Photocatalytic Hproduction from water splitting has a promising prospect for alleviating energy and environmental issues.However,the fast recombination of photogenerated charge carriers limits the photocatalytic effic...Photocatalytic Hproduction from water splitting has a promising prospect for alleviating energy and environmental issues.However,the fast recombination of photogenerated charge carriers limits the photocatalytic efficiency and its practical application.Cocatalyst engineering is an effective strategy to spatially separate photogenerated charge carriers.In this work,noble-metal-free MoSand CoOcocatalysts are loaded on CdS nanorods by a two-step photodeposition method.The MoSfunctions as the reduction cocatalyst to trap electrons and Co Oas the oxidation cocatalyst to trap holes.Transmission electron microscopy(TEM),inductively coupled plasma(ICP),X-ray photoelectron spectroscopy(XPS)and MottSchottky results demonstrate the effectiveness of photodeposition for loading MoSand CoOdual cocatalysts on CdS and their impact on the photochemical properties.The optimized CdS-MoS-CoOcomposite exhibits a high photocatalytic H-production rate of 7.4 mmol g^(-1)h^(-1)and an apparent quantum efficiency(QE)of 7.6%at 420 nm.Further analysis on time-resolved photoluminescence(TRPL)indicates that the introduction of dual cocatalysts greatly prolongs the lifetime of photogenerated charge carriers and deceases the charge recombination rates,consequently leading to superior photocatalytic H-production performance.This work provides a facile and effective strategy for the construction of highly efficient dual-cocatalyst-modified CdS photocatalyst for high-performance photocatalytic Hproduction.展开更多
A series of cobalt doped TiO2(Co-TiO2) and Co Oxloaded TiO2(Co/TiO2) catalysts prepared by sol–gel and impregnation methods respectively were investigated on selective catalytic reduction with NH3(NH3-SCR) of N...A series of cobalt doped TiO2(Co-TiO2) and Co Oxloaded TiO2(Co/TiO2) catalysts prepared by sol–gel and impregnation methods respectively were investigated on selective catalytic reduction with NH3(NH3-SCR) of NO. It was found that Co-TiO2 catalyst showed more preferable catalytic activity at low temperature range. From characterization results of XRD,TEM, Raman and FT-IR, Co species were proved to be doped into TiO2 lattice by replaced Ti atoms. After being characterized and analyzed by NH3-TPD, PL, XPS, EPR and DRIFTS, it was found that the better NH3-SCR activities of Co-TiO2 catalysts, compared with Co/TiO2 catalyst, were ascribed to the formation of more oxygen vacancies which further promoted the production of more superoxide ions(O-2). The superoxide ions were crucial for the formation of low temperature SCR reaction intermediates(NO-3) by reacting with adsorbed NO molecule. Therefore, these aspects were responsible for the higher low temperature NH3-SCR activity of Co-TiO2 catalysts.展开更多
基金the National Science Foundation of China(Nos.22005228 and 52063028)。
文摘Photocatalytic Hproduction from water splitting has a promising prospect for alleviating energy and environmental issues.However,the fast recombination of photogenerated charge carriers limits the photocatalytic efficiency and its practical application.Cocatalyst engineering is an effective strategy to spatially separate photogenerated charge carriers.In this work,noble-metal-free MoSand CoOcocatalysts are loaded on CdS nanorods by a two-step photodeposition method.The MoSfunctions as the reduction cocatalyst to trap electrons and Co Oas the oxidation cocatalyst to trap holes.Transmission electron microscopy(TEM),inductively coupled plasma(ICP),X-ray photoelectron spectroscopy(XPS)and MottSchottky results demonstrate the effectiveness of photodeposition for loading MoSand CoOdual cocatalysts on CdS and their impact on the photochemical properties.The optimized CdS-MoS-CoOcomposite exhibits a high photocatalytic H-production rate of 7.4 mmol g^(-1)h^(-1)and an apparent quantum efficiency(QE)of 7.6%at 420 nm.Further analysis on time-resolved photoluminescence(TRPL)indicates that the introduction of dual cocatalysts greatly prolongs the lifetime of photogenerated charge carriers and deceases the charge recombination rates,consequently leading to superior photocatalytic H-production performance.This work provides a facile and effective strategy for the construction of highly efficient dual-cocatalyst-modified CdS photocatalyst for high-performance photocatalytic Hproduction.
基金financially supported by the Key Project of Chinese National Programs for Research and Development(No.2016YFC0203800)the National Natural Science Foundation of China(Nos.51408309 and 51578288)+4 种基金the Science and Technology Support Program of Jiangsu Province(No.E2014713)the Natural Science Foundation of Jiangsu Province(No.BK20140777)the Industry-Academia Cooperation Innovation Fund Projects of Jiangsu Province(No.BY2014004-10)the Jiangsu Province Scientific and Technological Achievements into a Special Fund Project(No.BA2015062)the Top-notch Academic Programs of Jiangsu Higher Education Institutions
文摘A series of cobalt doped TiO2(Co-TiO2) and Co Oxloaded TiO2(Co/TiO2) catalysts prepared by sol–gel and impregnation methods respectively were investigated on selective catalytic reduction with NH3(NH3-SCR) of NO. It was found that Co-TiO2 catalyst showed more preferable catalytic activity at low temperature range. From characterization results of XRD,TEM, Raman and FT-IR, Co species were proved to be doped into TiO2 lattice by replaced Ti atoms. After being characterized and analyzed by NH3-TPD, PL, XPS, EPR and DRIFTS, it was found that the better NH3-SCR activities of Co-TiO2 catalysts, compared with Co/TiO2 catalyst, were ascribed to the formation of more oxygen vacancies which further promoted the production of more superoxide ions(O-2). The superoxide ions were crucial for the formation of low temperature SCR reaction intermediates(NO-3) by reacting with adsorbed NO molecule. Therefore, these aspects were responsible for the higher low temperature NH3-SCR activity of Co-TiO2 catalysts.
基金financially supported by the National Natural Science Foundation of China (51572136, 51772162, 21571112, 51802170 and 21801150)the Natural Science Foundation of Shandong Province (ZR2018BEM014, ZR2018LB008 andZR2019MB001)+2 种基金Taishan Scholar Foundation of Shandong Province (H. W., ts201712047)the Special Fund Project to Guide Development of Local Science and Technology by Central Government (H.W.)Taishan Scholar Program of Advantage and Characteristic Discipline Team of Eco Chemical Process and Technology