To provide theoretical basis and practical guidance for preparing composite rods of external diameter no larger than 12 mm by directly continuous casting,low melting point materials of lead and tin were selected to pr...To provide theoretical basis and practical guidance for preparing composite rods of external diameter no larger than 12 mm by directly continuous casting,low melting point materials of lead and tin were selected to prepare composite rods of external diameter 12 mm and inner diameter 8 mm with air pressing core filled continuous casting process.The orthogonal tests consisting of three factors and three levels were designed to investigate the parameters of melting lead temperature,continuous casting speed and air pressure that affect the performance of the composite rods.The results show that melting lead temperature is the most important factor that influences the solid/liquid interface location;continuous casting speed is the most important factor that influences the surface quality and lead and tin inter-diffusion amount;air pressure can improve the surface quality obviously and make the rods easily drawn out,but the surface quality cannot get obvious improvement when the air pressure is above 0.03 MPa.The composite rods have excellent surface quality,obvious intermediate layer,even thick clad,and metallurgical bonding interface under the condition of melting lead temperature of 375 °C,continuous casting speed of 10 mm/min,and air pressure of 0.03 MPa.展开更多
A novel statistical approach to evaluate the manufacturing quality of press coated tablets in terms of the centering of their core is presented. We also provide a formula to determine the necessary sample size. This a...A novel statistical approach to evaluate the manufacturing quality of press coated tablets in terms of the centering of their core is presented. We also provide a formula to determine the necessary sample size. This approach is applied to real data.展开更多
Friction spun core yarn has two components: filament core and staple fiber sheath. Under axial rubbing action, the failure mode of the core yarn is the stripping of the sheath from the core. This paper introduces a me...Friction spun core yarn has two components: filament core and staple fiber sheath. Under axial rubbing action, the failure mode of the core yarn is the stripping of the sheath from the core. This paper introduces a method to test the anti - stripping property of the core yarn. With a modified Universal Testing Machine, the stripping resistance of friction spun core yarn can be continuously measured. Some factors Influencing the measurements are discussed in detail. The testing results are compared with those from a Y731 Yarn Abrasion Tester and fur - ther confirmed by weaving practice.展开更多
基金Project(2009AA03Z532) supported by the National High Technology Research and Development Program of ChinaProject(50774009) supported by the National Natural Science Foundation of China
文摘To provide theoretical basis and practical guidance for preparing composite rods of external diameter no larger than 12 mm by directly continuous casting,low melting point materials of lead and tin were selected to prepare composite rods of external diameter 12 mm and inner diameter 8 mm with air pressing core filled continuous casting process.The orthogonal tests consisting of three factors and three levels were designed to investigate the parameters of melting lead temperature,continuous casting speed and air pressure that affect the performance of the composite rods.The results show that melting lead temperature is the most important factor that influences the solid/liquid interface location;continuous casting speed is the most important factor that influences the surface quality and lead and tin inter-diffusion amount;air pressure can improve the surface quality obviously and make the rods easily drawn out,but the surface quality cannot get obvious improvement when the air pressure is above 0.03 MPa.The composite rods have excellent surface quality,obvious intermediate layer,even thick clad,and metallurgical bonding interface under the condition of melting lead temperature of 375 °C,continuous casting speed of 10 mm/min,and air pressure of 0.03 MPa.
文摘A novel statistical approach to evaluate the manufacturing quality of press coated tablets in terms of the centering of their core is presented. We also provide a formula to determine the necessary sample size. This approach is applied to real data.
文摘Friction spun core yarn has two components: filament core and staple fiber sheath. Under axial rubbing action, the failure mode of the core yarn is the stripping of the sheath from the core. This paper introduces a method to test the anti - stripping property of the core yarn. With a modified Universal Testing Machine, the stripping resistance of friction spun core yarn can be continuously measured. Some factors Influencing the measurements are discussed in detail. The testing results are compared with those from a Y731 Yarn Abrasion Tester and fur - ther confirmed by weaving practice.