The CeO_2-ZrO_2 solid solutions were prepared by a reverse microemulsion method. The effect of preparation parameters on the surface area and crystalline form of the solid solutions were studied by the BET surface are...The CeO_2-ZrO_2 solid solutions were prepared by a reverse microemulsion method. The effect of preparation parameters on the surface area and crystalline form of the solid solutions were studied by the BET surface area and XRD analysis. The studies indicate that the separation of the microemulsion phase during the preparation procedure can decrease the specific surface area of sample, adding hydrogen peroxide in the matrix solution can increase the specific surface area and stability of sample. The surface area of sample calcined at 550 ℃ for 5 h is 149 m^2·g^(-1), and that calcined at 900 ℃ for 6 h is 88 m^2·g^(-1). The sample with tetragonal symmetry Ce_(0.5)Zr_(0.5)O_2 phase has a higher stability.展开更多
A series of monolithic Ni/CeO_2-ZrO_2/γ-Al_2O_3 catalysts for the POM reaction were prepared. The activity test shows that the catalyst has the best performance when CeO_2-ZrO_2 content is 8 wt%.The synergistic actio...A series of monolithic Ni/CeO_2-ZrO_2/γ-Al_2O_3 catalysts for the POM reaction were prepared. The activity test shows that the catalyst has the best performance when CeO_2-ZrO_2 content is 8 wt%.The synergistic actions between CeO_2-ZrO_2 and γ-Al_2O_3 improve highly catalytic activity by increasing CH_4 conversion, H_2 and CO selectivity. XPS analysis of the used catalyst indicates that there coexist Ce^(4+) and Ce^(3+).展开更多
文摘The CeO_2-ZrO_2 solid solutions were prepared by a reverse microemulsion method. The effect of preparation parameters on the surface area and crystalline form of the solid solutions were studied by the BET surface area and XRD analysis. The studies indicate that the separation of the microemulsion phase during the preparation procedure can decrease the specific surface area of sample, adding hydrogen peroxide in the matrix solution can increase the specific surface area and stability of sample. The surface area of sample calcined at 550 ℃ for 5 h is 149 m^2·g^(-1), and that calcined at 900 ℃ for 6 h is 88 m^2·g^(-1). The sample with tetragonal symmetry Ce_(0.5)Zr_(0.5)O_2 phase has a higher stability.
文摘A series of monolithic Ni/CeO_2-ZrO_2/γ-Al_2O_3 catalysts for the POM reaction were prepared. The activity test shows that the catalyst has the best performance when CeO_2-ZrO_2 content is 8 wt%.The synergistic actions between CeO_2-ZrO_2 and γ-Al_2O_3 improve highly catalytic activity by increasing CH_4 conversion, H_2 and CO selectivity. XPS analysis of the used catalyst indicates that there coexist Ce^(4+) and Ce^(3+).