A series of Ni catalysts supported on alumina with different Ce contents(1.0%–6.0%,mass fraction)was prepared by the impregnation method and used for dry reforming of methane(DRM)at a relatively low temperature of 65...A series of Ni catalysts supported on alumina with different Ce contents(1.0%–6.0%,mass fraction)was prepared by the impregnation method and used for dry reforming of methane(DRM)at a relatively low temperature of 650°C.The promotion effect of Ce with different loading amounts on the physicochemical properties of the catalysts was systematically characterized by transmission electron microscopy(TEM),X-ray diffraction(XRD),N_(2) adsorption-desorption,thermo elemental IRIS Intrepid inductively coupled plasma atomic emission spectrometer(ICP-AES),UV-visible diffuse reflectance spectroscopy(UV-Vis DRS),Fourier transformation infrared(FTIR)spectra,H_(2)-temperature programmed reduction(H_(2)-TPR)analysis,H_(2)-temperature programmed desorption(H_(2)-TPD),and The X-ray photoelectron spectroscopy(XPS)techniques.The results indicate that all the catalysts mainly exist in the NiAl_(2)O_(4) phase after being calcined at 750°C with small Ni particle sizes due to the strong metal-support interaction derived from the reduction of the NiAl_(2)O_(4) phase.The Ce-promoted catalysts show better catalytic performance as well as the resistance against sintering of Ni particles and deposition of carbon compared to the Ni/Al_(2)O_(3) catalyst.The Ni-6Ce/Al_(2)O_(3) exhibits the best catalytic stability and coke resistance among the four catalysts studied,which is due to its small Ni nanoparticles sizes,excellent reducibility as well as high amount of active oxygen species.In a 400 h stability test for DRM reaction at 650°C,Ni-6Ce/Al_(2)O_(3) exhibits less coke deposition and small growth of Ni nanoparticles.This work provides a simple way to preparing the Ni-Ce/Al_(2)O_(3) catalyst with enhanced catalytic performance in DRM.The Ni-6Ce/Al_(2)O_(3) catalyst has great potential for industrial application due to its anti-sintering ability and resistance to carbon deposition.展开更多
In this study, Ni/YZrOcatalysts prepared with impregnation method and treated by dielectric barrier discharge plasma(DBD) in different atmospheres have been investigated for methane dry reforming. It is revealed by H-...In this study, Ni/YZrOcatalysts prepared with impregnation method and treated by dielectric barrier discharge plasma(DBD) in different atmospheres have been investigated for methane dry reforming. It is revealed by H-TPR that plasma treatment can enhance the interaction between Ni O/Ni particles and the YZrOpyrochlore support. Therefore, catalysts with smaller Ni O and Ni grains sizes, higher metallic Ni active surface areas can be achieved, as evidenced by XRD, TEM and Hadsorption-desorption measurements. As a consequence, the plasma-treated catalysts show significantly improved activity, stability and coke resistance, as testified by the TEM and TGA-DSC results. Plasma treatment in H/Ar gas mixture is found to be the best condition to prepare Ni/YZrO, which can be used to obtain a catalyst with the highest activity, stability and most potent coke resistance. It is believed that the smaller Ni grain size and higher metallic Ni active surface area induced by plasma treatment are the inherent reasons accounting for the promoted reaction performance of the Ni/YZrOpyrochlore catalysts.展开更多
Carbon deposition is one of the major issues for catalytic methanation,especially when using high CO content syngas(such as H2/CO=1)due to the inevitable Boudouard reaction.Here we report the significant enhancement o...Carbon deposition is one of the major issues for catalytic methanation,especially when using high CO content syngas(such as H2/CO=1)due to the inevitable Boudouard reaction.Here we report the significant enhancement on the coke-resistance of Ni/MgAl2 O4 catalyst during methanation by modifying with Au.The coke-resistant property was increased with Au addition while the catalytic activity decreased with excess Au.High and stable syngas conversions can be obtained over Au-Ni/MgAl2O4 catalyst at 450-500℃.With comprehensive characterizations by using BET,H2 chemisorption,H2-TPR,XPS,XRD,STEM,EDS,TEM,TG/DTA,Raman and TPH,we found that Au and Ni formed bimetallic nanoparticles of^10 nm with electron donation from Ni to Au.The deposited carbon on the spent Au-Ni/MgAl2O4 is very similar to that on the spent Ni/MgAl2O4 in the nature and in the gasification behaviour but is significantly less.These results suggest that the enhanced coke-resistance of Au-Ni/MgAl2 O4 is presumably due to the suppression on CO disproportionation by modifying Ni with Au.展开更多
Carbon dioxide and methane are two main greenhouse gases which are contributed to serious global warming.Fortunately,dry reforming of methane(DRM),a very important reaction developed decades ago,can convert these two ...Carbon dioxide and methane are two main greenhouse gases which are contributed to serious global warming.Fortunately,dry reforming of methane(DRM),a very important reaction developed decades ago,can convert these two major greenhouse gases into value-added syngas or hydrogen.The main problem retarding its industrialization is the seriously coking formation upon the nickel-based catalysts.Herein,a series of confined indium-nickel(In-Ni)intermetallic alloy nanocatalysts(In_(x)Ni@SiO_(2))have been prepared and displayed superior coking resistance for DRM reaction.The sample containing 0.5 wt.%of In loading(In_(0.5)Ni@SiO_(2))shows the best balance of carbon deposition resistance and DRM reactivity even after 430 h long term stability test.The boosted carbon resistance can be ascribed to the confinement of core–shell structure and to the transfer of electrons from Indium to Nickel in In-Ni intermetallic alloys due to the smaller electronegativity of In.Both the silica shell and the increase of electron cloud density on metallic Ni can weaken the ability of Ni to activate C–H bond and decrease the deep cracking process of methane.The reaction over the confined InNi intermetallic alloy nanocatalyst was conformed to the Langmuir-Hinshelwood(L-H)mechanism revealed by in situ diffuse reflectance infrared Fourier transform spectroscopy(in-situ DRIFTS).This work provides a guidance to design high performance coking resistance catalysts for methane dry reforming to efficiently utilize these two main greenhouse gases.展开更多
The conversion of methane to olefins,aromatics,and hydrogen(MTOAH)can be used to stably obtain hydrocarbons when the effect of the catalytic surface is optimized from the reaction engineering perspective.In this study...The conversion of methane to olefins,aromatics,and hydrogen(MTOAH)can be used to stably obtain hydrocarbons when the effect of the catalytic surface is optimized from the reaction engineering perspective.In this study,Fe/Si C catalysts were packed into a quartz tube reactor.The catalytic surfaces of Si C and the impregnated Fe species decreased the apparent activation energies(E_a)of methane consumption in the blank reactor between 965 and 1020℃.Consequently,the hydrocarbon yield increased by 2.4times at 1020℃.Based on the model reactions of ethane,ethylene,and acetylene mixed with hydrogen in the range of 500-1020℃,an excess amount of Fe in the reactor favored the C-C coupling reaction over the selective hydrogenation of acetylene;consequently,coke formation was favored over the hydrogenation reaction.The gas-phase reactions and catalyst properties were optimized to increase hydrocarbon yields while reducing coke selectivity.The 0.2Fe catalyst-packed reactor(0.26 wt%Fe)resulted in a hydrocarbon yield of 7.1%and a coke selectivity of<2%when the ratio of the void space of the postcatalyst zone to the catalyst space was adjusted to be≥2.Based on these findings,the facile approach of decoupling the reaction zone between the catalyst surface and the gas-phase reaction can provide insights into catalytic reactor design,thereby facilitating the scale-up from the laboratory to the commercial scale.展开更多
A series of Ni/La2Zr2O7 pyrochlore catalysts prepared by impregnation method and treated by dielectric barrier discharge(DBD) plasma in different atmospheres and varied sequences were prepared and applied for dry re...A series of Ni/La2Zr2O7 pyrochlore catalysts prepared by impregnation method and treated by dielectric barrier discharge(DBD) plasma in different atmospheres and varied sequences were prepared and applied for dry reforming of methane(DRM). It is found that all of the plasma treated catalysts show evidently improved activity and coke resistance in comparison with the non-plasma treated one. The best performance is achieved on Ni/La2Zr2O7–H2P–C,a catalyst treated in H2 plasma before calcination. TGA-DSC and SEM demonstrate that carbon deposition is significantly suppressed on all of the plasma treated samples. Moreover,XRD and TEM results testify that both Ni O and Ni sizes on the calcined and reduced samples treated by plasma are also decreased,which results in higher Ni metal dispersion on the reduced and used catalysts and enhances the interactions between Ni sites and the support. It is believed that these are the inherent reasons accounting for the promotional effects of plasma treatment on the reaction performance of the Ni/La2Zr2O7 pyrochlore catalysts.展开更多
Highly coke-resisting ZrO2-decorated Ni/A1203 catalysts for CO methanation were prepared by a two-step process. The support was first loaded with NiO by impregnating method and then modified with ZrO2 by deposition-pr...Highly coke-resisting ZrO2-decorated Ni/A1203 catalysts for CO methanation were prepared by a two-step process. The support was first loaded with NiO by impregnating method and then modified with ZrO2 by deposition-precipitation method (IM-DP). Nitrogen adsorption- desorption, X-ray diffraction, scanning electron microscopy, transmission electron microscopy, thermogravimetdc analysis, H2 temperature- programmed reduction and desorption, NH3 temperature-programmed desorption, and zeta potential analysis were employed to characterize the samples. The results revealed that, compared with the catalysts with the same composition prepared by co-impregnation (CI) and sequential impregnation (SI) methods, the Ni/A1203 catalyst prepared by IM-DP showed much enhanced catalytic performance for syngas methanation under the condition of atmospheric pressure and a high weight hourly space velocity of 120000 mL.g-1 .h-1. In a 80 h life time test under the condition of 300-600 ~C and 3.0 MPa, this catalyst showed high stability and resistance to coking, and the amount of deposited carbon was only 0.4 wt%. On the contrary, the deposited carbon over the catalyst without ZrO2 reached 1.5 wt% after a 60 h life time test. The improved catalytic performance was attributed to the selective deposition of ZrO2 nanoparticles on the surface of NiO rather than A1203, which could he well controlled via changing the electrostatic interaction in the DP procedure. This unique structure could enhance the dissociation of CO2 and generate surface oxygen intermediates, thus preventing carbon deposition on the Ni particles in syngas methanation.展开更多
Hierarchical ZSM-5 zeolites with micro-, meso- and macroporosity were prepared from diatomite zeolitization through a vapor-phase transport process on solid surfaces. The aromatization performance of the catalysts was...Hierarchical ZSM-5 zeolites with micro-, meso- and macroporosity were prepared from diatomite zeolitization through a vapor-phase transport process on solid surfaces. The aromatization performance of the catalysts was in- vestigated on a fixed bed reactor by using FCC gasoline as feedstock. The crystal phase, morphology, pore struc- tures, acidity and coke depositions of the hierarchical ZSM-5 zeolites were characterized by means of X-ray diffrac- tion (XRD), scanning electron microscope (SEM), N2 adsorption/desorption, Fourier transform infrared (FT-IR) and thermogravimetry-mass spectrogram (TG-MS), respectively. The results show that the prepared hierarchical ZSM-5 zeolite possesses excellent porosity and high crystallinity, displaying an improved aromatization performance and carbon deposition resistance due to its meso- and macroporous structures.展开更多
Metal oxides have been used as the supports for heterogeneous catalysis formany years,but they still suffer from coking in some high-temperature applications.The main reasons for coking are the uncontrollable dissocia...Metal oxides have been used as the supports for heterogeneous catalysis formany years,but they still suffer from coking in some high-temperature applications.The main reasons for coking are the uncontrollable dissociation of C-H and the overbalance between carbon deposition and removal.Herein,we find a boron nitride(BN)-immobilized Ni catalyst shows unprecedented coking resistance in dry reforming of methane via the incomplete decomposition of methane.Unlike the Ni-based catalysts supported by traditional metal oxides,BN-supported Ni accelerates the first C-H dissociation while inhibiting the breaking of the final C-H bond;hence,the suppression of the complete decomposition of methane thoroughly addresses the coking issue.This work reveals the fundamental reason for the coking resistance over BN-supported Ni catalysts is selective activation of the C-H bond,which can provide an inspiring idea for other applications.展开更多
Reasonable control on CRI(coke reaction index)is one of the key factors for BF(blast furnace)low-carbon smelting.However,there are contrary opinions.One is increasing CRI to improve reaction efficiency in BF and t...Reasonable control on CRI(coke reaction index)is one of the key factors for BF(blast furnace)low-carbon smelting.However,there are contrary opinions.One is increasing CRI to improve reaction efficiency in BF and the other is decreasing CRI to suppress coke degradation in furnace.Different methods are adopted to realize effective catalysis(increasing CRI)and passivation(decreasing CRI)of coke.Simulation tests of coke in BF lumpy zone under gradual temperature rising have been done.Effect of CRI on gas composition,ore reduction,burden column permeability and heat reserve zone′s temperature under non-isothermal condition are studied.Then combined with iron making calculations,a novel BF operation suggestion is proposed as coke nut with small size be catalyzed and mixed with ore while skeletal coke with large size be passivated and separately charged into BF.展开更多
基金supported by the National Natural Science Foundation of China(No.22088101)the fund of China Petroleum&Chemical Corporation(No.420068-2).
文摘A series of Ni catalysts supported on alumina with different Ce contents(1.0%–6.0%,mass fraction)was prepared by the impregnation method and used for dry reforming of methane(DRM)at a relatively low temperature of 650°C.The promotion effect of Ce with different loading amounts on the physicochemical properties of the catalysts was systematically characterized by transmission electron microscopy(TEM),X-ray diffraction(XRD),N_(2) adsorption-desorption,thermo elemental IRIS Intrepid inductively coupled plasma atomic emission spectrometer(ICP-AES),UV-visible diffuse reflectance spectroscopy(UV-Vis DRS),Fourier transformation infrared(FTIR)spectra,H_(2)-temperature programmed reduction(H_(2)-TPR)analysis,H_(2)-temperature programmed desorption(H_(2)-TPD),and The X-ray photoelectron spectroscopy(XPS)techniques.The results indicate that all the catalysts mainly exist in the NiAl_(2)O_(4) phase after being calcined at 750°C with small Ni particle sizes due to the strong metal-support interaction derived from the reduction of the NiAl_(2)O_(4) phase.The Ce-promoted catalysts show better catalytic performance as well as the resistance against sintering of Ni particles and deposition of carbon compared to the Ni/Al_(2)O_(3) catalyst.The Ni-6Ce/Al_(2)O_(3) exhibits the best catalytic stability and coke resistance among the four catalysts studied,which is due to its small Ni nanoparticles sizes,excellent reducibility as well as high amount of active oxygen species.In a 400 h stability test for DRM reaction at 650°C,Ni-6Ce/Al_(2)O_(3) exhibits less coke deposition and small growth of Ni nanoparticles.This work provides a simple way to preparing the Ni-Ce/Al_(2)O_(3) catalyst with enhanced catalytic performance in DRM.The Ni-6Ce/Al_(2)O_(3) catalyst has great potential for industrial application due to its anti-sintering ability and resistance to carbon deposition.
基金supported by the National Natural Science Foundation of China (21567016, 21566022, 21263015)the Natural Science Foundation of Jiangxi Province (20151BBE50006, 20151BAB203024)the Education Department of Jiangxi Province (KJLD14005, GJJ150016)
文摘In this study, Ni/YZrOcatalysts prepared with impregnation method and treated by dielectric barrier discharge plasma(DBD) in different atmospheres have been investigated for methane dry reforming. It is revealed by H-TPR that plasma treatment can enhance the interaction between Ni O/Ni particles and the YZrOpyrochlore support. Therefore, catalysts with smaller Ni O and Ni grains sizes, higher metallic Ni active surface areas can be achieved, as evidenced by XRD, TEM and Hadsorption-desorption measurements. As a consequence, the plasma-treated catalysts show significantly improved activity, stability and coke resistance, as testified by the TEM and TGA-DSC results. Plasma treatment in H/Ar gas mixture is found to be the best condition to prepare Ni/YZrO, which can be used to obtain a catalyst with the highest activity, stability and most potent coke resistance. It is believed that the smaller Ni grain size and higher metallic Ni active surface area induced by plasma treatment are the inherent reasons accounting for the promoted reaction performance of the Ni/YZrOpyrochlore catalysts.
基金supported by the National Key R&D Program of China(2016YFA0202801)the National Natural Science Foundation of China(21673226,21673187)the “Transformational Technologies for Clean Energy and Demonstration”,Strategic Priority Research Program of the Chinese Academy of Sciences(XDA21040200)
文摘Carbon deposition is one of the major issues for catalytic methanation,especially when using high CO content syngas(such as H2/CO=1)due to the inevitable Boudouard reaction.Here we report the significant enhancement on the coke-resistance of Ni/MgAl2 O4 catalyst during methanation by modifying with Au.The coke-resistant property was increased with Au addition while the catalytic activity decreased with excess Au.High and stable syngas conversions can be obtained over Au-Ni/MgAl2O4 catalyst at 450-500℃.With comprehensive characterizations by using BET,H2 chemisorption,H2-TPR,XPS,XRD,STEM,EDS,TEM,TG/DTA,Raman and TPH,we found that Au and Ni formed bimetallic nanoparticles of^10 nm with electron donation from Ni to Au.The deposited carbon on the spent Au-Ni/MgAl2O4 is very similar to that on the spent Ni/MgAl2O4 in the nature and in the gasification behaviour but is significantly less.These results suggest that the enhanced coke-resistance of Au-Ni/MgAl2 O4 is presumably due to the suppression on CO disproportionation by modifying Ni with Au.
基金supported by the National Natural Science Foundation of China(21976078 and 21773106)the National Key R&D Program of China(2016YFC0205900)+1 种基金the Natural Science Foundation of Jiangxi Province(20202ACB213001)National Engineering Laboratory for Mobile Source Emission Control Technology(NELMS2019A12)。
文摘Carbon dioxide and methane are two main greenhouse gases which are contributed to serious global warming.Fortunately,dry reforming of methane(DRM),a very important reaction developed decades ago,can convert these two major greenhouse gases into value-added syngas or hydrogen.The main problem retarding its industrialization is the seriously coking formation upon the nickel-based catalysts.Herein,a series of confined indium-nickel(In-Ni)intermetallic alloy nanocatalysts(In_(x)Ni@SiO_(2))have been prepared and displayed superior coking resistance for DRM reaction.The sample containing 0.5 wt.%of In loading(In_(0.5)Ni@SiO_(2))shows the best balance of carbon deposition resistance and DRM reactivity even after 430 h long term stability test.The boosted carbon resistance can be ascribed to the confinement of core–shell structure and to the transfer of electrons from Indium to Nickel in In-Ni intermetallic alloys due to the smaller electronegativity of In.Both the silica shell and the increase of electron cloud density on metallic Ni can weaken the ability of Ni to activate C–H bond and decrease the deep cracking process of methane.The reaction over the confined InNi intermetallic alloy nanocatalyst was conformed to the Langmuir-Hinshelwood(L-H)mechanism revealed by in situ diffuse reflectance infrared Fourier transform spectroscopy(in-situ DRIFTS).This work provides a guidance to design high performance coking resistance catalysts for methane dry reforming to efficiently utilize these two main greenhouse gases.
基金supported by the C1 Gas Refinery Program through the National Research Foundation of Korea (NRF)funded by the Ministry of Science,ICT&Future Planning (NRF2017M3D3A1A01037001)supported by the Ministry of Trade,Industry and Energy (MOTIE),Korea Institute for Advancement of Technology (KIAT)through the Virtual Engineering Platform Program (P0022334)。
文摘The conversion of methane to olefins,aromatics,and hydrogen(MTOAH)can be used to stably obtain hydrocarbons when the effect of the catalytic surface is optimized from the reaction engineering perspective.In this study,Fe/Si C catalysts were packed into a quartz tube reactor.The catalytic surfaces of Si C and the impregnated Fe species decreased the apparent activation energies(E_a)of methane consumption in the blank reactor between 965 and 1020℃.Consequently,the hydrocarbon yield increased by 2.4times at 1020℃.Based on the model reactions of ethane,ethylene,and acetylene mixed with hydrogen in the range of 500-1020℃,an excess amount of Fe in the reactor favored the C-C coupling reaction over the selective hydrogenation of acetylene;consequently,coke formation was favored over the hydrogenation reaction.The gas-phase reactions and catalyst properties were optimized to increase hydrocarbon yields while reducing coke selectivity.The 0.2Fe catalyst-packed reactor(0.26 wt%Fe)resulted in a hydrocarbon yield of 7.1%and a coke selectivity of<2%when the ratio of the void space of the postcatalyst zone to the catalyst space was adjusted to be≥2.Based on these findings,the facile approach of decoupling the reaction zone between the catalyst surface and the gas-phase reaction can provide insights into catalytic reactor design,thereby facilitating the scale-up from the laboratory to the commercial scale.
基金supported by the Chinese Natural Science Foundation (21263015 and 21203088)the Education Department of Jiangxi Province (KJLD14005 and GJJ14205)the Natural Science Foundation of Jiangxi Province (20142BAB213013)
文摘A series of Ni/La2Zr2O7 pyrochlore catalysts prepared by impregnation method and treated by dielectric barrier discharge(DBD) plasma in different atmospheres and varied sequences were prepared and applied for dry reforming of methane(DRM). It is found that all of the plasma treated catalysts show evidently improved activity and coke resistance in comparison with the non-plasma treated one. The best performance is achieved on Ni/La2Zr2O7–H2P–C,a catalyst treated in H2 plasma before calcination. TGA-DSC and SEM demonstrate that carbon deposition is significantly suppressed on all of the plasma treated samples. Moreover,XRD and TEM results testify that both Ni O and Ni sizes on the calcined and reduced samples treated by plasma are also decreased,which results in higher Ni metal dispersion on the reduced and used catalysts and enhances the interactions between Ni sites and the support. It is believed that these are the inherent reasons accounting for the promotional effects of plasma treatment on the reaction performance of the Ni/La2Zr2O7 pyrochlore catalysts.
基金supported by the National Natural Science Foundation of China(No.21476238)the National Basic Research Program(No.2014CB744306)+1 种基金the National Key Technology R&D Program of China(No.2010BAC66B01)the"Strategic Priority Research Program"of Chinese Academy of Sciences(Nos.XDA07010100 and XDA07010200)
文摘Highly coke-resisting ZrO2-decorated Ni/A1203 catalysts for CO methanation were prepared by a two-step process. The support was first loaded with NiO by impregnating method and then modified with ZrO2 by deposition-precipitation method (IM-DP). Nitrogen adsorption- desorption, X-ray diffraction, scanning electron microscopy, transmission electron microscopy, thermogravimetdc analysis, H2 temperature- programmed reduction and desorption, NH3 temperature-programmed desorption, and zeta potential analysis were employed to characterize the samples. The results revealed that, compared with the catalysts with the same composition prepared by co-impregnation (CI) and sequential impregnation (SI) methods, the Ni/A1203 catalyst prepared by IM-DP showed much enhanced catalytic performance for syngas methanation under the condition of atmospheric pressure and a high weight hourly space velocity of 120000 mL.g-1 .h-1. In a 80 h life time test under the condition of 300-600 ~C and 3.0 MPa, this catalyst showed high stability and resistance to coking, and the amount of deposited carbon was only 0.4 wt%. On the contrary, the deposited carbon over the catalyst without ZrO2 reached 1.5 wt% after a 60 h life time test. The improved catalytic performance was attributed to the selective deposition of ZrO2 nanoparticles on the surface of NiO rather than A1203, which could he well controlled via changing the electrostatic interaction in the DP procedure. This unique structure could enhance the dissociation of CO2 and generate surface oxygen intermediates, thus preventing carbon deposition on the Ni particles in syngas methanation.
文摘Hierarchical ZSM-5 zeolites with micro-, meso- and macroporosity were prepared from diatomite zeolitization through a vapor-phase transport process on solid surfaces. The aromatization performance of the catalysts was in- vestigated on a fixed bed reactor by using FCC gasoline as feedstock. The crystal phase, morphology, pore struc- tures, acidity and coke depositions of the hierarchical ZSM-5 zeolites were characterized by means of X-ray diffrac- tion (XRD), scanning electron microscope (SEM), N2 adsorption/desorption, Fourier transform infrared (FT-IR) and thermogravimetry-mass spectrogram (TG-MS), respectively. The results show that the prepared hierarchical ZSM-5 zeolite possesses excellent porosity and high crystallinity, displaying an improved aromatization performance and carbon deposition resistance due to its meso- and macroporous structures.
基金financial support from the National Natural Science Foundation of China(grant nos.22006098 and 22125604)Shanghai Sailing Program(grant no.20YF1413300)+1 种基金J.D.thanks Dr.Lei Xie at Fudan University for fruitful discussions.The computational part is also supported by the JSPS KAKENHI(grant no.JP20K05217)the supercomputer at RCCS(grant no.22-IMS-C002),Okazaki,Japan.
文摘Metal oxides have been used as the supports for heterogeneous catalysis formany years,but they still suffer from coking in some high-temperature applications.The main reasons for coking are the uncontrollable dissociation of C-H and the overbalance between carbon deposition and removal.Herein,we find a boron nitride(BN)-immobilized Ni catalyst shows unprecedented coking resistance in dry reforming of methane via the incomplete decomposition of methane.Unlike the Ni-based catalysts supported by traditional metal oxides,BN-supported Ni accelerates the first C-H dissociation while inhibiting the breaking of the final C-H bond;hence,the suppression of the complete decomposition of methane thoroughly addresses the coking issue.This work reveals the fundamental reason for the coking resistance over BN-supported Ni catalysts is selective activation of the C-H bond,which can provide an inspiring idea for other applications.
基金Sponsored by National Natural Science Foundation of China(61271303)Fundamental Research Funds for CentralUniversities of China(FRF-TP-12-029A)
文摘Reasonable control on CRI(coke reaction index)is one of the key factors for BF(blast furnace)low-carbon smelting.However,there are contrary opinions.One is increasing CRI to improve reaction efficiency in BF and the other is decreasing CRI to suppress coke degradation in furnace.Different methods are adopted to realize effective catalysis(increasing CRI)and passivation(decreasing CRI)of coke.Simulation tests of coke in BF lumpy zone under gradual temperature rising have been done.Effect of CRI on gas composition,ore reduction,burden column permeability and heat reserve zone′s temperature under non-isothermal condition are studied.Then combined with iron making calculations,a novel BF operation suggestion is proposed as coke nut with small size be catalyzed and mixed with ore while skeletal coke with large size be passivated and separately charged into BF.