Effects of rare earth element lanthanum on the microstructure of copper matrix diamond tool materials

Effects of rare earth element La on the microstructure of Cumatrix diamond tools were researched under the conditions of variousmaterials components and the process parameters in order to improvematerials properties. SEM, XPS and X-ray were used to investigate thefracture section, microstructure and the element valence inmaterials. The Results shown that the combination of rare earthelement La and transition element Ti is advantageous to the bondingstate Between diamond particles and matrix, so it can improve thematerials properties. Suitable sintering temperature is 790 deg. C.

超细钨铜合金粉末在金刚石工具中的应用研究

采用超细钨铜合金粉末和单质钨、铜粉末热压烧结成两组金刚石胎体块,利用硬度计,排水法,万能实验机,扫描电镜和锯切实验等测试分析手段分别分析测量了胎体的硬度、致密度、抗弯强度、断口形貌和锯切性能。实验结果表明:在高钨基胎体配方中添加超细钨铜合金粉末比添加单质钨、铜粉末可以显著提高胎体的硬度10 HRB左右,改善胎体合金使之均匀化,在本实验配方中,干切硬花岗岩时,高钨基胎体配方中添加超细钨铜合金粉末比添加单质钨、铜粉末切割平稳,形成胎体和金刚石有效的磨损匹配,可以显著提高工具的使用寿命30%左右。烧结温度范围内,添加合金粉的胎体抗弯强度均比添加单质钨、铜粉末低100 MPa左右,这主要是使用的超细钨铜粉末的氧含量较高所致。

新型铁铜合金粉体材料及性能研究

为改善铁基胎体粉末在金刚石工具制造时的应用情况,通过力学实验,研究新型铁铜合金粉体材料对金刚石工具胎体抗弯强度和切割性能的影响。实验结果显示:较单质混合粉体材料,新型铁铜合金粉体材料的烧结温度略微降低;胎体在870℃时获得高的抗弯强度,为334.85 MPa,比单质混合粉高出11%;烧结硬度为61.72 HB,高于混合粉末12%。铜元素的预合金化行为和更为均匀弥散的分布,使金刚石工具胎体材料强度提高显著,切割性能大幅度上升,通过对相同配方单质混合粉末和新型铁铜合金粉末胎体材料切割性能的比较发现,新型铁铜合金粉体材料锋利度提高20%。