Resource-saving（PrNdCe）_2Fe_（14）B sintered magnets with nominal composition（PrNd）_（15-x）Ce_xFe_（77）B_8（x=0–10）were prepared using a dual alloy method by mixing（PrNd）_5Ce_（10）Fe_（77）B_8 with（PrNd）_...Resource-saving（PrNdCe）_2Fe_（14）B sintered magnets with nominal composition（PrNd）_（15-x）Ce_xFe_（77）B_8（x=0–10）were prepared using a dual alloy method by mixing（PrNd）_5Ce_（10）Fe_（77）B_8 with（PrNd）_（15）Fe_（77）B_8 powders. For Ce atomic percent of 1% and 2%, coercivity decreases dramatically. With further increase of Ce atomic percent, the coercivity increases, peaks at 6.38 kOe in（PrNd）_（11）Ce_4Fe_（77）B_8, and then declines gradually. The abnormal dependence of coercivity is likely related to the inhomogeneity of rare earth chemical composition in the intergranular phase, where Pr Nd concentration is strongly dependent on the additive amount of（PrNd）_5Ce_（10）Fe_（77）B_8 powders. In addition, for Ce atomic percent of 8%,7%, and 6% the coercivity is higher than that of magnets prepared by the conventional method, which shows the advantage of the dual alloy method in preparing high abundant rare earth magnets.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant Nos.51461033,51571126,51541105,and 11547032)the Natural Science Foundation of Inner Mongolia,China(Grant No.2013MS0110)the Inner Mongolia University of Science and Technology Innovation Fund,China
文摘Resource-saving（PrNdCe）_2Fe_（14）B sintered magnets with nominal composition（PrNd）_（15-x）Ce_xFe_（77）B_8（x=0–10）were prepared using a dual alloy method by mixing（PrNd）_5Ce_（10）Fe_（77）B_8 with（PrNd）_（15）Fe_（77）B_8 powders. For Ce atomic percent of 1% and 2%, coercivity decreases dramatically. With further increase of Ce atomic percent, the coercivity increases, peaks at 6.38 kOe in（PrNd）_（11）Ce_4Fe_（77）B_8, and then declines gradually. The abnormal dependence of coercivity is likely related to the inhomogeneity of rare earth chemical composition in the intergranular phase, where Pr Nd concentration is strongly dependent on the additive amount of（PrNd）_5Ce_（10）Fe_（77）B_8 powders. In addition, for Ce atomic percent of 8%,7%, and 6% the coercivity is higher than that of magnets prepared by the conventional method, which shows the advantage of the dual alloy method in preparing high abundant rare earth magnets.