Possibility of Inducing Compressive Residual Stresses in Welded Joints of SS400 Steels

Since the welded constructions produce easily stress corrosion cracking (SCC) or fatigue disruption in corrosive medium or under ripple load, two methods inducing compressive stress on structural surfaces by anti-welding-heating treatment (AWHT) and explosion treatment (ET) are presented. The results show that they are good ways to resisting SCC on the welded SS400 steel or other components.

An Overview of Techniques for Measuring Residual Stress in Metal Matrix Composites

Measurement of residual stress is significant to ensure safety, reliability and the life of composites, and currently has been a hot issue in scientific research. The fabrication processes such as machining, and heat treatment inherit either kind of residual stress which had either positive consequences or negative ones, for example, the fatigue limit of a component enhances by compressive stress, whereas corrosion resistance gets reduced by tensile stress. This study is aimed at a brief overview of the recent advancement in this field to help researchers in the in-depth study of measuring residual stress. It helps them in selecting the most appropriate techniques among destructive methods i.e., mainly Contour, ring core, deep hole-drilling method, and non-destructive techniques i.e., diffraction, ultrasonic method, depending on their requirements and applications. For each available technique, working methodology, physical limitations, and applications are discussed. At the end of this paper, future trends regarding an assessment of residual stress have been forecasted.

Dynamics along the epithelial-cancer biointerface:Hidden system complexities

The biointerface dynamics influence any cancer spreading through the epithelium since it is documented in the early stages some malignancies(like epithelial cancer).The altered rearrangement of epithelial cells has an impact on the development of cancer.Therefore,it is necessary to comprehend the underlying biological and physical mechanisms of this biointerface dynamics for early suppression of cancer.While the biological mechanisms include cell signaling and gene expression,the physical mechanisms are several physical parameters such as the epithelial-cancer interfacial tension,epithelial surface tension,and compressive stress accumulated within the epithelium.Although the segregation of epithelia-cancer co-cultured systems was widely investigated,the role of these physical parameters in cell reorganization is still not fully recognized.Hence,this review is focused on clarifying the role that some physical parameters have during cell reorganization within the epithelial cell clusters and cancer spread within co-cultured spheroids.We have applied the developed biophysical model to point out the inter-relations among physical parameters that influence cell reorganization within epithelial-cancer co-cultured systems.The main results of this theoretical consideration have been assessed by integrating the biophysical model with biological and bio-mechanical experiments from the available literature.The epithelial-cancer interfacial tension leads to the reduction of the biointerface area,which leads to an increase in the compressive residual stress within the epithelial clusters depending on the viscoelasticity of the epithelial subpopulation.This stress impacts epithelial rearrangement and the dynamics along the biointerface by influencing the epithelial surface tension and epithelial-cancer interfacial tension.Further,the interrelation between the epithelial surface tension and epithelial-cancer interfacial tension influences the spread of cancer cells.

Mechanical properties of strengthened surface layer in Ti-6Al-4V alloy induced by wet peening treatment

A modified surface layer was formed on Ti-6Al-4V alloy by wet peening treatment. The variations of the residual stress,nano-hardness and microstructure of the modified layer with depth from surface were studied using X-ray diffraction analysis,nano-indentation analysis, scanning electron microscopy and transmission electron microscopy observations. The results show thatboth the compressive residual stress and hardness decrease with increasing depth, and the termination depths are 160 and 80 μm,respectively. The microstructure observation indicates that within 80 μm, the compressive residual stress and the hardness areenhanced by the co-action of the grain refinement strengthening and dislocation strengthening. Within 80–160 μm, the compressiveresidual stress mainly derives from the dislocation strengthening. The strengthened layer in Ti-6Al-4V alloy after wet peeningtreatment was quantitatively analyzed by a revised equation with respect to a relation between hardness and yield strength.

New Developed Welding Electrode for Improving the Fatigue Strength of Welded Joints

A new welding electrode, low transformation temperature electrode (LTTE), was introduced in this paper. It was described in design principle, mechanics, chemical compositions of their deposited metal and manufacturing methods. It was proved that the best transformation starting temperature from austenite to martensite of the deposited metal of LTTE was at about 191℃ and it was obtained by adding alloying elements such as Cr, Ni, Mn and Mo. The microstructure of the weld metal of the LTTE was low carbon martensite and residual austenite. The compressive residual stress was induced around the weld of the LTTE and the -145 MPa in compression could be obtained in middle of weld metal. The fatigue tests showed that the fatigue strength of the longitudinal welded joints welded with the LTTE at 2×106 cycles was improved by 59% compared with that of the same type of welded joints welded with conventional E5015 and the fatigue life was increased by 47 times at 162 MPa. It is a very valuable method to improve the fatigue performance of welded joints.

Experimental study on laser shock processing of brass

Laser shock processing （LSP） is a new surface treatment technique for improving hardness, wear resistance, and fatigue. In this paper, basic theories were introduced and the influence of laser pulse intensity on the laser shock processing of brass specimens was investigated by experiments. Microhardness, roughness, microstructure, wear resistance, friction coefficient evolution, and residual stress were examined with different laser pulse intensities of LSP. The results show that the microhardness increases after LSP treatment, and the higher the pulse intensity, the higher the microhardness. Though the microstructure shows no remarkable change, the roughness and wear resistance increase with the increase in pulse density. Laser shock processing has great potential as a means to improve the mechanical properties of components.

Improving the fatigue performance of longitudinal welded joints by low transformation temperature electrodes

For a longitudinal welded joint, the tensile residual stresses are as high as the yield stress of the metal, so that the weld toes are sensitive to fatigue load. In this case a low transformation temperature electrode (LTTE) is one of the most useful methods used to improve the fatigue strength of the longitudinal welded joint, because the tensile residual stress is reduced or changed into compressive stress. Three kinds of longitudinal welded joints were selected to conduct fatigue tests. The tests results show that the fatigue strengths at 2×10 6 cycles of the joints welded with LTTE were improved by 41%, 47% and 59% respectively compared with those of the joints welded with E5015, and the fatigue lives at 162 MPa were improved by 9.9 times, 9.6 times and 46.8 times respectively. Furthermore, the LTTE method is not necessary to add process after welding and so that it can be valuable method to improve the fatigue performance of longitudinal welded joints.

Compressive Strength and Interface Microstructure of PCBN Grains Brazed with High-Frequency Induction Heating Method

In order to prepare monolayer brazed superabrasive wheels, the polycrystalline cubic boron nitride（PCBN）grains were brazed to AISI 1045 steel matrix with Ag–Cu–Ti filler alloy using the high-frequency induction heating technique. The compressive strengths of brazed grains were measured. Morphology, chemical composition and phase component of the brazing resultant around PCBN grain were also characterized. The results show that the maximum compressive strength of brazed grains is obtained in the case of brazing temperature of 965 °C, which does not decrease the original grain strength. Strong joining between Ag–Cu–Ti alloy and PCBN grains is dependent on the brazing resultants,such as TiB_2, TiN and AlTi_3, the formation mechanism of which is also discussed. Under the given experimental conditions, the optimum heating parameters were determined to be current magnitude of 24 A and scanning speed of0.5 mm/s. Finally, the brazing-induced residual tensile stress, which has a great influence on the grain fracture behavior in grinding, was determined through finite element analysis.