Microstructure of Ni /WC Surface Composite Layer on Gray Iron Substrate

The surface infiltrated composite （Ni/WC） layers on gray iron substrate were fabricated through a vacuum infiltration casting technique （VICT） using Ni-based composite powder with different WC particles content as raw materials.The microstructures of surface infiltrated composite layer,the interface structures between surface composite layer and the substrate,the changes of macro-hardness with the increasing of WC content and the micro-hardness distribution are investigated.The infiltrated composite layer includes a surface composite layer and a transition layer,and the thickness of the transition layer decreases with the increasing content of WC.The thickness of transition layer with 20%WC content in the surface infiltrated composite layer was 170 μm which was the thickest for all transition layers with different WC content.The surface composite layer was mainly composed of WC,W2C,FeB and NiB,along with Ni-Cr-Fe,Ni （Cr） solid solution,Ni （Si） solid solution and Ni （Fe） solid solution.The transition layer was composed of Ni （Cr） solid solution,Ni （Fe） solid solution,Ni （Si） solid solution,Fe （Ni） solid solution and eutectic.The surface macro-hardness and micro-hardness of the infiltrated layer had been evaluated.The macro-hardness of the surface composite layer decreases with the WC content increasing,and the average macro-hardness is HRC60.The distribution of micro-hardness presents gradient change.The average micro-hardness of the infiltrated layer is about HV1000.

Formation mechanism of bimetal composite layer between LCS and HCCI

A low carbon steel （LCS）/high chromium white cast iron （HCCI） bimetal wear plate about 20 mm in thickness was prepared by liquid-liquid bimetal composite casting technology to substitute for the welding wear plate. A clear and distinguishable composite layer between the LCS and the HCCI was detected with SEM, and the composition and phase were analyzed through EDS and XRD. The composite layer was composed of three sublayers from the LCS to the HCCI： pearlite transition layer, composite layer, and HCCI transition layer. The Vickers hardness from the pearlite transition layer to the HCCl transition layer was 360 HV to 855 HV. The austenite grows as dendrites between the composite layer and the HCCI transition layer under constitutional undercooling. A large amount of C and Cr, and a small amount of Si and Mn dissolve in the matrix. Granular Cr7C3 is uniformly distributed. Due to the solute redistribution at the solid-liquid interface, the primary austenite grows from planar to cellular and finally to the distinct dendrite crystals. The dendrite crystals have an obvious growth direction perpendicular to the composite layer.

Wear Performance of Ni/ZrO_2 Infiltrated Composite Layer

The Ni/ZrO2 was used as raw materials to fabricate the surface infiltrated composite layer with 1-4 mm thickness on cast steel substrate through vacuum infiltrated casting technology. The microstructure indicated that the infiltrated composite layer included surface composite layer and transition layer. Wear property was investigated under room temperature and 450 ~C. The results indicated that the abrasion volume of substrate was 8 times that of the infiltrated composite layer at room temperature. The friction coefficient of infiltrated composite layer decreased with the increasing load. The wear resistance of infiltrated composite layer with different ZrO2 contents had been improved obviously under high temperature. The friction coefficient of infiltrated composite layer was decreased comparing with that at room temperature. The oxidation, abrasive and fatigue abrasion was the main wear mechanism at room temperature. Oxidation abrasion, fatigue wear and adhesive wear dominated the wearin~ process under elevated temperature.

Polypyrrole Chitosan Cobalt Ferrite Nanoparticles Composite Layer for Measuring the Low Concentration of Fluorene Using Surface Plasmon Resonance

Fluorene is a polycyclic aromatic hydrocarbon, which is a hazardous toxic chemical in the environment. The measurement of low concentrations of fluorene is a subject of intense interest in chemistry and in the environment. Polypyrrole chitosan cobalt ferrite nanoparticles are prepared using the electrochemical method. The prepared layers are characterized using field emission scanning electron microscopy, Fourier transform infrared spectroscopy, and energy dispersive spectroscopy. The layers are used to detect fluorene using the surface plasmon resonance technique at room temperature. The composite layer is evaluated after detection of fluorene using atomic force microscopy. The fluorene is bound on the layer, and the shift of the resonance angle is about 0.0052°, corresponding to the limitation of 0.01 ppm.

Effect of silicon content on microstructure of Al-Si/SiC_p composite layer cladded on A380 Al alloy by TIG welding process

Tungsten inert gas（TIG） welding was applied to creating a composite layer on the surface of cast aluminum alloy A380. Different mixtures of Al, Si and SiC powders mixed with sodium silicate solution were pasted on substrates. Surface melting was conducted by TIG welding to produce Al-SiC layer on the surface. Microstructural evolution was investigated by X-ray diffractometry（XRD）, optical and scanning electron microscopy（SEM） and elemental microanalysis（EDS）. Properties of clad layers were studied by microhardness and sliding wear testing. The results showed a uniform distribution of SiC particles in dendritic aluminum matrix. Addition of excess silicon caused the formation of eutectic crystals and coarse silicon particles in the clad layer which resulted in higher hardness and wear resistance of clad layers.

In-situ additive manufacturing of high strength yet ductility titanium composites with gradient layered structure using N_(2)

It has always been challenging work to reconcile the contradiction between the strength and plasticity of titanium materials.Laser powder bed fusion(LPBF) is a convenient method to fabricate innovative composites including those inspired by gradient layered materials.In this work,we used LPBF to selectively prepare Ti N/Ti gradient layered structure(GLSTi)composites by using different N_(2)–Ar ratios during the LPBF process.We systematically investigated the mechanisms of in-situ synthesis Ti N,high strength and ductility of GLSTi composites using microscopic analysis,TEM characterization,and tensile testing with digital image correlation.Besides,a digital correspondence was established between the N_(2) concentration and the volume fraction of LPBF in-situ synthesized Ti N.Our results show that the GLSTi composites exhibit superior mechanical properties compared to pure titanium fabricated by LPBF under pure Ar.Specifically,the tensile strength of GLSTi was more than 1.5times higher than that of LPBF-formed pure titanium,reaching up to 1100 MPa,while maintaining a high elongation at fracture of 17%.GLSTi breaks the bottleneck of high strength but low ductility exhibited by conventional nanoceramic particle-strengthened titanium matrix composites,and the hetero-deformation induced strengthening effect formed by the Ti N/Ti layered structure explained its strength-plasticity balanced principle.The microhardness exhibits a jagged variation of the relatively low hardness of 245 HV0.2 for the pure titanium layer and a high hardness of 408 HV0.2 for the N_(2) in-situ synthesis layer.Our study provides a new concept for the structure-performance digital customization of 3D-printed Ti-based composites.

Microstructure characteristics and thermodynamic properties of A357-SiCp/A357 layered composites prepared by semi-solid vacuum stirring suction casting

A357-SiCp/A357 layered composites were prepared using a semi-solid vacuum stirring suction casting method.The microstructures,mechanical properties,and thermal conductivities of the composites fabricated under different suction casting processes were compared.Additionally,the microstructural evolution characteristics and performance enhancement mechanism of the A357-SiCp/A357 layered composites were discussed.The results demonstrate that suction casting at 610°C with a low solid phase ratio can significantly enhance the material density and reduce the agglomeration of SiCp.The A357-SiC_(p)/A357 interface is clear and straight with good bonding.With an increase in the suction casting temperature,the bending resistance and thermal conductivity of the A357-SiC_(p)/A357 layered composites exhibit a trend of significantly increase at first and then slowly decrease owing to casting defects,interface bonding,and SiCp distribution.Compared with SiCp/A357 composites,the bending strength,deflection,and thermal conductivity of the A357-SiCp/A357 layered composites increase from 257 MPa,1.07 mm,and 155.72 W·(m·K)^(-1) to 298 MPa,2.1 mm,and 169.86 W·(m·K)^(-1),respectively.This study provides a reference for improving the rheological casting of aluminum matrix layered composites.

Preparation and characterization of diamond film on Cu substrate using Cu-diamond composite interlayer

Large area diamond films were fabricated on copper substrates by a multi-step process comprised of electroplating Cu-diamond composite layer on Cu substrate, plating a Cu layer to fix the protruding diamond particles, and depositing continuous diamond film on composite interlayer by hot-filament chemical vapor deposition （HFCVD）. The interface characteristics, internal stress and adhesion strength were investigated by scanning electron microscopy, Raman analysis and indentation test. The results show that the continuous film without cracks is successfully obtained. The microstructure of the film is a mixture of large cubo-octahedron grains grown from homo-epitaxial growth and small grains with （111） apparent facets grown from lateral second nuclei. The improved adhesion between diamond film and substrate results from the deep anchoring of the diamond particles in the Cu matrix and the low residual stress in the film.

Crack evolution of soft–hard composite layered rock-like specimens with two fissures under uniaxial compression

Acoustic emission and digital image correlation were used to study the spatiotemporal evolution characteristics of crack extension of soft and hard composite laminated rock masses(SHCLRM)containing double fissures under uniaxial compression.The effects of different rock combination methods and prefabricated fissures with different orientations on mechanical properties and crack coalescence patterns were analyzed.The characteristics of the acoustic emission source location distribution,and frequency changes of the crack evolution process were also investigated.The test results show that the damage mode of SHCLRM is related to the combination mode of rock layers and the orientation of fractures.Hard layers predominantly produce tensile cracks;soft layers produce shear cracks.The first crack always sprouts at the tip or middle of prefabricated fractures in hard layers.The acoustic emission signal of SHCLRM with double fractures has clear stage characteristics,and the state of crack development can be inferred from this signal to provide early warning for rock fracture instability.This study can provide a reference for the assessment of the fracture development status between adjacent roadways in SHCLRM in underground mines,as well as in roadway layout and support.

Construction of bio-functional Mg/HA composite layered coating for orthopedic application

Magnesium was considered as a revolutionary biodegradable implant material for orthopedic application. Concerning the weakness of intrinsic strength and corrosion behavior, a novel strategy of Mg/metal hybrid system was proposed for extension of orthopedic application, especially at load-bearing site. In this work, an Mg and HA composite layered coating was constructed on titanium by means of chemical conversion and vapor deposition. The HA transition interlayer was introduced to enhance the bonding between Mg film and Ti substrate. Compared with the bare Mg coating, the Mg/HA coating presented good interface bonding, which avoided the occurrence of Mg film peeling off from the substrate. The Mg/HA coating showed a uniform degradation and kept integrity after immersion of 14 d. The Mg ions release by degradation played a crucial role in osteopromotion and antibacterial effect. Incubation of MC3T3-E1 osteoblasts with the Mg/HA coating showed significant promotion on osteogenic differentiation according to ALP activity and Alizarin Red staining assays. Meanwhile the degradation of Mg exhibited strong suppression of bacteria proliferation. It was believed that this novel Mg/HA composite layered coating could be potentially applied in further development of bio-functional hybrid orthopedic implants.

Research on quantum well intermixing of 680 nm AlGaInP/GaInP semiconductor lasers induced by composited Si-Si_(3)N_(4) dielectric layer

The optical catastrophic damage that usually occurs at the cavity surface of semiconductor lasers has become the main bottleneck affecting the improvement of laser output power and long-term reliability.To improve the output power of 680 nm AlGaInP/GaInP quantum well red semiconductor lasers,Si-Si_(3)N_(4)composited dielectric layers are used to induce its quantum wells to be intermixed at the cavity surface to make a non-absorption window.Si with a thickness of 100 nm and Si_(3)N_(4)with a thickness of 100 nm were grown on the surface of the epitaxial wafer by magnetron sputtering and PECVD as diffusion source and driving source,respectively.Compared with traditional Si impurity induced quantum well intermixing,this paper realizes the blue shift of 54.8 nm in the nonabsorbent window region at a lower annealing temperature of 600 ℃ and annealing time of 10 min.Under this annealing condition,the wavelength of the gain luminescence region basically does not shift to short wavelength,and the surface morphology of the whole epitaxial wafer remains fine after annealing.The application of this process condition can reduce the difficulty of production and save cost,which provides an effective method for upcoming fabrication.

Love Waves in Layered Graded Composite Structures with Imperfectly Bonded Interface

Theoretical analysis and numerical calculations of Love wave propagation in layered graded composites with imperfectly bonded interface are described in this paper. On the basis of WKB method, the approximate analytic solutions for Love waves are obtained. By the interface shear spring model, the dispersion relations for Love waves in layered graded composite structures with rigid, slip, and imperfectly bonded interfaces are given, and the effects of the interface conditions on the phase velocities of Love waves in SiC/Al layered graded composites are discussed. Numerical analysis shows that the phase velocity decreases when the defined flexibility parameter is greater. For the general imperfectly bonded interface, the phase velocity changes in the range of the velocities for the rigid and slip interface conditions.

Generation Mechanism of Interfacial Layer and Its Effect on Fe-Cr-Ni/Al-Si-Cu-Ni-Mg Composite Performance

Fe-Cr-Ni/Al-Si-Cu-Ni-Mg composite was taken as the experimental material. The chemical composition of interfacial layer was tested. The generation mechanism and influence of interfacial layer on the composite were analyzed. The results indicated that the generation of interfacial layer is sensitive to temperature. Interfacial layer will generate rapidly when temperature reaches 500 ℃ or above. The interfacial layer is mainly composed of Al, Si, Cu, Fe, and Cr, element Ni distributes at the outward of the interfacial layer for the precipitate of Ni later than Si and Cu, and there is almost no diffusion of Ni during the solution treatment. During heat treatment process, unequal quantity changing of metal atom results in disperse or concentrated vacancies or holes near the matrix. The existence of interfacial layer will induce a decrease of compression strength and plasticity at room temperature and an increase of strength at higher temperature comparing with composite without interfacial layer.

Preparation and Properties of the Composite Enhancement Layer of Bearing Ring

In this paper, the NU308 bearing rings were subjected to strengthen grinding treatment (SGT) at ambient temperature. And the running reliabilities of specimens that subjected to SGT and conventional treatment (CT) were respectively investigated by testing dynamic properties including the running temperature, vibrations, and surface burning. Moreover, the residual stress, microtopography, and microstructures on the cross-section were respectively tested with residual stress analyzer and field-emission scanning electron microscopy. The results showed that the running reliabilities of the specimen after SGT had been significantly improved with the reduction of running temperature, vibration, and surface burning. Further study showed that the specimen’s surface was filled with disordered micropores after SGT compared to the regular strip texture on the CT specimen’s surface, and the maximum residual compressive stress induced by SGT was about −900 MPa. Moreover, the thickness of the residual compressive stress layer was over 180 µm, while the thickness of severe plastic deformation layer was about 50 µm.

A Study on a Magnesium-Based Layered Composite Used as a Flame Retardant for Phenolic Epoxy Resins

The effects of a magnesium-based layered composite on the flammability of a phenolic epoxy resin(EP)are studied.In order to produce the required composite material,first,magnesium hydroxide,aluminum salt and deionized water are mixed into a reactor according to a certain proportion to induce a hydrothermal reaction;then,the feed liquid is filtered out using a solid-liquid separation procedure;finally,the material is dried and crushed.In order to evaluate its effects on the flammability of the EP,first,m-phenylenediamine is added to EP and vacuum defoamation is performed;then,EP is poured into a polytetrafluoroethylene mold,cooled to room temperature and demoulded;finally,the magnesium-based layered composite is added to EP,and its flame retardance is characterized by thermogravimetric analysis,limiting oxygen index and cone calorimetry.The X-ray diffraction patterns show that the baseline of magnesium-based layered composite is stable and the front shape is sharp and symmetrical when the molar ratio of magnesium to aluminium is 3.2:1;with the addition of magnesium-based layered composite,the initial pyrolysis temperature of EP of 10%,15%and 30%magnesium-based layered composite decreases to 318.2°C,317.9°C and 357.1°C,respectively.After the reaction,the amount of residual carbon increases to 0.1%,3.45%and 8.3%,and the limiting oxygen index increases by 28.3%,29.1%and 29.6%,respectively.The maximum heat release rate of cone calorimeter decreases gradually.The optimum molar ratio of Mg:Al for green synthesis is 3.2:1,and the NO_(3)-intercalated magnesium-based layered composite has the best flame retardance properties.

Finite element analysis and experimental investigation of the hydrostatic extrusion process of deforming two-layer Cu/Al composite

A concave die with an equal-strain contour line was used in the hydrostatic extrusion process to deform the two-layer Cu/A1 composite. The extruding process was simulated using the fi- nite element method （FEM）. The effect of the friction coefficients on the relative slippage of the contact surfaces between the internal and external metals was investigated, and the stress distribu- tion in the extruded specimen was studied. The simulation results reveal that the relative slippage de- creases with increasing friction coefficient at the contact surface of the two metals. However, the relative slippage increases rapidly with increasing friction coefficient at the contact surface between the specimen and die. No axial tensile stress appears in the plastic deformation zone near the axis, indicating that the inner fracture will not occur in internal metal in the hydrostatic extrusion process as the concave die with equal-strain contour lines is used. The experimental test reveals that the met- allurgical bond is formed between Cu and A1 when the friction coefficient at the surface between the two metals is 0. 3 and the extrusion ratio is 12.

AlGaN Channel High Electron Mobility Transistors with an AlxGa1-xN/GaN Composite Buffer Layer

We report an AlGaN channel high electron mobility transistor （HEMT） on a sapphire substrate with a 1000-nm A1xGa1-xN （x = 0-0.18）/GaN composite buffer layer, With a significant improvement of crystal quality, the device features a high product orris. #n. The AIGaN channel HEMTs presented show improved performance with respect to the conventional AIGaN channel HEMTs, including the on-resistance reduced from 31.2 to 8.1 Ω.mm, saturation drain current at 2 V gate bias promoted from 218 to 540 mA/mm, peak transconductance at 10 V drain bias promoted from 100 to a state-of-the-art value of 174 mS/ram, and reverse gate leakage current reduced from 1.85 × 10-3 to 2.15 × 10-5 mA/mm at VOD = -20 V.

Increased performance of an organic light-emitting diode by employing a zinc phthalocyanine based composite hole transport layer

We demonstrate that the electroluminescent performances of organic light-emitting diodes are significantly improved by employing a zinc phthalocyanine （ZnPc）-based composite hole transport layer （c-HTL）. The optimum ris-（8-hydroxyquinoline）aluminum （Alq3）-based organic light-emitting diode with a c-HTL exhibits a lower turn-on voltage of 2.8 V, a higher maximum current efficiency of 3.40 cd/A and a higher maximum power efficiency of 1.91 lm/W, which are superior to those of the conventional device （turn-on voltage of 3.8 V, maximum current efficiency of 2.60 cd/A, and maximum power efficiency of 1.21 lm/W）. We systematically studied the effects of different kinds of N’-diphenyl-N,N’-bis（1-naphthyl）（1,1’-biphenyl）-4,4’diamine （NPB）：ZnPc c-HTL. Meanwhile, we also investigate their mechanisms different from that in the case of using ZnPc as buffer layer. The specific analysis is based on the absorption spectra of the hole transporting material and current density–voltage characteristics of the corresponding hole-only devices.

Highly sensitive and stable SERS probes of alternately deposited Ag and Au layers on 3D SiO2 nanogrids for detection of trace mercury ions

The hazard of Hg ion pollution triggers the motivation to explore a fast, sensitive, and reliable detection method. Here, we design and fabricate novel 36-nm-thick Ag-Au composite layers alternately deposited on three-dimensional （3D） periodic SiO2 nanogrids as surface-enhanced Raman scattering （SERS） probes. The SERS effects of the probes depend mainly on the positions and intensities of their localized surface plasmon resonance （LSPR） peaks, which is confirmed by the absorption spectra from finite-difference time-domain （FDTD） calculations. By optimizing the structure and material to maximize the intrinsic electric field enhancement based on the design method of 3D periodic SERS probes proposed, high performance of the Ag-Au/SiO2 nanogrid probes is achieved with the stability further enhanced by annealing. The optimized probes show the outstanding stability with only 4.0% SERS intensity change during 10-day storage, the excellent detection uniformity of 5.78% （RSD）, the detection limit of 5.0 × 10-12 M （1 ppt）, and superior selectivity for Hg ions. The present study renders it possible to realize the rapid and reliable detection of trace heavy metal ions by developing high- performance 3D periodic structure SERS probes by designing novel 3D structure and optimizing plasmonic material.

Stabilizing semi-transparent perovskite solar cells with a polymer composite hole transport layer

Semi-transparent perovskite solar cells(ST-PSCs)have broad applications in building integrated photovoltaics.However,the stability of ST-PSCs needs to be improved,especially in n-i-p ST-PSCs since the doped 2,2',7,7'-tetrakis(N,N-di-p-methoxyphenyl-amine)-9,9'-spirobifluorene(Spiro-OMeTAD)is unstable at elevated temperatures and high humidity.In this work,aπ-conjugated polymer poly[(2,6-(4,8-bis(5-(2-ethylhexyl)thiophene-2-yl)-benzo[1,2-b:4,5-b']dithiophene))-alt-(5,5-(1',3'-di-2-thienyl-5',7'-bis(2-ethylhexyl)benzo[1',2'-c:4',5'-c']dithiophene-4,8-dione)](PBDB-T)is selected to form a polymer composite hole transport layer(HTL)with Spiro-OMeTAD.The sulfur atom of the thiophene unit and the carbonyl group of the polymer interact with the undercoordinated Pb2+at the perovskite surface,which stabilizes the perovskite/HTL interface and passivates the interfacial defects.The incorporation of the polymer also increases the glass transition temperature and the moisture resistance of Spiro-OMeTAD.As a result,we obtain ST-PSCs with a champion efficiency of 13.71%and an average visible light transmittance of 36.04%.Therefore,a high light utilization efficiency of 4.94%can be obtained.Moreover,the encapsulated device can maintain 84%of the initial efficiency after 751 h under continuous one-sun illumination(at 30%relative humidity)at the open circuit and the unencapsulated device can maintain 80%of the initial efficiency after maximum power tracking for more than 1250 h under continuous one-sun illumination.