An experimental investigation is outlined for the CO 2 laser cutting process of metallic coated sheet steels, GALVABOND. It shows that by proper control of the cutting parameters, good quality cuts are possible a...An experimental investigation is outlined for the CO 2 laser cutting process of metallic coated sheet steels, GALVABOND. It shows that by proper control of the cutting parameters, good quality cuts are possible at high cutting rate. Visual examination indicates that when increasing the cutting rate to as high as 5000 mm/min (about 100 times that suggested previously), kerfs of better quality can be achieved. Some kerf characteristics such as the width, heat affected zone and dross in terms of the process parameters are also discussed. A statistical analysis has arrived at a recommendatio on the optimum cutting parameters forprocessing GALVABOND.展开更多
To optimize the process parameters, it is necessary to exactly predict failure modes during deep drawing of coated metal sheets, where two main failure forms are fracture and wrinkling. In this paper, finite element s...To optimize the process parameters, it is necessary to exactly predict failure modes during deep drawing of coated metal sheets, where two main failure forms are fracture and wrinkling. In this paper, finite element simulations based on continuous damage mechanics were used to study the failure behavior during a cylindrical deep drawing of metal sheets with nickel coating. It is shown that taking the effect of blank holder force into account, these two failure modes can be predicted. The simulation results are well consistent with that obtained from experiments.展开更多
文摘An experimental investigation is outlined for the CO 2 laser cutting process of metallic coated sheet steels, GALVABOND. It shows that by proper control of the cutting parameters, good quality cuts are possible at high cutting rate. Visual examination indicates that when increasing the cutting rate to as high as 5000 mm/min (about 100 times that suggested previously), kerfs of better quality can be achieved. Some kerf characteristics such as the width, heat affected zone and dross in terms of the process parameters are also discussed. A statistical analysis has arrived at a recommendatio on the optimum cutting parameters forprocessing GALVABOND.
基金supported by the National Natural Science Foundation of China(Nos.51172192 and 11102176)Hunan Provincial Natural Science Foundation of China(No.09JJ3003)+1 种基金the Natural Science Foundation of Hunan Province for Innovation Group,China(No.09JJ7004)the Key Special Program for Science and Technology of Hunan Province,China(No.2009FJ1002)
文摘To optimize the process parameters, it is necessary to exactly predict failure modes during deep drawing of coated metal sheets, where two main failure forms are fracture and wrinkling. In this paper, finite element simulations based on continuous damage mechanics were used to study the failure behavior during a cylindrical deep drawing of metal sheets with nickel coating. It is shown that taking the effect of blank holder force into account, these two failure modes can be predicted. The simulation results are well consistent with that obtained from experiments.