Preparation,Characterization and Photothermal Study of PVA/Ti_(2)O_(3) Composite Films

In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The microstructures,XRD patterns,FTIR spectra,UV-Vis-NIR spectra thermo-conductivity,thermo-stability and photothermal effects of these composite films were all characterized.These results indicated that Ti_(2)O_(3) particles were well dispersed throughout the polyvinyl alcohol(PVA)matrix in the PVA/Ti_(2)O_(3) composite films.And Ti_(2)O_(3) particles could also effectively improve the photothermal properties of the composite films which exhibited high light absorption and generated a high temperature(about 57.4℃for film with 15 wt%Ti_(2)O_(3) amount)on the surface when it was irradiated by a simulated sunlight source(1 kW/m^(2)).

Preparation and release of curcumin/silk fibroin/sodium alginate film

The aim of this study was to prepare silk fibroin/sodium alginate composite film containing curcumin by casting method.Orthogonal test was used to optimize the formulation according to the values of tensile strength and elongation at break.The release of curcumin in the optimal film was studied in order to explore its application as wound dressing.The results showed that the optimum composition of curcumin/silk fibroin/sodium alginate composite film was as follows:Silk fibroin(70 mg/mL)2.7 g,sodium alginate(24 mg/mL)0.84 g,span 40(5.0 mg/mL)0.4 g,glycerol(3.75%,V/V)3 mL,curcumin(0.2 mg/mL)0.016 g.The optimum film showed the tensile strength and the elongation at break was(0.628±0.032)MPa and(0.794±0.046)%,respectively.

Preparation and Characterization of Cellulose Nanofibril-Waterborne Polyurethane Composite Films

To improve the performance of polyurethane films,small amounts of cellulose nanofibrils(CNF)were physically blended with a waterborne polyurethane(WPU)emulsion,and then CNF/WPU composite films were prepared by cast-coating and drying.The particle size of the emulsions and the chemical structure,micromorphology,thermal stability,mechanical properties,and water resistance of the composite films were characterized using a Malvern laser particle size analyzer,Fourier transform infrared spectroscopy(FT-IR),scanning electron microscopy(SEM),thermogravimetric analysis(TGA),an electronic strength machine,water contact angle analysis(WCA),and water absorption tests,respectively.The results showed that at a low CNF content of 0.3 wt%,the particle size of the WPU emulsion and chemical structure of the film did not change significantly.In addition,the tensile strength of the composite film increased by up to 108%compared to the neat WPU film,and the thermal stability and water resistance were slightly improved.The addition of CNF greatly enhanced the tensile strength while maintaining the other original properties of the WPU film,which may greatly improve the service life and tear resistance of commercial coatings in the future.

Enhancement of catalytic and anti-carbon deposition performance of SAPO-34/ZSM-5/quartz films in MTA reaction by Si/Al ratio regulation

In order to further improve the catalytic performance of zeolite catalyst for methanol to aromatics(MTA)technology, the double-tier SAPO-34/ZSM-5/quartz composite zeolite films were successfully synthesized via hydrothermal crystallization. The Si/Al ratio of SAPO-34 film was used as the only variable to study this material. The composite zeolite material with 0.6Si/Al ratio of SAPO-34 has the largest mesoporous specific surface area and the most suitable acid distribution. The catalytic performance for the MTA process showed that 0.6-SAPO-34/ZSM-5/quartz film has as high as 50.3% benzene-toluenexylene selectivity and 670 min lifetime. The MTA reaction is carried out through the path we designed to effectively avoid the hydrocarbon pool circulation of ZSM-5 zeolite, so as to improve the aromatics selectivity and inhibit the occurrence of deep side reactions to a great extent. The coke deposition behavior was monitored by thermogravimetric analysis and gas chromatograph/mass spectrometer, it is found that with the increase of Si/Al ratio, the active intermediates changed from low-substituted methylbenzene to high-substituted methylbenzene, which led to the rapid deactivation of the catalyst. This work provides a possibility to employ the synergy effect of composite zeolite film synthesizing anti-carbon deposition catalyst in MTA reaction.

Preparation and Properties of Vegetable-Oil-Based Thioether Polyol and Ethyl Cellulose Supramolecular Composite Films

Ethyl cellulose(EC),an important biomass-based material,has excellent film-forming properties.Nevertheless,the high interchain hydrogen bond interaction leads to a high glass transition temperature of EC,which makes it too brittle to be used widely.The hydroxyl group on EC can form a supramolecular system in the form of a non-covalent bond with an effective plasticizer.In this study,an important vegetable-oil-based derivative named dimer fatty acid was used to prepare a novel special plasticizer for EC.Dimer-fatty-acid-based thioether polyol(DATP)was synthesized and used to modify ethyl cellulose films.The supramolecular composite films of DATP and ethyl cellulose were designed using the newly-formed van der Waals force.The thermal stability,morphology,hydrophilicity,and mechanical properties of the composite films were all tested.Pure EC is fragile,and the addition of DATP makes the ethyl cellulose films more flexible.The elongation at the break of EC supramolecular films increased and the tensile strength decreased with the increasing DATP content.The elongation at the break of EC/DATP(60/40)and EC/DATP(50/50)was up to 40.3%and 43.4%,respectively.Noticeably,the thermal initial degradation temperature of the film with 10%DATP is higher than that of pure EC,which may be attributed to the formation of a better supramolecular system in this composite film.The application of bio-based material(EC)is environmentally friendly,and the novel DATP can be used as a special and effective plasticizer to prepare flexible EC films,making it more widely used in energy,chemical industry,materials,agriculture,medicine,and other fields.

Preparation and characterization of ZrO_2/TiO_2 composite photocatalytic film by micro-arc oxidation

ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.

Properties of W/DLC/W-S-C composite films fabricated by magnetron sputtering

A kind of W/DLC/W-S-C composite film was fabricated by magnetron sputtering method.Effects of WSx content on the structure and the adhesion of the composite films were investigated.In addition,tribological behavior of the composite films was studied in the conditions of the ambient air and N2 gas atmosphere by ball-on-disk tester.The results indicate that the composite films show dense and amorphous microstructure.The WCx and WSx compounds are found in amorphous diamond like carbon matrix in the top layers of W-S-C.A proper WSx content is beneficial for improving the adhesion of the composite films.In air atmosphere,the composite films with high C content have better wear resistance and the friction coefficients range from 0.15 to 0.25.In N2 condition,high WSx content is benefit for the wear resistance and the friction coefficients of the composite films range from 0.03 to 0.1.

MXene@c-MWCNT Adhesive Silica Nanofiber Membranes Enhancing Electromagnetic Interference Shielding and Thermal Insulation Performance in Extreme Environments

A lightweight flexible thermally stable composite is fabricated by com-bining silica nanofiber membranes(SNM)with MXene@c-MWCNT hybrid film.The flexible SNM with outstanding thermal insulation are prepared from tetraethyl orthosilicate hydrolysis and condensation by electrospinning and high-temperature calcination;the MXene@c-MWCNT_(x:y)films are prepared by vacuum filtration tech-nology.In particular,the SNM and MXene@c-MWCNT_(6:4)as one unit layer(SMC_(1))are bonded together with 5 wt%polyvinyl alcohol(PVA)solution,which exhibits low thermal conductivity(0.066 W m^(-1)K^(-1))and good electromagnetic interference(EMI)shielding performance(average EMI SE_(T),37.8 dB).With the increase in func-tional unit layer,the overall thermal insulation performance of the whole composite film(SMC_(x))remains stable,and EMI shielding performance is greatly improved,especially for SMC_(3)with three unit layers,the average EMI SET is as high as 55.4 dB.In addition,the organic combination of rigid SNM and tough MXene@c-MWCNT_(6:4)makes SMC_(x)exhibit good mechanical tensile strength.Importantly,SMC_(x)exhibit stable EMI shielding and excellent thermal insulation even in extreme heat and cold environment.Therefore,this work provides a novel design idea and important reference value for EMI shielding and thermal insulation components used in extreme environmental protection equipment in the future.

Application of ultra-smooth composite diamond film coated WC-Co drawing dies under water-lubricating conditions

A specific revised HFCVD apparatus and a novel process combining HFCVD and polishing technique were presented to deposit the micro-and nano-crystalline multilayered ultra-smooth diamond（USCD） film on the interior-hole surface of WC-Co drawing dies with aperture ranging from d1.0 mm to 60 mm.Characterization results indicate that the surface roughness values（Ra） in the entry zone,drawing zone and bearing zone of as-fabricated USCD coated drawing die were measured as low as 25.7,23.3 and 25.5 nm,respectively.Furthermore,the friction properties of USCD films were examined in both dry sliding and water-lubricating conditions,and the results show that the USCD film presents much superior friction properties.Its friction coefficients against ball-bearing steel,copper and silicon nitride balls（d4 mm）,is always lower than that of microcrystalline diamond（MCD） or WC-Co sample,regardless of the lubricating condition.Meanwhile,it still presents competitive wear resistance with the MCD films.Finally,the working lifetime and performance of as-fabricated USCD coated drawing dies were examined under producing low-carbon steel pipes in dry-sliding and water-lubricating conditions.Under the water-lubricating drawing condition,its production significantly increases by about 20 times compared with the conventional WC-Co drawing dies.

Magnetostatic Coupling in CoFe204/Pb（Zr0.53Ti0.47）O3 Magnetoelectric Composite Thin Films of 2-2 Type Structure

CoFe204/Pb（Zr0.53Ti0.47）O3 （CFO/PZT） magnetoelectric composite thin films of 2-2 type structure had been prepared onto Pt/Ti/SiO2/Si substrate by a sol-gel process and spin coat- ing technique. The structure of the prepared thin film is substrate/PZT/CFO/PZT/CFO. Two CFO ferromagnetic layers are separated from each other by a thin PZT layer. The upper CFO layer is magnetostatically coupled with the lower CFO layer. Subsequent scan- ning electron microscopy （SEM） investigations show that the prepared thin films exhibit good morphologies and compact structure, and cross-sectional micrographs clearly display a multilayered nanostructure of multilayered thin films. The composite thin films exhibit both good magnetic and ferroelectric properties. The spacing between ferromagnetic layers can be varied by adjusting the thickness of intermediate PZT layer. It is found that the strength of magnetostatic coupling has a great impact on magnetoelectric properties of composite thin films, i.e., the magnetoelectric voltage coefficient of composite thin film tends to increase with the decreasing of pacing between two neighboring CFO ferromagnetic layers as a result of magnetostatic coupling effect.

Novel Sustainable Cellulose Acetate Based Biosensor for Glucose Detection

In this study,green zinc oxide(ZnO)/polypyrrole(Ppy)/cellulose acetate(CA)film has been synthesized via solvent casting.This film was used as supporting material for glucose oxidase(GOx)to sensitize a glucose biosensor.ZnO nanoparticles have been prepared via the green route using olive leaves extract as a reductant.ZnO/Ppy nanocomposite has been synthesized by a simple in-situ chemical oxidative polymerization of pyrrole(Py)monomer using ferric chloride(FeCl3)as an oxidizing agent.The produced materials and the composite films were characterized using X-ray diffraction analysis(XRD),scanning electron microscope(SEM),Fourier transform infrared(FTIR)and thermogravimetric analysis(TGA).Glucose oxidase was successfully immobilized on the surface of the prepared film and then ZnO/Ppy/CA/GOx composite was sputtered with platinum electrode for the current determination at different initial concentrations of glucose.Current measurements proved the suitability and the high sensitivity of the constructed biosensor for the detection of glucose levels in different samples.The performance of the prepared biosensor has been assessed by measuring and comparing glucose concentrations up to 800 ppm.The results affirmed the reliability of the developed biosensor towards real samples which suggests the wide-scale application of the proposed biosensor.

Nonlinear Optical Properties of Al-Doped nc-Si-SiO_2 Composite Films

The nonlinear optical properties of Al-doped nc-Si-SiO2 composite films have been investigated using the time-resolved four-wave mixing technique with a femtosecond laser. The off-resonant third-order nonlinear susceptibility is observed to be 1.0 × 10-10 esu at 800nm. The relaxation time of the optical nonlinearity in the films is as short as 60fs. The optical nonlinearity is enhanced due to the quantum confinement of electrons in Si nanocrystals embedded in the SiO2 films. The enhanced optical nonlinearity does not originate from Al dopant because there are no Al clusters in the films.

Lithium intercalation/de-intercalation behavior of a composite Sn/C thin film fabricated by magnetron sputtering

A tin film of 320 nm in thickness on Cu foil and its composite film with graphite of-50 nm in thickness on it were fabricated by magnetron sputtering. The surface morphology, composition, surface distributions of alloy elements, and lithium intercalation/de-intercalation behaviors of the fabricated films were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, electron probe microanalyzer （EPMA）, X-ray photoelectron spectroscopy （XPS）, inductively coupled plasma atomic emission spectrometry （ICP）, cyclic voltammetry （CV）, and galvanostatic charge/discharge （GC） measurements. It is found that the lithium intercalation/de-intercalation behavior of the Sn film can be significantly improved by its composite with graphite. With cycling, the discharge capacity of the Sn film without composite changes from 570 mAh/g of the 2nd cycle to 270 mAh/g of the 20th cycle, and its efficiency for the discharge and charge is between 90% and 95%. Nevertheless, the discharge capacity of the composite Sn/C film changes from 575 mAh/g of the 2nd cycle to 515 mAh/g of the 20th cycle, and its efficiency for the discharge and charge is between 95% and 100%. The performance improvement of tin by its composite with graphite is ascribed to the retardation of the bulk tin cracking from volume change during lithium intercalation and de-intercalation, which leads to the pulverization of tin.

Properties of TiO_2 Thin Films Prepared by Magnetron Sputtering

With rapid progressive application of TiO2 thin films, magnetron sputtering becomes a very interesting method to prepare such multi-functional thin films. This paper focuses on influences of various deposition processes and deposition rate on the structures and properties of TiO2 thin films. Anatase, rutile or amorphous TiO2 films with various crystalline structures and different photocatalytic, optical and electrical properties can be produced by varying sputtering gases, substrate temperature, annealing process, deposition rate and the characteristics of magnetron sputtering. This may in turn affect the functions of TiO2 films in many applications. Furthermore, TiO2-based composites films can overcome many limitations and improve the properties of TiO2 films.

Photocatalytic degradation of methyl orange over ITO/CdS/ZnO interface composite films

ITO/CdS/ZnO interface composite films were successfully prepared by subsequent electrodeposition of CdS and ZnO onto indium tin oxide （ITO） glass substrates. The obtained ITO/CdS/ZnO composite films were characterized with X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and UV-Vis spectroscopy. The photocatalytic activity of ITO/CdS/ZnO composite films were investigated using methyl orange （MO） as a model organic compound under UV light irradiation. The influence of operating parameters on MO degradation including initial concentration of MO, pH value of solution, and inorganic anion species over the composite films were examined. A blue shift of absorption threshold was observed for the ITO/CdS/ZnO film in comparison with ITO/ZnO film. ITO/CdS/ZnO composite films prepared under specific conditions showed a higher photocatalytic activity than that of ITO/ZnO films. It was also found that the photocatalytic degradation of MO on the composite films followed pseudo-first order kinetics.

Ni nanocomposite films formed by Ni nanowires embedded in Ni matrix using electrodeposition

Ni nanocomposite films formed by Ni nanowires embedded in Ni matrix(Ni nanowire/Ni composite films)were fabricated by electrodeposition combined with supersonic stirring in a conventional Watts'bath containing Ni nanowires with diameter about 30 nm.The deposition temperature-dependent microstructure,crystal orientation,lattice constant and corrosion behavior of the Ni nanowire/Ni composite films were investigated by field emission scanning electron microscope,X-ray diffraction and potentiodynamic polarization tests,respectively.And the possible mechanism was discussed.It is found that to some extent,the deposition temperature has an impact on the microstructure,crystal orientation,lattice constant and corrosion property of the Ni nanowire/Ni composite films.The Ni nanowire/Ni composite films prepared at 50℃exhibit a novel inter-twisted-nanowire microstructure and have the best corrosion resistance.

PREPARATION AND CORROSION RESISTANCE OF NiP/TiO_2 COMPOSITE FILM ON CARBON STEEL IN SULFURIC ACID SOLUTION

A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion behavior of the NiP/TiO2 composite film was investigated by polarization resistance measurement, anode polarization, ESEM （environmental scanning electron microscopy） and EIS （electrochemical impedance spectroscopy） measurements. Results showed that the NiP/ TiO2 composite film has a good corrosion resistance in 0.5mol/L H2SO4 solution. The element valence of the composite film was characterized by XPS （X-ray photoelectron spectroscopy） spectrum, and an anticorrosion mechanism of the composite film was discussed.

A flexible CNT@nickel silicate composite film for high-performance sodium storage

Due to the sufficient ion diffusion channels provided by the large interlayer spacing, layered silicates are widely considered as potential anode materials for lithium ion and sodium ion batteries. However, due to the poor electronic conductivity, the application of layered silicates for electrochemical energy storage has been greatly limited. Carbon nanotube(CNT) film has excellent electrical conductivity and a unique interconnected network, making it an ideal matrix for composite electrochemical material. We herein report a CNT@nickel silicate composite film(CNT@NiSiO) fabricated by a SiO2-mediated hydrothermal conversion process, for sodium storage with excellent electrochemical properties. The obtained composite possesses a cladding structure with homogeneous nanosheets as the outermost and CNT film as the inner network matrix, providing abundant ion diffusion channels, high electronic conductivity, and good mechanical flexibility. Due to these merits, this material possesses an excellent electrochemical performance for sodium storage, including a high specific capacity up to 390 mAh g-1 at 50 mA g-1, good rate performance up to 205 mAh g-1 at 500 mA g-1, and excellent cycling stability. On this basis, this work would bring a promising material for various energy storage devices and other emerging applications.

A Fiber Optic Sensor for 2,4-dichlorophenol Analysis based on Optical Composite Oxygen-sensitive Film

A novel fiber optic sensor based on optical composite oxygen-sensitive film was developed for determination of 2,4-dichlorophenol(DCP).The optical composite oxygen-sensitive film consists of tris(2,2’-bipyridyl)dichloro ruthenium(II)hexahydrate(Ru(bpy)3Cl2)as the fluorescence indicator and iron(III)tetrasulfophthalocyanine(Fe(III)PcTs)as bionic enzyme.A lock-in amplifier was used for detecting the lifetime of the composite oxygen-sensitive film by measuring the phase delay of the sensor head.The different variables affecting the sensor performance were evaluated and optimized.Under the optimal conditions(i e,pH 6.0,25℃,Fe(III)PcTs concentration of 5.0×10^-5 mol/L),the linear detection range,detection limit and response time of the fiber optic sensor are 3.0×10^-7-9.0×10^-5 mol/L,4.8×10^-8 mol/L(S/N=3),and 220 s,respectively.The sensor displays high selectivity,good repeatability and stability,which have good potentials in analyzing DCP concentration in practical water samples.