To improve the wear resistance of the FeCoCrNiB_(0.2)high entropy alloy(HEA),the FeCoCrNiB_(0.2)(WC_(0))and FeCoCrNiB_(0.2)+20wt%WC(WC_(20))HEA coatings were prepared on Q235 steel by laser cladding(LC).The microstruc...To improve the wear resistance of the FeCoCrNiB_(0.2)high entropy alloy(HEA),the FeCoCrNiB_(0.2)(WC_(0))and FeCoCrNiB_(0.2)+20wt%WC(WC_(20))HEA coatings were prepared on Q235 steel by laser cladding(LC).The microstructure,hardness,and tribometer of the HEA coatings were investigated using scanning electron microscopy with spectroscopy(SEM/EDS),X-ray diffraction(XRD),vickers microhardness tester,and pin-on-disc tribometer,respectively.The experimental results show that the WC0HEA coating comprises a simple BCC phase mixed with an M_(2)B phase.Adding 20wt%WC,the WC_(20)HEA coating is composed of a simple BCC phase mixed with the Cr_(23)C_(6)carbide phase.The microstructure of the WC_(20)HEA coating is simple,which consists of equiaxed grain and dendritic.The microhardness also increases from 625.5HV to 806.0HV,and the wear mass loss correspondingly decreases from 30.9 to 14.9 mg.W and C atoms formed by WC dissolution are mainly dissolved in the BCC phase,which leads to the solution strengthening effect.Besides,Cr_(23)C_(6)carbides inhibit the growth of the grains,play the role of fine-grain strengthening,and further improve the hardness and wear resistance of the HEA coating.展开更多
基金Funded by the National Natural Science Foundation of China (No.51879089)。
文摘To improve the wear resistance of the FeCoCrNiB_(0.2)high entropy alloy(HEA),the FeCoCrNiB_(0.2)(WC_(0))and FeCoCrNiB_(0.2)+20wt%WC(WC_(20))HEA coatings were prepared on Q235 steel by laser cladding(LC).The microstructure,hardness,and tribometer of the HEA coatings were investigated using scanning electron microscopy with spectroscopy(SEM/EDS),X-ray diffraction(XRD),vickers microhardness tester,and pin-on-disc tribometer,respectively.The experimental results show that the WC0HEA coating comprises a simple BCC phase mixed with an M_(2)B phase.Adding 20wt%WC,the WC_(20)HEA coating is composed of a simple BCC phase mixed with the Cr_(23)C_(6)carbide phase.The microstructure of the WC_(20)HEA coating is simple,which consists of equiaxed grain and dendritic.The microhardness also increases from 625.5HV to 806.0HV,and the wear mass loss correspondingly decreases from 30.9 to 14.9 mg.W and C atoms formed by WC dissolution are mainly dissolved in the BCC phase,which leads to the solution strengthening effect.Besides,Cr_(23)C_(6)carbides inhibit the growth of the grains,play the role of fine-grain strengthening,and further improve the hardness and wear resistance of the HEA coating.