A rationale for the development of thermally stable nanostructured CeO_2-ZrO_2-containing mixed oxides

CeO2-ZeO2 solid solutions are extensively used as oxygen storage promoters in the current automotive three-way catalysts. High thermal stability of the textural properties is one of the most important requirements for practical application since temperatures up to 1273 K are easily experienced by these materials under real working conditions. In the present paper, we investigated how hydrothermal treatments applied to cakes of doped and undoped ZrO2-rich CeO2-ZrO2 precursors might improve the thermal stability of the final CeO2-ZrO2 solid solution. A rationale was developed that allowed to correlate the morphology of the hydrothermaUy treated cake with the thermal stability at 1273 K of the final product, which did not depend on the composition of the mixed oxides.

Effect of Manganese Doping on Oxygen Storage Capacity of Ceria-Zirconia Mixed Oxides

CeO2-ZrO2-MnOx mixed oxide series were prepared by sol-gel method. CO pulse and CO-O2 cycle measurements were carried out to examine the oxygen storage complete capacity （OSCC） and dynamic oxygen storage capacity （OSC） of the samples. The doping method brought about strong interactions between manganese oxide and ceria, both in the bulk and on the surface. Only a small part of Mn cations are incorporated into the ceria lattice to form solid solutions and the remaining are left on the surface as finely dispersed Mn3O4. The OSC behaviors of the materials are influenced by the doping amount of Mn and the solubility of Mn in the CeO2 lattice. The OSC is more easily affected by available contents of oxygen storage components when the measurement frequency is low. Comparatively, the concentration of lattice defects, which affects the mobility of bulk oxygen, is the determining factor under high frequency.

Modification of CeO_2-ZrO_2 catalyst by potassium for NOx-assisted soot oxidation

Potassium-modified ceria-zirconia catalyst was synthesized by wetness impregnation method. The ageing treatment was performed in static air at 800℃ for 20 hr to evaluate the thermal stability of the catalyst. The catalysts were characterized by X-ray diffraction, BET surface area, oxygen storage capacity, NOx-temperature programmed desorption and soot-temperature programmed oxidation measurements. By introduction of potassium, the maximum soot oxidation rate temperature （Tin） of the ceria-zirconia based catalyst decreased from 525 to 428℃ in the presence of NO under a loose contact mode. The shift of Tm of the K-modified catalyst after ageing is only 15℃. The enhanced activity of the aged catalyst mainly lies in the promotional effect of potassium on the NOx/oxygen storage capacity as well as the soot-catalyst contact.

Effect of grain size on thermal stability and oxygen storage capacity of Ce_(0.17)Zr_(0.73)La_(0.02)Nd_(0.04)Y_(0.04)O_2 solid solutions

Nanostructured CeO_2-ZrO_2 materials are an irreplaceable constituent in catalytic systems for automobile exhaust purification due to their unique oxygen storage capacity(OSC). However, traditional CeO_2-ZrO_2 materials are easy to sinter at high temperature, which causes a sharp decrease of OSC. In this paper,La^(3+) , Nd^(3+) and Y^(3+) are chosen as dopants for CeO_2-ZrO_2 to improve anti-sintering and OSC properties.The Ce_(0.17) Zr_(0.73) La_(0.02) Nd_(0.04) Y_(0.04) O_2 powders(CZLNY) were prepared by co-precipitation method. The effects of grain sizes with different mixed chlorinated solution concentrations on performances were investigated. X-ray diffraction(XRD) and transmission electron micrograph(TEM) were performed to calculate the grain sizes of CZLNY. The specific surfaces, OSC and redox properties were investigated by N_2 adsorption/desorption and temperature programmed reduction(H2-TPR). The results show that introducing La^(3+) , Nd^(3+) and Y^(3+) into CeO_2-ZrO_2 lattice can improve the stability of phase structure and anti-sintering ability. Moreover, low concentration of mixed chlorinated solution remarkably improves structural and textural properties of CZLNY. Relatively large fresh grain exhibits superior thermal stability and OSC under the condition of being calcined at 800℃ for 3 h. The specific surface and OSC are42.37 m^2/g and 333.13 mmol/g after calcining at 1000℃ for 10 h, respectively. This is owing to the low sintered driving force of large grain and long-range migration energy of large pores during the sintering process, which are beneficial to the stability of structure in CZLNY materials.

Preparation and performance of coating on rare-earth compounds-immersed magnesium alloy by micro-arc oxidation

A composite ceramic coating containing Y2O3-ZrO2-MgO（YSZ-MgO） was prepared on AZ91D magnesium alloy,which was immersed in Y（NO3）3 aqueous solution as pretreatment,by micro-arc oxidation（MAO） process.The morphology,elemental and phase compositions,corrosion behavior and thermal stability of the coatings were studied by SEM,EDX,XRD,electrochemical corrosion test,high temperature oxidation and thermal shock test.The results show that the coating mainly consists of ZrO2,Y2O3,MgO,Mg2SiO4,and MgF2.Among these compounds,Y2O3 accounts for 26.7% of（Y2O3 ＋ ZrO2）.The thickness of YSZ-MgO coating is smaller than that of ZrO2-MgO coating,but its compactness and surface roughness are better than those of ZrO2-MgO coating.YSZ-MgO coating has a good corrosion resistance,and its corrosion rate in 5% NaCl aqueous solution is lower than that of ZrO2-MgO and only about 8.5% of that of AZ91D magnesium alloy.After oxidation at 410 °C,the mass gain of AZ91D magnesium alloy presents a linear increase with the oxidation time.The YSZ-MgO coating and ZrO2-MgO coating can remarkably decrease the oxidation mass gain.The oxidation mass gain of YSZ-MgO coating is lower than that of ZrO2-MgO coating,especially during a long oxidation period.The thermal shock resistance of YSZ-MgO coating is superior to ZrO2-MgO coating.