Magnesium and rare earth mixed oxides（Mg3 REOx（RE=La, Y. Ce）） were prepared and characterized by Xray diffraction（XRD）, N_2 adsorption-desorption, infrared spectra and microcalorimetry of CO_2. The results revea...Magnesium and rare earth mixed oxides（Mg3 REOx（RE=La, Y. Ce）） were prepared and characterized by Xray diffraction（XRD）, N_2 adsorption-desorption, infrared spectra and microcalorimetry of CO_2. The results reveal that the Mg_3 CeO_x catalyst is present in the form of Mg-Ce-O solid solution,while the Mg3 LaOx and Mg_3 YO_x catalysts are probably rare earth oxides dispersed on MgO surface. As a result, among the calcined Mg_3 REO_x catalysts, the Mg_3 CeO_x catalyst presents the highest rate constant for acetone aldolization, which is well correlated to its more homogeneous distribution of basic sites. In contrary, the Mg_3 YO_x catalyst exhibit the lowest catalytic activity for acetone aldolization. Upon hydration pre-treatment, the basic properties on the surface of the Mg_3 REO_x catalysts were changed markedly. The Mg_3 YO_x catalyst after hydration treatment shows the highest amount of basic sites on catalyst surface, and then exhibits the highest activity among the hydrated Mg_3 REO_x catalysts. These results make it possible to fine-tune basic sites for acetone aldolization.展开更多
基金Project supported by National Basic Research Program of China(2010CB732300)111 Project(B08021)China Scholarship Council for the Joint-Training Scholarship Program with Institut de Recherches sur la Catalyse et l'Environnement de Lyon(IRCELYON)and Universite Claude Bernard Lyon 1(UCBL1)
文摘Magnesium and rare earth mixed oxides（Mg3 REOx（RE=La, Y. Ce）） were prepared and characterized by Xray diffraction（XRD）, N_2 adsorption-desorption, infrared spectra and microcalorimetry of CO_2. The results reveal that the Mg_3 CeO_x catalyst is present in the form of Mg-Ce-O solid solution,while the Mg3 LaOx and Mg_3 YO_x catalysts are probably rare earth oxides dispersed on MgO surface. As a result, among the calcined Mg_3 REO_x catalysts, the Mg_3 CeO_x catalyst presents the highest rate constant for acetone aldolization, which is well correlated to its more homogeneous distribution of basic sites. In contrary, the Mg_3 YO_x catalyst exhibit the lowest catalytic activity for acetone aldolization. Upon hydration pre-treatment, the basic properties on the surface of the Mg_3 REO_x catalysts were changed markedly. The Mg_3 YO_x catalyst after hydration treatment shows the highest amount of basic sites on catalyst surface, and then exhibits the highest activity among the hydrated Mg_3 REO_x catalysts. These results make it possible to fine-tune basic sites for acetone aldolization.