-ray diffraction, selected area electron diffraction and high-resolution electron microscopy were used to identify the cubic C3N4 phase. The results reconfirm the ab initio calculations on metastable structure in C-N compounds展开更多
Hexagonal boron carbonitrogen (h-BCN) compound is synthesized from a mixture of boron powder and CNH compound prepared by pyrolysis of melamine (CaH6N6) under high temperature (1400-1500℃) and high pressure (5...Hexagonal boron carbonitrogen (h-BCN) compound is synthesized from a mixture of boron powder and CNH compound prepared by pyrolysis of melamine (CaH6N6) under high temperature (1400-1500℃) and high pressure (5.0-5.5 GPa). X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy and Raman spec- troscopy are used to determine the chemical composition and bonds of the product. The results show that the product has composition of B0.18C0.64N0.16 (near BC4N) and atomic-level hybrid. X-ray diffraction analysis indicates that the powder has a hexagonal network structure. Scanning and transmission electron microscopy results suggest that h-BCN compound morphology is mainly flaky in width about 1 μm and thickness 200nm.展开更多
文摘CN x /SiCN composite films were prepared on titanium ( Ti ) alloy substrates by Radio Frequency Plasma Enhanced Chemical Vapor Deposition ( RF\|PECVD ). As a buffer layer, SiCN ensured the adhesion of the CN x thin films on Ti substrates. X\|ray diffraction ( XRD) measurement revealed that the composite films possessed α\|C 3 N 4 structure. The microhardness of the films was 48 to 50 GPa. In order to test the characteristics of wear and corrosion resistances, we prepared Ti alloy samples with and without CN x /SiCN composite films. Also for strengthening the effect of wear and corrosion, the wear tests were carried out under high load (12 MPa) and in 0.9% NaCl solution. Results of the wear tests and the corrosive electrochemical measurements showed that the samples coated with CN x films had excellent characteristics of wear and corrosion resistances compared with Ti alloy substrate samples.
文摘Cubic C3N4 compound in the C-N thin films on Si and NaCl substrates was prepared by ion beam sputtering of a pure graphite target with discharge gas of pure N2. X-ray photoelectron spectroscopy indicated that nitrogen atoms combined with sp2- and sp3- coordinated C atoms in the film, respectively. X-ray diffraction, selected area electron diffraction and high-resolution electron microscopy were used to identify the cubic C3N4 phase. The results reconfirm the ab initio calculations on metastable structure in C-N compounds
文摘Hexagonal boron carbonitrogen (h-BCN) compound is synthesized from a mixture of boron powder and CNH compound prepared by pyrolysis of melamine (CaH6N6) under high temperature (1400-1500℃) and high pressure (5.0-5.5 GPa). X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy and Raman spec- troscopy are used to determine the chemical composition and bonds of the product. The results show that the product has composition of B0.18C0.64N0.16 (near BC4N) and atomic-level hybrid. X-ray diffraction analysis indicates that the powder has a hexagonal network structure. Scanning and transmission electron microscopy results suggest that h-BCN compound morphology is mainly flaky in width about 1 μm and thickness 200nm.