According to the results of accelerated tests of acidification corrosion depth and compressive strength of concretes subjected to sulfuric acid environments,the acidification depth laws of concretes were predicted bas...According to the results of accelerated tests of acidification corrosion depth and compressive strength of concretes subjected to sulfuric acid environments,the acidification depth laws of concretes were predicted based on the grey system theory.Thus,the remaining compressive strength was calculated when the acidification depth reached the protection layer thickness of concrete structures,which indicates that the limit state of durability failure can be defined based on strength degradation,and the calculation process was illustrated by an example.The calculated results show that the remaining compressive strength values in the durability failure limit state for the concrete structures exposed to p H=2 and 3 sulfuric acid water environments and wet-dry cyclic sulfuric acid environment with p H=2 are 74%,72%,and 80% of initialstrength,respectively.The method provides references for the durability evaluation of concrete structure design under the acidic environments.展开更多
In this study, we looked at a method quantifying EEC （embodied energy and CO2） and the effect when we prolonged the building life time particularly through the durable improvement of the structure. Increasing the co...In this study, we looked at a method quantifying EEC （embodied energy and CO2） and the effect when we prolonged the building life time particularly through the durable improvement of the structure. Increasing the covering thickness of concrete for reinforcing bars and the earthquake-resistant strength are methods to increase the durability of the structure. The calculation method to obtain the quantity of concrete and reinforcing bars is provided. The EEC increase is evaluated from the 2005 input-output table in Japan. These results show that EE （embodied energy） in the construction phase is increased by 11% to 20% and EC （embodied CO2） 17% to 32%. However, annual EE is reduced 66% to 72% and EC 70% to 79%,展开更多
The shajiang river bridge on the appearance test, concrete rebound detection, concrete cover depth detection, concrete carbonation depth detection, concrete chlorine ion content detection, and the detection results in...The shajiang river bridge on the appearance test, concrete rebound detection, concrete cover depth detection, concrete carbonation depth detection, concrete chlorine ion content detection, and the detection results in statistics and analysis. Based on the bridge of the service the atmospheric environment parameters and testing data, the paper calculates and analyzes the main stress components the carbonation bridge reliability index and remaining life of carbide, assessing the bridge for the service life and reinforcement maintenance and offer the scientific basis.展开更多
基金Funded by the Nnational Natural Science Foundation of China(51372185)
文摘According to the results of accelerated tests of acidification corrosion depth and compressive strength of concretes subjected to sulfuric acid environments,the acidification depth laws of concretes were predicted based on the grey system theory.Thus,the remaining compressive strength was calculated when the acidification depth reached the protection layer thickness of concrete structures,which indicates that the limit state of durability failure can be defined based on strength degradation,and the calculation process was illustrated by an example.The calculated results show that the remaining compressive strength values in the durability failure limit state for the concrete structures exposed to p H=2 and 3 sulfuric acid water environments and wet-dry cyclic sulfuric acid environment with p H=2 are 74%,72%,and 80% of initialstrength,respectively.The method provides references for the durability evaluation of concrete structure design under the acidic environments.
文摘In this study, we looked at a method quantifying EEC （embodied energy and CO2） and the effect when we prolonged the building life time particularly through the durable improvement of the structure. Increasing the covering thickness of concrete for reinforcing bars and the earthquake-resistant strength are methods to increase the durability of the structure. The calculation method to obtain the quantity of concrete and reinforcing bars is provided. The EEC increase is evaluated from the 2005 input-output table in Japan. These results show that EE （embodied energy） in the construction phase is increased by 11% to 20% and EC （embodied CO2） 17% to 32%. However, annual EE is reduced 66% to 72% and EC 70% to 79%,
文摘The shajiang river bridge on the appearance test, concrete rebound detection, concrete cover depth detection, concrete carbonation depth detection, concrete chlorine ion content detection, and the detection results in statistics and analysis. Based on the bridge of the service the atmospheric environment parameters and testing data, the paper calculates and analyzes the main stress components the carbonation bridge reliability index and remaining life of carbide, assessing the bridge for the service life and reinforcement maintenance and offer the scientific basis.