The effect of bainite transformation and microstructure on the mechanical properties in 0.3%C bainitic steel was investigated via the heat treatment process of quenching at higher initial temperature and partitioning ...The effect of bainite transformation and microstructure on the mechanical properties in 0.3%C bainitic steel was investigated via the heat treatment process of quenching at higher initial temperature and partitioning below martensite-start temperature. The results show that bainite transformation takes place with the partitioning time increasing during partitioning below martensite-start temperature. The microstructure of samples treated by this two-step quenching and partitioning process consists of lath bainite, lath martensite and retained austenite. This kind of multiphase microstructure exhibits better strength of 1420 MPa, ductility of 21.8 % and the product of strength and elongation of 30.8 GPa%. Furthermore, the excellent impact toughness of 103 J is exhibited by partitioning at 280 ℃ for 3 h. In addition, the coalescence of bainite platelets was found in the sample treated by partitioning for 8 h, leading to the deterioration of toughness.展开更多
文摘The effect of bainite transformation and microstructure on the mechanical properties in 0.3%C bainitic steel was investigated via the heat treatment process of quenching at higher initial temperature and partitioning below martensite-start temperature. The results show that bainite transformation takes place with the partitioning time increasing during partitioning below martensite-start temperature. The microstructure of samples treated by this two-step quenching and partitioning process consists of lath bainite, lath martensite and retained austenite. This kind of multiphase microstructure exhibits better strength of 1420 MPa, ductility of 21.8 % and the product of strength and elongation of 30.8 GPa%. Furthermore, the excellent impact toughness of 103 J is exhibited by partitioning at 280 ℃ for 3 h. In addition, the coalescence of bainite platelets was found in the sample treated by partitioning for 8 h, leading to the deterioration of toughness.